CN1508157A - Metallocene titanium compound and use thereof - Google Patents
Metallocene titanium compound and use thereof Download PDFInfo
- Publication number
- CN1508157A CN1508157A CNA02137452XA CN02137452A CN1508157A CN 1508157 A CN1508157 A CN 1508157A CN A02137452X A CNA02137452X A CN A02137452XA CN 02137452 A CN02137452 A CN 02137452A CN 1508157 A CN1508157 A CN 1508157A
- Authority
- CN
- China
- Prior art keywords
- titanium compound
- metallocene titanium
- cyclopentadienyl
- metallocene
- mmole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a metallocene titanium compound and its application, and is aimed at mainly resolving the problems of low catalytic efficiency and difficult adaptability for industrial requirement when the previous metallocene titanium compound is used for styrene syndiotactic polymerization. Said invention utilizes the technical scheme which adopts the metallocene compound whose structure general formula is R1Ti(O-C6H4-NR*2)3, R1 is cyclopentadinyl or cyclopentadingl containing 1-5 C1-4 alkyl groups, C6H4 is phenyl group, R is hydrogen or methyl and between Ti and R* the oxygen atom is connected and alkyl aluminoxythane to form the catalyst so as to resolve the above-mentioned problems. It can be used in industrial production of styrene syndiotactic polymerization.
Description
Technical field
The present invention relates to metallocene titanium compound and uses thereof.
Background technology
The homogeneous catalysis system that cyclopentadiene titanium compound and promotor methylaluminoxane (MAO) or boron fluorine cpd are formed is used for syndiotactic polymerization of phenylethylene and can obtains a normality at the syndiotactic polymer more than 96%.Melting point polymer is up to 270 ℃, and crystallization velocity is fast, chemically-resistant, and good heat resistance, narrow molecular weight distribution, dimensional stability is good, and has excellent electric performance, and its over-all properties can be compared with engineering plastics.The appearance of syndiotactic polystyrene (SPS) has caused people to its catalyst system, particularly the research of Primary Catalysts metallocene compound.Document US 5252693 and EP210615 have reported that structure is CpTiCl
3And Cp
*TiCl
3The catalyst system of forming with promotor MAO is used for the situation of syndiotactic polymerization of phenylethylene, and wherein CP is a cyclopentadienyl, Cp
*Be the pentamethyl-cyclopentadienyl, but its catalytic activity and catalytic efficiency are not high, poor stability, industrial application value is little.Patent US4978730, US5023222, US5045517 and US5196490 have reported the high CpTi of present catalytic efficiency (OR)
3And Cp
*Ti (OR)
3Type catalyzer (R is an alkyl or aryl), specific activity had raising in the past, but from industry distance need be arranged still.
Summary of the invention
One of technical problem to be solved by this invention is that the cyclopentadiene titanium compound catalytic activity that overcomes in the document in the past is lower, from industrial requirement the problem of gap is arranged still, and a kind of new metallocene titanium compound is provided.This compound and alkylaluminoxane are or/and the catalyst system that aluminum alkyls is formed when being used to prepare syndiotactic polystyrene, has the high characteristics of catalytic activity.Two of technical problem to be solved by this invention is purposes of above-mentioned metallocene titanium compound.
For one of solving the problems of the technologies described above, the technical solution used in the present invention is as follows: a kind of metallocene titanium compound, and its structure has following general formula:
R
1Ti(O-C
6H
4-NR
* 2)
3
R in the formula
1For cyclopentadienyl or contain 1~5 C
1~4The cyclopentadienyl of alkyl;
R
*Be hydrogen or methyl;
Wherein Ti and R
*Between have Sauerstoffatom to link to each other.
In the technique scheme, R
1Preferred version is cyclopentadienyl or pentamethyl-cyclopentadienyl, and more preferably scheme is the pentamethyl-cyclopentadienyl.Be phenyl ring between O and the N atom, NR
* 2For adjacent, or para-orientation, preferred version is a para-orientation.
For solve the problems of the technologies described above two, the technical solution used in the present invention is as follows: above-mentioned metallocene titanium compound is used for the preparation of syndiotactic polystyrene.
Metallocene titanium compound preparation method of the present invention is in the presence of chlorine hydride absorbent to be that the reaction of solvent obtains with the hydrocarbon polymer by corresponding cyclopentadienyl titanous chloride and substituted phenol.Chlorine hydride absorbent can be various aminated compoundss, and wherein trialkylamine is advisable, for example triethylamine.Hydrocarbon polymer can be aliphatic hydrocarbon or aromatic hydrocarbon, uses aromatic hydrocarbons better, benzene for example, toluene, dimethylbenzene etc.The mole ratio of cyclopentadienyl titanous chloride and hydroxyl is 1: 3.0~3.5, the mole ratio of cyclopentadienyl titanous chloride and triethylamine is 1: 3.0~4.0, temperature of reaction is 1~130 ℃, preferably 30~80 ℃, reaction times is 2~48 hours, best 6~24 hours, reaction process was preferably used intermittently heating operation.
During as the Syndiospecific Polymerization of Styrene catalyzer, its catalytic efficiency reaches as high as 400 kg of polymer/gram titanium to compound of the present invention, has obtained better technical effect with alkylaluminoxane.
Work as R
1Be pentamethyl-cyclopentadienyl, R
*Structural formula of compound is during for hydrogen: (A)
Work as R
1Be pentamethyl-cyclopentadienyl, R
*Structural formula of compound is during for methyl: (B)
Learn that through hydrogen nuclear magnetic resonance spectrogram and infrared spectra map analysis structure is the said structure formula.Its data are as follows:
Ultimate analysis (element analysis)
C
28H
33O
3N
3Ti:(A)
Calcd.For
C 66.30%
H 6.51%
Found
C 66.05%
H 6.79%
[HNMR?CDCl
3?TMS?intern]
δ6.75~7.25(m,12H,-(OPhH)
3)
δ1.90~2.15(s,15H,Cp-CH
3)
δ3.50~3.65(s,6H,-NH
2)
C
34H
45O
3N
3Ti:(B)
Calcd.For
C 69.06%
H 7.62%
Found
C 68.75%
H 7.79%
The proton nmr spectrum
[HNMR?CDCl
3?TMS?intern]
δ6.55~7.55(m,12H,-(OPhH)
3)
δ2.10~2.45(s,15H,Cp-CH
3)
δ2.80~3.20(s,18H,N-CH
3)
The invention will be further elaborated below by embodiment.
Embodiment
[embodiment 1]
The metallocene titanium compound preparation
In the there-necked flask of 250 milliliters of exsiccant, N
2Pump drainage 3 times adds the 1.41 single luxuriant titanium of gram pentamethyl-trichlorine and 100 milliliters of benzene, 1.62 gram p-aminophenol, vigorous stirring dissolving, mixture from 30 milliliters of benzene of top dropping and 1.5 gram triethylamines dripped off after 45 minutes, after the normal-temperature reaction 1 hour, reheat reacts after 2 hours to the benzene reflux temperature, stop heating, normal-temperature reaction 10 hours, reacting by heating is 2 hours once more, filter, filtrate is drained, and uses toluene, hexane solution recrystallization repeatedly, drain, get yellow crystals 1.92 grams, yield 78%.
[embodiment 2]
The metallocene titanium compound preparation
In the there-necked flask of 250 milliliters of exsiccant, N
2Pump drainage 3 times adds the 1.433 single luxuriant titanium of gram pentamethyl-trichlorine and 70 milliliters of benzene, from 0 milliliter of benzene of top Dropwise 5,2.0 gram drips off reacting by heating 4 hours to the mixture of dimethylamino phenol and 1.47 gram triethylamines after 45 minutes, normal-temperature reaction is 10 hours again, reacting by heating 4 hours is once more filtered at last, and filtrate is drained, use hexane extraction, drain, get yellow crystals 2.36 grams, productive rate 81%.
[embodiment 3]
On in baking, 50 milliliters of two mouthfuls of bottles of exsiccant, use high-purity N
2Pump drainage 3 times, add 10 milliliters of commercial benzene vinyl monomers, induction stirring was injected triisobutyl aluminium 0.2 mmole with syringe after 20 minutes in 60 ℃ of oil baths, MAO 0.4 mmole, the metallocene titanium compound 0.001 mmole reaction of embodiment 1 with ethanol-hydrochloric acid soln stopped reaction, was washed after 10 minutes, dry that powder solid 3.01 restrains, catalytic activity 375 kg of polymer/(the gram titanium. hour), a normality 96%, Mw=39 * 10
4
[embodiment 4]
On in baking, 50 milliliters of two mouthfuls of bottles of exsiccant, use high-purity N
2Pump drainage 3 times, add 10 milliliters of commercial benzene vinyl monomers, induction stirring was injected triisobutyl aluminium 0.2 mmole with syringe after 20 minutes in 60 ℃ of oil baths, MAO 0.6 mmole, the metallocene titanium compound 0.001 mmole reaction of embodiment 2 with ethanol-hydrochloric acid soln stopped reaction, was washed after 10 minutes, dry that powder solid 3.17 restrains, catalytic activity 402 kg of polymer/(gram titanium hour), a normality 97%, Mw=34 * 10
4
[comparative example 1]
On in baking, 50 milliliters of two mouthfuls of bottles of exsiccant, use high-purity N
2Pump drainage 3 times adds 10 milliliters of commercial benzene vinyl monomers, and induction stirring was injected triisobutyl aluminium 0.4 mmole with syringe after 20 minutes in 60 ℃ of oil baths, and MAO is mmole O.4, Cp
*TiCl
30.001 mmole reaction (Cp after 10 minutes
*Be the pentamethyl-cyclopentadienyl), with ethanol-hydrochloric acid soln stopped reaction, washing, dry powder solid 0.41 gram, catalytic activity 51 kg of polymer/(gram titanium hour), a normality 94%, Mw=15 * 10
4
[embodiment 5]
On 10 liters of mechanical stirring kettles, after 8 hours, be cooled to 60 ℃, N 90 ℃ of bakings earlier
2Pump drainage 3 times adds styrene monomer 2375 grams, stirs after 30 minutes, contain 52.8 mmole triisobutyl aluminiums with the syringe injection, 105.6 mmole MAO, the metallocene titanium compound toluene solution of 0.264 mmole embodiment 1 is at 300 rev/mins of following stirring reactions after 3 hours, with ethanol-hydrochloric acid soln stopped reaction, washing, dry that powder solid 1400 restrains catalytic efficiency 110 kg of polymer/(gram titanium), between normality 97%, Mw=40 * 10
4
[embodiment 6]
On 10 liters of mechanical stirring kettles, after 8 hours, be cooled to 60 ℃, N 90 ℃ of bakings earlier
2Pump drainage 3 times adds styrene monomer 2375 grams, stirs after 30 minutes, contain 52.8 mmole triisobutyl aluminiums with the syringe injection, 105.6 mmole MAO, the metallocene titanium compound toluene solution of 0.264 mmole embodiment 2 is at 300 rev/mins of following stirring reactions after 3 hours, with ethanol-hydrochloric acid soln stopped reaction, washing, dry that powder solid 1457 restrains catalytic efficiency 114 kg of polymer/(gram titanium), between normality 97%, Mw=41 * 10
4
Claims (7)
1, a kind of metallocene titanium compound, its structure has following general formula:
R
1Ti(O-C
6H
4-NR
* 2)
3
R in the formula
1For cyclopentadienyl or contain 1~5 C
1~4The cyclopentadienyl of alkyl;
R
*Be hydrogen or methyl;
Wherein Ti and R
*Between have Sauerstoffatom to link to each other.
2, according to the described metallocene titanium compound of claim 1, it is characterized in that R
1Be cyclopentadienyl or pentamethyl-cyclopentadienyl.
3, according to the described metallocene titanium compound of claim 2, it is characterized in that R
1Be the pentamethyl-cyclopentadienyl.
4,, it is characterized in that being between O and the N atom phenyl ring according to the described metallocene titanium compound of claim 1.
5, according to the described metallocene titanium compound of claim 4, it is characterized in that NR
* 2For adjacent, or para-orientation.
6, according to the described metallocene titanium compound of claim 5, it is characterized in that NR
* 2Be para-orientation.
7, be used for the preparation of syndiotactic polystyrene according to the described metallocene titanium compound of claim 1.