CN1335341A - Inorganic material for traffic marking - Google Patents
Inorganic material for traffic marking Download PDFInfo
- Publication number
- CN1335341A CN1335341A CN00113556A CN00113556A CN1335341A CN 1335341 A CN1335341 A CN 1335341A CN 00113556 A CN00113556 A CN 00113556A CN 00113556 A CN00113556 A CN 00113556A CN 1335341 A CN1335341 A CN 1335341A
- Authority
- CN
- China
- Prior art keywords
- inorganic material
- traffic marking
- exciting agent
- blast furnace
- furnace ironmaking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The inorganic material for traffic marking consists of water quenched blast furnace cinder 55-80 wt%, excitant 8-15 wt% and inorganic pigment 8-40 wt%, which are mixed to fineness over 320 sq m/ Kg before or after being milled. It has no smell, no toxicity, high wear resistance, high strength, aging resistance, certain reflectivity and low cost.
Description
The invention belongs to a kind of inorganic materials, be mainly used in the making road marking line.
At present, road marking line makes the organic materials of painting class make so far, exist low toxicity, flavor dense, easily aging, not wear-resisting, price is expensive, shortcoming such as not reflective.
Purpose of the present invention just provide a kind of tasteless, nontoxic, wear-resisting, intensity is high, anti-aging, reflective, inorganic material for traffic marking that price is low.
Inorganic material for traffic marking of the present invention, its component is: blast furnace ironmaking water-granulated slag 55～80%, exciting agent 8～15%, mineral dye are 8～40%, three's mixture fineness is at 350m
2More than/the kg, various materials can mix levigate, and it is even also can to distinguish levigate later remix.
As a further improvement on the present invention, described mineral dye is titanium dioxide (TiO
2) (white), each component concentration is titanium dioxide (TiO
2) 20～40%, blast furnace ironmaking water muck slag 55～70%, exciting agent is 8～15%; Described mineral dye also can be iron oxide yellow (FeOOH) (yellow), and each component concentration is a blast furnace ironmaking water-granulated slag 72～80%, iron oxide yellow (FeOOH) 8～15%, exciting agent 8～15%; Described exciting agent is the basic metal exciting agent, and its major ingredient is water glass (Na
2SiO
3), its modulus M is 1～1.3; Described blast furnace ironmaking water-granulated slag, its Chemical Composition content is CaO 32%～45%, SiO
225%～32%, Al
2O
39%～18%, MgO 5%～8%, MnO＜2%, Fe
2O
3＜3%, its total content must not be less than 95%, and all the other are impurity; Can add microglass bead when using inorganic material for traffic marking of the present invention, reach the reflective effect of road marking line.
In the described exciting agent, modulus M is SiO
2With Na
2The ratio of the molecule number of O, i.e. M=SiO
2/ Na
2O * 1.033, wherein 1.033 is constant.
In order to reach the requirement of slag Chemical Composition content, can differ according to various places iron ore composition, each steel mill's complete processing difference, realize by selecting the different location slag to prepare burden.
Inorganic material for traffic marking of the present invention and existing road indicate the organic materials that line uses and compare, and obviously have following advantage, tasteless, nontoxic, wear-resisting, intensity is high, anti-aging, reflective, price is low.
Embodiment 1: get blast furnace ironmaking water-granulated slag 65kg, its Chemical Composition content is: CaO 42%, SiO
228%, Al
2O
316%, MgO 6%, MnO1.5%, Fe
2O
32.5%, modulus is 1.2 exciting agent 10kg, titanium dioxide (TiO
2) 25kg, the three is mixed back levigate to 400m
2/ kg obtains inorganic material for traffic marking of the present invention.Just can brush road traffic after material of the present invention converted water and size mixing and indicate line, during use, indicate under the not dried situation of line, can add on its surface and spread microglass bead to strengthen reflecting effect.As follows through trial effect:
| Time of coagulation | Folding strength (Mpa) | Ultimate compression strength (Mpa) | ||||
| ?8h | ?1d | ?3d | ?8h | ?1d | ?3d | |
| ????15min | ?2.0 | ?3.8 | ?4.7 | ?11.1 | ?32.6 | ?54.6 |
Embodiment 2: get blast furnace ironmaking water-granulated slag 75kg, its Chemical Composition content is: CaO 38%, SiO
230%, Al
2O
316%, MgO 7%, and MnO 1.5%, Fe
2O
32.5%.Modulus is 1.2 exciting agent 12kg, and iron oxide yellow (FeOOH) 13kg mixes the three back levigate to 420m
2/ kg obtains inorganic material for traffic marking of the present invention.Just can brush road traffic after material of the present invention converted water and size mixing and indicate line, during use, indicate under the not dried situation of line, can add on its surface and spread microglass bead to strengthen reflecting effect.As follows through trial effect:
| Time of coagulation | Folding strength (Mpa) | Ultimate compression strength (Mpa) | ||||
| ?8h | ?1d | ?3d | ?8h | ?1d | ?3d | |
| ??10min | ?2.8 | ?4.5 | ?5.6 | ?20.7 | ?48.2 | ?68.8 |
Claims (6)
1, a kind of inorganic material for traffic marking is characterized in that it consists of: blast furnace ironmaking water-granulated slag 55～80%, and exciting agent 8～15%, mineral dye are 8～40%, three's mixture fineness is at 350m
2More than/the kg, various materials can mix levigate, and it is even also can to distinguish levigate later remix.
2, inorganic material for traffic marking according to claim 1 is characterized in that, described mineral dye is titanium dioxide (TiO
2), each component concentration is titanium dioxide (TiO
2) 20～40%, blast furnace ironmaking water muck slag 55～70%, exciting agent is 8～15%.
3, inorganic material for traffic marking according to claim 1, it is characterized in that described mineral dye is iron oxide yellow (FeOOH), each component concentration is a blast furnace ironmaking water-granulated slag 72～80%, iron oxide yellow (FeOOH) 8～15%, exciting agent 8～15%.
4, according to claim 1 or 2 or 3 described inorganic material for traffic marking, it is characterized in that described exciting agent is the basic metal exciting agent, its major ingredient is water glass (Na
2SiO
3), its modulus M is 1～1.3.
5, inorganic material for traffic marking according to claim 4 is characterized in that described blast furnace ironmaking water-granulated slag, and its Chemical Composition content is CaO 32%～45%, SiO
225%～32%, Al
2O
39%～18%, MgO 5%～8%, MnO＜2%, Fe
2O
3＜3%, its total content must not be less than 95%, and all the other are impurity.
6, inorganic material for traffic marking according to claim 5 can add microglass bead when it is characterized in that using.