CN1299846A - Weather-resistant high-flowbility fireproof shock-resistant polystyrene composite with less environment pollution - Google Patents
Weather-resistant high-flowbility fireproof shock-resistant polystyrene composite with less environment pollution Download PDFInfo
- Publication number
- CN1299846A CN1299846A CN 00124685 CN00124685A CN1299846A CN 1299846 A CN1299846 A CN 1299846A CN 00124685 CN00124685 CN 00124685 CN 00124685 A CN00124685 A CN 00124685A CN 1299846 A CN1299846 A CN 1299846A
- Authority
- CN
- China
- Prior art keywords
- resistant
- weather
- flowbility
- environment pollution
- less environment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Starting material | Proportioning (weight) |
EPDM cyclohexane peroxide CHP styrene monomer butyl acrylate | ????50 ????935 ????0.5 ????10 ????5 |
Component | ????1 | ????2 | ????3 | ????4 | ????5 * |
Resin HIPS | ?100 | ????73.2 | ????64.2 | ????69.2 | ????69.2 |
BT-93 fire retardant BEO (FR-2400) MBEO (FR-3030) | ????12 | ????3 ????17 | ????3 ????12 | ????3 ????12 | |
The fire-retardant tetrafluoroethylene that increases of zinc borate is imitated agent three (nonyl) phosphorous acid ester | ????6 ????0.3 ????1 | ????7 ????0.3 ????1 | ????7 ????0.3 ????1 | ????7 ????0.3 ????1 | |
Impact changes the EPDM-g-St/BA agent | ????3 | ????3 | ????3 | ????3 |
Titanium dioxide weather resisting agent UV-327 UV-770 | ????2 ????0.2 ????0.4 | ????2 ????0.2 ????0.4 | ????2 ????0.2 ????0.4 | ????2 ????0.2 ????0.4 | |
Coupling agent sulfonyl azide silane | ????0.5 | ????0.5 | ????0.5 | ????0.5 | |
BHT oxidation inhibitor 168 | ????0.2 ????0.2 | ????0.2 ????0.2 | ????0.2 ????0.2 | ????0.2 ????0.2 | |
Stearylamide processing helps calcium stearate agent butyl stearate | ????0.5 ????0.25 ????0.25 | ????0.5 ????0.25 ????0.25 | ????0.5 ????0.25 ????0.25 | ????0.5 ????0.25 ????0.25 | |
The crooked intensity burning property of the crooked modulus of physics performance melting index stretching intensity elongation at break Izod notched Izod impact strength heat distortion temperature (1.6mm) | ?2.7 ?27 ?40 ?11 ?85 ?2300 ?39 ?HB | ????3.0 ????25 ????40 ????8 ????80 ????2100 ????36 ????V-0 | ????16 ????23 ????30 ????10 ????78 ????2100 ????34 ????V-0 | ????15 ????25 ????45 ????11 ????80 ????2100 ????35 ????V-0 | ????15 ????24 ????45 ????8 ????78 ????2100 ????35 ????V-1 |
Xenon lamp artificial accelerated aging performance (300hour) Izod notched Izod impact strength DE | ??4 ??25 | ????6 ????0.9 | ????7 ????1.1 | ????9 ????1.8 | ????7 ????1.8 |
Claims (9)