CN1436872A - Fragile Ni-Fe alloy - Google Patents
Fragile Ni-Fe alloy Download PDFInfo
- Publication number
- CN1436872A CN1436872A CN 02100562 CN02100562A CN1436872A CN 1436872 A CN1436872 A CN 1436872A CN 02100562 CN02100562 CN 02100562 CN 02100562 A CN02100562 A CN 02100562A CN 1436872 A CN1436872 A CN 1436872A
- Authority
- CN
- China
- Prior art keywords
- nickel
- alloy
- steel
- iron alloy
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is one kind of easy-to-crush Ni-Fe alloy as steel-smelting additive. The alloy consists of Ni in 20-50 wt%, Mn is 8-25 wt% or Si in 5-20 wt% except Fe and inevitable impurities. The alloy has lower toughness and may be crushed into 10-50 mm size via conventional method for use in automatic material system.
Description
Technical field
The present invention relates to nickel---iron alloy, in particular as the frangible manganese or siliceous nickel one iron alloy of containing of steel-making additive.
Background technology
Nickel is stainless steel, deck of boat steel, bridge with steel, pipe line steel, and freight container is with the important alloying element in the steel grades such as steel.When smelting above-mentioned steel grade, the mode of adding the nickel plate in the common molten steel in the past makes the molten steel nickelalloyization.The shortcoming of this nickelalloyization is: the nickel plate is general to be dropped into artificial.The nickel plate that drops into evokes splashing of molten steel slag and molten steel, thereby very dangerous.Modern metallurgical equipment generally is provided with raw material and stores, the automation system of weighing and adding.For being suitable for this automatization feed circuit, raw material must be crushed to certain particle size.Because nickel has high toughness, thereby with the disintegrating apparatus of routine, be difficult to make the fragmentation of nickel plate as drop hammer, crusher etc.Though and available shears is cut into small pieces the nickel plate, this method is actually unpractical because of the effort of very taking a lot of work.Therefore the metallargist is badly in need of a kind of broken nickel one iron alloy that is easy to.
Summary of the invention
The objective of the invention is to by providing a kind of frangible manganese or siliceous nickel one iron alloy of containing to satisfy the requirement on metallurgical boundary.
Frangible manganiferous nickel one iron alloy of the present invention is made up of the Fe and the unavoidable impurities of (% weight) Ni of 20-50%, the Mn of 8-25% and surplus.
Manganese content in above-mentioned nickel one iron alloy is 10-15% preferably.
Frangible siliceous nickel one iron alloy of another kind of the present invention is made up of the iron and the unavoidable impurities of (% weight) Ni of 20-25%, the Si of 5-20% and surplus.
Si content in this not siliceous nickel one iron alloy is 8-15% preferably.
This siliceous nickel one iron alloy is applicable to smelts the low steel grade of si content
The toughness of above-mentioned two kinds of alloys is lower, thereby is easy to usual manner it is broken into the fritter of 10-50mm.
Below nickel one iron alloy of the present invention is described further book
Nickel is intended to be added on the element in the molten steel, and in nickel one iron alloy of the present invention, if nickel content greater than 50%, then causes the toughness of this alloy to rise, this is difficult to fragmentation as a result; When the Ni content in this Rhometal less than 20% the time, the amount of then adding this alloy is excessive, has increased the melting load.Therefore the Ni content in this alloy is decided to be 20-50%.
Manganese can make the toughness of nickel one iron alloy descend.When Mn content greater than 25% or less than 8% the time, the deleterious that it descends this alloy toughness.It is desirable especially that Mn content is decided to be 10-50%.
Silicon also can make the toughness of nickel one iron alloy descend.When Si content greater than 20% or less than 5% the time, the deleterious that it descends this alloy toughness, preferable Si content is 8-15%
The unavoidable impurities that contains in nickel one iron alloy of the present invention, such as, be Cu, Sn, C, P, S etc.
The toughness of nickel one iron alloy of the present invention is lower, thereby available ordinary method or as manual beat and disintegrating apparatus is crushed to the granularity of 10-50mm with it.
The preparation technology of nickel one iron alloy of the present invention is as follows:
Melt raw material nickel and steel cuttings in induction furnace.This raw material nickel comprises various recovery nickel and nickel plate.Behind raw material nickel and steel cuttings fine melt, take the lip-deep scum silica frost of molten metal off, to remove the impurity that raw material nickel and steel cuttings bring.Specification according to nickel one iron alloy of the present invention adds Mn-Fe or Si-Fe alloy and continues fusing then.Behind the alloy fine melt that adds, whether need further to adjust composition with decision by analysis of components to melt.After the composition adjustment finishes, in the liquid alloy injection model with gained, treat the cooling of this alloy graining after, the alloy that will solidify is poured out from mould, through finishing, the result obtains nickel of the present invention one iron alloy of designated size.
Embodiment
Further specify the present invention below by embodiment.
Embodiment 1:
Adding contains useless nickel screen 46kg and the clean rustless carbon element steel cuttings 40kg of the recovery of Ni98% from dyeing, the melting of switching on then in medium-frequency induction furnace.Behind the above-mentioned raw materials fine melt, take the lip-deep slag of molten metal off, add the mid-carbon fe-mn 14.5kg that contains Mn amount 78% again and continue the energising melting.Behind above-mentioned ferromanganese fine melt, take the lip-deep slag of molten metal off, the composition of sampling analysis molten metal, and fine setting composition.Adjusted alloy liquid is poured in the latticed opening model.Behind alloy graining, the alloy that will solidify is poured out, and carries out fragmentation and finishing again and obtains the nickel one iron alloy 100kg that granularity is 10-50mm, and its composition is:
Ni：44.08％、Mn：11.2％、Cu：0.83％、Sn：0.85％、
C:0.48%, P:0.022%, S:0.18%, Fe: surplus.
Embodiment 2
Add in medium-frequency induction furnace and contain Ni98% sheet nickel 46kg and clean rustless carbon element steel cuttings 42.5kg, the melting of switching on then is to above-mentioned raw material fine melt.After taking the lip-deep slag of molten metal off, add the ferrosilicon 12kg that contains Si78% again and continue the energising melting.Behind above-mentioned ferrosilicon fine melt, take the lip-deep slag of molten metal off, the composition of sampling analysis molten metal is also adjusted this composition.The alloy liquid of adjusting composition is poured in the latticed opening model.Behind alloy graining, the alloy that will solidify is poured out, and carries out fragmentation and finishing again, and obtaining granularity is the nickel one iron alloy 100kg of 10-50mm, and its composition is:
Ni：45.2％、Si：8.4％、Cu：0.75％、Sn：0.88％
C:0.52%, P:0.025%, S:0.020%, Fe: surplus.
The toughness that contains manganese or siliceous Rhometal of the present invention is very low, thereby available usual manner, at an easy rate it is broken into the fritter of 10-50mm degree as hand bumping, thereby this alloy can be used for automation system.The fusing point of this alloy is about 1280 ℃ in addition, and density is about 7,8g/cm
3, thereby be easy to sink in the molten steel and be fused to wherein.
Claims (5)
1. nickel one iron alloy as steel-making additive, it consists of (% weight): the Fe and the unavoidable impurities of the Ni of 20-50%, the Mn of 8-25%, surplus.
Claim 1 as nickel one iron alloy of steel-making additive, the Mn of this alloy amount is 10-15%.
3. frangible nickel one iron alloy as steel-making additive, it consists of (% weight): the Fe and the unavoidable impurities of the Ni of 20-25%, the Si of 5-20%, surplus.
Claim 3 as frangible nickel one iron alloy of steel-making additive, the si content of this alloy is 8-15%.
Among the claim 1-4 each as frangible nickel one iron alloy of steel-making additive, the granularity that it is characterized by this alloy is 10-50mm.