CN1523164A - Process for preparing disposable paper dinnerware latex paint and method of applying - Google Patents
Process for preparing disposable paper dinnerware latex paint and method of applying Download PDFInfo
- Publication number
- CN1523164A CN1523164A CNA03150969XA CN03150969A CN1523164A CN 1523164 A CN1523164 A CN 1523164A CN A03150969X A CNA03150969X A CN A03150969XA CN 03150969 A CN03150969 A CN 03150969A CN 1523164 A CN1523164 A CN 1523164A
- Authority
- CN
- China
- Prior art keywords
- monomer
- percentage
- weight
- total amount
- accounts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a latex coating for disposable paper tableware, its preparation method and its coating method. Said invention adopts the seed emulsion polymerization process to make preparation, and said process includes the following steps: adding 5-20% of mixed monomer including chlorovinylidene (VDC) into reactor still by once operation to polymerize 'seed', then adopting semi-continuous emulsion polymerization process to polymerize on the 'seed'. After the invented polyvinylidine chloride copolymerized latex coating coating is film-formed, it has high barrier property for water vapour and oxygen gas, and can resist oil and resist heat, does not cohere with viscosity foods of rice and steamed bread, and is non-toxic and smellless, and has the action of keeping freshness and keeping taste.
Description
The present invention relates to a kind of preparation method and using method of copolymer, specifically be meant preparation method and the coating process thereof of dispensable paper tableware coating with polyvinylidene chloride copolymer latex (PVDC) coating.
Technical field
Once boffo disposable foaming plastic tableware, along with the growing interest of the whole world to white pollution, oneself is disabled gradually.At present, the environment-protection type tableware that replaces disposable foaming plastic tableware mainly contains two big classes: a class is the tableware that adopts the compacting of degradation plastic material to form, and another kind of is the paper tableware that is formed by the compacting of pulp type string.With the paper tableware of common pulp production, can not directly contact succulence food and beverage.Because the residual treatment agent in can dissolving paper of the soup juice of food or beverage makes food or beverage produce peculiar smell, simultaneously, after soup juice or beverage are absorbed by paper, also can cause tableware seepage or distortion damaged.In order to overcome above-mentioned shortcoming, people adopt surface at paper tableware way compound with plastic film and that be coated with coating such as wax, PE film to solve.But viscous foodstuffs such as the scarcely high temperature resistant or easy glutinous rice of this class paper tableware, steamed bun, the original flavor that also can influence food or beverage that has, and product cost height.The paper tableware of coating PE film uses the back because paper is difficult to separate, and does not recycle basically to be worth, and causes the waste of resource.
In addition, at present, the coating process of paper tableware generally is earlier coating to be coated on whole volume to produce on the paper of paper tableware, and the paper that will the be coated with shape size that is cut into the paper tableware is made product then, cut down leftover pieces and then fall, cause waste and cost to increase as waste disposal.
Summary of the invention
Main purpose of the present invention provides a kind of preparation method of dispensable paper tableware latex paint, thereby obtain a kind of high temperature resistant, oil resistant, nontoxic, sticking food, do not influence the F﹠B taste, and cost paper tableware coating low, pollution-free, easy to use.
Another object of the present invention provides a kind of coating process of dispensable paper tableware coating, especially with the coating process of the dispensable paper tableware latex paint of method of the present invention preparation.
Purpose of the present invention mainly is achieved through the following technical solutions.
A kind of preparation method of dispensable paper tableware latex paint, concrete steps are as follows:
1. earlier 70 parts of still material deionized waters, 0.0035 part of organic peroxide, 0.00023 part of ferrous salt, 0.018 part of acetate, sodium alkyl benzene sulfonate are added in the withstand voltage reactor for 1.0 parts, thoroughly replace with nitrogen; With material heating in the still, stir simultaneously; When temperature rises to 55 ℃, the mix monomer of disposable adding 5-20% weight portion, mix monomer comprises: (a) vinylidene chloride (VDC), it accounts for the 80-94 percentage by weight of monomer total amount, (b) acrylate or methyl acrylic ester, it accounts for the 1-15 percentage by weight of monomer total amount, (c) acrylonitrile or methacrylonitrile, it accounts for the 1-10 percentage by weight of monomer total amount, (d) has the acrylic or methacrylic acid of functional group carboxyl, it accounts for the 0.5-5 percentage by weight of monomer total amount, stirs simultaneously, and squeezes in the still with measuring pump with initator (a) with (b) with continuous constant speed; Temperature in the kettle keeps 55 ℃, pressure 0.1Mpa, and when pressure descended and remains unchanged, the latex seed polymerization was finished;
2. subsequently, with continuous constant speed with the remaining described mix monomer of 80-95% weight portion and remaining described emulsifying agent, described initator (a) with (b) squeeze in the still simultaneously respectively, reaction time is 15 hours, and temperature keeps 55 ± 2 ℃, and pressure keeps 0.1 ± 0.02Mpa; After mix monomer and emulsifying agent have been beaten, continue to squeeze into described initator (a) and (b) about 1 hour, the latex polymerization reaction finishes when constant when pressure drops to; Temperature of charge in the still is risen to 65 ℃, removed residual monomer 3 hours with vacuum gas formulation; Material in the still is cooled to 35 ℃, surface tension is transferred to below the 40mN/m with the alkyl sulfonic acid sodium solution, last, filter discharging with the above stainless steel cloth of 100 orders;
As preferably, described mix monomer: monomer (a) vinylidene chloride (VDC) accounts for preferably 85-92 percentage by weight of monomer total amount; Monomer (b) acrylate or methyl acrylic ester account for preferably 2-8 percentage by weight of monomer total amount; Monomer (c) acrylonitrile or methacrylonitrile account for preferably 3-6 percentage by weight of monomer; The acrylic or methacrylic acid that monomer (d) has the functional group carboxyl accounts for preferably 1-4 percentage by weight of monomer total amount;
As preferably, described emulsifying agent is the sodium alkyl benzene sulfonate that accounts for monomer total amount 3.2 percentage by weights;
As preferably, described initator (a) is for accounting for the organic peroxide of monomer total amount 0.23 percentage by weight; Described initator (b) is for accounting for the rongalite of monomer total amount 0.12 percentage by weight.
A kind of coating process of dispensable paper tableware latex paint, concrete steps are as follows:
(1). latex paint is poured in the paper tableware that is fixed on the turntable;
(2). turntable is rotated at a high speed, the coating that fills in the paper tableware is thrown out, until getting rid of all unnecessary coating;
(3). take off the paper tableware, put it into drying in oven.
As preferably, described baking oven is the baking ovens of 110 ℃ of bands of temperature circulated air.
The present invention adopts the seed emulsion copolymerization method to prepare polyvinylidene chloride copolymer latex (PVDC) coating, and preparation is carried out in two steps: prepare latex seed 1.; 2. polymerization on latex seed.Therefore, the present invention has following characteristics:
1. adopt the preparation of seeded emulsion polymerization method, earlier what is called " seed " polymerization will be carried out in the disposable adding reactor of the mix monomer of 5-20%, on this seed, carry out the polymerization of " on the seed " then, help controlling the quantity and the size of present latex particulate, all even enough big to guarantee the present latex particulate diameter.
2. adopt the semi-continuous emulsion polymerizing method to carry out polymerization in the polymerization of " on the seed ", add mix monomer, emulsifying agent, initator to control the growth of present latex particulate, improved the stability and the filming performance of latex with continuous constant speed.
3. after adopting the polyvinylidene chloride copolymer latex coating film forming of method preparation of the present invention, has high barrier, oil resistant, heat-resisting, not viscous foodstuff such as glutinous rice, steamed bun to steam, oxygen etc.; Nontoxic odorless, and fresh-keeping, guarantor's flavor effect is arranged.Therefore, it is suitable as the coating of the paper tableware that the pulp type string makes very much, especially as the coating of viscous foodstuff papery mess tins such as splendid attire rice and steamed bun.
The specific embodiment
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment 1, and mix monomer is pre-mixed and is formed by comonomer vinylidene chloride (VDC), butyl acrylate (BA), acrylonitrile (AN), acrylic acid (AA), and latex paint component prescription is as follows:
Weight percentages of components
Still material deionized water 70
Organic peroxide 0.0035
Ferrous salt 0.00023
Acetate 0.018
Sodium alkyl benzene sulfonate 1.0
Mix monomer VDC 86.7
BA 5.0
AN 5.0
AA 3.3
Emulsifying agent deionized water 16.0
Sodium alkyl benzene sulfonate 3.2
Initator (a) deionized water 7.0
Organic peroxide 0.23
(b) deionized water 7.0
Rongalite 0.12
Earlier the still material is added in 10 liters of withstand voltage reactors of stainless steel, thoroughly replace with nitrogen.With material heat temperature raising to 55 in the still ℃, follow stirring simultaneously.When temperature rises to 55 ℃, 10% weight portion of disposable adding mix monomer, follow stirring simultaneously, and the initator (a) and (b) are squeezed in the still with measuring pump with continuous constant speed, temperature keeps 55 ℃, pressure 0.1Mpa, seeded emulsion polymerization reaction beginning this moment, when pressure began to descend and remains unchanged, the latex seed polymerization was finished.
Subsequently, mix monomer, emulsifying agent, the initator (a) and (b) of 90% weight portion that will be left with continuous constant speed are squeezed in the still respectively simultaneously.In 15 hours reaction time, temperature keeps 55 ± 2 ℃, and pressure keeps 0.1 ± 0.02MPa that mix monomer and emulsifying agent have been beaten.Continued to squeeze into initator about 1 hour, the latex polymerization reaction finishes when constant when pressure drops to.Temperature of charge in the still is risen to 65 ℃, removed residual monomer 3 hours with vacuum gas formulation.Material in the still is cooled to 35 ℃, surface tension is transferred to below the 40mN/m with the alkyl sulfonic acid sodium solution.Filter discharging with the above stainless steel cloth of 100 orders.The latex physical index that obtains is as follows:
Solid content (%) 50 ± 2
Surface tension (mN/m)≤40
Viscosity (mPaS)≤70
pH 1～3
Density (g/cm
3) 1.20～1.30
Embodiment 2: repeat embodiment 1, following difference is arranged:
Mix monomer is formed percentage by weight (%)
VDC 90
BA 6
AN 3
AA 1
The latex that obtains is fit to the surface coated of dispensable paper tableware equally.
Embodiment 3: repeat embodiment 1, following difference is arranged:
Mix monomer is formed percentage by weight (%)
VDC 88
BA 6
MAN 5
MAA 1
The latex that obtains is fit to the surface coated of dispensable paper tableware equally.
Embodiment 4: repeat embodiment 1, difference accounts for 5% of mix monomer total amount for the mix monomer amount of preparation seed, and the mix monomer amount of squeezing into subsequently accounts for 95% of mix monomer total amount, and the latex that is obtained is fit to the surface coated of dispensable paper tableware equally.
The embodiment of the coating process of dispensable paper tableware latex paint of the present invention: the paper tableware is fixed on the turntable, to pour in the paper tableware with the latex paint that preparation method of the present invention obtained, pouring volume is about 1/2nd or 2/3rds of paper tableware volume, then, turntable is rotated at a high speed, the coating that fills in the paper tableware is thrown out, until getting rid of all unnecessary coating, rotational time about 2～5 seconds; So on the inner surface of paper tableware, be coated with the very thin coating of last layer, and the coating of throwing out re-uses by the dish recovery circulation that connects on the turntable.Take off the paper tableware at last and put it into 110 ℃ of drying in oven of being with circulated airs, about 2 minutes of time.The thickness that the paper tableware is filmed can be controlled by the solid content of regulating rotary speed and latex.Characteristics such as coating process of the present invention has easy to operate, saves coating, and coating is even.
Adopt the paper tableware of the latex paint coating of the inventive method preparation to have coating film gloss good, anti-120 ℃ of greases, soak the back through boiling water and do not have infiltration, free from extraneous odour, the hot and cold F﹠B of splendid attire suits.
Claims (6)
1. the preparation method of a dispensable paper tableware latex paint is characterized in that:
(1). earlier 70 parts of still material deionized waters, 0.0035 part of organic peroxide, 0.00023 part of ferrous salt, 0.018 part of acetate, sodium alkyl benzene sulfonate are added in the withstand voltage reactor for 1.0 parts, thoroughly replace with nitrogen; With material heating in the still, stir simultaneously; When temperature rises to 55 ℃, the mix monomer of disposable adding 5-20% weight portion, mix monomer comprises: (a) vinylidene chloride (VDC), it accounts for the 80-94 percentage by weight of monomer total amount, (b) acrylate or methyl acrylic ester, it accounts for the 1-15 percentage by weight of monomer total amount, (c) acrylonitrile or methacrylonitrile, it accounts for the 1-10 percentage by weight of monomer total amount, (d) has the acrylic or methacrylic acid of functional group carboxyl, it accounts for the 0.5-5 percentage by weight of monomer total amount, stirs simultaneously, and squeezes in the still with measuring pump with initator (a) with (b) with continuous constant speed; Temperature in the kettle keeps 55 ℃, pressure 0.1Mpa, and when pressure descended and remains unchanged, the latex seed polymerization was finished;
(2). subsequently, with continuous constant speed with the remaining described mix monomer of 80-95% weight portion and remaining described emulsifying agent, described initator (a) with (b) squeeze in the still simultaneously respectively, reaction time is 15 hours, and temperature keeps 55 ± 2 ℃, and pressure keeps 0.1 ± 0.02Mpa; After mix monomer and emulsifying agent have been beaten, continue to squeeze into described initator (a) and (b) about 1 hour, the latex polymerization reaction finishes when constant when pressure drops to; Temperature of charge in the still is risen to 65 ℃, removed residual monomer 3 hours with vacuum gas formulation; Material in the still is cooled to 35 ℃, surface tension is transferred to below the 40mN/m with the alkyl sulfonic acid sodium solution, last, filter discharging with the above stainless steel cloth of 100 orders.
2. the preparation method of dispensable paper tableware latex paint according to claim 1 is characterized in that described mix monomer: monomer (a) vinylidene chloride (VDC) accounts for preferably 85-92 percentage by weight of monomer total amount; Monomer (b) acrylate or methyl acrylic ester account for preferably 2-8 percentage by weight of monomer total amount; Monomer (c) acrylonitrile or methacrylonitrile account for preferably 3-6 percentage by weight of monomer; The acrylic or methacrylic acid that monomer (d) has the functional group carboxyl accounts for preferably 1-4 percentage by weight of monomer total amount.
3. the preparation method of dispensable paper tableware latex paint according to claim 1 and 2 is characterized in that described emulsifying agent is the sodium alkyl benzene sulfonate that accounts for monomer total amount 3.2 percentage by weights.
4. the preparation method of dispensable paper tableware latex paint according to claim 1 and 2 is characterized in that described initator (a) is for accounting for the organic peroxide of monomer total amount 0.23 percentage by weight; Described initator (b) is for accounting for the rongalite of monomer total amount 0.12 percentage by weight.
5. the coating process of the latex paint of a method according to claim 1 preparation is characterized in that:
(1). latex paint is poured in the paper tableware that is fixed on the turntable;
(2). turntable is rotated at a high speed, the coating that fills in the paper tableware is thrown out, until getting rid of all unnecessary coating;
(3). take off the paper tableware, put it into drying in oven.
6. the coating process of a latex paint according to claim 5 is characterized in that described baking oven is the baking oven of 110 ℃ of bands of temperature circulated air.