CN1454765A - Hollow ceramic rod and manufacturing process thereof, and its application for producing light refractory material - Google Patents
Hollow ceramic rod and manufacturing process thereof, and its application for producing light refractory material Download PDFInfo
- Publication number
- CN1454765A CN1454765A CN 03140536 CN03140536A CN1454765A CN 1454765 A CN1454765 A CN 1454765A CN 03140536 CN03140536 CN 03140536 CN 03140536 A CN03140536 A CN 03140536A CN 1454765 A CN1454765 A CN 1454765A
- Authority
- CN
- China
- Prior art keywords
- hollow
- ceramic rod
- base substrate
- rod
- hollow ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of hollow porcelain stick and its manufacture technology, as well as its application in producing the light fire-resistant stuff. Firstly shape the porcelain material to the pipe shape material by squeezing, then cut the pipe into some sections, and envelop the two ends to form the hollow porcelain material. After drying and firing, the hollow porcelain stick will be shape. In the course of producing the light fire-resistant stuff, add the hollow porcelain stick to the mixed material, therefore it can support and joint the whole fire-resistant stuff. The technology can resist squeezing, breaking, vibrating.
Description
Affiliated technical field: the present invention relates to the application in producing lightweight refracrory of a kind of hollow ceramic rod and manufacture craft thereof and hollow ceramic rod.
Background technology: usually, the mode of production of lightweight refracrory has multiple, and for example: be raw material system with natural or artificial porous light-weight material such as hollow ball etc. 1., wherein its forming method is generally vibratory drilling method.2. in pug, add the combustible of easily burning, as sawdust, foam styrene; Or add sublimate such as naphthalene, and the volatilization back of burnouting forms the porous knot, and its forming method is generally the mud method of squeezing.3. add blowing agent in pug, burn till the back and obtain loose structure, its forming method is generally casting.As the backing of various Thermal Equipments, on Industrial Stoves, also be used as working lining sometimes the purposes of lightweight refracrory (as refractory brick).Generally speaking, no matter be backing or working lining, the mode of its damage mainly is that material production is peeled off under the effect of thermal stress, for specific material normally the heat-proof quality of material the antistrip performance of good material is poor more more.How on the basis that guarantees the fire-resistant material heat insulation performance, improve antistrip performance and be people and be expected the problem that solves for a long time.
Summary of the invention: the object of the invention provides the application in producing lightweight refracrory of a kind of hollow ceramic rod and manufacture craft and hollow ceramic rod thereof, special hollow ceramic rod is added in the batching of current material, improve the antistrip performance of refractory material, solve the problems referred to above that background technology exists.
Technical scheme of the present invention is:
Hollow ceramic rod and manufacture craft thereof: at first common ceramic batch is molded the tubulose base substrate with known extruding method, then the tubulose base substrate is cut into plurality of sections, and the two ends of sealing pipeline section, make it to become the bar-shaped base substrate of hollow, hollow rod-shape base substrate drying and burn till after obtain final product---the hollow ceramic rod.
The features of shape of the bar-shaped base substrate of hollow be the diameter at its two ends greater than mid portion, its equivalent diameter is 0.5～5 millimeter, its effective length is 3～15 times of equivalent diameter.
The purposes of hollow ceramic rod: in the process of producing the typing lightweight refracrory or in the construction work of unsetting light thermal-shield refractory material, can the hollow ceramic rod that make be joined in the batching according to 20～40% volume ratio, wherein need to make the chemical composition of hollow ceramic rod and mineral composition and the required material of allocating into approaching as much as possible, so that make both in production process and use, have enough compatibilities.
The lightweight refracrory component that can produce is as required made the close hollow ceramic rod of composition, also can be used to make the close lightweight refracrory of composition according to the component of hollow ceramic rod.
The ceramic rod of hollow is embedded in can effectively play in the lightweight refracrory and supports and the effect of embedding connection, compare the resistance to compression of goods with the goods that do not add the hollow ceramic rod under the same process conditions, anti-folding, especially thermal shock resistance improves significantly, thermal shock number under the wherein equal detection method can improve 3～5 times, its reason is the generation that the material of adding hollow ceramic rod can effectively prevent crackle on the one hand, even also can effectively stop further expanding of crackle after material internal cracks on the other hand, so the antistrip performance of refractory material is significantly improved.Because hollow ceramic rod itself is hollow, so the heat-proof quality that its introducing can't expendable material, having solved the good more spalling resistance of lightweight refracrory heat-proof quality effectively based on the material of this conception of species production can poor more contradiction.
Adopt similar proportion scale, can play and formalize that goods increase similarly that material cracking resistance line produces and expansion increases the effect in service life with the similar hollow ceramic rod of primary raw material material thereby in the unsetting material of traditional lightweight, add.
The present invention have product and production technology rationally, improve the antistrip performance of lightweight refracrory and do not sacrifice characteristics such as fire-resistant material heat insulation performance, solved people and be badly in need of the technical problem that solves for a long time.
The specific embodiment: further specify the present invention by the following examples.
In an embodiment, hollow ceramic rod and manufacture craft thereof are:
1. raw material fine grinding: required ceramic raw material fully is finely ground to below 20 microns with equipment such as vibromill or airflow milling.
2. blank preparation: the raw material after levigate and methylcellulose or polyvinyl alcohol etc. are joined in the de-airing mixer in order to the bond that increases blank plasticity, and the adding suitable quantity of water fully stirs and mixes, and becomes the good dough state of plasticity until mixture.
3. the moulding of hollow rod-shape ceramic body: the good blank that will mix is inserted in the mud extruder, extrudes the tubulose base substrate of required diameter and wall thickness as required by the mould at extrusion place; The tubulose base substrate is cut off and sealing two ends by Len req with cutting off sealing machine before dry.Hollow tubular ceramic rod base substrate after the moulding has following shape facility: the diameter at closed at both ends and two ends is greater than mid portion, and its equivalent diameter is 0.5～5 millimeter, and its effective length is 3～15 times of equivalent diameter, and its wall thickness is 0.1～1 millimeter.
4. hollow rod-shape ceramic body dry and burning till: drying is usually at room temperature or about 100 degrees centigrade.Burn till the calcining system suitable usually according to raw materials used employing, for example the material firing temperature of trioxygen-containingization two aluminium more than 99% is about 1800 degrees centigrade, the firing temperature of mullite material about 1670 degrees centigrade, this and general ceramic drying and not significantly difference of sintering process.
The purposes of hollow ceramic rod: in the process of producing the typing lightweight refracrory or in the construction work of unsetting light thermal-shield refractory material, can the hollow ceramic rod that make be joined in the batching according to 20～40% volume ratio, be preferably the hollow ceramic rod of volume ratio 30%, wherein need to make the chemical composition of hollow ceramic rod and mineral composition and the required material of allocating into approaching as much as possible, so that make both in production process and use, have enough compatibilities.
Claims (9)
1, a kind of hollow ceramic rod, it is characterized in that this hollow ceramic rod made by following technology: at first ceramic batch is molded the tubulose base substrate with extruding method, then the tubulose base substrate is cut into plurality of sections, and the two ends of sealing pipeline section, make it to become the bar-shaped base substrate of hollow, hollow rod-shape base substrate drying and burn till after obtain final product.
2, according to claim 1 described among empty ceramic rod, the diameter that it is characterized in that closed at both ends and two ends is greater than mid portion.
3, according to claim 2 described among empty ceramic rod, the equivalent diameter that it is characterized in that the hollow ceramic rod is 0.5～5 millimeter, its effective length is 3～15 times of equivalent diameter.
4, according to claim 1 or 2 described among empty ceramic rod, the wall thickness that it is characterized in that the hollow ceramic rod is 0.1～1 millimeter.
5, a kind of manufacture craft of hollow ceramic rod, it is characterized in that at first ceramic batch being molded the tubulose base substrate with extruding method, then the tubulose base substrate is cut into plurality of sections, and the two ends of sealing pipeline section, make it to become the bar-shaped base substrate of hollow, hollow rod-shape base substrate drying and burn till after obtain final product---the hollow ceramic rod.
6, according to claim 5 described among the manufacture craft of empty ceramic rod, it is characterized in that supplying process as follows:
1. raw material fine grinding: required ceramic raw material fully is finely ground to below 20 microns with equipment such as vibromill or airflow milling;
2. blank preparation: the raw material after levigate and methylcellulose or polyvinyl alcohol etc. are joined in the de-airing mixer in order to the bond that increases blank plasticity, and the adding suitable quantity of water fully stirs and mixes, and becomes the good dough state of plasticity until mixture;
3. the moulding of hollow rod-shape ceramic body: the good blank that will mix is inserted in the mud extruder, extrude the tubulose base substrate of required diameter and wall thickness as required by the mould at extrusion place, the tubulose base substrate is cut off and sealing two ends by Len req with cutting off sealing machine before dry, the hollow tubular ceramic rod base substrate closed at both ends after the moulding and the diameter at two ends are greater than mid portion, its equivalent diameter is 0.5～5 millimeter, its effective length is 3～15 times of equivalent diameter, and its wall thickness is 0.1～1 millimeter;
4. hollow rod-shape ceramic body dry and burning till, drying is usually in room temperature-100 degree centigrade, burn till the calcining system suitable according to raw materials used employing, the material firing temperature of trioxygen-containingization two aluminium more than 99% is at 1800 degrees centigrade, and the firing temperature of mullite material is at 1670 degrees centigrade.
7, the application of hollow ceramic rod in producing lightweight refracrory, it is characterized in that in the process of producing the typing lightweight refracrory or in the construction work of unsetting light thermal-shield refractory material, the volume ratio according to 20～40% joins the hollow ceramic rod in the batching.
8, according to claim 7 described among the application of empty ceramic rod in producing lightweight refracrory, it is characterized in that the chemical composition of hollow ceramic rod and mineral composition and the required lightweight refracrory of allocating into are approaching as much as possible, so that make both in production process and use, have enough compatibilities.
9, according to claim 7 or 8 described among the application of empty ceramic rod in producing lightweight refracrory, it is characterized in that the volume ratio according to 30% joins the hollow ceramic rod in the batching.