CN1450133A - Nano polyester powder coating - Google Patents
Nano polyester powder coating Download PDFInfo
- Publication number
- CN1450133A CN1450133A CN 03116381 CN03116381A CN1450133A CN 1450133 A CN1450133 A CN 1450133A CN 03116381 CN03116381 CN 03116381 CN 03116381 A CN03116381 A CN 03116381A CN 1450133 A CN1450133 A CN 1450133A
- Authority
- CN
- China
- Prior art keywords
- weight
- nano
- solidifying agent
- powder coating
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The composition of nano polyester powder coating material is composed of (wt%) 20-50% of unsaturated polyester resin, 2-5% of inorganic nano powder, 5-10% of solidifying agent, 30-50% of inorganic filling material and 0-10% of other adjuvant, in which the inorganic nano powder is titanium oxide, silicon oxide or zinc oxide, and said invented nano polyester coating layer has the advantages of good levelling property, uniform coating layer colour, strong resistance to UV-ray and long time for resisting ageing.
Description
Technical field
The present invention relates to a kind of coating, a kind of polyester powder coating that contains nanoscale powder.
Background technology
Powder coating because of it seldom discharges the volatility obnoxious flavour to environment when applying and solidify, do not cause such as the air-polluting environmental problem, thereby Application Areas constantly enlarges.But powder coating is when heating and melt kneading resin and solidifying agent, because solidifying agent dispersive ununiformity, advection is relatively poor, therefore produces the not good enough problem of appearance of film.Also have the dispersed relatively poor of pigment and filler in addition, compare with liquid coating, powder coating is difficult to obtain distinctness, clear and glossiness filming.Nanotechnology impels coating to update in the application of coating industry, makes powder coating really become green environmental friendly coatings, has started the breakthrough development direction.Utilize the nano material optical characteristics to make coating decompose ultraviolet radiation, improve the weather-proof and ageing-resistant performance of coating; Utilize the nanoparticle polymolecularity, be dispersed in and form the distributed nuclei nano-composite coating in the organic polymer, improve the advection of nano coating.It is thin to have coating, and materials are economized, characteristics such as strong adhesion and good toughness.With nanoparticle and resin-bonded be used to absorb ultraviolet sunblock lotion, makeup are put on market, Chinese patent 01110586.0 is mentioned a kind of nanometer environmental protection paint that is used for body of wall of water-based, does not find the patent report of relevant nanometer polyester powder coating as yet.
Summary of the invention
The objective of the invention is to utilize some feature of nano material, for example polymolecularity, uvioresistant, ageing-resistant etc., trial-production contains the polyester powder coating of nanoparticle, to improve the advection and the glossiness of polyester powder coating, reaches that coating is thin, the purpose of materials province, strong adhesion and good toughness.
Main contents of the present invention: the nanometer polyester powder coating, comprise vibrin, solidifying agent, pigment, mineral filler and other auxiliary agents, wherein inorganic nanometer powder is the 1-10% of gross weight, is preferably the 2-5% of gross weight.
The prescription of said nanometer polyester powder coating consists of, and unsaturated polyester resin is a 20-50% weight, and inorganic nanometer powder is a 2-5% weight, solidifying agent is a 7-10% weight, mineral filler is a 30-50% weight, and pigment is 1-5% weight, and other auxiliary agents are 0-10% weight.
Said vibrin is gone up substantially and is the unsaturated polyester resin class, and for example dibasic alcohol and unsaturated dibasic acid all or partly make the vibrin of straight chain type.The most frequently used dibasic alcohol is ethylene glycol, propylene glycol, glycerol etc., and diprotic acid is phthalic anhydride, hexanodioic acid, maleic acid, FUMARIC ACID TECH GRADE etc.
Said solidifying agent is that TGIC is an isocyanuric acid three-glycidyl fat.
The rarest one dimension of particle of said inorganic nanometer powder is of a size of 10-100nm, as zinc oxide, titanium oxide, manganese oxide, magnesium oxide, calcium oxide, aluminum oxide and silicon oxide etc., and wherein preferred nanometer SiO
x, nano-ZnO, nano-TiO
2With nanometer Al
2O
3
Nanometer SiO
xBe unformed white powder, it is a kind of nonpoisonous and tasteless free of contamination inorganic nonmetallic nanometer material, has accurate grain pattern, particle diameter 1-15nm, specific surface area is big, the surface exists a large amount of unsaturated residual bonds and different bonding state hydroxyl, is convenient to the remaining carboxylic root esterification with unsaturated polyester, can increase substantially rheological, smooth finish, resistance to deterioration and the surface hardness of filming and the self-cleaning ability of polyester powder coating.
Nano-ZnO is a white, tasteless, nontoxic ultrafine particle, its warp is between 1-100nm, low price, Heat stability is good, it is strong to absorb ultraviolet ability, and the nano zine oxide size is little, and specific surface area is big, the key attitude on surface is different with granule interior, the surface atom coordination is not congruent, strengthens the reaction contact surface, and nano zine oxide is a kind of photocatalyst, under uviolizing, its energy decomposing organic matter has the sterilization antibacterial, and the compound coating that nano zine oxide and unsaturated polyester form has absorption hertzian wave and antistatic property, and coating quality is light, thin thickness, of light color, the strong characteristics of absorption hertzian wave ability.
Nano-TiO
2Also be the powder of a kind of white particle diameter at 10-80nm, nano titanium oxide has the feature that optical effect changes with particle diameter, the mixture that nano titanium oxide and polyester are formed is formed a kind of photoeffect coating, enriches and mysterious color effect with adding different generation of particle diameter.As absorb ultraviolet effect and can obviously improve the weathering resistance of coating and use the nano titanium dioxide photocatalysis characteristic, make polyester coatings to toxic and harmful in the air, as the absorption and the Decomposition of oxynitrides, sulfide and benzene-alkylation compound.
Embodiment
Embodiment 1, prescription are formed: unsaturated polyester resin 20% weight, and nano silicon oxide 3% weight, solidifying agent is 7% weight, and mineral filler is 50% weight, and pigment is 10% weight, and other auxiliary agents are 10% weight.
Main raw material(s) is selected: unsaturated polyester resin is selected acid number 55-75KOH/ gram, and softening temperature is 85-105 ℃, second-order transition temperature＞50 ℃; Nano silicon oxide granularity 5-15nm, SiO
xContent＞99.9; Solidifying agent is a white powder, and oxirane value is about 0.9, and fusing point is 88-92 ℃, organic chlorine number＜0.02 equivalent/kg.
Technological process summary: unsaturated polyester resin, nano silicon oxide, solidifying agent, pigment and mineral filler are mixed pulverizing, alternately mix with low speed at a high speed, 1500-5000 rev/min was stirred 5 minutes, changeed low speed and stirred 5 minutes for 300-500 rev/min, change high-speed stirring again, high low speed repeats repeatedly.Reaching unsaturated polyester resin and nano silicon oxide, solidifying agent, pigment and filler fully pulverizes and mixes.Regulate and controlled temperature 100-120 ℃ of mixing extruding, crushing screening, grain particle degree control 160-220 order stores.
The film performance test result is as follows: condition of cure 180-190 ℃/15-20min; Appearance of film, color and luster is even, smooth; Glossiness is 20-30% for 60 °, resistance to impact shock 60cm, weathering resistance 1200 hours.
Embodiment 2, prescription are formed: unsaturated polyester resin 30% weight, and nano zine oxide 5% weight, solidifying agent is 8% weight, and mineral filler is 50% weight, and pigment is 2% weight, and other auxiliary agents are 5% weight.
Main raw material(s) is selected: unsaturated polyester resin is selected acid number 55-75KOH/ gram, and softening temperature is 85-105 ℃, second-order transition temperature＞50 ℃; Nano zine oxide granularity 50-100nm, ZnO
2Content＞99.9; Solidifying agent is a white powder, and oxirane value is about 0.9, and fusing point is 88-92 ℃, organic chlorine number＜0.02 equivalent/kg.
Technological process summary: unsaturated polyester resin, nano zine oxide, solidifying agent, pigment and filler are mixed pulverizing, alternately mix with low speed at a high speed, 1500-5000 rev/min was stirred 5 minutes, changeing low speed stirred 5 minutes for 300-500 rev/min, after high low speed repeats repeatedly, regulate and controlled temperature 100-120 ℃ of mixing extruding, grain particle degree control 160-220 order sieves, and stores.
The film performance test result is as follows: condition of cure 180-190 ℃/15-20min; Appearance of film, color and luster is even, smooth; Glossiness is 30-40% for 60 °, resistance to impact shock 60cm, weathering resistance 1200 hours.
Embodiment 3, prescription are formed: unsaturated polyester resin 40% weight, and nano-titanium oxide 2% weight, solidifying agent is 10% weight, and mineral filler is 40% weight, and pigment is 2% weight, and other auxiliary agents are 6% weight.
Main raw material(s) is selected: unsaturated polyester resin is selected acid number 55-75KOH/ gram, and softening temperature is 85-105 ℃, second-order transition temperature＞50 ℃; Nano-titanium oxide granularity 10-50nm, TiO
2Content＞99.9; Solidifying agent is a white powder, and oxirane value is about 0.9, and fusing point is 88-92 ℃, organic chlorine number＜0.02 equivalent/kg.
Technological process summary: unsaturated polyester resin, nano silicon oxide, solidifying agent, pigment and filler are mixed pulverizing, alternately mix with low speed at a high speed, being 1500-5000 rev/min stirred 5 minutes, changeing low speed stirred 5 minutes for 300-500 rev/min, change high-speed stirring again, low speed again, high low speed repeats repeatedly.Regulate and controlled temperature 100-120 ℃ of mixing extruding, broken the sieving of grain, grinding particle size control 160-220 order stores.
The film performance test result is as follows: condition of cure 180-190 ℃/15-20min; Appearance of film, color and luster is even, smooth; Glossiness is 30-40% for 60 °, resistance to impact shock 60cm, weathering resistance 1200 hours.
Embodiment 4, prescription are formed: unsaturated polyester resin 40% weight, nano aluminium oxide are 4% weight, and solidifying agent is 10% weight, and mineral filler is 40% weight, and pigment is 2% weight, and other auxiliary agents are 4% weight.
Main raw material(s) is selected: unsaturated polyester resin is selected acid number 55-75KOH/ gram, and softening temperature is 85-105 ℃, second-order transition temperature＞50 ℃; Nano oxidized aluminium particle size 10-50nm, Al
2O
3Content＞99.9; Solidifying agent is a white powder, and oxirane value is about 0.9, and fusing point is 88-92 ℃, organic chlorine number＜0.02 equivalent/kg.
Technological process summary: unsaturated polyester resin, nano aluminium oxide, solidifying agent, pigment and filler are mixed pulverizing, adopt at a high speed and alternately mix with low speed, being 1500-5000 rev/min stirred 5 minutes, changeing low speed stirred 5 minutes for 300-500 rev/min, high low speed circulation like this repeatedly, regulate and controlled temperature 100-120 ℃ of mixing extruding, the broken 160-220 order of grain sieves, and stores for future use.
The film performance test result is as follows: condition of cure 180-190 ℃/15-20min; Appearance of film, color and luster is even, smooth; Glossiness is 40-50% for 60 °, resistance to impact shock 65cm, weathering resistance 1200 hours.
Claims (6)
1, nanometer polyester powder coating, it comprises vibrin, solidifying agent, pigment, mineral filler and other auxiliary agents, and wherein inorganic nanometer powder is the 1-10% of gross weight, is preferably the 2-5% of gross weight.
2, the prescription of nanometer polyester powder coating as claimed in claim 1 is formed, it is characterized in that unsaturated polyester resin is a 20-50% weight, inorganic nanometer powder is a 2-5% weight, solidifying agent is a 7-10% weight, mineral filler is a 30-50% weight, pigment 1-5% weight, other auxiliary agents are 0-10% weight.
3, nanometer polyester powder coating as claimed in claim 1 or 2 is characterized in that unsaturated polyester resin is 20% weight, nano silicon oxide 3% weight, solidifying agent is 7% weight, mineral filler is 50% weight, and pigment is 10% weight, and other auxiliary agents are 10% weight.
4, nanometer polyester powder coating as claimed in claim 1 or 2 is characterized in that unsaturated polyester resin is 30% weight, nano zine oxide 5% weight, and solidifying agent is 8%, and mineral filler is 50% weight, and pigment is 2% weight, and other auxiliary agents are 5% weight.
5, nanometer polyester powder coating as claimed in claim 1 or 2 is characterized in that unsaturated polyester resin is 40% weight, and nano-titanium oxide is 2% weight, solidifying agent is 10% weight, mineral filler is 40% weight, and pigment is 2% weight, and other auxiliary agents are 6% weight.
6, nanometer polyester powder coating as claimed in claim 1 or 2 is characterized in that unsaturated polyester is 40% weight, and nano aluminium oxide is 4% weight, and solidifying agent is 10% weight, and mineral filler is 40% weight, and pigment is 2% weight, and other auxiliary agents are 4% weight.