CN1351096A - Asphalt cementing material for drainage-type pavement and its preparing process - Google Patents

Asphalt cementing material for drainage-type pavement and its preparing process Download PDF

Info

Publication number
CN1351096A
CN1351096A CN 00123145 CN00123145A CN1351096A CN 1351096 A CN1351096 A CN 1351096A CN 00123145 CN00123145 CN 00123145 CN 00123145 A CN00123145 A CN 00123145A CN 1351096 A CN1351096 A CN 1351096A
Authority
CN
China
Prior art keywords
pitch
bituminous cements
described bituminous
polymkeric substance
toughness
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 00123145
Other languages
Chinese (zh)
Other versions
CN1132883C (en
Inventor
李志军
宁爱民
吴佩尊
陈杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
China Petroleum and Chemical Corp
Sinopec Fushun Research Institute of Petroleum and Petrochemicals
Original Assignee
China Petroleum and Chemical Corp
Sinopec Fushun Research Institute of Petroleum and Petrochemicals
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by China Petroleum and Chemical Corp, Sinopec Fushun Research Institute of Petroleum and Petrochemicals filed Critical China Petroleum and Chemical Corp
Priority to CN 00123145 priority Critical patent/CN1132883C/en
Publication of CN1351096A publication Critical patent/CN1351096A/en
Application granted granted Critical
Publication of CN1132883C publication Critical patent/CN1132883C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

A polymer modified asphalt cementing material for drainage-type pavement is prepared from asphalt, thermoplastic elastomer, rubber-type polymer, and resin-type polymer through proportional mixing under high-temp and high-shearing condition. Its characteristic parameters are 40-80 1/10 mm (25 deg.C) of penetration, 55-105 deg.C of soft point, 10000-100000 Pa.s (60 deg.C) of viscosity, and toughness of more than 10N.m.

Description

Asphalt cementing material for drainage-type pavement and preparation method thereof
The invention relates to a kind of have high viscosity and high sticking flexible polymer modified asphalt agglutinate, it is suitable for use as advanced road, particularly the making of drainage road.The present invention is relevant with the method for this agglutinate of preparation simultaneously.
Drainage road is the pavement structure of a kind of open gradation, big voidage, the watertight layer below the surface gathered water when it can be with rainfall infiltrates, and drain rapidly by the curb position, thereby alleviated the infringement that ponding road pavement structure causes.This pavement structure also can be eliminated the moisture film level and smooth phenomenon of rainy day during high vehicle speeds, improves travel safety.In addition, also can reduce the vehicle serious day by day noise pollution that high speed brought day by day of travelling.
Though drainage road has many advantages, because its structure is special, the road surface voidage reaches (voidage on general dense-graded asphalt concrete road surface is 3~6%) about 20%, and this has just proposed requirements at the higher level to the performance of road tar agglutinate.Major cause has: the fine aggregate component is few in (1) drainage road, must use the sticking big agglutinate of toughness to improve the intensity and the stability of compound; (2) pavement structure of big voidage has increased the chance that pitch contacts with airborne oxygen, must use full-bodied agglutinate to form thicker asphalt membrane, reduces the ager process on road surface; (3), must use and the good agglutinate of aggregate adhesivity improves the water resisting property on road surface because ponding oozes down internally, and the influence that drainage road is peeled off by water is more serious.Obviously, use general road tar agglutinate to be difficult to satisfy above-mentioned requirements.
In order to satisfy the needs of making drainage road, it is main component with pitch that Japanese patent laid-open 4-357202 has disclosed a kind of, and mixes and convert the drainage road bituminous cements that petroleum-type solvent-extracted oil, resin, thermoplastic elastomer etc. are made; Te Kaiping 9-291219 has described pitch and 5~10 parts of thermoplastic elastomers, 1~10 part of lubricating oil distillate of a kind of 100 parts of penetration degrees 40~100 and has extracted oil and 2~15 parts of mixed drainage modifying asphalt mixtures that get of hydrocarbon resin out.Yet above-mentioned patent all needs to add the solvent-extracted oil in the refined course of lubricating oil in the process of preparation drainage asphalt agglutinate, and this has increased the difficulty of producing concerning the refinery that does not have the lubricating oil processing device.Simultaneously, the used raw material of above-mentioned patent meets the pitch of Japanese Industrial Standards' (JIS standard) all at penetration degree 40~1001/10mm, and the source of raw material is very restricted.
The objective of the invention is to satisfy the particular requirement of making drainage road and the weak point in the Japanese relevant patent, polymer modified asphalt agglutinate that a kind of raw material sources are extensive, the simple making drainage road of preparation process is used and preparation method thereof is provided at the performance of general bituminous cements.
The invention provides the bituminous cements that a kind of making drainage road is used, this bituminous cements is mixed getting under high temperature, shear conditions by pitch and a kind of thermoplastic elastomer, a kind of rubber polymer and a kind of resene polymkeric substance.Wherein the polymkeric substance weight percent that accounts for total mixture enough makes formed agglutinate have following feature: penetration degree (25 ℃) 40~80 1/10mm, preferably 40~60 1/10mm; 55~105 ℃ of softening temperatures, preferably 80~100 ℃; 60 ℃ of viscosity 10000~100000Pas, preferably 20000~50000Pas; Sticking toughness is greater than 15Nm, preferably greater than 20Nm; Toughness is greater than 10Nm, preferably greater than 15Nm.
Constituting major ingredient of the present invention is pitch, and is blended into a kind of thermoplastic elastomer, a kind of rubber polymer and a kind of resene polymkeric substance to form agglutinate of the present invention to wherein mixing.Wherein the add-on of each polymkeric substance is different according to the specific requirement of indexs such as raw material composition, complete processing and 60 ℃ of viscosity of the finished product of basic asphalt, sticking toughness, toughness, general relative basic asphalt, each polymkeric substance add-on is between 3~10wt.%.Specifically consisting of of agglutinate of the present invention: 100 parts of (1) pitches (wt); (2) 5~10 parts of thermoplastic elastomers (wt); (3) 3~10 parts of rubber polymers (wt); (4) 3~10 parts in resene polymkeric substance (wt).
The pitch that the present invention uses is a kind of visco-elasticity semisolid that obtains by crude distillation, solvent extraction, oxidation, blending or their combination process, and 25 ℃ of penetration degree scopes are between 0~300.In addition, the used bituminous asphalt content of the present invention is generally 1~20wt.%, and pitch and polymkeric substance that common asphalt content is lower than 7wt.% have better consistency, so the present invention is specially adapted to the pitch that asphalt content is 1~7wt.%.
Thermoplastic elastomer of the present invention mainly is meant the segmented copolymer that is formed by vinyl aromatic monomer (as vinylbenzene) and the aliphatics group polymerization that contains at least two unsaturation alkene,---------------ethene---divinyl---styrol copolymer (SEBS) etc., wherein SBS is owing to have good distortion self-reparability and crack self-healing property and form and be first-selected material for styrol copolymer (SIS), vinylbenzene for isoprene for styrol copolymer (SBS), vinylbenzene for divinyl as vinylbenzene.
Rubber polymer of the present invention is selected from the multipolymer that is formed by conjugated diolefine homopolymer or conjugated diolefine and polymerisable vinyl aromatic monomer, can use many well-known natural rubbers or synthetic rubber, as natural rubber (NR), styrene-butadiene rubber(SBR) (SBR), vinyl cyanide---butadienecopolymer (ABR) etc. wherein it is desirable to the multipolymer that is formed by vinylbenzene and polymerizing butadiene---styrene-butadiene rubber(SBR).
Resene polymkeric substance of the present invention is the byproduct C by petroleum cracking 4, C 5Above liquid unsaturated hydrocarbons, the resinous substance that copolymerization obtains under the effect of catalyzer such as aluminum chloride (petroleum resin).
Penetration degree, softening temperature are pressed the method test of GB/T 4509 and GB/T 4507 regulations respectively among the present invention, and 60 ℃ of viscosity and sticking toughness test are undertaken by the method T0620 and the T0624 of regulation among the industry standard JTJ of the Ministry of Communications 052 " highway engineering pitch and asphalt testing regulation ".The test method of penetration degree, softening temperature and viscosity is all very familiar concerning the pitch researchist.Sticking toughness test is a kind of fine method of estimating performance of modified bitumen, and the sphere with metal hemisphere during test immerses in the pitch, under 25 ℃ of conditions, with the speed of 50mm/min hemisphere is pulled out, and obtains sticking toughness, flexible numerical value according to loading and deformation curve.
The personnel that are familiar with technology can easily select many kinds of modes to make pitch and mixed with polymers together.Suitable method comprises: elder generation dissolves polymkeric substance with appropriate solvent (as benzene, toluene), and the polymkeric substance after will dissolving by the mode that stirs then mixes with the pitch that is heated to liquid state; Also can pitch be heated to 150~250 ℃ earlier, preferably 180~220 ℃, under agitation condition, be added into polymkeric substance in the pitch gradually then, stir and preferably use high shear mixing equipment such as colloidal mill, high shearing mixing emulsor to finish, this will guarantee that polymkeric substance disperses in pitch more even.The mixing time of pitch and polymkeric substance is different according to the method and apparatus of selecting, and generally in 0.5~24 hour scope, uses any method should guarantee that all polymkeric substance enough disperses in pitch.In general, add to be stirred under the normal pressure during the polymkeric substance and carry out.
If desired, can or in pitch, feed oxygen-containing gas (as air) before adding polymkeric substance simultaneously to change each components contents in the pitch.Yet the adding of oxygen-containing gas will cause pitch medium pitch matter content to increase, thereby the stability in storage of the finished product is had a negative impact.Also can be when stirring, by decompression or take the method for nitrogen protection, avoid pitch under the condition of high temperature, to take place to wear out.
To further understanding be arranged to the present invention by the reference following Example, but this does not limit the scope of back accessory claim.
Embodiment 1,2
The de-oiled asphalt that obtains with a kind of solvent extraction device is a basic material, after being heated to 180 ℃, under the high-shear agitation condition, slowly add petroleum resin respectively in varing proportions, three kinds of polymkeric substance of SBS, SBR carry out modification, and continuously stirring 30 minutes is to polymkeric substance homodisperse in pitch, then every performance of test products respectively.The analytical test result of gained drainage asphalt product is as shown in table 1 after basic material and the modification.By table as seen, indexs such as the softening temperature of modified product, viscosity, sticking toughness, toughness have been compared large increase with basic asphalt, meet the bituminous cements requirement that this patent proposes, and can be used for the making of drainage road.
Table 1 item base pitch example 1 example 2 cooperation ratio (weight) basic asphalts 100 100 petroleum resin 55 SBS, 99 SBR, 97 penetration degrees (25 ℃), 1/10mm 144 59 64 softening temperatures, ℃ 41.0 89.5 91.0 ductilities (15 ℃), cm>140 71 72 flash-points,>260>260>260 thin film heating test mass losses, %-0.136 0.117 penetration ratio, %-94.9 96.9 sticking toughness (25 ℃), Nm 1.73 26.8 21.8 toughness (25 ℃), Nm 0.71 22.1 17.7 viscosity (60 ℃), Pas 93.8 19,100 13400
Embodiment 3,4
With a kind of normal, VACUUM TOWER BOTTOM residual oil of reliever and a kind of de-oiled asphalt of solvent deasphalting unit is raw material, earlier with the two with 1: 1 ratio stir under 150 ℃ of conditions of temperature be mixed after, add petroleum resin more in varing proportions respectively, three kinds of polymkeric substance of SBS, SBR carry out modification.By the raw material of table 2 and product analysis result as seen, the product after the modification also can satisfy the bituminous cements performance requriements that this patent proposes.
Table 2 project vacuum residuum de-oiled asphalt example 3 examples 4 cooperation ratio (weight) vacuum residuum 50 50 de-oiled asphalts 50 50 petroleum resin 36 SBS, 98 SBR, 64 penetration degrees (25 ℃), 1/10mm 209 35 45 41 softening temperatures, ℃ 42.5 50.6 95.5 92.3 ductilities (15 ℃), cm>140 65 65 64 flash-points, ℃>260>260>260>260 thin film heating test mass losses, % 0.134 0.321 0.285-penetration ratio, % 56 54 75.6-sticking toughness (25 ℃), Nm--25.4 28.5 toughness (25 ℃), Nm--17.4 21.4 viscosity (60 ℃), Pas 21.5 259 84,600 21700

Claims (15)

1. bituminous cements that the making drainage road is used, this agglutinate has following feature: 25 ℃ of penetration degree 40~80 1/10mm; 55~105 ℃ of softening temperatures; 60 ℃ of viscosity 10000~100000Pas; Sticking toughness is greater than 15Nm; Toughness is greater than 10Nm.
2. according to the described bituminous cements of claim 1, it is characterized in that 25 ℃ of penetration degree 40~60 1/10mm of this agglutinate; 80~100 ℃ of softening temperatures; 60 ℃ of viscosity 20000~50000Pas; Sticking toughness is greater than 20Nm; Toughness is greater than 15Nm.
3. according to the described bituminous cements of claim 1, it is characterized in that this agglutinate composition is by weight: 100 parts of (1) pitches; (2) thermoplastic elastomer is 5~10 parts; (3) rubber polymer is 3~10 parts; (4) the resene polymkeric substance is 3~10 parts.
4. according to the described bituminous cements of claim 3, it is characterized in that 25 ℃ of penetration degree scopes of said pitch between 0~300, asphalt content is 1~20wt.%.
5. according to the described bituminous cements of claim 4, it is characterized in that said pitch medium pitch matter content is 1~7wt.%.
6. according to the described bituminous cements of claim 3, it is characterized in that said thermoplastic elastomer is meant the segmented copolymer that is formed by vinyl aromatic monomer and the aliphatics group polymerization that contains at least two unsaturation alkene.
7.---divinyl---styrol copolymer, vinylbenzene---isoprene---styrol copolymer, vinylbenzene---ethene---divinyl---styrol copolymer that according to claim 3 or 6 described bituminous cements, it is characterized in that said thermoplastic elastomer is a vinylbenzene.
8. according to claim 3 or 7 described bituminous cements, it is characterized in that said thermoplastic elastomer is vinylbenzene---divinyl---styrol copolymer.
9. according to the described bituminous cements of claim 3, it is characterized in that said rubber polymer is natural rubber or synthetic rubber.
10. according to the described bituminous cements of claim 9, it is characterized in that the multipolymer of said synthetic rubber for forming by conjugated diolefine homopolymer or conjugated diolefine and polymerisable vinyl aromatic monomer.
11., it is characterized in that said rubber polymer is styrene-butadiene rubber(SBR), vinyl cyanide a---butadienecopolymer according to the described bituminous cements of claim 10.
12., it is characterized in that said resene polymkeric substance is the byproduct C by petroleum cracking according to the described bituminous cements of claim 3 4, C 5Above liquid unsaturated hydrocarbons, the resinous substance that copolymerization obtains under the effect of catalyzer such as aluminum chloride, i.e. petroleum resin.
13. the preparation method of the described bituminous cements of claim 1: earlier with polymer dissolution, polymkeric substance after will dissolve by the mode that stirs then mixes with the pitch that is heated to liquid state, and the mixing time of pitch and polymkeric substance is in 0.5~24 hour scope.
14. the preparation method of the described bituminous cements of claim 1: earlier pitch is heated to 150~250 ℃, then under agitation condition, polymkeric substance is added in the pitch gradually, makes pitch and mixed with polymers together, the mixing time of pitch and polymkeric substance is in 0.5~24 hour scope.
15., it is characterized in that the temperature of pitch heating is 180~220 ℃ according to the described preparation method of claim 14.
CN 00123145 2000-10-26 2000-10-26 Asphalt cementing material for drainage-type pavement and its preparing process Expired - Lifetime CN1132883C (en)