CN1511872A - Nylon particle toughness increased polypropylene composite material and preparing method - Google Patents
Nylon particle toughness increased polypropylene composite material and preparing method Download PDFInfo
- Publication number
- CN1511872A CN1511872A CNA021608172A CN02160817A CN1511872A CN 1511872 A CN1511872 A CN 1511872A CN A021608172 A CNA021608172 A CN A021608172A CN 02160817 A CN02160817 A CN 02160817A CN 1511872 A CN1511872 A CN 1511872A
- Authority
- CN
- China
- Prior art keywords
- nylon
- polypropylene
- matrix material
- interfacial compatibilizer
- ester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The nylon particle toughened composite polypropylene material consists of polypropylene 40-90 (in weight portions, the same below), nylon 5-30, interface compatilizer 5-30, cross-linking agent 0.1-1.0, antioxidant 0.1-0.5 and lubricant 0.1-0.5. The preparation process includes the following steps: pre-mixing ethylene-alpha olefin copolymer and polyolefin in the ratio of 1:1.5 to 1.5:1, mixing further with grafting monomer and extruding and pelletizing in a double-screw extruder at 160-220 deg.c to obtain the interface compatilizer; pre-mixing the said materials in a stirrer and extruding and pelletizing in a double-screw extruder at 190-240 deg.c to obtain the nylon particle toughened composite polypropylene material. Owing to the synergistic effect of nylon particle and interface compatilizer, the composite material has the features of high toughness and good comprehensive performance.
Description
Technical field
The present invention relates to a kind of nylon/polypropene blended material, relate in particular to a kind of nylon particle toughened polypropylene composite.
The invention still further relates to the preparation method of above-mentioned materials.
Background technology
Polypropylene material is big, cheap because of its annual production, good combination property, and density is little, and advantages such as easy-formation are widely used in a lot of industries such as household electrical appliances, automobile, building materials, agricultural by people.But, limited the application of polypropylene material as structured material because polypropylene material exists poor toughness, low these two the topmost shortcomings of modulus.
The blend method that adds other polymkeric substance in polypropylene is to improve one of polypropylene material flexible main method.Add rubber-like elastomerics and the polypropene blended toughness that can effectively improve polypropylene material, but can cause the modulus of polypropylene material to be even lower; Add high performance polymer such as nylon with it blend can effectively keep or improve the modulus of polypropylene material, but the toughness that whether can improve polypropylene material then depends on both consistency and the form of high-performance polymer in polypropylene matrix.
Gonzalez-Montiel, people such as A. have reported the method for styrene-butadiene rubber(SBR) (SBR) the raising nylon 6/ polypropene blended toughness of material of the ethene-acrylic rubber (EPR) that adds maleation and maleation in " Polymer Material Science andEngineering " 1993 the 70th volume 194-195 page or leaf.
Kim, G.M. and Michler, G.H. wait the people in " Polymer Advance Technology " 1998 the 9th volumes 10-11 phase 709-715 page or leaf and " Acta Polymer " 1998 the 49th volumes 2-3 phase 88-95 page or leaf, to report the styrene-ethylene-1-butylene segmented copolymer (SEBS-g-MA) that in polypropylene/nylon (70/30vol.%), adds maleic anhydride graft, formation is shell with SEBS-g-MA rubber, and nylon is the i.e. nuclear-shell particles method of coming flexibilized polypropylene material of nuclear.
All be to adopt graft rubber in the prior art, improve the consistency of nylon and polypropylene matrix on the one hand as interfacial compatibilizer, the surface that is present in the polypropylene matrix as disperse phase on the other hand or is coated on the nylon disperse phase forms nylon-rubber " nuclear-shell " particle, flexibilized polypropylene material.Because rubber can produce crosslinked because of the effect of initiator, heat or shearing force etc. in the grafting process, partial cross-linked graft rubber is with polypropylene, nylon blending the time, it is even to be difficult to redispersion in polypropylene matrix, can not form thin and uniform shell on nylon disperse phase surface, thus poor to the toughening effect of polypropylene material.
Summary of the invention
The object of the present invention is to provide a kind of nylon particle toughened polypropylene composite.
Another purpose of the present invention is to provide the preparation method of above-mentioned materials.
For achieving the above object, the invention provides the interfacial compatibilizer that a kind of and polypropylene and nylon all have excellent compatibility, with the polypropylene matrix blend time, interfacial compatibilizer can be at the thin and shell uniformly of nylon disperse phase surface formation on the throne; A kind of linking agent is provided simultaneously, can the shell of interfacial compatibilizer is on the throne partial cross-linked.
Nylon particle toughened polypropylene composite provided by the invention is made up of following component and content thereof, and its content is in weight part:
Polypropylene 40-90
Nylon 5-30
Interfacial compatibilizer 5-30
Linking agent 0.1-1.0
Oxidation inhibitor 0.1-0.5
Lubricant 0.1-0.5
Described polypropylene is homo-polypropylene, Co-polypropylene, and its melt flow rate is 0.1-30.0 gram/10 minutes, and optimum content is the 50-70 weight part.
Described nylon is nylon 6, nylon 66, nylon 1010, and its melt flow rate is 0.1-10.0 gram/10 minutes, and optimum content is the 15-30 weight part.
Described interfacial compatibilizer is the alpha olefin copolymer of ethene-4-10 carbon atom and the grafts of polyolefin blends, its melt flow rate is 0.5-15 gram/10 minutes, the blend ratio is 1: 1.5-1.5: 1, the grafting group is the functional group that can produce chemical reaction with nylon, be specially MALEIC ANHYDRIDE, vinylformic acid, methacrylic acid or methylene-succinic acid etc., the optimum content of interfacial compatibilizer is the 5-20 weight part.
Described linking agent is bifunctional Resins, epoxy, polyfunctional epoxy resin.
Described oxidation inhibitor is four [β-(3,5-di-tert-butyl-4-hydroxy phenyl) propionic acid] pentaerythritol ester, 1,1,3-three (2-methyl-4-hydroxyl-5-t-butyl-phenyl) butane, 4,4-thiobis (6-tertiary butyl-3-methylphenol), tetramethylolmethane diphosphite two (2,4-di-tert-butyl phenyl) compound of one or more in ester, tricresyl phosphite (2, the 4-di-tert-butyl phenyl) ester etc.
Described lubricant is one or more in petroleum resin, Poly Propylene Wax, polyethylene wax, solid paraffin, whiteruss, naphthenic oil, laurate, oleic acid ester, oleic acid, stearate, stearic acid and salt such as the calcium stearate etc.
The preparation method of nylon particle toughened polypropylene composite of the present invention in turn includes the following steps:
(1) with ethylene-alpha-olefin copolymer and polyolefine in 1: 1.5-1.5: 1 ratio is pre-mixed, mix with grafted monomer again, on the twin screw extruder with 160-220 ℃ processing temperature under grafting, granulation obtain interfacial compatibilizer.
(2) with the lubricant of the oxidation inhibitor of the linking agent of the interfacial compatibilizer of the nylon of the polypropylene of 40-90 part, 5-30 part, 5-30 part, 0.1-1.0 part, 0.1-0.5 part, 0.1-0.5 part in homogenizer after the pre-mixing, on twin screw extruder 190-240 ℃ extrude, granulation, obtain nylon particle toughened polypropylene composite.
Although do not plan to be confined to theoretic explanation, the mechanism that the present invention may exist is as follows:
Because interfacial compatibilizer is the grafts of ethylene-alpha-olefin copolymer and polyolefin blends, very similar to the polypropylene matrix molecular chain structure, interfacial compatibilizer and polypropylene matrix consistency are good; Behind the grafting polar group with the nylon molecular chain in amino can produce chemical reaction, increase with consistency on the nylon interface; The raising of consistency impels the discrete particles degree of nylon particle in polypropylene matrix to diminish, and is uniformly dispersed.Owing to all do not contain unsaturated link(age) on the molecular chain of contained two components in the interfacial compatibilizer, in the grafting process, be not easy to produce crosslinking reaction, therefore with polypropylene, nylon blending the time, easily disperse, easily uniform coating layer is a shell in that the formation of nylon surface is thin, and this shell makes the nylon particle can produce deformation when material is subjected to impacting.By linking agent crosslinked established shell on the throne when the blend, increase the deformability and the tearing toughness of nylon granule sub-surface shell.But have under deformation, the synergy at nylon particle and surface thereof, cause polypropylene matrix and produce shear zone, thereby the toughness of polypropylene material is greatly improved in conjunction with good interface compatilizer shell.
Nylon particle toughened polypropylene composite toughness height of the present invention, good combination property.
The present invention will be further described below in conjunction with embodiment, and wherein embodiment 1-3 is the embodiment that carries out according to the present invention, and embodiment 4-6 is not for adding the interfacial compatibilizer of grafting group, and embodiment 7-8 is not for adding any interfacial compatibilizer, with this as a comparison.
Embodiment 1
Ethylene-alpha-olefin copolymer and the new LDPE (film grade) ratio in 1: 1.5 is pre-mixed, mix with MALEIC ANHYDRIDE again, on the twin screw extruder with 200-220 ℃ processing temperature under grafting, granulation obtain the MALEIC ANHYDRIDE graftomer as interfacial compatibilizer.
With 64 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.3 part polyfunctional epoxy resin, 0.1 part tetramethylolmethane diphosphite two (2 of 6,6 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain nylon particle toughened polypropylene composite.The mechanical performance data of gained material sees Table 1.
Embodiment 2
Interfacial compatibilizer is identical with embodiment 1.
With 52 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.3 part polyfunctional epoxy resin, 0.1 part tetramethylolmethane diphosphite two (2 of 6,18 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder by 230-240 ℃ processing temperature extrude, water-cooled, granulation, obtain nylon particle toughened polypropylene composite.The mechanical performance data of gained material sees Table 1.
Embodiment 3
Interfacial compatibilizer is identical with embodiment 1.
With 40 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.3 part polyfunctional epoxy resin, 0.1 part tetramethylolmethane diphosphite two (2 of 6,30 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder by 230-240 ℃ processing temperature extrude, water-cooled, granulation, obtain nylon particle toughened polypropylene composite.The mechanical performance data of gained material sees Table 1.
Embodiment 4
Ethylene-alpha-olefin copolymer and the new LDPE (film grade) ratio in 1: 1.5 is pre-mixed, extrude under with 200-220 ℃ processing temperature on the twin screw extruder, granulation obtains blend as interfacial compatibilizer.
With 64 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.1 part tetramethylolmethane diphosphite two (2 of 6,6 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain polypropylene/nylon blending material.The mechanical performance data of gained material sees Table 1.
Embodiment 5
Interface modifier is identical with embodiment 4.
With 52 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.1 part tetramethylolmethane diphosphite two (2 of 6,18 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain polypropylene/nylon blending material.The mechanical performance data of gained material sees Table 1.
Embodiment 6
Interface modifier is identical with embodiment 4.
With 40 parts homo-polypropylene, 30 parts the interfacial compatibilizer, 0.1 part tetramethylolmethane diphosphite two (2 of 6,30 parts of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain polypropylene/nylon blending material.The mechanical performance data of gained material sees Table 1.
Embodiment 7
With 70 parts homo-polypropylene, 30 parts the tetramethylolmethane diphosphite two (2 of 6,0.1 part of nylon, 4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain polypropylene/nylon blending material.The mechanical performance data of gained material sees Table 1.
Embodiment 8
With 100 parts homo-polypropylene, 0.1 part tetramethylolmethane diphosphite two (2,4-di-tert-butyl phenyl) ester, 0.2 part calcium stearate, in homogenizer after the pre-mixing, on twin screw extruder in 230-240 ℃ extrude, water-cooled, granulation, obtain polypropylene material.The mechanical performance data of gained material sees Table 1.
Table 1, polypropylene/nylon composite materials mechanical property
Notched Izod impact strength (J/m) | Modulus in flexure (GPa) | Flexural strength (MPa) | Tensile strength (MPa) | Elongation at break (%) | |
Embodiment 1 | ????23.8 | ????1.2 | ????50.8 | ????39.7 | ????32.2 |
Embodiment 2 | ????109.0 | ????0.8 | ????33.3 | ????30.2 | ????182.2 |
Embodiment 3 | ????182.5 | ????0.5 | ????22.2 | ????24.1 | ????435.6 |
Embodiment 4 | ????36.0 | ????1.2 | ????41.7 | ????34.1 | ????18.6 |
Embodiment 5 | ????48.0 | ????1.0 | ????37.1 | ????28.9 | ????19.2 |
Embodiment 6 | ????70.5 | ????0.7 | ????32.9 | ????26.6 | ????78.5 |
Embodiment 7 | ????32.5 | ????1.4 | ????48.0 | ????36.9 | ????16.9 |
Embodiment 8 | ????12.3 | ????1.1 | ????45.2 | ????36.1 | ????655.0 |
Claims (12)
1, a kind of nylon particle toughened polypropylene composite, its component and content are as follows, and wherein content is in weight part:
Polypropylene 40-90; Nylon 5-30; Interfacial compatibilizer 5-30; Linking agent 0.1-1.0; Oxidation inhibitor 0.1-0.5; Lubricant 0.1-0.5.
2, according to the matrix material of claim 1, it is characterized in that: described polypropylene is homo-polypropylene or Co-polypropylene, and its melt flow rate is 0.1-30.0 gram/10 minutes.
3, matrix material according to claim 1 and 2 is characterized in that: described polyacrylic content is the 50-70 weight part.
4, according to the matrix material of claim 1, it is characterized in that: described nylon is nylon 6, nylon 66 or nylon 1010, and its melt flow rate is 0.1-10.0 gram/10 minutes.
5, according to claim 1 or 4 described matrix materials, it is characterized in that: the content of described nylon is the 15-30 weight part.
6, according to the matrix material of claim 1, it is characterized in that: described interfacial compatibilizer is the alpha olefin copolymer of ethene-4-10 carbon atom and the grafts of polyolefin blends, its melt flow rate is 0.5-15 gram/10 minutes, and the blend ratio is 1: 1.5-1.5: 1.
7, matrix material according to claim 6 is characterized in that: described grafting group is MALEIC ANHYDRIDE, vinylformic acid, methacrylic acid or methylene-succinic acid.
8, matrix material according to claim 1 is characterized in that: the content of described interfacial compatibilizer is the 5-20 weight part.
9, according to the matrix material of claim 1, it is characterized in that: described linking agent is bifunctional Resins, epoxy or polyfunctional epoxy resin.
10, according to the matrix material of claim 1, it is characterized in that: described oxidation inhibitor is four [β-(3,5-di-tert-butyl-4-hydroxy phenyl) propionic acid] pentaerythritol ester, 1,1,3-three (2-methyl-4-hydroxyl-5-t-butyl-phenyl) butane, 4, the compound of one or more in 4-thiobis (6-tertiary butyl-3-methylphenol), tetramethylolmethane diphosphite two (2,4-di-tert-butyl phenyl) ester, tricresyl phosphite (2, the 4-di-tert-butyl phenyl) ester.
11, according to the matrix material of claim 1, it is characterized in that: described lubricant is one or more in petroleum resin, Poly Propylene Wax, polyethylene wax, solid paraffin, whiteruss, naphthenic oil, laurate, oleic acid ester, oleic acid, stearate, stearic acid and the salt thereof.
12, a kind of preparation matrix material as claimed in claim 1, its key step is as follows:
A) with ethylene-alpha-olefin copolymer and polyolefine in 1: 1.5-1.5: 1 ratio is pre-mixed, and mixes with grafted monomer again, obtains interfacial compatibilizer in 160-220 ℃ of grafting, granulation on twin screw extruder;
B) in proportion in stirrer after the pre-mixing, on twin screw extruder in 190-240 ℃ extrude, granulation, obtain nylon particle toughened polypropylene composite.