CN1468938A - Improved oxygen-isolating fire-retardant cable material - Google Patents
Improved oxygen-isolating fire-retardant cable material Download PDFInfo
- Publication number
- CN1468938A CN1468938A CNA031318738A CN03131873A CN1468938A CN 1468938 A CN1468938 A CN 1468938A CN A031318738 A CNA031318738 A CN A031318738A CN 03131873 A CN03131873 A CN 03131873A CN 1468938 A CN1468938 A CN 1468938A
- Authority
- CN
- China
- Prior art keywords
- flame
- oxygen barrier
- cable material
- proof material
- oxygen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The improved oxygen-isolating fire-retardant cable material with excellent forming performance consists of acetic acid-ethylene copolymer 30-50 wt%, polyethylene 3-10 wt%, magnesium hydroxide 30-55 wt%, aluminum hydroxide 10-35 wt%, smoke eliminator 1-5 wt% and maleic anhydride 0.2-1 wt%. The cable material may be produced into granulated material for easy transport and storing and may be extruded and coated onto various cable to form oxygen-isolating fire-retardant layer in a extruding and coating machine. It is non-toxic, and has excellent fire retarding effect and oxygen index over 65.
Description
Technical field
The present invention relates to a kind of cable oxygen barrier flame-proof material of improvement, the cable oxygen barrier flame-proof material that especially a kind of forming process is good.
Background technology
Chinese patent 99114157 discloses a kind of cable high flame-proofing protective layer material, and it consists of the jelly that 68～70% aluminium hydroxides, 22～24% cured resins, 2.5～4.5% Resins, epoxy, 2.0～3.5% red phosphorus mix.Difficulty is not only stored, transported to this kind flame-proof material owing to be jelly, therefore, and moulding need adopt the mould injection forming, requires the mould complexity; Adopt Resins, epoxy owing in the material in addition, thereby cost is higher relatively; Besides, the aluminium hydroxide fire retardant that single interpolation is relatively large, the flame-proof material flexibility of composition is poor, and embrittlement easily is difficult to extrude moulding with the common plastics forcing machine, thereby makes complicated.Adopt cured resin in the base-material besides, make that side crops can not regeneration, increased use cost.
Summary of the invention
The objective of the invention is to overcome the deficiency of above-mentioned prior art, provide a kind of shaping characteristic good, can extrude moulding, storage period is long, and is easy to use, and the cable oxygen barrier flame-proof material of recyclable regeneration.
Cable oxygen barrier flame-proof material of the present invention consists of the vinyl acetate copolymer of 30-50% (weight), the polyethylene of 3-10%, the magnesium hydroxide of 30-55%, the aluminium hydroxide of 10-35%, the smoke suppressor of 1-5%, the toxilic acid bar of 0.2-1%.
Vinyl acetate copolymer of the present invention (EVA) as the moulding base-material, has good toughness, flexibility and stress cracking resistance and cohesiveness, and good relatively flame retardant resistance; The main effect of polyethylene (PE) is that EVA is carried out modification, and both have consistency preferably, can increase the mechanical and physical performance of base-material, as improve tensile strength, the unit elongation of base-material, reduce base-material viscosity, improve extrusion moulding, making it has better toughness at normal temperatures.For improving workability, polyethylene of the present invention better selects for use melt index comparatively suitable about 2g/10min, melt index is too high or too low, all can influence processing forming, too high as melt index, can cause processing temperature to raise, viscosity reducing effect is obvious inadequately, the screw rod extrusion pressure is big, extrudes not smooth; Melt index is low excessively, and material is difficult to slaking and mixes.The present invention adopts magnesium hydroxide and aluminium hydroxide composite anti-flaming agent, can improve the flexibility of material on the one hand, helps improving the material processing forming, secondly both mix, can give full play to flame retardant synergistic effect, can improve flame retardant effect, make in each stage of burning and all can work.Smoke suppressor mainly is to suppress burning to produce black smoke.The toxilic acid bar is as coupling agent, and main effect is the interfacial characteristics that improves organic polyolefine and inorganic combustion inhibitor material, thereby improves its bonding properties, improves Chemical bond power, helps strengthening the physical strength of material.Toxilic acid bar of the present invention, to adopt MEVA800 ideal, effect is best especially.
Oxygen barrier flame-proof material of the present invention, by common plastic granulating method, each mixing of materials is even, granulation are as using the twin screw extruder extruding pelletization, packing.During use, directly the pellet of making is put into forcing machine and be extruded in the insulated wire cores appearance, constitute flame-retardant layer.
Oxygen barrier flame-proof material of the present invention, owing to adopt flame retardant resistance and all good EVA of workability to make base-material, and carry out modification by polyethylene, not only the modifying material flexibility is good, and can adopt common plastic granulating method, it is standby to make pellet, and extrusion moulding is improved greatly.The application of composite flame-retardant agent has improved flame retardant properties greatly, all can play flame retardant effect preferably in each stage of burning, and oxygen index can reach more than 65.Toxilic acid bar coupling agent is greatly improved organic polyolefine and inorganic combustion inhibitor associativity, can strengthen the bonding strength of component material.Oxygen barrier flame-proof material of the present invention, nontoxic, even meet the naked light burning, can not produce toxic gas yet, can granulation, be convenient to transportation, storage period is long, and cost is low, suitability is wide, can extrude moulding with various plastics extruding machines, extrudes simple, the recyclable regeneration of side crops, the oxygen barrier that can be used for various cables is fire-retardant.
Below in conjunction with three indefiniteness embodiment, further specify the present invention and form.
Embodiment
Embodiment 1: get 40 parts of (weight) EVA320,3 parts of PE112A, 44 parts of magnesium hydroxides, 10 parts of aluminium hydroxides, 2.5 parts of smoke suppressors, 0.5 part of toxilic acid bar MEVA800.Material weighing is mixed, at the twin screw extruder extruding pelletization.During use, be extruded in the insulated wire cores appearance by the cable plastics machine of extruding, constitute the oxygen barrier flame-retardant layer, oxygen index can reach 65.
Embodiment 2: prescription consists of: 35 parts of EVA-450,5 parts of PE112A, 39 parts of magnesium hydroxides, 18 parts of aluminium hydroxides, 2.5 parts of smoke suppressors, 0.5 part of toxilic acid bar MEVA800.Oxygen index 67.
Embodiment 3: prescription consists of: 30 parts of EVA-450,7 parts of PE WD100,30 parts of magnesium hydroxides, 30 parts of aluminium hydroxides, 2.5 parts of smoke suppressors, 0.5 part of toxilic acid bar.Oxygen index 67.5.
Claims (4)
1, a kind of cable oxygen barrier flame-proof material is characterized in that consisting of the vinyl acetate copolymer of 30-50% (weight), the polyethylene of 3-10%, the magnesium hydroxide of 30-55%, the aluminium hydroxide of 10-35%, the smoke suppressor of 1-5%, the toxilic acid bar of 0.2-1%.
2,, it is characterized in that said vinyl acetate copolymer is EVA-450 according to the described cable oxygen barrier of claim 1 flame-proof material.
3,, it is characterized in that said poly melt index is about 2g/10min according to the described cable oxygen barrier of claim 1 flame-proof material.
4,, it is characterized in that said toxilic acid bar is MEVA800 according to the described cable oxygen barrier of claim 1 flame-proof material.