CN1425708A - Process for preparing waste rubber powder/poly olefine resin blend - Google Patents
Process for preparing waste rubber powder/poly olefine resin blend Download PDFInfo
- Publication number
- CN1425708A CN1425708A CN02155008A CN02155008A CN1425708A CN 1425708 A CN1425708 A CN 1425708A CN 02155008 A CN02155008 A CN 02155008A CN 02155008 A CN02155008 A CN 02155008A CN 1425708 A CN1425708 A CN 1425708A
- Authority
- CN
- China
- Prior art keywords
- polyolefin resin
- waste rubber
- rubber powder
- resin blend
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to the preparation process of waste rubber produce/polyolefin resin blend. The waste rubber produce/polyolefin resin blend is prepared through mixing waste rubber produce/polyolefin resin, rubber, silicon oil and organic peroxide in an opened mixer or double-screw extruder; and sulfurizing in a platen press. The waste rubber produce/polyolefin resin blend has high impact strength and great extension at break. The said process is simple, low in cost and less environmental pollution, and the utilization of waste rubber is favorable to protecting ecological environment.
Description
Technical field: the present invention relates to a kind of polymer blended preparation methods, the preparation method of particularly a kind of waste rubber powder/polyolefin resin blend.
Background technology: the mankind enter 21 century, and the recovery of spent high molecular material and utilization have become a urgent problem.In these spent high molecular materials, waste rubber next in number only to plastic waste, occupy second.The accumulation of a large amount of waste rubbers has not only caused the waste of resource, and provides the place for the breeding of mouse, mosquito.The waste rubber of piling up is easy to cause fire, and the waste rubber incomplete combustion can be emitted hydrocarbon polymer and toxic gas, and its flame is difficult to put out.In recent years, both at home and abroad waste rubber product is recycled, utilized or the like as thermolysis recovering liquid fuel and chemical, fuel utilization, reclaimed rubber utilization, rubber powder.Wherein, make that the rubber powder utilization is simple, energy-conservation because of its technology, water saving, reduce advantages such as environmental pollution, product performance be better and obtained more and more widely application.Rubber powder adds in rubber, pitch, the concrete, can make rubber item, pavior and material of construction or the like.In addition, mix rubber powder in the plastics, can improve the erosion-resisting characteristics of plastic material plastic toughening.Yet because the cross-linked structure of rubber powder, surface inertness makes that the consistency between they and the matrix is very poor, directly mixes in body material, is difficult to form bonding interface preferably, and the mechanical property of intermingling material is relatively poor.For this reason, some method of modifying of report in the domestic and foreign literature are to improve the mechanical property of waste rubber powder intermingling material.As USP5,506,283, KR2002017293-A, J.Appl.Polym.Sci., 2000,77:2595, Rubb.Chem.Technol., 1993,66:664, J.Mater.Sci., 1986, the surface of 21:1769 report Cement Composite Treated by Plasma, radiation grafting, solution graft copolymerization or chloridized rubber powder, the polarity of raising vulcanized rubber powder, but these complex treatment process, the equipment requirements height is difficult to realize industrialization; Plastic.Rubb.Comp.Proces.Appl., 1991,15:87, Plastic.Rubb.Comp.Proces.Appl., 1995,24:229, Plastic.Rubb.Comp.Proces.Appl., 1996,25:448, Polym.Eng.Sci., 1993,33:166, Rubb.Chem.Technol., 1992,65:908, improved combining of rubber powder and matrix resin by the method for adding various compatilizers, limited but the intermingling material mechanical property that adopts these methods to obtain improves, effect is not too obvious.
Summary of the invention: the objective of the invention is to waste rubber powder/polyolefin resin is body material, adopt a kind of new modified system, improve the mechanical property of intermingling material, and complete processing is simple, production cost is low, for the recycling of waste rubber provides new technological method.
The present invention utilizes polyolefin resin and waste rubber powder blend under certain melting temperature, adding rubber, silicone oil and organo-peroxide successively in waste rubber powder/polyolefin resin blend carries out mixing, the intermingling material that makes moulding under suitable condition obtains the plastic material that shock strength and elongation at break improve a lot.Owing to adopt rubber and silicone oil, between rubber powder particle and resin, formed the softish interfacial layer, help alleviating rubber powder stress concentration on every side.After adding organo-peroxide, waste rubber powder and matrix bond tightr, thus improved the mechanical property of intermingling material.
The preparation method of waste rubber powder of the present invention/polyolefin resin blend is in mill or twin screw extruder, at first add polyolefin resin, add waste rubber powder, rubber, silicone oil and organo-peroxide more successively, under 100 ℃～200 ℃ temperature, carry out mixing, mixing time is 1～30 minute, wherein polyolefin resin is 100 weight parts, waste rubber powder is 10～60 weight parts, rubber is 0～30 weight part, silicone oil is 0～10 weight part, and organo-peroxide is 0～0.5 weight part.Vulcanize in vulcanizing press then, curing temperature is 100 ℃～200 ℃, and curing time is 1～20 minute, obtains waste rubber powder/polyolefin resin blend.
The polyolefin resin that the present invention uses is new LDPE (film grade) (LDPE), high density polyethylene(HDPE) (HDPE), linear low density polyethylene (LLDPE), polypropylene (PP).
The particle diameter of the waste rubber powder that the present invention uses is 30～200 orders.
The rubber that the present invention uses is ethylene propylene rubber (EPR), terpolymer EP rubber (EPDM), natural rubber (NR), ethylene-octene copolymer, ethene-vinyl acetate copolymer.
The silicone oil that the present invention uses is methyl-silicone oil, ethyl silicon oil, methyl phenyl silicone oil, and its molecular weight is 1000～50000.
The organo-peroxide that the present invention uses is dicumyl peroxide, ditertiary butyl peroxide, 2,5-dimethyl-2,5-di-t-butyl peroxide hexane.
The shock strength and the elongation at break of the waste rubber powder that modified system of the present invention makes/polyolefin resin intermingling material are significantly improved, and can be used for making various products of rubber and plastic such as various pavement materials, roof Material, bed course, rubber and plastic boards.Complete processing of the present invention is simple, cost is low, environmental pollution is little, has solved the recycling problem of waste rubber to a great extent, and excellent industrial application foreground is arranged.
Embodiment: following embodiment is to further specify of the present invention, rather than limits the scope of the invention.
Embodiment 1-7: waste rubber powder/HDPE/EPDM/ dimethyl silicone oil/DCP blend
Embodiment 1-7 presses prescription separately, 180 ℃ of temperature of under, at first adds HDPE in the HAAKE torque rheometer, adds waste rubber powder, EPDM, dimethyl silicone oil and DCP then successively, and the blend time is 13min.The above-mentioned blend that obtains is vulcanized with vulcanizing press, 190 ℃ of * 8min.The of and cure conditions is Impact Test batten is of a size of 63.0mm * 3.2mm * 12.66mm, at a side mechanical workout v-notch that impacts batten, notch depth 2.66mm, 23 ℃ of breach bottom radius 0.25mm.Test mode is carried out according to ASTM256:selecting temperature is, socle girder notch shock mode, impact velocity 3.5m/s.The measurement of tensile strength is tested according to ASTMD638.Test result is as shown in the table. example 1234567 prescription (parts by weight) HDPE 100 100 100 100 100 100 100 waste rubber powder 40 10 20 30 40 50 60EPDM-10 10 10 10 10 10 dimethicone-4 4444 4DCP-0.2 0.2 0.2 0.2 0.2 0.2 physical and mechanical properties impact strengths; J/m 124 390 374 353 298 296 260 hot strengths; MPa 14.3 15.7 14.4 13.2 11.6 11.0 10.1 elongation at breaks, % 46 233 195 123 113 83 69
Embodiment 8-9 waste rubber powder/PP/NR/ dimethyl silicone oil/DCP blend
Under 190 ℃ temperature, at first the PP with 100 weight parts drops in the HAAKE torque rheometer, adds the waste rubber powder of 40 weight parts, the NR of 10 weight parts, the dimethyl silicone oil of 4 weight parts, the DCP of 0.2 weight part then successively, and the blend time is 13min.The above-mentioned blend that obtains is vulcanized with vulcanizing press, respectively according to ASTM D638, ASTM D256 test tensile property and impact property.Test result is as shown in the table.
Example 89
Prescription (parts by weight)
PP 100 100
Waste rubber powder 40 10
NR - 10
Dimethyl silicone oil-4
DCP - 0.2
Physical and mechanical properties
Shock strength, J/m 19 56
Tensile strength, MPa 28 22
Elongation at break, % 14 37
Claims (6)
1. the preparation method of waste rubber powder/polyolefin resin blend, it is characterized in that in mill or twin screw extruder, at first add polyolefin resin, add waste rubber powder, rubber, silicone oil and organo-peroxide more successively, under 100 ℃～200 ℃ temperature, carry out mixing, mixing time is 1～30 minute, wherein polyolefin resin is 100 weight parts, waste rubber powder is 10～60 weight parts, rubber is 5～30 weight parts, silicone oil is 0～10 weight part, and organo-peroxide is 0～0.5 weight part.Vulcanize in vulcanizing press then, curing temperature is 100 ℃～200 ℃, and curing time is 1～20 minute, obtains waste rubber powder/polyolefin resin blend.
2. the preparation method of waste rubber powder according to claim 1/polyolefin resin blend is characterized in that polyolefin resin is new LDPE (film grade), high density polyethylene(HDPE), linear low density polyethylene, polypropylene.
3. the preparation method of waste rubber powder according to claim 1/polyolefin resin blend, the particle diameter that it is characterized in that waste rubber powder is 30～200 orders.
4. the preparation method of waste rubber powder according to claim 1/polyolefin resin blend is characterized in that rubber is ethylene propylene rubber, terpolymer EP rubber, natural rubber, ethylene-octene copolymer, ethene-vinyl acetate copolymer.
5. the preparation method of waste rubber powder according to claim 1/polyolefin resin blend is characterized in that silicone oil is methyl-silicone oil, ethyl silicon oil, methyl phenyl silicone oil, and its molecular weight is 1000～50000.
6. the preparation method of waste rubber powder according to claim 1/polyolefin resin blend is characterized in that organo-peroxide is dicumyl peroxide, ditertiary butyl peroxide, 2,5-dimethyl-2,5-di-t-butyl peroxide hexane.