CN1426963A - Manufacturing method of nano cerium oxide powder - Google Patents
Manufacturing method of nano cerium oxide powder Download PDFInfo
- Publication number
- CN1426963A CN1426963A CN 01130088 CN01130088A CN1426963A CN 1426963 A CN1426963 A CN 1426963A CN 01130088 CN01130088 CN 01130088 CN 01130088 A CN01130088 A CN 01130088A CN 1426963 A CN1426963 A CN 1426963A
- Authority
- CN
- China
- Prior art keywords
- nano
- cerium
- manufacture method
- cerium oxide
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A nanometre-class cerium oxide powder is prepared through reaction between Ce-ion solution and alkaline solution under the existance of surfactant and normal temp. and pressure. Its advantages are fine and uniform granularity (20-50 nm), normal temp. and normal pressure reaction and low cost.
Description
Technical field
The present invention relates to the manufacture method of nano material, especially the manufacture method of nano-cerium oxide.
Background technology
Nano material is the novel material that development in recent years is got up, demonstrate purposes and special excellent effect widely in each field, particularly consumption is big aspect special glass, and at present, the vehicle glass of America and Japan all adds the radiation that cerium oxide is used for antiultraviolet, infrared rays and other ray.Because technology limitation, the cerium oxide particles granularity of making can't reach nano level at present, does not far reach the production scientific research requirements.Application number is the manufacture method that 99114908 Chinese invention patent application discloses a kind of nanometer cobalt oxide, it is characterized in that in chemical precipitation method, introducing tensio-active agent, the cobalt oxide granularity that produces reaches 5~60nm, but this method will be carried out in heating condition, thereby the production unit requirement is high, and cost improves greatly.
Summary of the invention
Purpose of the present invention will provide a kind of working condition requirement simple exactly, the little and manufacture method of uniform nano-cerium oxide of product granularity.
For reaching above-mentioned purpose, the method that the present invention makes nano-cerium oxide is as follows:
A, contain the preparation of Industrial intermediates solution or other aqueous solution that contains cerium ion of cerium ion;
The preparation of B, basic solution;
C, cerium ion solution and basic solution react under the condition of introducing tensio-active agent, and reaction is carried out at normal temperatures and pressures;
The washing of D, resultant, oven dry;
In the aforesaid method, described basic solution be in sodium hydroxide, potassium hydroxide, sodium oxalate, yellow soda ash or the ammoniacal liquor any.
Described tensio-active agent is at least a in Sodium dodecylbenzene sulfonate, stearic acid oxygen Vinyl Ether series, alkylphenol polyoxyethylene class (OP series), fatty acid loss water sorbit ester class (Tween series), polyvinyl alcohol, silicone oil, the polyacrylamide, consumption be cerium in the raw material weight percent 0.1~15%.
Adopt manufacture method of the present invention, the particle diameter of cerium oxide reaches 20~50nm, and granularity is tiny evenly; Reaction is carried out at normal temperatures and pressures, and production unit requires simple.
Embodiment
Embodiment 1: get the Industrial intermediates solution 60L that contains cerium ion 0.01~0.1M concentration, the adding weight percent is 20~45% sodium carbonate solution 50L and oxygen ethene sodium stearate 2~4KG, polyvinyl alcohol 0.5~1.5KG, normal temperature and pressure is reaction down, obtain light-yellow precipitate, washing, oven dry, 200~620 ℃ of sintering obtain light yellow nano level ceria oxide powder, and granularity is 50nm.
Embodiment 2: get the Industrial intermediates solution 50L that contains cerium ion 0.05~0.1M concentration, the adding weight percent is 20~45% sodium hydroxide solution 50L and Sodium dodecylbenzene sulfonate 1.5~3.5KG, polyacrylamide 0.5~1.5KG, normal temperature and pressure is reaction down, obtain light pink purple precipitation, washing, oven dry obtain light yellow nano level ceria oxide powder, and granularity is 20nm.
Claims (5)
1, a kind of manufacture method of nano-cerium oxide comprises the steps:
A, the Industrial intermediates solution that contains cerium ion or other aqueous solution that contains cerium ion
Preparation;
The preparation of B, basic solution;
C, cerium ion solution and basic solution react under the condition of introducing tensio-active agent;
The washing of D, resultant, oven dry;
It is characterized in that: the reaction under the condition of introducing tensio-active agent of cerium ion solution and basic solution is carried out at normal temperatures and pressures.
2, the manufacture method of nano-cerium oxide according to claim 1 is characterized in that: described basic solution be in sodium hydroxide, potassium hydroxide or the ammoniacal liquor any.
3, the manufacture method of nano-cerium oxide according to claim 1 is characterized in that: described alkaline dissolubility liquid is a kind of in sodium oxalate, the yellow soda ash.
4, according to the manufacture method of claim 1,2 or 3 described nano-cerium oxides, it is characterized in that: described tensio-active agent is at least a in Sodium dodecylbenzene sulfonate, stearic acid oxygen Vinyl Ether series, alkylphenol polyoxyethylene class (OP series), fatty acid loss water sorbit ester class (Tween series), polyvinyl alcohol, silicone oil, the polyacrylamide, consumption be cerium in the raw material weight percent 0.1~15%.
5, the manufacture method of nano cerium oxide powder according to claim 3 is characterized in that: need sintering after described resultant washing, the oven dry, sintering temperature is 200~620 ℃.