CN1322625A - Method of producing double-layer color rubber mat with waste tyre - Google Patents
Method of producing double-layer color rubber mat with waste tyre Download PDFInfo
- Publication number
- CN1322625A CN1322625A CN 00108529 CN00108529A CN1322625A CN 1322625 A CN1322625 A CN 1322625A CN 00108529 CN00108529 CN 00108529 CN 00108529 A CN00108529 A CN 00108529A CN 1322625 A CN1322625 A CN 1322625A
- Authority
- CN
- China
- Prior art keywords
- rubber
- kilogram
- adhesive
- mentioned
- kilograms
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The double-layer colour rubber cushion is produced by cutting waste tyre into black rubber grains in certain size to produce base layer material, mixing SBR, butadiene rubber, natural rubber, chloroprene rubber, butyl rubber, EPDM, promoter, sulfur, stearic acid, stuffifng, softener, pigment, antioxidant, fungicide, UV absorbent and aromatic gasoline; surfuring the mixture; cutting the mixture into colour and wear resistant grains to be used as surface layer material; adhesion and hot pressing. Utilizing waste tyre can reduce cost and is favorable to environment protection.
Description
The present invention relates to the innovation of the preparation method of rubber floor mat, particularly a kind of method of utilizing waste and old tire to make double-layer color rubber mat.
General kindergarten, sports center etc. prevent the rubber floor mat that collides, and with the synthetic rubber compacting, shortcoming is that cost height, poor flexibility, resource consumption are big.
The objective of the invention is to adopt junked tire, make bottom through handling, adopt the synthetic material of number of chemical raw material and synthetic rubber refining to do the top layer, not only reduce cost, improve the elasticity of product, the more important thing is to have solved junked tire resource reutilization environmental issue.
The object of the present invention is achieved like this:
1, the black micelle of preparation is made primer:
After the junked tire screening, be cut into black micelle by the specification of 0.5-6 millimeter, make primer.
2, the colored synthetic rubber particle of preparation is made skin-material:
Select for use by weight calculating (down together) 20-50% rubber (as butadiene-styrene rubber, butadiene rubber, natural rubber, neoprene, butyl rubber, ethylene propylene diene rubber etc.), the captax that adds 0.1-2%, the TM monex TS of 0.1-5%, the altax of 0.1-1%, the accelerant CZ of 0.1-2%, the sulphur of 0.5-3%, the stearic acid of 0.2-5%, the filler of 40-60% is (as talcum powder, calcium carbonate etc.), the softening agent of 2-10% is (as machine oil, vaseline oil, aromatic naphtha, the cycloalkanes wet goods, the pigment of 1-5% is (as iron oxide, the titanium viridescent, everbright fast yellow, the titanium ultramarine, titanium dioxide etc.), the antioxidant A of 0.05-0.5%, the mould inhibitor of 0.05-0.5% (as 8-hydroxy-quinoline ketone etc.), the ultra-violet absorber of 0.05-0.5% (as UV531 etc.), the aromatic naphtha of 1-6%.After, the sulfuration mixing, be cut into the colour of 0.5-6 millimeter, the synthetic rubber particle of wear-resisting, ageing-resistant, good springiness, make skin-material above-mentioned chemical raw material.
3, adhesive:
Select nontoxic EPDM adhesive or neoprene adhesive for use.
4, production technology:
Take by weighing the black micelle of the 80-90% of above-mentioned preparation, add EPDM adhesive or the rubber adhesive of 10-18%, drop into mixer, stirred 1-5 minute, said mixture is poured in the hot-die of electric heating press of preheating, shakeout and make bottom.
Take by weighing the colored synthetic rubber particle of 10-20% of above-mentioned preparation, add EPDM adhesive or the rubber adhesive of 1.5-3.5%, drop in the mixer, stirred 1-5 minute, above-mentioned mixture is poured in the hot-die of above-mentioned electric heating press, shakeout and do the top layer.
Under 0.2-0.8mpa pressure, 100-130 ℃ temperature, double-layer color rubber mat is made in hot pressing 10-20 minute moulding.
Owing to adopt the present invention, make full use of the waste and used rubber tyre resource and make bottom, the synthetic material that adopts the special process prescription to make is done the top layer, produces the anticollision rubber floor mat, not only reduces cost, and improves product elasticity, and utilizes environmental protection.
In conjunction with the embodiments, further describe the present invention:
Embodiment 1:
1, the black micelle primer of preparation:
After the junked tire screening, be cut into black micelle by 3 millimeters specifications, make primer.
2, the colored synthetic rubber skin-material of preparation: 100 kilograms of ethylene propylene diene rubbers, add 1.6 kilograms captax, 1.5 kilograms TM monex TS, 0.8 kilogram altax, 1.2 kilograms accelerant CZ, 2.5 kilograms sulphur, 2 kilograms stearic acid, 135 kilograms talcum powder, 0.2 kilogram antioxidant A, 0.2 kilogram mould inhibitor 8-hydroxy-quinoline ketone, 0.2 kilogram ultra-violet absorber UV531.5 kilograms aromatic naphtha, 2 kilograms of vaseline oils, 6 kilograms of iron oxide.After, the sulfuration mixing, be cut into the colour of 0.5-3 millimeter, the synthetic rubber particle of wear-resisting, ageing-resistant, good springiness, make skin-material above-mentioned chemical raw material.
3, adhesive:
Select nontoxic EPDM adhesive for use.
4, production technology:
Take by weighing 160 kilograms black micelle of above-mentioned preparation, add 25 kilograms EPDM adhesive, drop into mixer, stirred 2 minutes, said mixture is poured in the hot-die of electric heating press of preheating, shakeout and make bottom.
Take by weighing 25 kilograms of colored synthetic rubber powder of above-mentioned preparation, add 4 kilograms EPDM adhesive or rubber adhesive, drop in the mixer, stirred 3 minutes, above-mentioned mixture is poured in the hot-die of above-mentioned electric heating press, shakeout and do the top layer.
Under 0.4mpa pressure, 120 ℃ of temperature, double-layer color rubber mat is made in hot pressing moulding in 15 minutes.
Embodiment 2:
1, the black micelle primer of preparation:
After the junked tire screening, be cut into black micelle by 3 millimeters specifications, make primer.
2, the colored synthetic rubber skin-material of preparation:
Take by weighing 40 kilograms of butadiene-styrene rubber, 30 kilograms of natural rubbers, 30 kilograms of ethylene propylene diene rubbers, the altax, 1.5 kilograms TM monex TS, 1 kilogram promoter TT, 0.6 kilogram accelerant CZ that add 2 kilograms, 2.3 kilograms sulphur, 0.2 kilogram stearic acid, 158 kilograms filler talcum powder, 0.2 kilogram antioxidant A, 0.3 kilogram mould inhibitor 8-hydroxy-quinoline ketone, 0.3 kilogram ultra-violet absorber (as UV531 etc.).4 kilograms aromatic naphtha, 4 kilograms of blue or green edge of titanium, 4 kilograms of machine oil.After, the sulfuration mixing, be cut into the colour of 1-3 millimeter, a synthetic rubber grain of wear-resisting, ageing-resistant, good springiness, make skin-material above-mentioned chemical raw material.
3, adhesive:
Select nontoxic EPDM adhesive for use.
4, production technology:
Take by weighing 160 kilograms black micelle of above-mentioned preparation, add 25 kilograms EPDM adhesive, drop into mixer, stirred 2 minutes, said mixture is poured in the hot-die of electric heating press of preheating, shakeout and make bottom.
Take by weighing 25 kilograms of colored synthetic rubber powder of above-mentioned preparation, add 4 kilograms EPDM adhesive, drop in the mixer, stirred 3 minutes, above-mentioned mixture is poured in the hot-die of above-mentioned electric heating press, shakeout and do the top layer.
Under 0.4mpa pressure, 120 ℃ of temperature, double-layer color rubber mat is made in hot pressing moulding in 15 minutes.
Claims (1)
1, utilize junked tire to make the method for double-layer color rubber mat, adopt junked tire, make bottom through handling, adopt the synthetic material of number of chemical raw material and synthetic rubber refining to do the top layer, it is characterized in that: after the junked tire screening, specification by the 0.5-6 millimeter is cut into black micelle, makes primer; Select for use by weight calculating (down together) 20-50% rubber: butadiene-styrene rubber, butadiene rubber, natural rubber, neoprene, butyl rubber, ethylene propylene diene rubber, the captax that adds 0.1-2%, the TM monex TS of 0.1-5%, the altax of 0.1-1%, the accelerant CZ of 0.1-2%, the sulphur of 0.5-3%, the stearic acid of 0.2-5%, the filler of 40-60%: talcum powder or calcium carbonate, the softening agent of 2-10%: machine oil, vaseline oil, aromatic naphtha, naphthenic oil, the pigment of 1-5%: iron oxide, the titanium viridescent, everbright fast yellow, the titanium ultramarine, titanium dioxide, the antioxidant A of 0.05-0.5%, the mould inhibitor 8-hydroxy-quinoline ketone of 0.05-0.5%, the ultra-violet absorber UV531 of 0.05-0.5%, the aromatic naphtha of 1-6%, mixing above-mentioned chemical raw material, after the sulfuration, be cut into the colour of 0.5-6 millimeter, wear-resisting, ageing-resistant, the synthetic rubber particle of good springiness, make skin-material, select nontoxic EPDM adhesive or neoprene adhesive for use, take by weighing above-mentioned preparation 80-90% the kilogram black micelle, the EPDM adhesive that adds the 10-18% kilogram, drop into mixer, stirred 1-5 minute, said mixture is poured in the hot-die of electric heating press of preheating, shakeout and make bottom, take by weighing the colored synthetic rubber powder of 10-20% kilogram of above-mentioned preparation, the EPDM adhesive or the rubber adhesive that add the 1.5-3.5% kilogram, drop in the mixer, stirred 1-5 minute, above-mentioned mixture is poured in the hot-die of above-mentioned electric heating press, shakeout and do the top layer, at 0.2-0.8mpa pressure, under the 100-130 ℃ of temperature, double-layer color rubber mat is made in hot pressing 10-20 minute moulding.