CN1399007A - Chemical deactivation process of martensite stainless steel - Google Patents
Chemical deactivation process of martensite stainless steel Download PDFInfo
- Publication number
- CN1399007A CN1399007A CN 02122917 CN02122917A CN1399007A CN 1399007 A CN1399007 A CN 1399007A CN 02122917 CN02122917 CN 02122917 CN 02122917 A CN02122917 A CN 02122917A CN 1399007 A CN1399007 A CN 1399007A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- martensite stainless
- passivation
- technology according
- deactivation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention is a chemical passivation process of martensite stainless steel. Martensite stainless steel part is washed, eroded, passivation and closed treated to form anticorrosive oxide film on the surface to strengthen the anticorrosive capacity of the part.
Description
The part that the present invention relates to Martensite Stainless Steel processing cleans, the technology of etch, passivation, sealing.
Have the Martensite Stainless Steel passivation now mainly based on electrochemical method, energy consumption height, not easy to operate.
The invention provides a chemical deactivation process, this technological operation is simple, good reliability.
The present invention after the Martensite Stainless Steel part that will process is adjusted hardness by thermal treatment, carries out the Cleaning and Passivation art breading, makes the stainless steel components surface form the strong oxide film of erosion resistance.
Fig. 1 is a kind of Martensite Stainless Steel chemical deactivation process schema.
Below in conjunction with accompanying drawing the present invention is realized that the Martensite Stainless Steel passivation is elaborated.
The thermal treatment of Martensite Stainless Steel part is carried out mechanical polishing by operation 1 after adjusting hardness, operation 2 washings, and operation 3 electrochemical deoilings, operation 4 washings enter operation 5 etches, 2~20 minutes etch time, 5~50 ℃ of temperature, etching solution is by H
2SO
4(140~160g/L), (50~150g/L) form H.F.S.Enter operation 7 chemical passivations after operation 6 washings, passivation time 10~180 minutes, 25~70 ℃ of temperature, passivating solution is by Na
2Cr
2O
72H
2O (20~30g/L), 65%HNO
3(300~500g/L) form.Enter operation 9 sealings after operation 8 washings, 5~30 minutes off-periods, 10~55 ℃ of temperature, confining liquid is by Na
2Cr
2O
72H
2O (5~15g/L), Na
2CO
3(5~30g/L), GH~713 (28g/L) form.Enter operation 11 neutralizations after operation 10 washing, in and 10~60 minutes time, 30~75 ℃ of temperature, neutralizer is 1~10% NaOH solution.Then enter operation 12 washings, operation 13DI water floats, operation 14 dewatered dryings.
The present invention has process stabilizing, energy savings, low, the efficient high of cost. By this The product produced of invention has stronger resistance to corrosion, can be by 4 hours boiling tests and Non-corrosive.
Claims (6)
1, the present invention is characterized in that the Martensite Stainless Steel passivation technology be made up of mechanical polishing, cleaning, etch, chemical passivation, sealing.
2, technology according to claim 1 is characterized in that the sealing after the chemical passivation.
3, technology according to claim 1 is characterized in that the etch that chemical passivation is preceding.
4, technology according to claim 1 is characterized in that the chemical passivation condition is 1~180 minute time, 25~70 ℃ of temperature, and passivating solution is by Na
2CrO
72H
2O (20~30g/L), 65%HNO
3(300~500g/L) form.
5, technology according to claim 1 is characterized in that sealing condition is 5~30 minutes time, 10~55 ℃ of temperature, and confining liquid is by Na
2CrO
72H
2O (5~15g/L), Na
2CO
3(5~30g/L), GH~713 (28g/L) form.
6, technology according to claim 1 is characterized in that the etch condition is 2~20 minutes time, 5~50 ℃ of temperature, and etching solution is by H
2SO
4(140~160g/L), (50~150g/L) form H.F.S.