CN1341754A - Leather retanning agent preparation method - Google Patents
Leather retanning agent preparation method Download PDFInfo
- Publication number
- CN1341754A CN1341754A CN 00113158 CN00113158A CN1341754A CN 1341754 A CN1341754 A CN 1341754A CN 00113158 CN00113158 CN 00113158 CN 00113158 A CN00113158 A CN 00113158A CN 1341754 A CN1341754 A CN 1341754A
- Authority
- CN
- China
- Prior art keywords
- monomer
- leather
- tanning agent
- composite tanning
- leather composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The retanning agent for leather is made up by using (wt%) 30-80% of acrylic acid or methyl acrylic acid, 0-30% of methyl acrylate or acrylonitrile and 10-50% of unsaturated aldehyde, making them formed into monomer, adding once to twice water and adopting polymerization process. Said retanning agent can make leather possess soft and full handle and fine structure, at the same time possesses good filling property, and can raise alkali resistance, adsorption of perspiration and laundering durability of leather, can be used for retanning sofa leather, clothing leather and elk, etc.
Description
The invention belongs to the preparation method of leather agent, particularly relate to the preparation method of leather composite tanning agent.
Leather composite tanning agent is the fine chemistry industry material that is used for the chrome tanned leather retanning in the leather production process, occupies critical role in the tanning chemistry product.Existing leather composite tanning agent is divided into acrylic resin retanning agent and contains aldehyde retanning agent two big classes.Wherein acrylic resin retanning agent is based on acrylic or methacrylic acid, or homopolymerization, oligomerisation or with copolymerization such as ethyl propenoate, vinyl cyanide and make, though they have good filling property and select fillibility, can increase the thickness and the fullness of leather, but because the second-order transition temperature of its polymkeric substance is higher, when tanning, exist the leather body hard inevitably, the coarse shortcoming of grain.And contain the aldehyde retanning agent is low-molecular weight compound based on glutaraldehyde, though the effect that they have is soft, graining is fine and smooth, the flat defective thin, that put easy yellowing for a long time of expensive price, tanning has limited their widespread use.
The object of the present invention is to provide a kind of preparation method of leather composite tanning agent, the leather composite tanning agent that obtains can be given leather softness, plentiful feel, fine and smooth graining, possess simultaneously good filling property again and select fillibility, and can improve alkali resistant, sweat proof, the washing resistance performance of leather, and with low cost, production technique is simple.
The objective of the invention is to realize by following technical solution:
By acrylic or methacrylic acid, methyl acrylate, vinyl cyanide compositing monomer, get leather composite tanning agent by aqueous solution polymerization technology, it is characterized in that also having unsaturated aldehyde in the monomer, wherein, acrylic or methacrylic acid account for monomer heavy 30～80%, unsaturated aldehyde account for monomer heavy 10～50%, methyl acrylate or vinyl cyanide account for monomer heavy 0～30%, water is heavy 1～2 times of monomer.
In the such scheme, unsaturated aldehyde is propenal or crotonaldehyde.
Aqueous solution polymerization technology in the such scheme is common process, or selects following technology: earlier with acrylic or methacrylic acid 30～50 ℃ down with 10～30% alkali lye neutralization, to the pH value be 5～7; Add all the other monomers again, and add monomer and weigh 0～0.2% sodium lauryl sulphate, mixed 10～30 minutes down at 30～50 ℃; Add monomer again and weigh 0.2～2% water soluble starter, monomer weighs 0.01～0.2% chain-transfer agent, reacts 3～9 hours down at 40～80 ℃.
In the above-mentioned polymerization technique, alkali lye is the aqueous solution of sodium hydroxide or potassium hydroxide; Water soluble starter is an ammonium persulphate; Chain-transfer agent is a mercaprol.
The prepared retanning agent of the present invention contains carboxyl and aldehyde radical simultaneously owing in the component, thereby can give leather softness, plentiful feel, fine and smooth graining, possesses good filling simultaneously again and selects filling properties, and can improve alkali resistant, the sweat proof of leather.Washing resistance performance, can avoid that pure acrylic resin retanning agent tanning feel plate is hard, graining is sent out thick and tradition contains the tanning of aldehyde retanning agent flat thin, easily yellowing and expensive shortcoming, be the retanning material of a kind of over-all properties and ratio of performance to price excellence, can be used for the retanning processing of sofa artificial leather, clothing leather, upper leather etc.This retanning agent also can reduce the possibility that chromic salts is washed out in retanning and the later operation in addition, and good environmental protection effect is arranged.
Table one to table four is respectively that the prepared leather composite tanning agent of the present invention is used for thickening effect, soft effect, grain effect and anti-yellowing effect after the tanning.Wherein, according to the feel of doing the soft leather of ura-rate soft effect is divided into 1～5 grade, according to the graining sophistication behind the revolutionary cadre of retanning the grain effect is divided into 1～5 grade, situation according to the leather surface yellowing after illumination of the leather after the retanning also is divided into 1～5 grade with anti-yellowing effect, corresponding respectively very poor, poor, general, good, fine five class.
Table one thickens effect
| The leather composite tanning agent title | Consumption (%) | Pigskin garment leather thickens rate (%) | The buffalo sofa artificial leather thickens rate (%) | ||
| The back | The limit belly | The back | The limit belly | ||
| Leather composite tanning agent of the present invention | ????5 | ????17.8 | ????23.5 | ????21.3 | ????24.9 |
| The pure acrylic resin retanning agent | ????5 | ????18.1 | ????23.2 | ????20.8 | ????24.8 |
| Modified glutaraldehyde | ????5 | ????10.4 | ????11.5 | ????11.7 | ????13.8 |
Table two soft effect
| The leather composite tanning agent title | Not stuffing | Stuffing |
| Leather composite tanning agent of the present invention | ????4 | ????5 |
| The pure acrylic resin retanning agent | ????1 | ????3 |
| Modified glutaraldehyde | ????4 | ????5 |
Table three grain effect
| The leather composite tanning agent title | The grain effect |
| Leather composite tanning agent of the present invention | ????4 |
| The pure acrylic resin retanning agent | ????3 |
| Modified glutaraldehyde | ????5 |
The anti-yellowing effect of table four
| The leather composite tanning agent title | Fruit is held back in anti-yellowing |
| Leather composite tanning agent of the present invention | ????5 |
| The pure acrylic resin retanning agent | ????5 |
| Modified glutaraldehyde | ????1 |
Be embodiments of the invention below.
Embodiment one
In the 250ml four-necked bottle of band stirring, condenser, add the vinylformic acid of 20.0g and the distilled water of 20.0g, after stirring mixes evenly, slowly dropping sodium solution (4.0g sodium hydroxide+16.0g distilled water is made into) neutralizes, logical water coolant, keep the interior temperature of bottle to be no more than 35 ℃, the pH value for the treatment of mixed liquid becomes at 5.0～7.0 o'clock, stops the hydro-oxidation sodium solution.With the 12.0g crotonaldehyde, 8.0g acrylon, the distilled water of 0.05g sodium lauryl sulphate and 10.0g add in the four-necked bottle then, and logical nitrogen stirred 30 minutes in 35 ℃.
The mercaprol of 0.4g ammonium persulphate and 0.02g is dissolved in respectively in the 5.0g distilled water, places filling tube standby more respectively.Be warming up to 75 ℃, treat that temperature steadily dripped ammonium persulphate and mercaprol the back in 1.5 hours.75 ℃ are incubated 2 hours, the 0.4g ammonium persulphate are dissolved in the 5.0g distilled water again, splash in the four-necked bottle in 15 minutes, are incubated logical water coolant after 1 hour, are cooled to 30 ℃ of dischargings.Promptly making solid content is 38%～42%, viscosity be 500～10000CP (35 ℃) contain aldehyde macromolecule resin retanning agent.
Embodiment two
In the 250ml four-necked bottle of band stirring, condenser, add the methacrylic acid of 24.0g and the distilled water of 20.0g, after stirring mixes evenly, slowly dropping sodium solution (5.0g sodium hydroxide+36.0g distilled water is made into) neutralizes, logical water coolant, keep the interior temperature of bottle to be no more than 40 ℃, the pH value for the treatment of mixed liquid becomes at 5.0～7.0 o'clock, stops the hydro-oxidation sodium solution.With the 4.0g crotonaldehyde, 12.0g methyl acrylate, the distilled water of 00.8g sodium lauryl sulphate and 10.0g add in the four-necked bottle then, and logical nitrogen stirred 30 minutes in 40 ℃.
The mercaprol of 0.4g ammonium persulphate and 0.01g is dissolved in respectively in the 5.0g distilled water, places filling tube standby more respectively.Be warming up to 70 ℃, treat that temperature steadily dripped ammonium persulphate and mercaprol the back in 1.5 hours.70 ℃ are incubated 2 hours, the 0.4g ammonium persulphate are dissolved in the 5.0g distilled water again, splash in the four-necked bottle in 15 minutes, are incubated logical water coolant after 1 hour, are cooled to 30 ℃ of dischargings.
Embodiment three
In the 250ml four-necked bottle of band stirring, condenser, add the vinylformic acid of 12g and the distilled water of 20.0g, after stirring mixes evenly, slowly dropping sodium solution (5.0g sodium hydroxide+16.0g distilled water is made into) neutralizes, logical water coolant, keep the interior temperature of bottle to be no more than 30 ℃, the pH value for the treatment of mixed liquid becomes at 5.0～7.0 o'clock, stops the hydro-oxidation sodium solution.With the 20.0g crotonaldehyde, 8.0g methyl acrylate, the distilled water of 0.04g sodium lauryl sulphate and 10.0g add in the four-necked bottle then, and logical nitrogen stirred 30 minutes in 30 ℃.
The mercaprol of 0.3g ammonium persulphate and 0.08g is dissolved in respectively in the 5.0g distilled water, places filling tube standby more respectively.Be warming up to 40 ℃, treat that temperature steadily dripped ammonium persulphate and mercaprol the back in 2 hours.40 ℃ are incubated 4 hours, the 0.4g ammonium persulphate are dissolved in the 5.0g distilled water again, splash in the four-necked bottle in 1 hour, are incubated logical water coolant after 2 hours, are cooled to 30 ℃ of dischargings.
Embodiment four
In the 250ml four-necked bottle of band stirring, condenser, add the methacrylic acid of 32.0g and the distilled water of 14.0g, after stirring mixes evenly, slowly dripping potassium hydroxide solution (5.0g potassium hydroxide+12.0g distilled water is made into) neutralizes, logical water coolant, keep the interior temperature of bottle to be no more than 50 ℃ of pH values for the treatment of mixed liquid and become at 5.0～7.0 o'clock, stop the hydro-oxidation potassium solution.Then the 8.0g propenal is added in the four-necked bottle, logical nitrogen stirred 10 minutes in 50 ℃.
The mercaprol of 0.06g ammonium persulphate and 0.03g is dissolved in respectively in the 5.0g distilled water, places filling tube standby more respectively.Be warming up to 80 ℃, treat that temperature steadily dripped ammonium persulphate and mercaprol the back in 1 hour.80 ℃ are incubated 1 hour, the 0.02g ammonium persulphate are dissolved in the 5.0g distilled water again, splash in the four-necked bottle in 15 minutes, are incubated logical water coolant after 1 hour, are cooled to 30 ℃ of dischargings.
Claims (4)
1. the preparation method of a leather composite tanning agent, by acrylic or methacrylic acid, methyl acrylate, vinyl cyanide compositing monomer, get leather composite tanning agent by aqueous solution polymerization technology, it is characterized in that also having unsaturated aldehyde in the monomer, wherein, acrylic or methacrylic acid account for monomer heavy 30～80%, unsaturated aldehyde account for monomer heavy 10～50%, methyl acrylate or vinyl cyanide account for monomer heavy 0～30%, water is heavy 1～2 times of monomer.
2. the preparation method of leather composite tanning agent according to claim 1 is characterized in that unsaturated aldehyde is propenal or crotonaldehyde.
3. the preparation method of leather composite tanning agent according to claim 1 and 2, it is characterized in that aqueous solution polymerization technology is common process, or select following technology: earlier with acrylic or methacrylic acid 30～50 ℃ down with 10～30% alkali lye neutralization, to the pH value be 5～7; Add all the other monomers again, and add monomer and weigh 0～0.2% sodium lauryl sulphate, mixed 10～30 minutes down at 30～50 ℃; Add monomer again and weigh 0.2～2% water soluble starter, monomer weighs 0.01～0.2% chain-transfer agent, reacts 3～9 hours down at 40～80 ℃.
4. the preparation method of leather composite tanning agent according to claim 3 is characterized in that alkali lye is the aqueous solution of sodium hydroxide or potassium hydroxide; Water soluble starter is an ammonium persulphate; Chain-transfer agent is a mercaprol.