CN1305016C - Relief type active display device and method for manufacturing the same - Google Patents
Relief type active display device and method for manufacturing the same Download PDFInfo
- Publication number
- CN1305016C CN1305016C CNB021168717A CN02116871A CN1305016C CN 1305016 C CN1305016 C CN 1305016C CN B021168717 A CNB021168717 A CN B021168717A CN 02116871 A CN02116871 A CN 02116871A CN 1305016 C CN1305016 C CN 1305016C
- Authority
- CN
- China
- Prior art keywords
- case
- glue
- coated
- sculptured
- circuit board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention relates to a relief type active display device and a manufacturing method thereof. The manufacturing method of the device is that a plaster female die is copied according to the relief type housing model, and a release agent is coated on the plaster female die for 2-3 times; after the release agent is solidified, coating a housing glue solution on the plaster female die, covering a glass fiber fabric until the thickness requirement is met, and drying and demoulding to form the relief type housing.
Description
Technical field
The present invention relates to a kind of relief type active display device and manufacture method thereof, this device is a kind of display device that adopts built-in light source illumination, and the embossment face shield with design can be used for beautifying the environment and as advertising media.
Background technology
Chinese patent ZL98122552.7 discloses a kind of luminous advertisement board, this billboard is basic base with plastic plate, plank, iron sheet, one deck noctilucence layer is set on basic base, to reach copy and clear patterns, this patent does not need power supply, permanent light, every day noctilucence, character pattern is clear, can solve advertising and the contradiction that influences environmental beauty well.But the brightness of this patent is limited, and can not show three-dimensional shape or moulding.At present, the picture and text entity that is applied to exploitation realizes that the mode of brightening at night generally adopts neon bulb or scalding lamp directly target to be illuminated with figure style crisperding or with external lights, the also lamp box of useful inner light, but only be confined to plane pattern, its content displayed and effect lack unitarity round the clock, in addition, can not show three-dimensional shape or moulding.Therefore, need a kind of relief type active display device of design.
Summary of the invention
The purpose of this invention is to provide a kind of relief type active display device, this installs and not only can show its sculptured design daytime, also can show its sculptured design at night, can realize the unitarity round the clock that moulding of the present invention shows, brightening is beautified the environment.
Another object of the present invention provides a kind of method of making the sculptured case in the relief type active display device.
A further object of the present invention provides a kind of method of making relief type active display device.
The objective of the invention is to realize by following technical proposals:
A kind of relief type active display device, base plate is arranged, this base plate is provided with electric light source, circuit board and optical processing plate, its main points are: cover is adorned sculptured case on the described base plate, be coated with decorative coveringn on this case outside surface, described electric light source is the LED transistor, and described circuit board surface adheres to wrinkle shape optical processing plate, and the raw material that constitutes described case comprises transparent resin, plastic pigment, glass microballoon, organic cobalt salt catalyzer, ketonic compound hardening agent, glass fabric.
A kind of method of making relief type active display device is characterized in that: when making sculptured case, adopt following steps:
A, turn over system gypsum former according to sculptured case model, calcium plaster by gesso, white cement,
Fibre object is formed;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Organic cobalt salt catalyzer 0.05-4 part
Ketonic compound hardening agent 0.5-4 part.
A kind of method of making relief type active display device, its main points are:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Organic cobalt salt catalyzer 0.05-4 part
Ketonic compound hardening agent 0.5-4 part
Phosphorus benzene plasticiser 1-5 part;
E, circuit board manufacturing mantle are coated with one deck resin glue earlier on a substrate, cover the layer of glass fabric, outside described glass fabric, be coated with one deck resin glue then, treat to carry out second time coating after the described resin glue drying, till reaching thickness requirement, make the circuit board mantle;
F, on described soft mode, directly arrange circuit lead, form circuit board, coated with resins glue on described circuit board;
G, adhere to wrinkle shape optical processing plate at described circuit board surface;
H, the LED transistor is installed on described circuit board;
I, described base plate and circuit board are installed in the described sculptured case;
J, in described sculptured case outside surface spraying and decorating coating.
Compared with the prior art the present invention has following advantage:
1, the present invention since except that sculptured figure and literal without any attachment, can fully give prominence to figure and literal itself, the appreciation effect at daytime and night is consistent.。
2, the present invention can accomplish that " face " is bright, rather than the only bright line of traditional neon bulb, and color and luster can be adjustable continuously in full spectral range.
3, overlong service life of the present invention, but successively-ignited 10-20 ten thousand hours.
4, power consumption of the present invention is humble, has only about 1/10 of traditional neon bulb.
5, the present invention easily seals, and can move in the water.
6, the present invention is an environmentally friendly machine, and unharmful substance is released.
7, application of the present invention is wide, removes the exploitation industry, beautifies outside the brightening environment, also can widen the photoelectric markers in fields such as road traffic, space flight navigation, can be made into light-emitting floor tile, railing, is used for building and beautifies.
Description of drawings
The invention will be further described below in conjunction with drawings and Examples.
Fig. 1 is structural representation of the present invention (cut-open view)
Fig. 2 is an alternative embodiment of the invention synoptic diagram (cut-open view)
Embodiment
Referring to Fig. 1, relief type active display device of the present invention has base plate 6, and this base plate is provided with electric light source 1, circuit board 4 and optical processing plate 3, and cover is adorned sculptured case 2 on the described base plate, is coated with decorative coveringn 5 on this case outside surface.Wherein electric light source is used to produce the light of different wave length; Sculptured case is the formation thing of figure style, and geometric configuration has different geometric cross section sizes with the difference of figure style, and its thickness can be determined according to size, intensity and the light transmittance requirement of figure style; Electric light source welding is connected on the circuit board, and the optical processing plate places circuit board light source one side; Electric light source, circuit board and optical processing plate are formed entity and are placed in the described sculptured case, and it is fixing that particular location can be adjusted the back; The section configuration of optical processing plate and circuit board is straight line not necessarily, also may be the combination of curve or curve and straight line.It depends on sculptured case section trend; Base plate is the bonnet of figure style.Referring to Fig. 2, when making full stereographic map style, do not use bonnet, be the sculptured cover of a global shape, decorative layer is in order to express the art color of figure style; Obturage with fluid sealant in the junction of sealed picture style table body.
Electric light source is generally arranged into an array on circuit board, also can be that monomer exists.Lighting of electric light source by rectification, pressure regulation, mu balanced circuit power supply.The density number that uses according to electric light source can be series, parallel or series-parallel connection.
Described electric light source is the LED transistor, and described circuit board surface adheres to wrinkle shape optical processing plate, and the raw material that constitutes described case comprises transparent resin, plastic pigment, glass microballoon, organic cobalt salt catalyzer, ketonic compound hardening agent, glass fabric.
Embodiment one: a kind of manufacture method of sculptured case:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Cobalt iso-octoate catalyzer 0.05-4 part
Methyl ethyl ketone peroxide hardening agent 0.5-4 part.
Embodiment two: a kind of manufacture method of sculptured case: this embodiment is that with the difference of embodiment one used case glue proportioning is different:
Described case glue is made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Cobalt iso-octoate catalyzer 0.05-4 part
Methyl ethyl ketone peroxide hardening agent 0.5-4 part
Phosphorus benzene plasticiser 1-5 part.
Embodiment three: a kind of manufacture method of relief type active display device:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object; Present embodiment is a red five-pointed star; The proportioning of calcium plaster is in the present embodiment, 1 part of gesso, 0.05 part of white cement, 0.05 part of glass fibre;
B, on red five-pointed star gypsum former coating release agent 2-3 time; Described release agent is a shellac varnish; Be coated with shellac varnish earlier, and then coated floor wax.
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, present embodiment applies twice altogether, can form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment is 0.01 part of a red
3 parts of glass microballoons
0.15 part of cobalt iso-octoate catalyzer
0.8 part in methyl ethyl ketone peroxide hardening agent
1.5 parts of phosphorus benzene plasticisers (can use DBP);
Above-mentioned raw materials stirs, leave standstill 5-10 minute stand-by;
E, circuit board manufacturing mantle are coated with one deck resin glue earlier on a rigid substrates, cover the layer of glass fabric, outside described glass fabric, be coated with one deck resin glue then, treat to carry out second time coating after the described resin glue drying, till reaching thickness requirement, make the circuit board mantle;
F, on described soft mode, directly arrange circuit lead, form circuit board, coated with resins glue on described circuit board;
G, adhere to wrinkle shape optical processing plate at described circuit board surface;
H, the LED transistor is installed on described circuit board; Present embodiment adopts red LED pitch arrays by 12 millimeters on useful area to arrange, and electrically connects then;
I, described base plate and circuit board are installed in the described sculptured case;
J, in described sculptured case outside surface spraying and decorating coating, be the red resin lacquer herein,
K, go to plate unnecessary edge, back, with fluid sealant sealing, drying.
Claims (4)
1, a kind of relief type active display device, base plate (6) is arranged, this base plate is provided with electric light source (1), circuit board (4) and optical processing plate (3), it is characterized in that: cover is adorned sculptured case (2) on the described base plate, be coated with decorative coveringn (5) on this case outside surface, described electric light source is the LED transistor, described circuit board surface adheres to wrinkle shape optical processing plate, and the raw material that constitutes described case comprises transparent resin, plastic pigment, glass microballoon, organic cobalt salt catalyzer, ketonic compound hardening agent, glass fabric.
2, a kind of method of making relief type active display device is characterized in that: when making sculptured case, adopt following steps:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Organic cobalt salt catalyzer 0.05-4 part
Ketonic compound hardening agent 0.5-4 part.
3, a kind of method of making relief type active display device is characterized in that: when making sculptured case, adopt following steps:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Organic cobalt salt catalyzer 0.05-4 part
Ketonic compound hardening agent 0.5-4 part
Phosphorus benzene plasticiser 1-5 part.
4, a kind of method of making relief type active display device is characterized in that:
A, turn over system gypsum former according to sculptured case model, calcium plaster is made up of gesso, white cement, fibre object;
B, on the gypsum former coating release agent 2-3 time;
C, coating release agent solidify the back and be coated with one deck case glue on the gypsum formers, cover the layer of glass fabric, outside described glass fabric, be coated with one deck case glue then, treat to carry out second time coating after the described case glue drying, till reaching thickness requirement, form sculptured case after the dry demoulding;
D, described case glue are made of following raw materials by weight portion ratio:
100 parts of transparent resins
Plastic pigment 0.005-3 part
Glass microballoon 5-20 part
Organic cobalt salt catalyzer 0.05-4 part
Ketonic compound hardening agent 0.5-4 part
Phosphorus benzene plasticiser 1-5 part;
E, circuit board manufacturing mantle: on a rigid substrates, be coated with one deck resin glue earlier, cover the layer of glass fabric, outside described glass fabric, be coated with one deck resin glue then, treat to carry out second time coating after the described resin glue drying, till reaching thickness requirement, make the circuit board mantle;
F, on described soft mode, directly arrange circuit lead, form circuit board, coated with resins glue on described circuit board;
G, adhere to wrinkle shape optical processing plate at described circuit board surface;
H, the LED transistor is installed on described circuit board;
I, described base plate and circuit board are installed in the described sculptured case;
J, in described sculptured case outside surface spraying and decorating coating.