CN1493758A - Processing method of high-density glass fiber board - Google Patents
Processing method of high-density glass fiber board Download PDFInfo
- Publication number
- CN1493758A CN1493758A CNA031528651A CN03152865A CN1493758A CN 1493758 A CN1493758 A CN 1493758A CN A031528651 A CNA031528651 A CN A031528651A CN 03152865 A CN03152865 A CN 03152865A CN 1493758 A CN1493758 A CN 1493758A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- fiber board
- thickness
- processing method
- shaping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A high-density glass fiber board relates to the processing technology of new indoor decoration materials, in particular to the hot curing forming process technology of the glass fiber board, which mainly comprises the following steps: weighing; paving the glass fiber to a required thickness, and spraying a resin adhesive; automatic heat curing, shaping, treating and shaping; cutting edges, taking out the shaped fiber board, and cutting edges according to a set size to obtain the fiber board. The processing method is simple, convenient and reliable, has high production efficiency, can process the glass fiber plate with the thickness of 1-5 cm, and has flat and smooth surface and uniform thickness, and the flatness can reach +/-0.5 mm. Has better sound absorption, heat insulation and flame retardant effects and excellent sinking resistance. The composite material is suitable for places such as hotels, exhibition halls, office buildings, movie theaters and the like, and is used for indoor decoration ceiling, wall boards and the like.
Description
Technical field
The high-density glass fiberboard relates to interior decoration new material process technology, relates in particular to glass wool board heat cure forming technology technology.
Background technology
Domestic indoor is decorated main at present adopt flat fibreboard made, gypsum plank, mineral wool board etc., make indoor suspended ceiling, wallboard for reclaiming the glass fiber material made from discarded glass, also useful automatic production line mask-making technology, but its cost height, have that carrier bar is that coarse injustice, thickness are irregular, surface finish and hardness all can not reach the use needs, and is second-rate.
Technical scheme
The purpose of this invention is to provide a kind of certain thickness that has, the high-density glass fiberboard processing method of certain degree of hardness and planeness.
Processing method of the present invention is as follows:
1.1 weighing by required sheet thickness, claims the cotton-shaped glass fiber of constant weight;
1.2 pave glass fiber to desired thickness (fixed by weight), blown resin bonding adhesive;
1.3 the heat cure typing is handled automatically, with two clampings of glass fiber that the black iron plate will spray resin adhesive, sends into the hydraulic press of the heating of existing uniform temperature, temperature is 200~250 ℃, and stoving time 20~40 minutes carries out the heat cure typing;
Handle 1.4 cut the limit, take out the fiberboard of having finalized the design, make by setting the size cutting edge.
Simple and convenient processing method of the present invention, reliable, the production efficiency height can be processed the glass wool board that thickness is 1~5cm, and plate surface is smooth, smooth, thickness is even, glacing flatness Da Keda ± 0.5mm.Have better sound-absorbing, heat insulation, flame retardant effect, the anti-property of sinking is superior.Be applicable to places such as hotel, hotel, museum, office building, cinema, be used for interior decoration suspended ceiling, wallboard etc.
Specific embodiment
Weighing, glass fiber 150g/m
3Being pressed into thickness is the high-density glass fiberboard of 2cm, after spraying coating, add the black iron plate, send in 300 t hydraulic press that have uniform temperature, through being steam heated to 200~250 ℃, extract iron plate out, stoving time 20~40 minutes, carry out the heat cure typing, carry out the surrounding by the finished product dimensional requirement then and cut the limit processing.
Claims (1)
1, the processing technology of high-density glass fiberboard, its feature may further comprise the steps:
1.1 weighing by required sheet thickness, claims the cotton-shaped glass fiber of constant weight;
1.2 pave glass fiber to desired thickness (fixed by weight), blown resin bonding adhesive;
1.3 the heat cure typing is handled automatically, with two clampings of glass fiber that the black iron plate will spray resin adhesive, sends into the hydraulic press of the heating of existing uniform temperature, temperature is 200~250 ℃, and stoving time 20~40 minutes carries out the heat cure typing;
Handle 1.4 cut the limit, take out the fiberboard of having finalized the design, make by setting the size cutting edge.