CN1302727A - Cellular compound plate - Google Patents
Cellular compound plate Download PDFInfo
- Publication number
- CN1302727A CN1302727A CN00101336A CN00101336A CN1302727A CN 1302727 A CN1302727 A CN 1302727A CN 00101336 A CN00101336 A CN 00101336A CN 00101336 A CN00101336 A CN 00101336A CN 1302727 A CN1302727 A CN 1302727A
- Authority
- CN
- China
- Prior art keywords
- aluminum metal
- composite plate
- metal panel
- honeycomb
- honeycomb composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A composite cellular plate is disclosed, and features low cost, high toughness, compression strength, rigidity and decorative performance, and long service life. The plastic or paper honeycomb as sandwich layer is adhered between aluminium-alloy surface and bottom sheets. The polyvinylidene difluoride, acrylic or polyester paint is coated on its surface sheet.
Description
The invention belongs to composite material for decoration for building, be specifically related to a kind of honeycomb composite plate that is widely used in fields such as external and internal wall is decorated, building partition.
Existing honeycomb composite plate generally is to be core with aluminium matter honeycomb aluminium, makes panel and base plate with aluminium matter alloy, adopts epoxy resin glued membrane or liquid glue to make curing agent, with dull and stereotyped hydraulic press or the moulding of autoclave clearance-type.Hardening time is long, and production efficiency is low; And this honeycomb composite plate, tack coat is crisp, poor toughness, resistance to compression are low, poor rigidity, price are also expensive, gives to apply and has brought many difficulties.
The object of the present invention is to provide that a kind of cost is low, good toughness, compression strength are big, good rigidly, honeycomb composite plate that decorate properties is good.
Honeycomb composite plate of the present invention, it is characterized in that making core with plastic honeycomb or paper wasp nest, be bonded between aluminum metal panel and the aluminum metal base plate by thermoplastic adhesives and form sandwich, and be coated with polyvinylidene fluoride or acrylic acid, polyester organic coating at its aluminum metal panel surface.
Adopt the thermoplasticity PUR as binding agent, improved the temperature tolerance of honeycomb composite plate of the present invention, can use for a long time below 85 ℃; And adhesion strength is up to 5N/mm, the tack coat good toughness; Firm time is short, and the speed of production height can be continuously produced.
Above-mentioned honeycomb composite plate of the present invention adopts plastics and paper to make core, and 20-30% can reduce cost.Be convenient to extensively promote the use of; Paper honeycomb core if do simple waterproof, fire prevention processing, then has waterproof and flameproof effect with paper.
Honeycomb composite plate of the present invention, described aluminum metal panel and base plate can be the aluminium alloys of using always, fine aluminium or rustproof aluminum alloy base plate that panel preferably selects for use the surface to handle through chromaking, with the cohesive force of raising and coating or glue, its thickness is generally between 0.2-1.0mm.
Organic coating used in the present invention can be modified polyvinilidene difluoroethylene, acrylic acid baking vanish or enamel polyester paint.Surface coating modified polyvinylidene fluoride has not only improved the ornamental and corrosion resistance of composite plate, and because of its very superior ultraviolet-resistant capacity, can reach more than 10 years outdoor service life; If surface-coated acrylic acid baking vanish or enamel polyester paint then are applicable to indoor environment.
In order to protect honeycomb composite plate of the present invention surface in construction, to exempt from destruction, coated with protective film outside the organic coating of composite surface.
This honeycomb composite plate of the present invention is made core with plastics and paper, the 20-30% that can reduce cost, and also compression strength is big, good rigidly; Owing to adopt the thermoplasticity PUR as binding agent, improve the heat resistance of honeycomb composite plate of the present invention greatly, can use for a long time below 85 ℃; And adhesion strength is up to 5N/mm, the tack coat good toughness; Firm time is short, and the speed of production height can be continuously produced; Owing on the outer surface of aluminum metal panel, be coated with organic coating, make honeycomb composite plate of the present invention have excellent decoration and corrosion resistance, be a kind of desirable construction material composite plate; This honeycomb composite plate applies the modified polyvinilidene difluoroethylene in surface of aluminum plate, and very superior ultraviolet-resistant capacity is arranged, and can reach more than 10 years outdoor service life.If surface-coated acrylic acid baking vanish or enamel polyester paint can be used for indoor environment.
The invention will be further described below in conjunction with accompanying drawing:
Fig. 1 is the structural representation of a kind of embodiment of honeycomb composite plate of the present invention.
As shown in Figure 1; honeycomb composite plate of the present invention; make core 1 with plastic honeycomb or paper wasp nest; be bonded between aluminum metal panel 3 and the following aluminum metal panel 4 by thermoplastic adhesive layer 2 and form sandwich; and be coated with polyvinylidene fluoride or acrylic acid, polyester organic coating 5 at its aluminum metal panel surface; and outside this organic coating 5 coated with protective film 6, put down in writing the concrete structure and the performance thereof of above-mentioned this class formation flame-retardant aluminum plastic composite board among the embodiment one:
Embodiment one
Make panel with thick 3003 aluminiums of 1.0mm, outer surface of aluminum plate roller coat polyvinylidene fluoride coating, make core with the 8mm plastic honeycomb, adopt the thermoplastic bonded glued membrane to make tack coat, through 140 ℃ with compound 5 minutes of 1m/min speed heat, composite board bonding peel strength>5N/mm that cooling makes, rigidity>2.0KNm2/m.This material can be used for the external wall finishing.
Claims (3)
1. honeycomb composite plate, it is characterized in that making core (1) with plastic honeycomb or paper wasp nest, be bonded between aluminum metal panel (3) and the aluminum metal base plate (4) by thermoplastic adhesive layer (2) and form sandwich, and polyvinylidene fluoride or acrylic acid, polyester organic coating (5) are arranged in its aluminum metal panel (3) surface-coated.
2. honeycomb composite plate as claimed in claim 1 is characterized in that described aluminum metal panel (3) is that thickness is fine aluminium or rustproof aluminum alloy base plate 0.2-1.0mm, that handle through chromaking on the surface.
3. honeycomb composite plate as claimed in claim 1 or 2, the organic coating (5) that it is characterized in that described aluminum metal panel (3) is modified polyvinilidene difluoroethylene, acrylic acid baking vanish or enamel polyester paint.