CN1359956A - Process for preparing hydroxypropylmethyl cellulose by one-step method - Google Patents
Process for preparing hydroxypropylmethyl cellulose by one-step method Download PDFInfo
- Publication number
- CN1359956A CN1359956A CN 00129441 CN00129441A CN1359956A CN 1359956 A CN1359956 A CN 1359956A CN 00129441 CN00129441 CN 00129441 CN 00129441 A CN00129441 A CN 00129441A CN 1359956 A CN1359956 A CN 1359956A
- Authority
- CN
- China
- Prior art keywords
- vltra tears
- preparation
- single stage
- described single
- stage method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A one-step process for preparing hydroxypropylmethyl cellulose includes such steps as feeding refined cotton, caustic alkali, chloromethane and epoxy propane into high-pressure reactor, heating, pressurizing, dalkalizing-methylating-hydroxypropylating reaction, and post processing. Its advantages are short reaction times, high and stable product quality and high productivity.
Description
The invention belongs to the preparation of cellulose scope of replacement, relate to the preparation method of single stage method Vltra tears.
In the prior art; HPMC (Vltra tears; Hydroxypropanalmethyl cellulose) be to make soda cellulose through the alkali lye dipping by purified cotton; again through the unnecessary alkali lye of centrifugal removal; the soda cellulose that obtains is experienced at a certain temperature; after soda cellulose after experienced is put into the autoclave deoxygenation; add MeCl (methyl chloride, Methyl chliride) and PO (propylene oxide, Propylene oxide) temperature reaction; after reaction finishes; reclaim MeCl, discharging is centrifugal then, and the material after centrifugal is put into washing bath again; neutralize with hydrochloric acid; wash twice again with water, pH value reaches at 7 o'clock, discharging; centrifugally put into the tablets press granulation; through coarse reduction, dry again; pulverize and promptly get the HPMC finished product.
The defective that prior art exists:
1. because of adopting the alkali lye pickling process, consume a large amount of solid caustic soda, increased equipment such as choline pond, alkalization groove simultaneously, operator's labour intensity is big, and operating environment is arduous; Production cycle is long, production efficiency and yielding poorly;
2. amount of liquid is little in the steeping process, and solid-to-liquid ratio is little, stirs to be difficult for evenly, and the purified cotton alkalization is inhomogeneous, causes next step etherificate bad, and insolubles increases, and directly has influence on quality product.
Purpose of the present invention provides the preparation method of the single stage method Vltra tears that a kind of equipment is few, the cycle is short, production efficiency is high.
Technical scheme of the present invention is:
Develop a kind of preparation method of single stage method Vltra tears, it is characterized in that in autoclave, adding purified cotton, caustic alkali, methyl chloride and propylene oxide, heat up, boost, a step finishes alkalization, methylate and hydroxypropylation reacts, and gets the Vltra tears finished product through aftertreatment.
The proportioning raw materials of aforesaid method is:
Purified cotton: caustic alkali: methyl chloride: propylene oxide=1: 0.9～1.2: 6～25: 0.2～0.8, except that the methyl chloride consumption was volume, all the other were weight.
The reaction conditions of aforesaid method is 30～85 ℃, 0.4～2.4Mpa, reaction 2～6h.
The aftertreatment of aforesaid method comprises the recovery etherifying agent, neutralize crude product, crude product is again through crystal's system.
When aforesaid method reclaimed etherifying agent, separating liquid reclaimed etherifying agent from the reaction mass system earlier, and etherifying agent is reclaimed in redistillation.
In the aforesaid method and the time with acetic acid or hydrochloric acid.
The caustic alkali of aforesaid method adopts the 30-60% sodium hydroxide solution.
The advantage of technology of the present invention is:
1. having improved alkalization process, is not to be dissolved into liquid caustic soda with solid caustic soda earlier, again the method that alkalizes with excessive liquid caustic soda dipping; Alkalize but change the alkali lye that adds relative quantification into, the alkali lye and the etherifying agent that promptly add dosage in autoclave carry out alkalization, etherificate in same equipment, reduced facility investment, shortened the reaction times greatly, the corresponding working strength of workers that reduced, clean operating environment, with short production cycle, improved production efficiency and output.
In the steeping process except that the alkali lye of dosage, add the etherifying agent in step down in the lump, this moment, they used as solvent, thereby amount of liquid is big in the reactor, and solid-to-liquid ratio is reasonable, causes the purified cotton alkalization evenly, etherificate is complete, and substitution value is high and even, constant product quality.
3. suppress the side reactions such as hydrolysis of PO and MeCl, reduced raw material consumption, reduced cost.
The present invention is further elaborated below in conjunction with drawings and Examples:
Fig. 1 is a process flow sheet of the present invention.
Among the figure, feed purification cotton, liquid caustic, MeCl, PO go on foot through alkalization, etherificate operation one and finish alkalization, methylate and hydroxypropylation reaction (alkali lye recovery recycled), with in acetic acid or the hydrochloric acid and after crude product, again through washing, granulation, oven dry, after pulverizing, confuse, packing finished product.
Embodiment one
Add purified cotton, caustic alkali, methyl chloride and propylene oxide in autoclave, heat up, boost, a step finishes alkalization, methylate and hydroxypropylation reacts, and proportioning raw materials is:
Purified cotton: caustic alkali: methyl chloride: propylene oxide=1: 0.9: 25: 0.2.Except that the methyl chloride consumption was volume, all the other were weight.Reaction conditions is 30～85 ℃ (though be to finish three-step reaction in same reactor together, in fact still need experience alkalization, methylate and three reaction process of hydroxypropylation, so temperature span is bigger), 0.4～2.4Mpa, reaction 2～3h.Aftertreatment comprises the recovery etherifying agent, gets crude product after the neutralization, and crude product makes the Vltra tears finished product through the crystal again.Through checking with quadrat method, quality is better than prior art.
When reclaiming etherifying agent, separating liquid reclaims etherifying agent from the reaction mass system earlier, and etherifying agent is reclaimed in redistillation.
In and the time use acetic acid, caustic alkali employing 50～60% sodium hydroxide solutions.
Embodiment two
Proportioning raw materials is: purified cotton: caustic alkali: methyl chloride: propylene oxide=1: 1.2: 6: 0.8, reaction 5～6h, in and the time use hydrochloric acid, caustic alkali employing 30～40% sodium hydroxide solutions.All the other are with embodiment one.
Embodiment three
Proportioning raw materials is: purified cotton: caustic alkali: methyl chloride: propylene oxide=1: 1: 15: 0.6; Reaction 4～5h, caustic alkali adopts 40% sodium hydroxide solution, and all the other are with embodiment one.
Claims (7)
1. the preparation method of a single stage method Vltra tears, it is characterized in that in autoclave, adding purified cotton, caustic alkali, methyl chloride and propylene oxide, heat up, boost, a step finishes alkalization, methylate and hydroxypropylation reacts, and gets the Vltra tears finished product through aftertreatment.
2. according to the preparation method of the described single stage method Vltra tears of claim 1, it is characterized in that proportioning raw materials is: purified cotton: caustic alkali: methyl chloride: propylene oxide=1: 0.9～1.2: 6～25: 0.2～0.8, except that the methyl chloride consumption was volume, all the other were weight.
3. according to the preparation method of the described single stage method Vltra tears of claim 1, it is characterized in that reaction conditions is 30～85 ℃, 0.4～2.4Mpa, reaction 2～6h.
4. according to the preparation method of the described single stage method Vltra tears of claim 1, it is characterized in that described aftertreatment comprises the recovery etherifying agent, get crude product after the neutralization, crude product is again through crystal's system.
5. according to the preparation method of the described single stage method Vltra tears of claim 4, when it is characterized in that reclaiming etherifying agent, separating liquid reclaims etherifying agent from the reaction mass system earlier, and etherifying agent is reclaimed in redistillation.
6. according to the preparation method of the described single stage method Vltra tears of claim 3, in it is characterized in that and the time with acetic acid or hydrochloric acid.
7. according to the preparation method of the described single stage method Vltra tears of claim 1, it is characterized in that caustic alkali adopts 30～60% sodium hydroxide solutions.