CN1339622A - Fabric containing multifunctional composite ceramic material and its preparing method - Google Patents
Fabric containing multifunctional composite ceramic material and its preparing method Download PDFInfo
- Publication number
- CN1339622A CN1339622A CN 00123819 CN00123819A CN1339622A CN 1339622 A CN1339622 A CN 1339622A CN 00123819 CN00123819 CN 00123819 CN 00123819 A CN00123819 A CN 00123819A CN 1339622 A CN1339622 A CN 1339622A
- Authority
- CN
- China
- Prior art keywords
- fabric
- ceramic material
- multifunctional
- composite ceramic
- viscose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The fabric is blended fabric comprising multifunctional viscose fiber 5-40 wt% and common fiber 60-95 wt%. Multifunctional composite nanometer ceramic powder capable of emitting far infrared ray of 4-14 microns wavelength at 85-95 % emittivity and generating negative ions in the amount of 2-4 M/cu cm is first prepared. Multifunctional viscose fiber is then produced by using viscose as carrier and the blended fabric is finally produced. The fabric can promote blood circulation, strengthen the activity of tissues and promote the growth of enzyme.
Description
The present invention relates to a kind of textiles and preparation method who contains multifunctional composite ceramic material, particularly relate to a kind of multifunctional composite ceramic material of can be emitting far-infrared and producing anion that contains and mix multifunctional fabric and the method for making thereof that the multi-functional viscose made forms with the general fibre blending again with viscose glue.
The JP03137213 patent provides a kind of functional material, and it is to contain tiny ceramic powders in specialty fibers.This material reflection far infrared has far infrared irradiation, and is anticorrosion, heat conduction protection, functions such as deodorizing.The granularity of ceramic powders is less than 100 microns.But far infrared will be restricted purposes in that competence exertion effect under the situation of thermal source is arranged; In addition, the ceramic powders granularity is big, and its fibre strength is low, and the application of manufactured goods also is restricted.
The EP-331160 patent also provides a kind of functional material.This material is by Ti, Zr, and V, Nb, Ta, Cr, Ce, Co, the carbide of elements such as Mn, oxide, nitride, one or more compositions in oxygen-hydride are fibrous or graininess.This material has piezoelectricity, electron emission, biological nature and magnetic characteristic etc.Can be used for capacitor, piezoelectrics, catalyst, multilayer circuit board, artifical bone etc.But this material is difficult to make textiles, and purposes is restricted.
The CN1030536C patent provides another kind of functional material, and this material is by SiO
2, Al
2O
3, BO2, FeO, MgO, Na2O, TiO2, raw materials such as CaO and MnO are formed.The manufacture method of ceramic powders is to carry out fragmentation and correct grinding after raw material is equipped with by the composition scope, after granularity reaches 0.5 micron this ceramic powders is mixed in viscose last and cotton, braidings such as terylene.This textiles can be emitting far-infrared, has promotion, improves and adjusting human body blood circulation effect.But because this material is to be formed through mechanical lapping by several oxides, the emission effciency of its far infrared is limited, and function singleness, and viscose content must also make its application be restricted greater than 40% with braiding such as cotton the time.
The objective of the invention is to overcome the single shortcoming of existing fabric functional and overcome the emitting far-infrared efficient of more existing functional materials low, and it viscose content must be greater than 40% when weaving with cotton etc., the defective that its application is restricted; Thereby provide a kind of contain can high efficiency emitting far-infrared and produce the fabric and preparation method thereof of the multifunctional composite ceramic material of anion.
The fabric that contains multifunctional composite ceramic material provided by the invention has adopted following technical scheme: make a kind of can high efficiency emitting far-infrared and produce the nanometer grade powder of the Multifunction composite ceramic material of anion earlier, then with viscose glue as carrier, make multi-functional viscose, at last multi-functional viscose and general fibre blending are made; The fabric of this multifunctional composite ceramic material contains following component:
Multi-functional viscose 5-40wt%;
General fibre 95-60wt% blending makes the fabric that contains multifunctional composite ceramic material.
General fibre comprises: cotton, and terylene, nylon, polypropylene fibre, polyvinyl, any one in the spandex, or any two kinds, or any combination more than two kinds.
Wherein said multi-functional viscose is to be mixed by multifunctional compound ceramics nanometer grade powder 1-5wt% and viscose glue 99-95wt%.Described viscose glue is commercially available usually.
Wherein said multifunctional compound ceramics nanometer grade powder comprises following component, by weight percentage:
Al
2O
3，?19-30％，??ZrO
2，?13-19％.，????SiO
2，?18-23％
CrO，?????10-15％，??Fe
2O
3，?10-12.5％??TiO
2，??2-7％，
SnO
2，???5-8％??????Ce
2O
3，?0.5-2.5％???Pr
2O
3，?0.5-2.5％，
Nd
2O
3，?0.5-2.5％??Sm
2O
3，?0.5-2.5％。
A kind of manufacture method that contains the function fabric of multifunctional composite ceramic material provided by the invention, may further comprise the steps: make (1) can be emitting far-infrared and produce the multifunctional compound ceramics nanometer grade powder of anion: described multifunctional compound ceramics nanometer grade powder comprises following component, by weight percentage:
Al
2O
3??19-30％，???ZrO
2，??13-19％.，?SiO
2，??18-23％
CrO，????10-15％，???Fe
2O
3，?10-12.5％?TiO
2，??2-7％，
SnO
2，??5-8％???????Ce
2O
3，?0.5-2.5％??Pr
2O
3，?0.5-2.5％，
Nd
2O
3, 0.5-2.5%, Sm
2O
3, the 0.5-2.5% weighing, the good various oxide powders of weighing also mix, at 800-1000 ℃ of pre-burning 4-6 hour, through pulverizing. and grind, cross 200 mesh sieves; The polyvinyl alcohol adhesive that adds sample gross weight 1-5% is at 4-10t/cm
2The pressure lower lock block is shaped; In high temperature furnace, be warming up under 1050-1350 ℃ the high temperature sintering 12-36 hour, and made composite ceramic material, will pulverize through the ceramic material of oversintering at last, grind and make the multifunctional compound ceramics nanometer grade powder of particle mean size less than 0.5 μ m;
2. make the viscose that contains the multifunctional compound ceramics nanometer grade powder: multifunctional compound ceramics nanometer grade powder 1-5wt% and the viscose glue 99-95wt% less than 0.5 μ m mixes with the above-mentioned particle mean size of preparing, become viscose solution, be emitted into viscose by conventional multi-holed jet;
3. make the fabric of multifunctional composite ceramic material: multi-functional viscose 5-40wt% and 95-60wt% general fibre that said method is made mix also spun yarn, be made into function fabric (or making no gauze) then, perhaps, earlier with multi-functional viscose spun yarn, then with general fibre also spun yarn, according to forming by weight percentage, be woven into multifunctional fabric again.
Wherein general fibre comprises: cotton, and terylene, nylon, polypropylene fibre, polyvinyl, any one in the spandex, or any two kinds, or any combination more than two kinds.
Multifunctional fabric of the present invention can the high efficiency emission wavelength be the far infrared of 4-14 micron, and its emissivity is 85-95%; Can also produce anion, its generation rate is (2-4) * 10
6Individual/cm
3Because the wavelength of the far infrared that multifunctional fabric of the present invention is launched is consistent with the intrinsic absorbing wavelength of human body, the far infrared and the human body of absorption of human body are empathized, resonance motion takes place, make temperature rising in deep layer place under the skin by fuel factor, cause the expansion of capillary, promote blood microcirculation, strengthen the activity of tissue and the growth of promotion biology enzyme.Owing to promoted metabolism, make the metabolic waste that remains in sweat gland and the body, useless accumulate thing and various harmful heavy metal is able to smooth discharge, so after far infrared absorbs by human body well as the heat radiation energy, the effect with the cytoactiveization that makes human body.Again because function fabric of the present invention constantly produces a large amount of anions in air, stimulate the cell of reduction simultaneously, increase cytoactive, by making acidification physique become alkalization physique, for strengthening tissue activity, promote the biology enzyme growth, quicken metabolism only atmosphere is provided.In addition, through physics, chemistry, biological and medical science etc. multiple means test (shown in table 5 and 6), prove that multifunctional fabric of the present invention can improve the volume of blood flow of body surface significantly, quicken blood flow circulation and metabolism, strengthen the body tissue activity, promote human tissue cell's activate, thereby have the health-care function of keeping fit to get rid of illness.
Preparation method's technology provided by the invention is reasonable, and technology is simple, is suitable for large-scale industrial production.
The present invention is described in detail below in conjunction with embodiment:
Embodiment 1-3
Prepared 3 function fabric samples altogether by preparation method provided by the invention, its concrete preparation process is:
1. at first according to table 1 listed component and prescription weighing and listed three the composite ceramic material samples of process conditions preparation of table 2; Wherein employed raw material all is commercially available.
Table 1, the constituent (percentage by weight) of Multifunction composite ceramic material sample
| ????Ce 2O 3 | ????0.5 | ????1.2 | ????2.1 |
| ????Pr 2O 3 | ????0.5 | ????2.5 | ????2.0 |
| ????Nd 2O 3 | ????0.5 | ????1.1 | ????2.5 |
| ????Sm 2O 3 | ????0.5 | ????1.0 | ????2.5 |
The preparation condition of table 2 multifunctional composite ceramic material test agent
2. the nano level superfine powder with above 3 multifunctional compound ceramics samples mixes by proportioning listed in the table 3 and viscose glue, makes viscose solution, sprays by multi-holed jet under 50-70 ℃ temperature.Prepare 3 function viscose fiber samples that contain multifunctional composite ceramic material.
The composition percentage by weight that contains multifunctional compound ceramics powder and viscose glue in the multi-functional viscose of table 3
3. with 3 function viscose fiber samples of above-mentioned preparation, the proportioning and the cotton of pressing table 4, terylene, nylon, polypropylene fibre, polyvinyl, any one in the spandex, or any two kinds, or any blending more than two kinds, blending becomes to contain the fabric of multifunctional composite ceramic material.Function viscose fiber in table 4 function fabric and cotton, terylene, nylon, polypropylene fibre, polyvinyl, the composition percentage by weight of spandex
To use above-mentioned 3 prepared function fabric samples and carried out following test: (1). function fabric is at the emissivity measurement of far infrared band, (2) test of function fabric generating negative ions amount, (3). function fabric is for the contrast test of human body skin surface volume of blood flow.Existing division is as follows:
1. function fabric is at the emissivity measurement of far infrared band
Use Fu's 5DX mouth leaf transformation infrared spectrometer and spectrum emissivity measurement annex thereof that America NI COLET company produces.Spectral region 4600cm
-1-400cm
-1, noise＜0.7%.Annex noise＜3%.Employed black matrix is the TD-1 blackbody furnace that Jilin University produces, effective emissivity＞0.998, aperture 10mm.Result of the test is listed in table 5
Table 5, function fabric is at the normal emittance of far infrared band
| Sample number into spectrum | ????1 | ????2 | ????3 |
| Emissivity (%) | ????88 | ????92 | ????90 |
2. the test of function fabric generating negative ions
Answer U.S. BECKETTDE air ion measuring instrument and Yadu humidifier, exported at humidifier by the brake gauze is topped, with the measuring instrument collecting board at a distance of 30cm, record total anion number earlier, deduct background then, promptly obtain the quality amount of the actual generation of function gauze.Result of the test is listed in table 6
The anion-generating capacity of table 6 function fabric
| Sample | ????1 | ????2 | ????3 |
| The negative ion amount (10 that is taken place 6Individual/cm 3) | ????2-3 | ????2-4 | ????1-2 |
3. the check experiment of multifunctional fabric rising human body skin surface volume of blood flow is selected 20-50 year men and women totally 30 people, 15 people are one group, nameless leftward respectively going up applied function fabric of the present invention (test group) and common fabric (control group), the latter is not except that containing the function composite ceramic material, and all the other conditions are all identical with the function gauze.Before applying, measured index of correlation in back 30 minutes with applying.Exchange in second day.Double-blind study is adopted in test.Result of the test: use function fabric of the present invention and apply back microcell volume of blood flow and obviously rise, and the do not raise effect of microcell volume of blood flow of common fabric.Show that through the rank test (Wicoxon method) of sample the function fabric of test group applies the caused microcell volume of blood flow in back and increases obvious; With control group statistical significance (P＜0.001) is arranged relatively.
Claims (6)
1. fabric that contains multifunctional composite ceramic material, it is characterized in that: described fabric contains following component, by weight the percentage meter:
Multi-functional viscose 5-40%;
General fibre 95-60% blending makes the fabric that contains multifunctional composite ceramic material.
2. by the described a kind of fabric that contains multifunctional composite ceramic material of claim 1, it is characterized in that: described multi-functional viscose mixes with viscose glue 99-95wt% and forms by containing multifunctional compound ceramics nanometer grade powder 1-5wt%.
3. by the described a kind of fabric that contains multifunctional composite ceramic material of claim 1, it is characterized in that: described multifunctional compound ceramics nanometer grade powder is to comprise following composition, by weight percentage:
Al
2O
3，19-30％，??ZrO
2，?13-19％.，?SiO
2，?18-23％
CrO，??10-15％，???Fe
2O
3，10-12.5％?TiO
2，?2-7％，
SnO
2，?1.5-8％?????Ce
2O
3，0.5-2.5％?Pr
2O
3，0.5-2.5％，
Nd
2O
3，0.5-2.5％??Sm
2O
3，0.5-2.5％。
4. by the described a kind of fabric that contains multifunctional composite ceramic material of claim 1, it is characterized in that: described general fibre comprises: cotton, and terylene, nylon, polypropylene fibre, polyvinyl, any one in the spandex, or any two kinds, or any combination more than two kinds.
5. one kind prepares the described a kind of method that contains the fabric of multifunctional composite ceramic material of claim 1, it is characterized in that: may further comprise the steps: make (1) can be emitting far-infrared and produce the multifunctional compound ceramics nanometer grade powder of anion: at first by the percentage by weight of following component:
Al
2O
3???19-30％，??ZrO
2，??13-19％.，??SiO
2，??18-23％
CrO，????10-15％，??Fe
2O
3，?10-12.5％??TiO
2，??2-7％，
SnO
2，???5-8％??????Ce
2O
3，?0.5-2.5％??Pr
2O
3，?0.5-2.5％，
Nd
2O
3, 0.5-2.5% Sm
2O
3, the 0.5-2.5% weighing, the good various oxide powders of weighing also mix, and at 800-1000 ℃ of pre-burning 4-6 hour, through pulverizing, grind, and cross 200 mesh sieves; The polyvinyl alcohol adhesive that adds sample gross weight 1-5% is at 4-10t/cm
2The pressure lower lock block is shaped; In high temperature furnace, be warming up under 1050-1350 ℃ the high temperature sintering 12-36 hour, and made composite ceramic material, will pulverize through the ceramic material of oversintering at last, grind and make the multifunctional compound ceramics nanometer grade powder of particle mean size less than 0.5 μ m; (2). make the viscose contain the multifunctional compound ceramics nanometer grade powder: the above-mentioned particle mean size of preparing is mixed into viscose solution less than multifunctional compound ceramics nanometer grade powder 1-5wt% and the viscose glue 99-95wt% of 0.5 μ m, under 50-70 ℃ of temperature, be sprayed into viscose by conventional multi-holed jet; (3). make multifunctional compound ceramics mouth fabric, multi-functional viscose 5-40wt% and 95-60wt% general fibre blending resultant yarn with said method is made are made into the multifunctional composite ceramic material fabric then.
6. by a kind of method that contains the fabric of multifunctional composite ceramic material of the described preparation of claim 5, it is characterized in that: comprise that also elder generation with multi-functional viscose spun yarn, with the general fibre spun yarn, is woven into multifunctional fabric to both then again.