CN1306036A - Inorganic filler reinforced polypropylene composite material for microwave oven - Google Patents
Inorganic filler reinforced polypropylene composite material for microwave oven Download PDFInfo
- Publication number
- CN1306036A CN1306036A CN 00131017 CN00131017A CN1306036A CN 1306036 A CN1306036 A CN 1306036A CN 00131017 CN00131017 CN 00131017 CN 00131017 A CN00131017 A CN 00131017A CN 1306036 A CN1306036 A CN 1306036A
- Authority
- CN
- China
- Prior art keywords
- coupling agent
- material according
- microwave oven
- toughner
- inorganic filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
An inorganic filler reinforced composite polypropylene material for microwave oven contains polypropylene resin (40-92 Wt%), inorganic filler (5-40 wt.%), antioxidizing agent (1-2 wt.%), coupling agent (0.05-2.5 wt.%) and toughening agent (2.8-20 wt.%). Its advantages include high rigidity, toughness, thermal deformation temp, size stability and thermal ageing performance, and low expansibility, and shrinkage.
Description
The present invention relates to a kind of matrix material, particularly a kind of inorganic filler reinforced polypropylene composite material for microwave oven.
Acrylic resin is one of five big resins for universal use, and the kind of modified polypropene also has broad variety, and purposes is also very extensive.Microwave oven requires polypropylene composite material to have higher rigidity, toughness, good dimensional stability and thermal ageing, higher heat-drawn wire, lower thermal expansivity, lower shrinking percentage and lower cost preferably with the acrylic plastering part.
The object of the present invention is to provide a kind of firm, good toughness, higher heat-drawn wire, good dimensional stability and thermal ageing, lower thermal expansivity and the inorganic filler reinforced polypropylene composite material for microwave oven of shrinking percentage.
Purpose of the present invention can reach by following measure: the weight percent of component of the present invention is an acrylic resin 40～92%, mineral filler 5～40%, oxidation inhibitor 0.1～2%, coupling agent 0.05～2.5%, toughner 2.8～20%.
Purpose of the present invention can also reach by following measure: the weight percent of component can be acrylic resin 65%, mineral filler 25%, oxidation inhibitor 1%, coupling agent 1.2%, toughner 7.8%.Described mineral filler can be talcum powder, lime carbonate, barium sulfate or their composition.Described oxidation inhibitor can be hindered phenol, thioesters class and phosphite ester kind antioxidant.Described coupling agent comprises silane coupling agent, titanic acid ester coupling agent, aluminium esters of gallic acid coupling agent, the compound coupling agent of aluminium titanium.Described toughner comprises SBS, SEDS, POE, EPDM, second handle glue, HDPE, LDPE, LLDPE.Described acrylic resin is copolymerization and the homo-polypropylene of melting index between 0.8～40g/10min.
In system, dose rigidity, heat-drawn wire and dimensional stability that the part mineral filler can increase material, reduce shrinking percentage, thermal expansivity and the cost of material.
Oxidation inhibitor makes polypropylene in processing and use satisfactory stability be arranged, and avoids color and luster, performance to change, and especially in the life-time service process, provides good thermal-oxidative aging property.
Coupling agent carries out surface treatment to mineral filler, forms the chemical bond bridge between mineral filler and polypropylene, increases interface interaction power and consistency, improves the over-all properties of material.
The effect of toughner provides the normal temperature toughness and the low-temperature flexibility of material, improves the breach and the non-notch resistance to impact shock of material.
The present invention has following advantage compared to existing technology: have higher rigidity and heat-drawn wire, toughness preferably, good dimensional stability and thermal ageing, lower thermal expansivity, shrinking percentage and cost can be used as microwave oven plastic pastes such as door for microwave oven envelope, fan for microwave oven support, microwave oven wind scooper, microwave oven stove pin.
The present invention is described in further detail below in conjunction with accompanying drawing (embodiment):
Embodiment one
Get 75% poly-interior olefine resin, 18% mineral filler, 0.8% oxidation inhibitor, 1% coupling agent, the mixing of 5.2% toughner, mixture is used the screw extrusion press granulation after stirrer mixes, obtain modified polypropylene resin.150 ℃ of baking oven thermal ageings, the material efflorescence time is 110 hours; Heat-drawn wire is 125 ℃; Yield strength is 34MPA; Flexural strength is 35MPA; Shock strength is 3.5KG/m
2Modulus in flexure is 1904MPA.
Embodiment two
Get 65% poly-in olefine resin, 25% mineral filler, 1% oxidation inhibitor, 1.5% coupling agent, 7.5% toughner mix, use the technology identical with embodiment one, obtain modified polypropylene resin.150 ℃ of baking oven thermal ageings, the material efflorescence time is 114 hours; Heat-drawn wire is 125 ℃; Yield strength is 35MPA; Flexural strength is 35MPA; Shock strength is 3.6KG/m
2Modulus in flexure is 1904MPA.
Embodiment three
Get 69.2% poly-in olefine resin, 19% mineral filler, 0.8% oxidation inhibitor, 1% coupling agent, 10% toughner mix, use the technology identical with embodiment one, obtain modified polypropylene resin.150 ℃ of baking oven thermal ageings, the material efflorescence time is 114 hours; Heat-drawn wire is 123 ℃; Yield strength is 34MPA; Flexural strength is 34MPA; Shock strength is 5.0KG/m
2Modulus in flexure is 1904MPA.
Embodiment four
Get 55% poly-in olefine resin, 35% mineral filler, 1.8% oxidation inhibitor, 2% coupling agent, 6.2% toughner mix, use the technology identical with embodiment one, obtain modified polypropylene resin.150 ℃ of baking oven thermal ageings, the material efflorescence time is 112 hours; Heat-drawn wire is 120 ℃; Yield strength is 35MPA; Flexural strength is 35MPA; Shock strength is 4.0KG/m
2Modulus in flexure is 1900MPA.
Claims (7)
1, a kind of inorganic filler reinforced polypropylene composite material for microwave oven is characterized in that: the weight percent of component is an acrylic resin 40～92%, mineral filler 5～40%, oxidation inhibitor 0.1～2%, coupling agent 0.05～2.5%, toughner 2.8～20%.
2, material according to claim 1 is characterized in that: the weight percent of component can be acrylic resin 65%, mineral filler 25%, oxidation inhibitor 1%, coupling agent 1.2%, toughner 7.8%.
3, material according to claim 1 is characterized in that: described mineral filler can be talcum powder, lime carbonate, barium sulfate or their composition.
4, material according to claim 1 is characterized in that: described oxidation inhibitor can be hindered phenol, thioesters class and phosphite ester kind antioxidant.
5, material according to claim 1 is characterized in that: described coupling agent comprises silane coupling agent, titanic acid ester coupling agent, aluminium esters of gallic acid coupling agent, the compound coupling agent of aluminium titanium.
6, material according to claim 1 is characterized in that: described toughner comprises SBS, SEDS, POE, EPDM, second handle glue, HDPE, LDPE, LLDPE.
7, material according to claim 1 is characterized in that: described acrylic resin is copolymerization and the homo-polypropylene of melting index between 0.8～40g/10min.