CN1424351A - High specific weight film material - Google Patents
High specific weight film material Download PDFInfo
- Publication number
- CN1424351A CN1424351A CN 02157783 CN02157783A CN1424351A CN 1424351 A CN1424351 A CN 1424351A CN 02157783 CN02157783 CN 02157783 CN 02157783 A CN02157783 A CN 02157783A CN 1424351 A CN1424351 A CN 1424351A
- Authority
- CN
- China
- Prior art keywords
- film material
- high specific
- tungsten powder
- agent
- specific weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A film material with high specific weight for effectively reducing noise contains PVC (5-35 wt.%), tungsten powder (40-90), coupling agent (1-10) and assistant (4-15). Its advantages are high mechanical performance and specific weight, high fire-retarding nature and machinability and no poison.
Description
Technical field
What the present invention relates to is a kind of matrix material, and particularly a kind of high specific gravity film composite material belongs to polymeric material field.
Background technology
In Composite Preparation, the density of filler itself and the ratio that can insert all play a decisive role to the density that improves the gained matrix material.Find by literature search, China Patent No. is: 97197487.X, patent name is: high density composite, announced a kind of high density composite, this patent the tungsten powder combination of 2~40 microns of the fiber that improves intensity and diameters, is made a kind of material (as projectile core equivalent material nontoxic, unleaded, environmentally safe, that save money) that can be used as plumbous substitute by binding agent.Its material composition is tungsten powder and fiber and caking agent, by injection moulding, compression molding, is used to be sought after the occasion that plumbous high-density does not wish to have Lead contamination again, and as the substitute of leaded high density material.But this material since its composition (fiber and caking agent) only determined can be with injection moulding or compression molding, so difficulty is made large-area film.
Summary of the invention
The present invention is directed to disadvantages of background technology and defective, provide a kind of and designed, produce, the simple high specific gravity thin-film material of technology according to Principles of Acoustics.The present invention is achieved by the following technical solutions, and each component of the present invention and weight percent thereof are specific as follows: PVC:5%~35%; Particle diameter is less than 2 microns tungsten powder: 40%~90%; Coupling agent: 1%~10%; Auxiliary agent: 4%~15%; By can particularly making large-area film through injection moulding or compression molding after mixing by calendering formation technology.
Wherein the diameter of tungsten powder is preferably 0.1~1.8 micron, and coupling agent adopts one or more in the titante coupling agent, one or more in the common stablizer of selection of auxiliary, softening agent and the antiaging agent.
The present invention has substantive distinguishing features and marked improvement.Material of the present invention not only has very high density, and has good mechanical mechanics property, and is nontoxic, fire-retardant, particularly abandoned fiber and caking agent in material composition, therefore can make flexible film by rolling continuously shaped technology.This material can be used for the sound insulation and noise reducing of noise.
Embodiment
Further provide following examples: embodiment the density of one material over-all properties Different Weight proportioning institute prepared material in conjunction with content of the present invention
The every performance of material
Percentage ratio % (tungsten powder) | ????60 | ????75 | ????80 | ????85 | ????90 |
Density (g/cm 3) | ????3.2 | ????3.75 | ????4.16 | ????4.58 | ????5.3 |
Percentage ratio % (tungsten powder) | ????60 | ????75 | ??80 | ????85 | ????90 | |
Tensile strength MPa | Laterally | ????24.77 | ????10.067 | ??9.038 | ????7.276 | ????6.2 |
Vertically | ????28.31 | ????9.875 | ??8.779 | ????7.12 | ????5.67 | |
Elongation at break % | Laterally | ????214.5 | ????239.6 | ??276.37 | ????320.3 | ????194.17 |
Vertically | ????250 | ????223.87 | ??263.53 | ????216.83 | ????178.5 | |
Flame retardant resistance | Fire-retardant | Fire-retardant | Fire-retardant | Fire-retardant | Fire-retardant |
Annotate: the tungsten powder diameter is 0.2 micron in the table
Embodiment two
Each component is with following proportioning uniform mixing, and mixing in mill, make 1 millimeter soft thin slice, its mean transmission loss is about 32 decibels.
PVC:35%, tungsten powder (0.6 micron): 40%, monoalkoxy three (dioctylphosphato) titanic acid ester: 10%, dibutyl phthalate: 10%, barium stearate: 2%, lead sulfate tribasic: 3%.
Embodiment three
It is mixing in mill that following component is mixed the back, makes 1 millimeter soft thin slice, and its oise insulation factor is between 18 ~ 30 decibels (100 ~ 1600Hz).
PVC:5%, tungsten powder (1.8 microns): 90%, sec.-propyl three carboxyl titanic acid ester 1%, dibutyl phthalate: 3%, barium stearate: 0.5%, lead sulfate tribasic: 0.5%.
Embodiment four
Get PVC:20%, tungsten powder (0.6 micron): 65%, monoalkoxy three (dioctylphosphato) titanic acid ester: 5%, dibutyl phthalate: 8%, barium stearate: 1%, organotin: 1%.Made composite density is 3.54g/cm
3
Claims (4)
1, a kind of high specific gravity thin-film material, it is characterized in that: each component and weight percent thereof are specific as follows: PVC:5%~35%; Particle diameter is less than 2 microns tungsten powder: 40%~90%; Coupling agent: 1%~10%; Auxiliary agent: 4%~15%.
2, this high specific gravity thin-film material according to claim 1 is characterized in that wherein the diameter of tungsten powder is preferably 0.1~1.8 micron.
3, this high specific gravity thin-film material according to claim 1 is characterized in that described coupling agent, and it adopts in the titante coupling agent one or more.
4, this high specific gravity thin-film material according to claim 1 is characterized in that described auxiliary agent, is to select in stablizer, softening agent and the antiaging agent one or more for use.