CN1485861A - Application of fluorinated silicone rubber to prepare synthetic insulator - Google Patents
Application of fluorinated silicone rubber to prepare synthetic insulator Download PDFInfo
- Publication number
- CN1485861A CN1485861A CNA031527310A CN03152731A CN1485861A CN 1485861 A CN1485861 A CN 1485861A CN A031527310 A CNA031527310 A CN A031527310A CN 03152731 A CN03152731 A CN 03152731A CN 1485861 A CN1485861 A CN 1485861A
- Authority
- CN
- China
- Prior art keywords
- fluorine
- rubber
- synthetic insulator
- insulator
- silicon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention refers to the usage of silicon fluoride latex to prepare synthetic insulator in high-voltage transmission and transformation lines. It enhances hydrophobic property and age resistance of high-silicon latex, the core rod being routine epoxy glass-cloth, makes the insulator extrude metal fitting, casts silicon fluoride latex, heats and vulcanizes to make it.
Description
(1), technical field
The invention belongs to the purposes of fluorosioloxane rubber at the synthetic insulator of the defeated modified line Lu Shangyong of preparation high pressure.
(2), background technology
Best synthetic insulator is to make plug by epoxy glass fiber at present, suppresses the synthetic insulator that forms with silicon rubber.Though it has many advantages, the problem of aging of silastic material is very serious.According to the king ancestral of Foshan electrical power industry bureau woods, yellow pine ripple: the insulator that moves 7 years has completely lost hydrophobicity, can't re-use.Analyze its reason: silicon rubber is because acid-proof alkaline is poor, and at acid rain, ultraviolet ray is under the factor effects such as the temperature of alternate, due to the silicon rubber chain rupture.In addition, silicon rubber itself does not possess the ability of anti creepage trace.The hydrophobicity of silicon rubber is that the methyl on the silicon atom points to the interface because flexible polysiloxane backbone is rotated under capillary effect, and hydrophobicity mainly produces by methyl.In a single day the surface destroyed, exposes filler, loses hydrophobicity and be inevitable, and severe patient also can efflorescence.
(3), summary of the invention
In order to overcome the shortcoming of prior art, the invention provides the purposes of a kind of fluorosioloxane rubber at the preparation synthetic insulator, it is not only ageing-resistant, has excellent acid alkalescence, and its surface energy is lower than silicon rubber, and hydrophobicity is better, and anti-pollution flashover ability is stronger.
The present invention solves the technical scheme that its technical problem takes: fluorosioloxane rubber is in the purposes of the synthetic insulator of the defeated modified line Lu Shangyong of preparation high pressure, produce synthetic insulator with fluorosioloxane rubber, plug is conventional epoxy glass cloth, behind the crimping armor clamp, the pressure injection fluorine-silicon compounded rubber stock, sulfuration forms through heating.
Described fluorine-silicon compounded rubber stock, by the silica-based plinth glue of fluorine, reinforced filling, arc resistant filler, vulcanizing agent and auxiliary agent, mixing the making of under vacuum, heating.
The silica-based plinth glue of described fluorine can be pure fluorinated polysiloxane, or the mixture of fluorinated polysiloxane and high-temperature sulfuration silicon rubber raw rubber.
Described fluorinated polysiloxane is explained by following formula:
R1 is a methyl in the formula, and R2 is a vinyl, and R3 is a fluoro-containing group, and n1 is 0～50 number, and n2 is 1～2 number, and n3 is 1～50 number, and n is 100～5000 number.
Described fluoro-containing group can be perfluor or the part fluoro-containing group of C3-C21, as trifluoro propyl, and five fluorine butyl, seven fluorine amyl groups, nine fluorine hexyls, 11 fluorine heptyl, ten trifluoro octyl groups, 15 fluorine nonyls, 17 fluorine decyls, 19 fluorine undecyls, 21 fluorine dodecyls or the like.
The present invention has following advantage: (1), fluoro-carbon bond have very high bond energy, and the Organic fluoride group is introduced in the siloxane chain, and the fluorosioloxane rubber of making has excellent acid alkalescence, and its surface energy is lower than silicon rubber, and is more ageing-resistant.(2), anti-soil dodges that performance is good, synthetic insulator has good hydrophobicity, the umbrella shape corrugated surface at synthetic insulator when raining can not bedew the formation moisture film, but be globule shape drippage, be difficult for constituting conductive channel, its pollution flashover voltage is higher, is 3 times with the electric pressure porcelain insulator.(3), the electric erosion resistance excellence, insulator surface electric leakage flashover forms the bad change of irreversibility and plays the trace phenomenon, general standard is for being not less than 4.5 grades (they being 4.5kV), and synthetic insulator is 6～7 grades.(4), structural stability is good, general porcelain suspension insulator is interior mucilage binding distribution structure, because couple corrosion, in service can the generation hanged down the null value insulation resistance, and synthetic insulator is outer mucilage binding distribution structure, and its heart is the solid bar insulating material, do not exist deterioration to make a joint attack on and wear, zero resistance insulator can not occur.(5), circuit operational efficiency height because the wind and rain self-cleaning of synthetic insulator is good, do not produce zero resistance insulator again, so cleaning inspection work can change per 4～5 years into once, thereby shorten overhaul, interruption duration.(6), in light weight, it is light to contain into the insulator own wt, in transportation, in the construction operation, can alleviate staff's labour intensity greatly.
(4), embodiment
Embodiment 1:
With 100 parts of the fluorosioloxane rubber of 80% fluorine-containing siloxanes link unit, add 10 parts of fume colloidal silicas, 30 parts in aluminium hydroxide is handled 3 parts of auxiliary agents, at vacuum degree-0.095MPa, in the container that temperature is 180 ℃ mixing 2 hours, deposits and spends the night.Add 0.4 part of vulcanizing agent, 160 ℃ of injection mouldings.Through test, at 8 hours 500kv fluorosioloxane rubber insulator of 180 ℃ of post vulcanizations, surperficial water droplet contact angle is 104 °, is that 50 ℃, concentration are to soak no change 20 days in 5% the hydrochloric acid in temperature.
Embodiment 2:
With 100 parts of the fluorosioloxane rubber of 98% fluorine-containing siloxanes link unit, add 10 parts of fume colloidal silicas, 30 parts in aluminium hydroxide is handled 3 parts of auxiliary agents, at vacuum degree-0.095MPa, in the container that temperature is 180 ℃ mixing 2 hours, deposits and spends the night.Add 0.4 part of vulcanizing agent, 160 ℃ of injection mouldings.Through test, at 8 hours 330kv fluorosioloxane rubber insulator of 180 ℃ of post vulcanizations, surperficial water droplet contact angle is 106 °, is that 50 ℃, concentration are that 50 ℃ were soaked no change 20 days in 5% the hydrochloric acid in temperature.
Claims (5)
1, a kind of fluorosioloxane rubber is in the purposes of preparation synthetic insulator, it is characterized in that: fluorosioloxane rubber is in the purposes of the synthetic insulator of the defeated modified line Lu Shangyong of preparation high pressure, produce synthetic insulator with fluorosioloxane rubber, plug is conventional epoxy glass cloth, behind the crimping armor clamp, the pressure injection fluorine-silicon compounded rubber stock, sulfuration forms through heating.
2, purposes according to claim 1 is characterized in that: described fluorine-silicon compounded rubber stock, and by the silica-based plinth glue of fluorine, reinforced filling, arc resistant filler, vulcanizing agent and auxiliary agent, mixing the making of under vacuum, heating.
3, purposes according to claim 1 is characterized in that: the silica-based plinth glue of described fluorine can be pure fluorinated polysiloxane, or the mixture of fluorinated polysiloxane and high-temperature sulfuration silicon rubber raw rubber.
4, purposes according to claim 1 is characterized in that: described fluorinated polysiloxane is explained by following formula:
R1 is a methyl in the formula, and R2 is a vinyl, and R3 is a fluoro-containing group, and n1 is 0～50 number, and n2 is 1～2 number, and n3 is 1～50 number, and n is 100～5000 number.
5, purposes according to claim 1, it is characterized in that: described fluoro-containing group can be perfluor or the part fluoro-containing group of C3-C21, as trifluoro propyl, and five fluorine butyl, seven fluorine amyl groups, nine fluorine hexyls, 11 fluorine heptyl, ten trifluoro octyl groups, 15 fluorine nonyls, 17 fluorine decyls, 19 fluorine undecyls, 21 fluorine dodecyls or the like.