CN1478844A - Bridge surface water resistant binding admixture and its preparation method - Google Patents

Bridge surface water resistant binding admixture and its preparation method Download PDF

Info

Publication number
CN1478844A
CN1478844A CNA031283063A CN03128306A CN1478844A CN 1478844 A CN1478844 A CN 1478844A CN A031283063 A CNA031283063 A CN A031283063A CN 03128306 A CN03128306 A CN 03128306A CN 1478844 A CN1478844 A CN 1478844A
Authority
CN
China
Prior art keywords
properties
agent
correcting agent
sbr
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA031283063A
Other languages
Chinese (zh)
Inventor
刘国清
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUHAN LUXIANG INDUSTRY AND TRADE Co Ltd
Original Assignee
WUHAN LUXIANG INDUSTRY AND TRADE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUHAN LUXIANG INDUSTRY AND TRADE Co Ltd filed Critical WUHAN LUXIANG INDUSTRY AND TRADE Co Ltd
Priority to CNA031283063A priority Critical patent/CN1478844A/en
Publication of CN1478844A publication Critical patent/CN1478844A/en
Pending legal-status Critical Current

Abstract

A water-proof adhesive for the pavement of bridge is prepared from asphalt, gasoline, ionic surfactant, the modified chosen from SBS, GS, under EPS or VAE, SBR, CR and PVc, and polyvinyl alcohol through proportional mixing and stirring. Its advantages are high adhesion, high shear strength, and high water-proofing performance.

Description

Bridge deck water-proof binding agent and preparation method
Technical field the present invention relates to water-proof adhesive that a kind of bridge floor uses and preparation method thereof.
Background technology is two incomplete same notions at the bituminous pavement of mating formation on the bridge floor with the bituminous pavement of mating formation on sub-surface, making bituminous pavement on sub-surface, road surface and sub-surface are organic wholes, bear jointly and the load that travels of the vehicle that rationally distributing.Bridge floor is quite different, bituminous pavement is mated formation on the rigidity basal plane, the Young's modulus of Cement Concrete and asphalt concrete differs hundreds of times, so asphaltic road-mix surface course is in pressured state basically, the major cause that the road surface is damaged no longer is that tensile stress causes, and only may be the slippage that causes of the disengaging between the levels and come off, and the shop layer is thin more, problem is big more, so interlayer is in conjunction with most important.
Relevant specification regulation, when on the Cement Concrete bridge deck paving of asphalt being set, oil mat should have with the concrete slab bonding firmly, waterproof infiltrates, antiskid is wear-resisting, the superperformance of low temperature cracking resistance, the anti-rut of high temperature, antistripping
Relevant specification points out that the cement concrete bridge deck asphalt pavement should be made up of adhesion coating, waterproof layer, protective layer and oil mat, and bridge deck water-proof tack coat promptly is the address that adhesion coating and waterproof layer are united two into one.How to carry out this one deck, along with improving constantly of road quality classification, its requirement is also more and more higher.
Summary of the invention the objective of the invention is at above-mentioned present situation, aim to provide that a kind of adhesive power to Cement Concrete is strong, inter-layer shearing strength is big, softening temperature is high, elastic recovery rate is big, bridge deck water-proof binding agent and preparation method that water resistance is good, can adapt to any temperature, environment uses.
The implementation of the object of the invention is, the bridge deck water-proof binding agent is combined by pitch and solvent or emulsifying agent, properties-correcting agent, solvent or organic stabilizer.Solvent is a gasoline, emulsifying agent is an ionogenic surfactant, properties-correcting agent comprises VAE (ethene-Vinyl Acetate Copolymer multipolymer), SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber), PVAc (Vinyl Acetate Copolymer) emulsion polymerization that SBS (thermoplastic elastomer), GS (SBR powder), waste and old EPS (electric product bubble wrap, the mess-tin abandoned) or viscosity are good, and organic stabilizer is a polyvinyl alcohol.
1) solvent borne bridge deck water-proof binding agent is made up of pitch, solvent and properties-correcting agent, properties-correcting agent comprises SBS (thermoplastic elastomer), GS (SBR powder), waste and old EPS (electric product bubble wrap, the mess-tin abandoned), properties-correcting agent and bituminous weight ratio are 6~20: 94~80, and solvent accounts for 30% of water-proof adhesive total amount.
2) emulsion bridge deck water-proof binding agent is made up of pitch, emulsifying agent, water, properties-correcting agent and organic stabilizer, properties-correcting agent comprises VAE (ethylene-vinyl acetate copolymer), SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber), PVAc (Vinyl Acetate Copolymer) emulsion polymerization, emulsifying agent, water, organic stabilizer are formed soap lye, emulsifying agent, organic stabilizer account for 1%, 2.5% of soap lye weight, soap lye and bituminous weight ratio are 4: 6, and the weight ratio of properties-correcting agent and bitumen emulsion is 6~10: 94~90.
The preparation method of bridge deck water-proof binding agent with the pitch heating, adds the soap lye emulsification that modifier solution or adding have organic stabilizer earlier again, is specially:
1) selects properties-correcting agent for use, to be that 6~20: 94~80 properties-correcting agent is added in the container with the bituminous weight ratio, the gasoline that adds output 30% fully dissolves by properties-correcting agent, form modifier solution, 80~100 ℃ pitches are added in the modifier solution, stir, until pitch and polymkeric substance complete miscibility, the barrelling sealing is preserved
2) form soap lye with emulsifying agent, water, organic stabilizer, emulsifying agent, organic stabilizer account for 1%, 2.5% of soap lye weight, it by soap lye and bituminous weight ratio 4: 6 proportional arrangement bitumen emulsion, it by the weight ratio of properties-correcting agent and bitumen emulsion 6~10: 94~90 proportional arrangement emulsion-type waterproofing agent, stir, the barrelling sealing is preserved.
The present invention pitch is dissolved or emulsification after be configured to solvent-borne type or emulsion-type bridge deck water-proof binding agent, particular case is as follows:
1, solvent type bridge floor water-proof adhesive;
The properties-correcting agent that chooses by use temperature and bridge floor character, by properties-correcting agent account for asphalt content 5~20% measure properties-correcting agent, and put into container; 30% the amount that accounts for the finished product total amount by industrial naptha is added in the container of containing properties-correcting agent, stirs evenly until the properties-correcting agent off-bottom and makes modifier solution; 80~100 ℃ pitches are added in the modifier solution, stir, until pitch and polymkeric substance complete miscibility, the barrelling sealing is preserved.
2, liquid type bridge deck water-proof binding agent:
AH-70 pitch is heated to 145 ℃; Form soap lye with emulsifying agent, water, organic stabilizer, emulsifying agent, organic stabilizer account for 1%, 2.5 ‰ of soap lye weight; By soap lye and bituminous weight ratio be 4: 6 mixed, in colloidal mill, grind bitumen emulsion, be 6~10%: 94~90% proportional arrangement emulsion-type waterproofing agent by the weight ratio of properties-correcting agent and bitumen emulsion, stir, the barrelling sealing is preserved.
Properties-correcting agent comprises SBS (styrene-butadiene-styrene multipolymer), waste and old EPS (electric product bubble wrap, the mess-tin abandoned), EVA (ethene-Vinyl Acetate Copolymer multipolymer), SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber) or PVAc (Vinyl Acetate Copolymer) emulsion.
Bridge deck water-proof binding agent of the present invention
Adhesive power to Cement Concrete:>1Mpa; Inter-layer shearing strength:>1.4Mpa;
Softening temperature:>80 ℃; Elastic recovery rate:>80%;
Water resistance: 30min is waterproof under the 0.3Mpa pressure; State: be in a liquid state under the normal temperature
Construction temperature: the solvent type bridge floor water-proof adhesive is adapted under any temperature environment, and emulsion-type bridge deck water-proof binding agent adapts in environment use more than 5 ℃.
This bridge deck water-proof binding agent uses on Huangshi Yangtze Highway Bridge, yellow motorway, the white sand continent Yangtze Bridge, all receives promising result.
Enumerate specific embodiments of the invention below the embodiment:
Example 1, first preparation polyvinyl alcohol solution: in 80~90 ℃ of water, add granule of polyvinyl alcohol, polyvinyl alcohol: water=1: 2, stir and allow its dissolving; Prepare soap lye again: in the water of 40~50 ℃ of 350kg, add polyvinyl alcohol solution (containing polyvinyl alcohol 10kg) and the 4kg emulsifying agent water (being as the criterion) that 30kg makes, stir with the pure content of tensio-active agent; AH-70 pitch and the soap lye of 145 ℃ of 600kg are sent into the colloidal mill grinding simultaneously, generate bitumen emulsion, the cooling back adds 100kg VAE emulsion fully stirs, and barrelling seals preserves.
Example 2, with example 1, different is, bitumen emulsion cooling back add 70kg VAE emulsion fully stir product.
Example 3, with example 1, different is, bitumen emulsion cooling back add 60kg SBR emulsion fully stir product.
Example 4, with example 1, different is, bitumen emulsion cooling back add 70kg SBR emulsion fully stir product.
Example 5, with example 1, different is, bitumen emulsion cooling back add 80kg PVAc emulsion fully stir product.
Example 6, with example 1, different is, bitumen emulsion cooling back add 100kg PVAc emulsion fully stir product.
Example 7,2.6kgSBS is added in the container, add 7.4kg gasoline, allow it fully dissolve and make modifier solution, again in modifier solution: the ratio of pitch=41: 59 slowly adds modifier solution with the AH-70 pitch of 80~100 ℃ of 14kg, fully stirs back barrelling sealing and preserves.
Example 8, with example 7, different is, adds 8.1kg gasoline among the 1.9kgGS, by modifier solution: the ratio of pitch=37: 63 is in the 17kg pitch adding modifier solution, fully stir product.
Example 9, with example 7, different is, adds 6kg gasoline among the 1.4kgSBS, by modifier solution: the ratio of pitch=37: 63 is in the 12.6kg pitch adding modifier solution, fully stir product.
Example 10, with example 7, different is, adds 6kg gasoline among the 1.4kgEPS, by modifier solution: the ratio of pitch=37: 63 is in the 12.6kg AH-70 pitch adding modifier solution, fully stir product.
Example 11, with example 7, different is, adds 6kg gasoline among the 2.1kgSB, by modifier solution: the ratio of pitch=40: 60 is in the 11.9kg pitch adding modifier solution, fully stir product.
Example 12, with example 7, different is, adds 6kg gasoline among the 2.8kgSBS, by modifier solution: the ratio of pitch=44: 56 is 11.2kg pitch adding modifier solution, fully stir product.
Example 13, with example 7, different is, adds 6kg gasoline among the 2.1kgEPS, by modifier solution: the ratio of pitch=40: 60 is 11.9kg pitch adding modifier solution, fully stir product.
Example 14, with example 7, different is, adds 6kg gasoline among the 1.68kgEPS, by modifier solution: the ratio of pitch=38: 62 is in the 12.32kg pitch adding modifier solution, fully stir product.
Example 15, with example 1, different is, adds 6kg gasoline among the 1.68kgSBS, by modifier solution: the ratio of pitch=38: 62 is in the 12.32kg pitch adding modifier solution, fully stir product.

Claims (3)

1, the bridge deck water-proof binding agent, it is characterized in that by pitch and solvent or emulsifying agent, properties-correcting agent, solvent or organic stabilizer combine, solvent is a gasoline, emulsifying agent is an ionogenic surfactant, properties-correcting agent comprises SBS (thermoplastic elastomer), GS (SBR powder), waste and old EPS (the electric product bubble wrap of abandoning, mess-tin) or the good VAE (ethene-Vinyl Acetate Copolymer multipolymer) of viscosity, SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber), PVAc (Vinyl Acetate Copolymer) emulsion polymerization, organic stabilizer is a polyvinyl alcohol
1) solvent borne bridge deck water-proof binding agent is made up of pitch, solvent and properties-correcting agent, properties-correcting agent comprises SBS (thermoplastic elastomer), GS (SBR powder), waste and old EPS (electric product bubble wrap, the mess-tin abandoned), properties-correcting agent and bituminous weight ratio are 6~20: 94~80, solvent accounts for 30% of water-proof adhesive total amount
2) emulsion bridge deck water-proof binding agent is made up of pitch, emulsifying agent, water, properties-correcting agent and organic stabilizer, properties-correcting agent comprises VAE (ethylene-vinyl acetate copolymer), SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber), PVAc (Vinyl Acetate Copolymer) emulsion polymerization, emulsifying agent, water, organic stabilizer are formed soap lye, emulsifying agent, organic stabilizer account for 1%, 2.5% of soap lye weight, soap lye and bituminous weight ratio are 4: 6, and the weight ratio of properties-correcting agent and bitumen emulsion is 6~10: 94~90.
2, the preparation method of the described bridge deck water-proof binding agent of claim 1, its feature formerly with the pitch heating, add the soap lye emulsification that modifier solution or adding have organic stabilizer again, are specially:
1) selects properties-correcting agent for use, to be that 6~20: 94~80 properties-correcting agent is added in the container with the bituminous weight ratio, the gasoline that adds output 30% fully dissolves by properties-correcting agent, form modifier solution, 80~100 ℃ pitches are added in the modifier solution, stir, until pitch and polymkeric substance complete miscibility, the barrelling sealing is preserved
2) form soap lye with emulsifying agent, water, organic stabilizer, emulsifying agent, organic stabilizer account for 1%, 2.5% of soap lye weight, it in soap lye and bituminous weight ratio 4: 6 ratio preparation bitumen emulsion, it by the weight ratio of properties-correcting agent and bitumen emulsion 6~10: 94~90 proportional arrangement emulsion-type waterproofing agent, stir, the barrelling sealing is preserved.
3, production method according to claim 2 is characterized in that properties-correcting agent comprises SBS (styrene-butadiene-styrene multipolymer), waste and old EPS (electric product bubble wrap, the mess-tin abandoned), EVA (ethene-Vinyl Acetate Copolymer multipolymer), SBR (styrene-butadiene rubber(SBR)), CR (chloroprene rubber) or PVAc (Vinyl Acetate Copolymer) emulsion.
CNA031283063A 2003-07-10 2003-07-10 Bridge surface water resistant binding admixture and its preparation method Pending CN1478844A (en)