CN1315239A - Light insulating polybenzene plate and its preparing process - Google Patents
Light insulating polybenzene plate and its preparing process Download PDFInfo
- Publication number
- CN1315239A CN1315239A CN 00106331 CN00106331A CN1315239A CN 1315239 A CN1315239 A CN 1315239A CN 00106331 CN00106331 CN 00106331 CN 00106331 A CN00106331 A CN 00106331A CN 1315239 A CN1315239 A CN 1315239A
- Authority
- CN
- China
- Prior art keywords
- magnesium oxide
- polybenzene
- polyphenyl
- pearlstone
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A light-weight insulating polybenzene board as building material is prepared from granular waste or used foam plastics of polystyrene through adding the solution of magnesium oxide and chloride and powdered expanded pearlite, stirring to uniformity, loading in mould, demoulding and drying in air. Its advantages include light weight, low cost, reducing white pollution, high insulating performance and toughness, and no need of special curing.
Description
The present invention relates to a kind of polyphenyl light thermal insulation board and manufacture craft thereof, belong to lagging material for building.
At present, warming plate for building is of a great variety.As the Metallurgical Research Institute, Department of Architecture material and the cement polystyrene board of the common development in Beijing City Building Design Inst. scientific research institution, it is with polystyrene foam grain, cement, EC pore forming material, suds-stabilizing agent, make through stirring blanks and moulding and conserving, its physicals sees Table:
| Project | Index |
| Unit weight (Kg/m 3) | 280-330 |
| Thermal conductivity (w/m.k) | ≤0.09 |
| Water-intake rate (%) | ≤30 |
This cement polystyrene board, unit weight is higher, and thermal conductivity and water-intake rate are bigger, and are to be tackiness agent with cement, need health, and preserving period, is long, and the finished product production cycle is long.
The object of the present invention is to provide a kind of in light weightly, cost is low, and is with short production cycle, do not need special curing, insulation, sound-proofing properties is good, both reduced the thermal conductivity and the water-intake rate of product, also reduced the polyphenyl light thermal insulation board and the manufacture craft thereof of white pollution simultaneously.
The object of the present invention is achieved like this:
Each material of the present invention is by weight ratio:
Particulate state polystyrene foamed plastics 5～15%;
Magnesium oxide 30～40%;
Magnesium chloride solution 50～70%;
Pearlstone 1～10%;
The present invention is to be light-weight aggregate with the granular waste old polystyrene foamed plastic of 5-10mm, get its 5～15%, add content greater than 60% magnesium oxide 30～40%, concentration greater than 20% magnesium chloride solution 50～70%, add pearlstone 1～10% again, through whipping appts, stir, go into mold forming, natural air drying after the demoulding and making.
The present invention is a main raw material owing to having adopted waste and old polystyrene foamed plastics, so this product light weight, cost is low, has not only reduced white pollution, and helps environmental protection.The tackiness agent that magnesium oxide used in the present invention and magnesium chloride solution are formed makes product not need special curing, and the production cycle shortens, and does not need any additives still can produce at-10～0 ℃.Because pearlstone also is a kind of lagging material, water-absorbent is strong, and particle is tiny, the present invention is used for the stopping composition between polystyrene foam grain, and its suction tackiness agent of satisfying wraps in around the polystyrene foam grain, prevent that tackiness agent from sinking, and makes finished product have certain intensity.And there are good insulation, sound-proofing properties, good toughness, technology simple.Be applicable to the insulation of industry, covil construction roofing, inside and outside body of wall and the sound insulation of floor gap.
Physicals of the present invention is:
| Project | Index |
| Unit weight (kg/m 3) | 230～280 |
| Thermal conductivity (w/m.k) | ≤0.06 |
| Water-intake rate (%) | ≤15 |
Embodiment 1:
Producing polyphenyl light thermal insulation board unit dry weight is 240kg/m
3The time by weight needing with 9 parts of polystyrene foam grains, 36 parts in magnesium oxide, 53 parts of magnesium chloride solutions, 2 parts of stirrers of packing into of pearlstone, after stirring, the film of living in groups of packing into, natural air drying behind the demoulding and making.
Embodiment 2:
Producing polyphenyl light thermal insulation board unit dry weight is 280kg/m
3The time by weight needing with 7 parts of polystyrene foam grains, 35 parts in magnesium oxide, 55 parts of magnesium chloride solutions, 3 parts of stirrers of packing into of pearlstone, after stirring, the film of living in groups of packing into, natural air drying behind the demoulding and making.
Embodiment 3:
As at 1000m
2The house on add a cover the polyphenyl light thermal insulation board, thickness is 80mm, unit dry weight is 240kg/m
3The time, with (5～10mm) waste old polystyrene foamed plastic particle 2016kg adds magnesium oxide 8064kg, magnesium chloride solution 11872kg and the pearlstone 448kg gradation stirrer of packing into, after stirring, the film of living in groups of packing into, natural air drying behind the demoulding and making can use.
Claims (2)
1, polyphenyl light thermal insulation board is characterized in that: each composition weight proportion:
Particulate state polystyrene foamed plastics 5～15%
Magnesium oxide 30～40%
Magnesium chloride solution 50～70%
Pearlstone 1～10%
2, the manufacture craft of polyphenyl light thermal insulation board according to claim 1, it is characterized in that: waste old polystyrene foamed plastic is ground into the particle that diameter is 5-10mm, get its 5～15%, add content greater than 60% magnesium oxide 30～40%, concentration greater than 20% magnesium chloride solution 50～70%, and then add pearlstone 1～10%, through whipping appts, after stirring, the film of living of packing in groups, natural air drying behind the demoulding and making.