CN1487010A - Non-asbestos stool plate and its making process - Google Patents
Non-asbestos stool plate and its making process Download PDFInfo
- Publication number
- CN1487010A CN1487010A CNA031388736A CN03138873A CN1487010A CN 1487010 A CN1487010 A CN 1487010A CN A031388736 A CNA031388736 A CN A031388736A CN 03138873 A CN03138873 A CN 03138873A CN 1487010 A CN1487010 A CN 1487010A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- backing plate
- seal backing
- asbestos
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The sealing non-asbestos stool plate is produced with the material including Twaron fiber, Rs440 fiber, oil resistant rubber, stuffing, rubber assistant and solvent. The preparation process includes mixing oil resistant rubber, stuffing, rubber assistant and solvent in certain proportion through stirring for 30-60 min, adding Rs440 fiber via stirring for 40-80 min, adding Twaron fiber via stirring for 40-80 min, adding co-volatiling agent solution via stirring for 30-40 min; sheeting and final sulfurizing. The sealing non-asbestos stool plate has no environmental pollution, simple preparation process, and high performance.
Description
(1) technical field:
The present invention relates to the sealed bolster plate technical field, is a kind of non-asbestos grommet type seal plate and preparation method thereof specifically.
(2) background technology:
Sealed bolster plate is as nonmetal primary gasket material, be widely used in industries such as automobile, oil, chemical industry, electric power, machinery, used sealed bolster plate is the asbestos backing plate, but there is stronger environmental pollution in the asbestos backing plate, along with the enhancing of environmental consciousness, the improvement of living environment obtains people's great attention, in addition along with the fast development of science and technology, use properties to sealed bolster plate requires more and more harshness, thereby a kind of non-asbestos grommet type seal plate of excellent property was not seen at present.
(3) summary of the invention:
Purpose of the present invention is intended to overcome the deficiency of above-mentioned prior art, and a kind of non-asbestos grommet type seal plate of excellent property is provided.
Another object of the present invention provides a kind of preparation method of non-asbestos seal backing plate.
The present invention has mainly solved existing asbestos seal backing plate problem of environment pollution caused.
In order to achieve the above object, the present invention is achieved in that a kind of non-asbestos seal backing plate, it is to make Twaron fiber 3-5 part, Rs440 fiber 20-48 part, oil resisting rubber 10-16 part, weighting agent 38-44 part, rubber ingredients 6-10 part, solvent 6-10 part by the following weight proportion raw material.
A kind of non-asbestos seal backing plate of the present invention, its described rubber ingredients are strengthening agent, vulcanizing agent, promotor, anti-aging agent, activator, can adopt conventional proportioning.
A kind of non-asbestos seal backing plate of the present invention, the optimum weight proportioning of its described raw material is 4 parts of Twaron fibers, 35 parts of Rs440 fibers, 13 parts of oil resisting rubbers, 40 parts of weighting agents, 2 parts of strengthening agents, 1 part of vulcanizing agent, 2 parts of promotor, anti-aging agent L part, 4 parts in activator, 8 parts of solvents.
A kind of non-asbestos seal backing plate of the present invention, its described oil resisting rubber is a paracril, weighting agent is kaolin, lime carbonate, strengthening agent is white carbon black, vulcanizing agent is sulphur, TMTD, and promotor is M, DM, TMTD, and anti-aging agent is anti-aging agent J, BLE, activator is zinc oxide, stearic acid, and solvent is a toluene.
A kind of non-asbestos seal backing plate of the present invention also can add and help volatilizer solution, and the weight proportion that helps volatilizer solution is 8 parts, and the volatilizer solution that helps of adding is ethanol, and concentration is 70-80%.
The preparation method of any one non-asbestos seal backing plate of the present invention, its complete processing is as follows:
A, spice, oil resisting rubber, rubber ingredients, weighting agent in the spice machine after the adding weighing, and add solvent, stir 30-60min;
Add the Rs440 fiber and stir 40-80min;
Add the Twaron fiber and stir 40-80min;
Add and help volatilizer solution stirring 30-40min;
B becomes to open, and the big roll temperature of Cheng Zhangji is risen, and when reaching 90-110 ℃, adjusts baffle plate and hangs cladding, drops into aniseed then, carries out blanking, after aniseed has descended, hangs outer material, then stops and cuts plate;
C, sulfuration adopts vulcanizer to vulcanize, and sulfuration process is as follows: curing temperature 110-130 ℃, curing time 15-25min, sulfide stress 0.5-2Mpa.
The Twaron fiber that a kind of non-asbestos seal backing plate of the present invention is adopted is produced by Dutch Nobel company; The Rs440 fiber that adopts is produced by Dutch lapinus company, and its characteristic is: 1, inorganic nature; 2, thermotolerance: 〉=700 ℃ (1300); 3, in rubber or solvent, easily disperse, easily mix in the short period of time; 4, easily reaction, by with rubber cross, form fine and close fibre network, thus with mechanical property that has improved sheet material and anti-loose property; 5, nonflammable, be difficult for oxidation, can improve the wearing quality and the stopping property of sheet material; 6, the fibre content height in the sheet material, because this fiber and rubber or solvent have good affinity, the fiber that makes content in sheet material can reach 40%, can improve the resistance against compression of high sheet material and can reduce loose property with this, when ageing of rubber, more high-load fiber can guarantee good sealing property.
The main physicochemical property of non-asbestos seal backing plate of the present invention:
| Project name | Test data | |
| Transverse tensile strength MPa 〉= | ????10 | |
| Density g/cm 3 | ????1.8±0.2 | |
| 550 ℃ * 1h of loss on ignition %≤ | ????40 | |
| 100 ℃ * 22h of stress relaxation rate %≤ | ????25 | |
| Rate of compression % | ????12±5 | |
| Rebound degree % 〉= | ????45 | |
| ASTMNO.1?OLL 150℃×5h | Thicken rate %≤ | ????10 |
| Weight rate %≤ | ????10 | |
| ASTMNO.1?OLL 150℃×5h | Thicken rate %≤ | ????15 |
| Weight rate %≤ | ????15 | |
| Rate of compression % | ????12±5 | |
| Rebound degree % 〉= | ????40 | |
| Transverse tensile strength MPa 〉= | ????7 | |
| ASTM Fuel:B normal temperature * 5h | Thicken rate %≤ | ????15 |
| Weight rate %≤ | ????15 | |
| Water: ethylene glycol=1: 1 130 ℃ * 22h | Thicken rate %≤ | ????15 |
| Weight rate %≤ | ????15 | |
| Rate of compression % | ????15±5 | |
| Rebound degree % 〉= | ????35 |
A kind of non-asbestos seal backing plate of the present invention and preparation method thereof compared with the prior art, have outstanding substantive distinguishing features and marked improvement, 1, changes the non-asbestos seal backing plate into by asbestos grommet type seal plate, thereby reduce environmentally safe, belong to on-contaminated sealed bolster plate; 2, its complete processing is simple; 3, good product performance, the course of processing easily realize, the yield height of product.
(4) embodiment:
In order to understand better and to implement, describe a kind of non-asbestos seal backing plate of the present invention and preparation method thereof in detail below in conjunction with embodiment.
Embodiment 1,4 kilograms of accurate weighing Twaron fibers, 35 kilograms of Rs440 fibers, 13 kilograms of paracrils, 40 kilograms in lime carbonate, 2 kilograms of white carbon blacks, 1 kilogram in sulphur, M2 kilogram, anti-old J1 kilogram, 4 kilograms of stearic acid, 8 kilograms of toluene, with the paracril after the weighing, white carbon black, sulphur, M, anti-aging agent J, stearic acid, toluene mixing, stir 45min; The Rs440 fiber that adds again after the weighing stirs 60min; The Twaron fiber stirs 60min after adding weighing again; Be carried out to then and open, the big roll temperature of Cheng Zhangji is risen, when reaching 100 ℃, adjust baffle plate and hang cladding, overwork and spare, drop into aniseed then, carry out blanking, after aniseed has descended, hang outer material, then stop and cut plate; Vulcanize at last, adopt vulcanizer to vulcanize, 120 ℃ of vulcanizer temperature are pressurized to 1.0Mpa, behind the sulfuration 20min, promptly obtain non-asbestos seal backing plate of the present invention.
Embodiment 2, with embodiment 1, add concentration and be 5 kilograms of 70% aqueous ethanolic solutions before becoming Zhang Gong to plant, stirring 35min.
Embodiment 3,3 kilograms of accurate weighing Twaron fibers, 20 kilograms of Rs440 fibers, 10 kilograms of paracrils, 38 kilograms of kaolin, 2 kilograms of white carbon blacks, TMTD1 kilogram, DM2 kilogram, BLE1 kilogram, 4 kilograms in zinc oxide, 8 kilograms of toluene, with the paracril after the weighing, white carbon black, TMTD, DM, BLE, zinc oxide, toluene mixing, stir 30min; The Rs440 fiber that adds again after the weighing stirs 40min; The Twaron fiber stirs 40min after adding weighing again; Add concentration at last and be 5 kilograms of 80% aqueous ethanolic solutions, be carried out to then and open, the big roll temperature of Cheng Zhangji is risen, when reaching 90 ℃, adjust baffle plate and hang cladding, overwork and spare, drop into aniseed then, carry out blanking, after aniseed has descended, hang outer material, then stop and cut plate; Vulcanize at last, adopt vulcanizer to vulcanize, 110 ℃ of vulcanizer temperature, pressurization 0.5MPa behind the sulfuration 15min, promptly gets non-asbestos seal backing plate of the present invention.
Embodiment 4,5 kilograms of accurate weighing Twaron fibers, 48 kilograms of Rs440 fibers, 16 kilograms of paracrils, 44 kilograms of kaolin, 2 kilograms of white carbon blacks, TMTD3 kilogram, BLE1 kilogram, 4 kilograms in zinc oxide, 8 kilograms of toluene, with the paracril after the weighing, white carbon black, TMTD, BLE, zinc oxide, toluene mixing, stir 60min; The Rs440 fiber that adds again after the weighing stirs 80min; The Twaron fiber stirs 80min after adding weighing again; Add concentration at last and be 75% aqueous ethanolic solution, be carried out to then and open, the big roll temperature of Cheng Zhangji is risen, when reaching 110 ℃, adjust baffle plate and hang cladding, overwork evenly, drop into aniseed then, carry out blanking, after aniseed descend, the extension outer material, plate is cut in parking then; Vulcanize at last, adopt vulcanizer to vulcanize, 130 ℃ of vulcanizer temperature, pressurization 2.0MPa behind the sulfuration 25min, promptly gets non-asbestos seal backing plate of the present invention.
Claims (8)
1, a kind of non-asbestos seal backing plate, it is to make Twaron fiber 3-5 part, Rs440 fiber 20-48 part, oil resisting rubber 10-16 part, weighting agent 38-44 part, rubber ingredients 6-10 part, solvent 6-10 part by the following weight proportion raw material.
2, by the described a kind of non-asbestos seal backing plate of claim 1, it is characterized in that described rubber ingredients are strengthening agent, vulcanizing agent, promotor, anti-aging agent, activator, can adopt conventional proportioning.
3, by claim 1 or 2 described a kind of non-asbestos seal backing plates, the optimum weight proportioning that it is characterized in that described raw material is 4 parts of Twaron fibers, 35 parts of Rs440 fibers, 13 parts of oil resisting rubbers, 40 parts of weighting agents, 2 parts of strengthening agents, 1 part of vulcanizing agent, 2 parts of promotor, 1 part in anti-aging agent, 4 parts in activator, 8 parts of solvents.
4, by claim 1 or 2 described a kind of non-asbestos seal backing plates, it is characterized in that described oil resisting rubber is a paracril, weighting agent is kaolin, lime carbonate, strengthening agent is white carbon black, vulcanizing agent is sulphur, TMTD, and promotor is M, DM, TMTD, and anti-aging agent is anti-aging agent J, BLE, activator is zinc oxide, stearic acid, and solvent is a toluene.
5, by the described a kind of non-asbestos seal backing plate of claim 1, it is characterized in that also can adding and help volatilizer solution.
6, by the described a kind of non-asbestos seal backing plate of claim 5, it is characterized in that the weight proportion that helps volatilizer solution that adds is 8 parts.
7, by the described a kind of non-asbestos seal backing plate of claim 5, it is characterized in that the volatilizer solution that helps that adds is ethanol, concentration is 70-80%.
8, the preparation method of described any one non-asbestos seal backing plate of claim 1-7, its complete processing is as follows:
A, spice, oil resisting rubber, rubber ingredients, weighting agent in the spice machine after the adding weighing, and add solvent, stir 30-60min;
Add the Rs440 fiber and stir 40-80min;
Add the Twaron fiber and stir 40-80min;
Add and help volatilizer solution stirring 30-40min;
B becomes to open, and the big roll temperature of Cheng Zhangji is risen, and when reaching 90-110 ℃, adjusts baffle plate and hangs cladding, drops into aniseed then, carries out blanking, after aniseed has descended, hangs outer material, then stops and cuts plate;
C, sulfuration adopts vulcanizer to vulcanize, and sulfuration process is as follows: curing temperature 110-130 ℃, curing time 15-25min, sulfide stress 0.5-2Mpa.