CN1318597A - Anticorrosive fireproof paint needing no rust elimination - Google Patents
Anticorrosive fireproof paint needing no rust elimination Download PDFInfo
- Publication number
- CN1318597A CN1318597A CN 01114214 CN01114214A CN1318597A CN 1318597 A CN1318597 A CN 1318597A CN 01114214 CN01114214 CN 01114214 CN 01114214 A CN01114214 A CN 01114214A CN 1318597 A CN1318597 A CN 1318597A
- Authority
- CN
- China
- Prior art keywords
- agent
- rust
- pigment
- parts
- solvent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention is the composition and production process of one kind of rust-preventing anticorrosive fireproof paint. It consists of mixed perhalide, solvent, pigment, fireproof agent, assistant, etc. It is suitable for surface of both metal and non-metal, and its use needs no primer and thus has low application cost.
Description
The present invention relates to a kind of prescription and manufacture method of coating, particularly a kind ofly be painted on formulation for coating material and the manufacture method that metal, nonmetallic surface have the antirust, anti-corrosive fire-proof function simultaneously.
Kind antirust, antifouling paste is a lot, and they respectively have relative merits, the good antirust property that has, but antiseptic property is poor, and the antiseptic property that has is good, and rustless property is poor, and the decorate properties that has is good, and fire line is poor, easy firing.Most antirust, antifouling paste necessary priming in brushing increases construction cost and time.
The purpose of this invention is to provide a kind of antirust, anti-corrosive flame retardant paint antirust, anticorrosion, fire-proof function that has simultaneously, can directly brush, not necessary priming has reduced construction cost and time.
The object of the present invention is achieved like this: a kind of anticorrosive fireproof paint needing no rust elimination, it is made up of following component: (weight %)
Mix high halogenide 15-30
Modified resin 0-20
Solvent 30-65
Composite antirust pigment 3-15
Tinting pigment 3-15
Composite fire-proof agent 3-10
Auxiliary agent 0.2-1.5
Wherein: mix high halogenide and be (following is weight part): modified high chlorinated polyethylene 10-18 part, chlorinated rubber 0-5 part, chlorosulfonated polyethylene 0-3 part, chlorinated polyvinyl chloride 0-5 part, clorafin 4-10 part;
Modified resin is: Synolac 0-15 part, acrylic resin 0-15 part;
Solvent is: dimethylbenzene 0-50 part, N-BUTYL ACETATE 0-15 part, zellon 0-65;
Composite antirust pigment is: zinc phosphate 2-8 part, aluminium triphosphate 2-10 part, ST rust-stabilising pigment 2-6 part; Tinting pigment is: red is iron oxide red, molybdenum red, and blue look is that Hua Lan and phthalein are blue or green blue, and white is titanium dioxide, and yellow for being chrome yellow, black is carbon black;
The composite fire-proof agent is: QD-SPA (Z) fire retardant 1-6 part, stibium trioxide 2-4 part, ammonium polyphosphate 1-5 part, fire retardant FB 1-3 part;
Auxiliary agent is: flow agent BYK-306,0.1-0.5 part, dispersion agent 963,0.1-0.4 part, anti-flood and anti-float agent 0.2-0.5 part, epoxy chloropropane 0.2-0.3 part, UV light absorber 0.3-0.5 part.
Its production technique is: earlier with after the stirring and dissolving in high halogenide and the solvent adding dissolution kettle, put into material-compound tank, adding modified resin mixes, add rust-stabilising pigment tinting pigment, fireproofing agent and auxiliary agent dispersed with stirring under 800-1200 rev/min rotating speed again, be ground to fineness with sand mill then and be not more than 50um, adjust viscosity with solvent at last and be not less than 40S (being coated with-4 glasss, 25 ℃), filter and package and be finished product.
The present invention is owing to adopted modified high chlorinated polyethylene, chlorinated rubber, chlorosulfonated polyethylene, the contour halogenated mixture of clorafin, be equipped with modified resin such as Synolac, acrylic resin, add composite antirust pigment, make it have antirust, rot-resistant function, the adding of composite fire-proof agent, increased the fp function again, thereby made the present invention reach antirust, anticorrosion, fp purpose.
The invention will be further described below in conjunction with embodiment.
Embodiment 1:(weight %) mixes high halogenide 27, solvent 54.75, rust-stabilising pigment 4, tinting pigment 10, composite fire-proof agent 4, auxiliary agent 0.25.
The proportioning of each component is: (weight part) mixes high halogenide: 15 parts of modified high chlorinated polyethylenes, 3 parts of chlorinated rubbers, 1 part of chlorosulfonated polyethylene, 8 parts of clorafins; 41 parts of dimethylbenzene, 8.75 parts of N-BUTYL ACETATEs, 5 parts of trielines; 10 parts of iron oxide reds, 4 parts of ST rust-stabilising pigments; 2 parts of stibium trioxides, 2 parts of ammonium polyphosphates; 0.25 part of epoxy chloropropane.
Embodiment 2:(weight %) mixes high halogenide 24, solvent 53.85, rust-stabilising pigment 5, tinting pigment 12, composite fire-proof agent 4, auxiliary agent 1.15.
The proportioning of each component is: (weight part) mixes high halogenide: 17 parts of modified high chlorinated polyethylenes, 7 parts of clorafins; 9.85 parts of N-BUTYL ACETATEs, 44 parts of dimethylbenzene, 12 parts of titanium dioxides, 2 parts of stibium trioxides, 2 parts of QD-SPA (z) fire retardants, 5 parts of zinc phosphates, 0.25 part of epoxy chloropropane, 0.3 part of UV light absorber, dispersion agent 963 is 0.2 part, 0.4 part of anti-flood and anti-float agent.
Embodiment 3:(weight %) mixes high halogenide 18, modified resin 10, solvent 54.15, rust-stabilising pigment 5, tinting pigment 6.5, composite fire-proof agent 6, auxiliary agent 1.35.
The proportioning of each component is: (weight part) mixes high halogenide: 14 parts of modified high chlorinated polyethylenes, 3 parts of clorafins; 10 parts of Synolac, 45 parts of dimethylbenzene, 8.15 parts of N-BUTYL ACETATEs, 5 parts of aluminium triphosphates, blue or green blue 1.5 parts of titanium, 5 parts of titanium dioxides, 2 parts of stibium trioxides, fire retardant FB2 part, 2 parts of ammonium polyphosphates; 0.25 part of epoxy chloropropane, flow agent BYK-306,0.2 part, 963,0.2 parts of dispersion agents, 0.4 part of anti-flood and anti-float agent, 0.3 part of UV light absorber.
Embodiment 4:(weight %) mixes high halogenide 21, modified resin 10, solvent 54.6, composite antirust pigment 6.5, tinting pigment 3.5, composite fire-proof agent 4, auxiliary agent 0.4.
The proportioning of each component is: 15 parts of (weight part) modified high chlorinated polyethylenes, 6 parts of clorafins, 10 parts of acrylic resins, 43 parts of dimethylbenzene, 11.6 parts of N-BUTYL ACETATEs, 3.5 parts of carbon blacks, 4.5 parts of zinc phosphates, aluminium triphosphate 2 minutes, 2 parts of stibium trioxides, 2 parts of QD-SPA (z) fire retardants, anti-flood and anti-float agent 0.4.
Embodiment 5:(weight %) mixes perchloride 23, solvent 59.95, rust-stabilising pigment 6, tinting pigment 6, fireproofing agent 4, auxiliary agent 1.05.
The each component proportioning is: 4 parts of (weight part) modified high chlorinated polyethylenes, 4 parts of chlorinated polyvinyl chloride, 7 parts of clorafins, 59.95 parts of zellons, 6 parts of zinc phosphates, 6 parts of iron oxide reds, 2 parts of stibium trioxides, 2 parts of QD-SPA (z) fire retardants, 0.25 part of epoxy chloropropane, 0.2 part of dispersion agent, 0.3 part of anti-flood and anti-float agent, 0.3 part of UV light absorber.No matter this prescription is liquid state, and still the paint film after the brushing sees that naked light does not all burn.
Earlier with after the stirring and dissolving in high halogenide and the solvent adding dissolution kettle, put into material-compound tank, adding modified resin mixes, add rust-stabilising pigment tinting pigment, fireproofing agent and auxiliary agent dispersed with stirring under 800-1200 rev/min rotating speed again, be ground to fineness with sand mill then and be not more than 50um, adjust viscosity with solvent at last and be not less than 40s (being coated with-4 glasss, 25 ℃), filter and package and be finished product.
Among the present invention, the flow agent model is BYK-306, is German Bi Ke company product; The dispersion agent model is 963, is Henkel KGaA company product; The anti-flood and anti-float agent model is D201, is Shanghai Resin Factory's product, and fire retardant FB is an inorganic institute product; The fire retardant model is QD-SPA (z), for reaching scientific and technological development company product together; The UV light absorber model is UV-9, is auxiliary reagent factory, Wuhan product.
Claims (2)
1, a kind of anticorrosive fireproof paint needing no rust elimination is characterized in that: it is made up of following component: (weight %)
Mix high halogenide 15-30
Modified resin 0-20
Solvent 30-65
Composite antirust pigment 3-15
Tinting pigment 3-15
Composite fire-proof agent 3-10
Auxiliary agent 0.2-1.5
Wherein: mix high halogenide and be (following is weight part): modified high chlorinated polyethylene 10-18 part, chlorinated rubber 0-5 part, chlorosulfonated polyethylene 0-3 part, chlorinated polyvinyl chloride 0-5 part, clorafin 4-10 part;
Modified resin is: Synolac 0-15 part, acrylic resin 0-15 part;
Solvent is: dimethylbenzene 0-50 part, N-BUTYL ACETATE 0-15 part, zellon 0-65;
Composite antirust pigment is: zinc phosphate 2-8 part, aluminium triphosphate 2-10 part, ST rust-stabilising pigment 2-6 part;
Tinting pigment is: red is iron oxide red, molybdenum red, and blue look is that Hua Lan and phthalein are blue or green blue, and white is titanium dioxide, and yellow for being chrome yellow, black is carbon black;
The composite fire-proof agent is: QD-SPA (Z) fire retardant 1-6 part, stibium trioxide 2-4 part, ammonium polyphosphate 1-5 part, fire retardant FB 1-3 part;
Auxiliary agent is: flow agent BYK-306,0.1-0.5 part, dispersion agent 963,0.1-0.4 part, anti-flood and anti-float agent 0.2-0.5 part, epoxy chloropropane 0.2-0.3 part, UV light absorber 0.3-0.5 part.
2, a kind of anticorrosive fireproof paint needing no rust elimination, it is characterized in that: its production technique is: earlier with after the stirring and dissolving in high halogenide and the solvent adding dissolution kettle, put into material-compound tank, adding modified resin mixes, add rust-stabilising pigment tinting pigment, fireproofing agent and auxiliary agent dispersed with stirring under 800-1200 rev/min rotating speed again, be ground to fineness with sand mill then and be not more than 50um, be not less than 40s with solvent adjustment viscosity at last and (be coated with-4 glasss, 25 ℃), filter and package and be finished product.