CN1369523A - Environment protecting green decorative material - Google Patents
Environment protecting green decorative material Download PDFInfo
- Publication number
- CN1369523A CN1369523A CN 02109126 CN02109126A CN1369523A CN 1369523 A CN1369523 A CN 1369523A CN 02109126 CN02109126 CN 02109126 CN 02109126 A CN02109126 A CN 02109126A CN 1369523 A CN1369523 A CN 1369523A
- Authority
- CN
- China
- Prior art keywords
- weight part
- agate
- environment protecting
- decorative material
- decorative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An environment protection type decorative material is prepared from powdered jade or agate, flame-retarding agent, solidifying agent, promotor, anticorrosion agent, harmless essence and butanediester through proportional mixing, casting, shaping, polishing, assembling trimming and patterning. Its advantagesa are good appearance, smooth surface, high fire-retarding effect, no poison, high resistance to water, oil, smoke, acid, alkali, etc. and high hardness and toughness.
Description
Technical field
The present invention relates to finishing material, is to utilize natural jade powder or agate powder, fire-retardant nontoxic macromolecule polyester resin composition synthetic finishing material specifically.
Background technology
Line in the present finishing material, plate, the side, moulding, engraving, as the ground linea angulata, heater cover, picture frame, screen cuts off, various ornamental pattern designs etc., a kind of is to adopt natural materials, as timber, lithotome etc., another kind of artificial simulated material, as imitative beautiful decorative sheet, artificial marbles etc., timber belong to the aquosity material, and are water funk, be afraid of oil, be afraid of cigarette, wood surface has many pores, time is long oil slightly, cigarette, water immerses, and falls to going up dust again, is difficult to dispose the recovery clean surface, influence decorative effect, wood materials also is not suitable for complex model, and natural resource more and more lack, so another kind of artificial simulated material is widely used recently, decorative imitation jade material adopts unsaturated polyester resin to add initiator, filler, promotor etc. are formulated, though decorative imitation jade material can imitate out the exquisitely carved aesthetic feeling of jade,, the nourishing function that does not have natural jade, also do not have the texture of natural jade, flame retardant properties is poor, has the danger that causes fire easily.Along with people improve constantly the living environment specification of quality, also more and more higher to the finishing requirement, finishing material also will have environmental protection, harmless except that having aesthetic feeling, have and be suitable for healthy health care etc.Material such as natural jade, agate not only has exquisitely carved U.S., and smooth surface does not have pore, not water funk, not oil suction, is not afraid of cigarette, acid and alkali-resistance, high temperature resistant, freezing indeformable, colour-fast, flame retardant properties is good, nontoxic, and have functions such as health care, always be subjected to liking of people, it is optimal finishing material, but owing to natural jade, agate reserves rareness cost an arm and a leg, it is too high to make the finishing material cost, and this material only is used on the craft articles at present.Natural jade, agate etc. be often remaining waste materials when being processed into artwork, if it is that the powder utilization is on finishing material that these waste materials are pulverized, the advantage that existing cost is low, serious, the natural, graceful and poised magnanimous makings of material such as natural jade, agate are arranged again, environmental protection, harmless has and is suitable for healthy health care, can improve the class of finishing, not raising the cost again, is new field of finishing material.
Summary of the invention
It is low, fire-retardant, nontoxic to the purpose of this invention is to provide a kind of cost, utilizes the environment protecting green decorative material of natural jade, agate powder.
The object of the present invention is achieved like this:
A kind of environment protecting green decorative material, it is characterized in that: with natural jade powder or agate is major ingredient, and proportioning is to add 600 weight part jade powder or agate powder, 60～80 parts by weight of flame retardant, 15～50 weight part solidifying agent, 10～40 weight part promotor, 20～50 weight part sanitass, the harmless essence of 0.5% weight part, 10～80 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
Above-mentioned finishing material can be made the decoration heater cover, decorates picture frame, decorates column cap, matting, decoration flower angle, decorative figure pattern, and finishing material such as other line, plate, side, moulding, engraving.
Above-mentioned environment protecting green decorative material, its manufacture craft is:
(1) batching: according to the above ratio each material is blended in the unsaturated polyester resin, is modulated into slurry;
(2) molding: make mould as required;
(3) cast: above-mentioned prepared slurry is poured in the mould;
(4) moulding:, dry through the molded curing typing;
(5) polishing: remove the unnecessary part of burr;
(6) combination: on base plate, mix decorative pattern, be combined into the integral installation exterior material;
(7) refine: reach design requirements with the process means processing.
Benefit of the present invention is:
Have the texture of natural jade, agate, cost is low, and smooth surface does not have pore, not water funk, not oil suction, be not afraid of cigarette, acid and alkali-resistance, flame retardant properties is good, and is nontoxic, high temperature resistant, freezing indeformable, colour-fast, the hardness that had both had natural jade, agate, have good toughness again, can saw, dig,, easily splicing nail, long service life has timber and the incomparable effect of other finishing material.
Description of drawings
Fig. 1 decorates the heater cover design sketch
Fig. 2 decorates the picture frame design sketch
Fig. 3 decorates the column cap design sketch
Fig. 4 matting design sketch
Fig. 5 decoration flower angle 1 design sketch
Fig. 6 decoration flower angle 2 design sketchs
Fig. 7 decorative figure pattern 1 design sketch
Fig. 8 decorative figure pattern 2 design sketchs
Fig. 9 decorative figure pattern 3 design sketchs
Figure 10 decorative figure pattern 4 design sketchs
Figure 11 decorative figure pattern 5 design sketchs
Figure 12 decorative figure pattern 6 design sketchs
Figure 13 decorative figure pattern 7 design sketchs
Figure 14 decorative figure pattern 8 design sketchs
Embodiment
Embodiment 1:
Proportioning is to add 600 weight part jade powder, 60 parts by weight of flame retardant, 30 weight part solidifying agent, 20 weight part promotor, 20 weight part sanitass, the harmless essence of 0.5% weight part, 20 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
Make the finished product finishing material by following technology:
(1) batching: according to the above ratio each material is blended in the unsaturated polyester resin, is modulated into slurry;
(2) molding: make mould as required;
(3) cast: above-mentioned prepared slurry is poured in the mould;
(4) moulding:, dry through the molded curing typing;
(5) polishing: remove the unnecessary part of burr;
(6) combination: on base plate, mix decorative pattern, be combined into the integral installation exterior material;
(7) refine: reach design requirements with the process means processing.
Make decoration heater cover as shown in Figure 1, decoration picture frame as shown in Figure 2, decoration column cap as shown in Figure 3, matting as shown in Figure 4, decoration flower angle shown in Fig. 5,6, as decorative figure pattern of Fig. 7～shown in Figure 14 or the like, and finishing material such as other line, plate, side, moulding, engraving.
Several main finishing material The performance test results are as follows:
| Performance | Decorate heater cover | Decorate picture frame | Wire rod and other |
| Glossiness | Half-light | Half-light | Half-light |
| The H of acid resistance 0.1mol 2SO 4Soaked 48 hours | Do not change | Do not change | Do not change |
| The NaOH of alkali resistance 0.1mol soaked 48 hours | Do not change | Do not change | Do not change |
| 30 seconds kinds of burning are from fire in the fire line naked light | Kind was extinguished in 5 seconds | Kind was extinguished in 5 seconds | Kind was extinguished in 5 seconds |
| The oil-proofness sample soaked in oil 8 hours | Do not immerse | Do not immerse | Do not immerse |
| The water-repellancy sample soaked in water 48 hours | Waterproof | Waterproof | Waterproof |
Embodiment 2:
Proportioning is to add 600 weight part agate powders, 60 parts by weight of flame retardant, 15 weight part solidifying agent, 10 weight part promotor, 20 weight part sanitass, the harmless essence of 0.5% weight part, 10 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
Embodiment 3:
Proportioning is to add 600 weight part jade powder, 60 parts by weight of flame retardant, 40 weight part solidifying agent, 30 weight part promotor, 20 weight part sanitass, the harmless essence of 0.5% weight part, 40 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
Embodiment 4:
Proportioning is to add 600 weight part agate powders, 60 parts by weight of flame retardant, 50 weight part solidifying agent, 40 weight part promotor, 20 weight part sanitass, the harmless essence of 0.5% weight part, 60 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
Claims (2)
1. environment protecting green decorative material, it is characterized in that: with natural jade powder or agate is major ingredient, and proportioning is to add 600 weight part jade powder or agate powder, 60～80 parts by weight of flame retardant, 15～50 weight part solidifying agent, 10～40 weight part promotor, 20～50 weight part sanitass, the harmless essence of 0.5% weight part, 10～80 weight part fourths, two fat in per 400 weight part unsaturated polyester resins.
2. environment protecting green decorative material according to claim 1, its manufacture craft is:
(1) batching: according to the above ratio each material is blended in the unsaturated polyester resin, is modulated into slurry;
(2) molding: make mould as required;
(3) cast: above-mentioned prepared slurry is poured in the mould;
(4) moulding:, dry through the molded curing typing;
(5) polishing: remove the unnecessary part of burr;
(6) combination: on base plate, mix decorative pattern, be combined into the integral installation exterior material;
(7) refine: reach design requirements with the process means processing.