CN1298033A - AC plasma melting reduction process and equipment for direct smelting of ferroalloy with very low carbon content - Google Patents
AC plasma melting reduction process and equipment for direct smelting of ferroalloy with very low carbon content Download PDFInfo
- Publication number
- CN1298033A CN1298033A CN99120078A CN99120078A CN1298033A CN 1298033 A CN1298033 A CN 1298033A CN 99120078 A CN99120078 A CN 99120078A CN 99120078 A CN99120078 A CN 99120078A CN 1298033 A CN1298033 A CN 1298033A
- Authority
- CN
- China
- Prior art keywords
- smelting
- parts
- plasma
- ferroalloy
- low carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
In a triphase AC plasma smelting furnace with small hole graphite electrode as melting equipment, Ar or coke oven gas as gas carrier is led in and one electrode is used also as material feeder electrode, via the central hole of which chromium concentrate powder, molybdenum concentrate powder, or tungsten concentrate powder, as well as duriron powder, lime, fluotrite, etc. are sprayed into molten bath. Reduced Cr, W, Mo and other metal are fused into molten steel or iron to produce alloy with required composition. The whole melting, reduction and alloying process has fast speed, high yield and low cost.
Description
The invention belongs to the plasma smelting reduction technology, relate in particular to the method and apparatus that in the AC plasma stove, carries out the direct smelting of ferroalloy with very low carbon content of melting and reducing.
At present, smelt the method for little carbon infusibility iron alloy both at home and abroad, useful electric furnace process (smelting ferrotungsten), the outer metallothermics (smelting molybdenum-iron) of electric furnace or vacuum resistance oven process (smelting micro-carbon chrome iron) and stove etc.In order to obtain ferroalloy with very low carbon content, adopt non-carbon raw material to make reductive agent, as use the silicochrome smelting micro-carbon chrome iron, make reductive agent with silicon, aluminium and smelt molybdenum-iron and ferrotungsten.The reduction temperature of this class iron alloy and fusing point are all than higher.More than 2800K, be the semi-melting state as the fusing point of ferrotungsten during with electrosmelting, can not flow automatically come out of the stove outside, tap to tap time is very long, energy consumption is excessive.As mentioned above, when smelting this class iron alloy, owing to need special smelting technology, maybe need to make reductive agent with expensive non-carbon raw material, or energy consumption that need be too high or the like, thereby cause the cost of this class iron alloy too high, finally also cause too high as the cost of the steel alloy of alloy addition with this class iron alloy.
The method and apparatus that the purpose of this invention is to provide a kind of quick, efficient, easy and economic direct smelting of ferroalloy with very low carbon content of melting and reducing that in plasma electric stove, carries out chromium, tungsten, concentrated molybdenum ore.
For achieving the above object, the present invention in the technical scheme that is adopted on the technology is: intact required steel scrap bits of disposable in advance filling or waste iron filing in the three-phase alternating current plasma heating furnace, and add fine chrome mine or tungsten concentrate or concentrated molybdenum ore, ferrosilicon, lime and magnesium oxide, account for about 2/3 of total heat size.
When smelting the Cr55 extra low carbon ferrochromium, the content percentage and the used share of the used composition of furnace charge are: Cr
2O
3Be 100 parts of 52.10% fine chrome mines; Silicon is 25～27 parts of 75% ferrosilicon powders; 8～10 parts in steel scrap bits; 8～10 parts in the lime of CaO 〉=75%; 4～6 parts in the magnesium oxide of MgO 〉=90%.
When smelting the W75 ferrotungsten, the content percentage and the used share of the used composition of furnace charge are: WO
3Be 100 parts of 67.87% tungsten concentrates; Silicon is 21～23 parts of 75% ferrosilicon powders; SiO
26～8 parts in 〉=95% silica; CaF
22～3 parts in 〉=85% fluorite; 4～5 parts in steel scrap bits.
When smelting Mo60 molybdenum-iron, the content percentage and the used share of the used composition of furnace charge are: MoO
3Be 100 parts of 69.82% concentrated molybdenum ores; Silicon is 30～32 parts of 75% ferrosilicon powders; 4～6 parts in the lime of CaO 〉=75%; CaF
21～2 part in 〉=85% fluorite; 15～17 parts in steel scrap bits.
The used gas carrier of plasma generator is an Ar gas, or coke-oven gas.Coke-oven gas can produce the reductibility plasma body, favourable smelting reduction process.
During smelting, treat the big fusing of furnace charge after, add the powder raw material that drying and mixing are crossed in the plasma heating furnace, control size＜20 orders.Its mode is evenly to spray into plasma heating furnace arc district with the fluidisation dusting device by an aperture Graphite Electrodes.As-reduced Metal Cr, W and Mo dissolve in the steel scrap bits or waste iron filing liquid that melted, reach the iron alloy target value of code designation.
For realizing goal of the invention, the technical scheme that the present invention adopts on device is: be used for the plasma heating furnace of melting and reducing chromium, tungsten, the direct smelting of ferroalloy with very low carbon content of concentrated molybdenum ore, be made up of three-phase AC plasma generator and body of heater two portions.This producer is made of three aperture Graphite Electrodess, and three electrodes are vertically installed parallel to each other, and the garden heart of three electrodes is equilateral triangle and evenly arranges.Every electrode all can move up and down and move with parallel, and every kind is moved all energy self-lockings.Body of heater is made up of bell and garden platform shape furnace shell, and liner is a high-temperature refractory, and bell and body of heater are welded with steel plate, and water flowing is cooled off; Have the hole on the bell, insert and lifting for electrode, furnace bottom has iron alloy spout and slag-drip opening.
Three root graphite electrodes bore a φ 4～φ 8mm aperture along the axle center, to inject the gas carrier of steady flow.With one in three root graphite electrodes, as the reinforced utmost point that dusts, the size in hole can flow smoothly to satisfy powder, and with certain gas-powder ratio powder is evenly sprayed into, make powder when the Graphite Electrodes port flows out major part by the plasma high-temperature fusion and be reduced to suitable.
Because adopt technique scheme, the present invention has following a series of characteristics:
Adopt melting and reducing can not produce to have reduced the re-oxidation of alloying element, can make in the iron alloy oxygen level reduce to very low-level;
Adopt ferrosilicon powder to make reductive agent, C content can once drop to the requirement of C content in little C iron alloy in the steel; Adopt the fluidisation dusting device that all raw materials are evenly sprayed into high-temperature plasma arc district by centre hole of electrode, not only melting and reducing speed is exceedingly fast, and has simplified reinforced process;
Adopt the three-phase alternating current low-voltage high-current transformer to provide plasma generator required power supply, the ordinary arc furnace of same capability can satisfy this requirement with transformer.Therefore, wide adaptability.
Adopt aperture Graphite Electrodes of the present invention, the plasma arc striking is easy, and the arc body is stable, not influenced by furnace charge.Can regulate the arc length of plasma arc by the lifting Graphite Electrodes; Also can be by the inferior pole tension of regulating transformer and power and the arc length that carrier gas flux is regulated plasma body, to satisfy the requirement of smelting technology process.
Also can adopt coke-oven gas substitute Ar gas as gas carrier to produce the reductibility plasma body, help the processing requirement of smelting reduction process, and more more economical than Ar gas, be suitable for.
Adopt powder to go into stove, need not make the ball clamp dog to furnace charge, without adding additives, the furnace charge wide adaptability does not all have particular requirement to furnace charge grade, granularity and the shape of needs yet.
Therefore the present invention can reach following technico-economical comparison:
1, tap to tap time＜30 minute;
2, the Cr rate of recovery can reach 90～95%, W and the Mo rate of recovery can reach 96～98%;
3, the iron alloy cost can reduce by 1/3.
Its index for details see attached table.
Now in conjunction with the accompanying drawings and embodiments the present invention is further described:
Fig. 1 is that three-phase alternating current plasma smelting reduction chromium of the present invention, tungsten, concentrated molybdenum ore are directly smelted little C iron alloy process flow diagram.
Fig. 2 is the apparatus structure synoptic diagram of three-phase alternating current plasma smelting reduction chromium of the present invention, tungsten, the direct smelting of ferroalloy with very low carbon content of concentrated molybdenum ore.
Technical process of the present invention is as shown in Figure 1:
The first step, earlier with granularity＜20 purpose chromium, tungsten, concentrated molybdenum ore powder, ferrosilicon powder and flux, 120 ℃ with the interior drying of carrying out, after batching, carry out mixing, the exsiccant purpose is to guarantee powder fluidisation and conveying smoothly in powder spraying pot, also guarantees batching accurately.
Second step, steel scrap bits or waste iron filing need once be packed in the stove by batching, add partially mixed material again, be filled into about 2/3 of whole heat size.All the other powders powder spraying pot of packing into, and with Ar gas pressurising fluidisation.
The 3rd step, plasma smelting reduction.Injected Ar gas before this in the aperture Graphite Electrodes, starting transformer power supply (transformer is the three-phase alternating current low-voltage high-current transformer) draws plasma arc.After about 5 minutes, when the fusion and when being full of plasma body substantially of the furnace charge in the plasma heating furnace, open powder spraying pot blanking ball valve and spray into remaining mixed powder, the control gas-powder ratio is suitable, makes the powder can be by fusion of high-temperature plasma arc and reduction once leaving electrode ports.Regulate electrode height then, adopt the refining of plasma submerged arc, and suitably reduce used plasma power.
In the 4th step, promote electrode, have a power failure, stop the supple of gas or steam, tap, slag tap.
Embodiment 1
When smelting the Cr55 extra low carbon ferrochromium, the content percentage and the used share of the used composition of furnace charge are: Cr
2O
3Be 100 parts of 52.10% fine chrome mines; Silicon is 25 parts of 75% ferrosilicon powders; 8 parts in steel scrap bits, 8 parts in the lime of CaO 〉=75%; 4 parts in the magnesium oxide of MgO 〉=90%.The ferrochrome composition that obtains is: Cr is 55～57%, and C is 0.1～0.25%, Si≤1.0～1.5%, S＜0.02%, P＜0.02%; The recovery rate of Cr is 90～95%.
Embodiment 2
When smelting the little carbon ferrotungsten of W75, the content percentage and the used share of the used composition of furnace charge are: WO
3Be 100 parts of 67.87% tungsten concentrates; Silicon is 21 parts of 75% ferrosilicon powders; SiO
26 parts in 〉=95% silica; CaF
22 parts in 〉=85% fluorite, 4 parts in steel scrap bits.The ferrotungsten composition that obtains is: W is 75～77%, and C is 0.1～0.2%, Si≤0.5～1.0%, S＜0.02%, P＜0.02%; The recovery rate of W is 96～98%.
Embodiment 3
When smelting the little carbon molybdenum-iron of Mo60, the content percentage and the used share of the used composition of furnace charge are: MoO
3Be 100 parts of 69.82% concentrated molybdenum ores; Silicon is 30 parts of 75% ferrosilicon powders, 4 parts in the lime of CaO 〉=75%, CaF
21 part in 〉=85% fluorite, 15 parts in steel scrap bits.The molybdenum-iron composition that obtains is: Mo is 60～62%, and C is 0.1～0.2%, S≤0.1～0.2%, P≤0.05～0.1%, Si≤1.0～1.5%; The recovery rate of Mo is 96～98%.
Three-phase alternating current plasma smelting reduction chromium, tungsten, the direct smelting of ferroalloy with very low carbon content device of concentrated molybdenum ore are as shown in Figure 2.It comprises plasma heating furnace and plasma generator two portions, and plasma heating furnace is made up of bell " 4 " and body of heater " 5 " two portions.Bell " 4 " is curved, and the center has electrode " 2 ", " 8 ", " 9 " insertion and hatch; Body of heater " 5 " is a garden platform shape, and the bottom corresponding site has slag-drip opening " 6 " and iron alloy outlet " 7 ", and the shell steel plate weldering knot of bell " 4 " and body of heater " 5 " forms all water flowing coolings, interior block high-temperature refractory.
Plasma generator is made up of three Graphite Electrodes " 2 ", " 8 ", " 9 " that are drilled with aperture along the axle center, and wherein the aperture of a brill is bigger, holds concurrently for spraying into furnace charge by powder spraying pot " 1 ".Water-cooled copper electrode jaw " 3 " is for the input of 100～135V three-phase alternating current, and connects with electrode lifting device and insulate the lifting of realization electrode, the processing requirement of translation.
Inject the plasma gas carrier Ar or the coke-oven gas of steady flow by the aperture of electrode, powder spraying pot " 1 " uses the Ar gas of certain pressure as source of the gas, provides the powder of steady flow to spray in the stove.
Concrete operations of the present invention are: promote electrode " 2 ", " 8 ", " 9 ", open bell " 4 ", in the steel scrap that will prepare burden required earlier bits or the disposable adding stove of scrap iron; Again the compound after drying, mixing and the batching is added in the stove, be loaded into about 2/3 of whole heat size, cover bell " 4 ", insert electrode " 2 ", " 8 ", " 9 ", start water pump and make bell " 4 ", furnace shell " 5 " and water-cooled copper electrode jaw " 3 " feed water coolant.With the remaining mixed powder powder spraying pot " 1 " of packing into, and with the pressurising of Ar gas to certain pressure; Electrode " 8 " and " 9 " are injected the plasma carrier gas, start power supply, draw plasma arc, regulate electrode and make plasma arc stable.After about 5 minutes, treat most of furnace charge fusion and reduction, charge level descends, and upper space has been full of plasma gas.At this moment plasma arc is very stable, and pellet cuts down under the unlatching powder spraying pot, and feed in stove has sprayed until material.Regulate electrode " 2 ", " 8 ", " 9 " lifting, carry out the submerged arc refining.Smelt and finish, promote electrode " 2 ", " 8 ", " 9 ", have a power failure, stop the supple of gas or steam, the band slag goes out iron alloy, has gone out whole slags at last.
Subordinate list
Claims (10)
1. method that adopts the direct smelting of ferroalloy with very low carbon content of plasma smelting reduction, its feature comprises: load steel scrap bits or iron filings in advance in three-phase alternating current aperture Graphite Electrodes plasma heating furnace, and add fine chrome mine or concentrated molybdenum ore or tungsten concentrate, ferrosilicon, lime and magnesium oxide.
2. the method for the direct smelting of ferroalloy with very low carbon content of plasma smelting reduction according to claim 1, when it is characterized in that smelting the Cr55 extra low carbon ferrochromium, the content percentage and the used share of the used composition of furnace charge are: Cr
2O
3Be 100 parts of 52.10% fine chrome mines; Silicon is 25～27 parts of 75% ferrosilicon powders; 8～10 parts in steel scrap bits; 8～10 parts in the lime of CaO 〉=75%; 4～6 parts in the magnesium oxide of MgO 〉=90%.
3. the method for the direct smelting of ferroalloy with very low carbon content of plasma smelting reduction according to claim 1, when it is characterized in that smelting the W75 ferrotungsten, the content percentage and the used share of the used composition of furnace charge are: WO
3Be 100 parts of 67.87% tungsten concentrates; Silicon is 21～23 parts of 75% ferrosilicon powders; SiO
26～8 parts in 〉=95% silica; CaF
22～3 parts in 〉=85% fluorite, 4～6 parts in steel scrap bits.
4. the method for the direct smelting of ferroalloy with very low carbon content of plasma smelting reduction according to claim 1, when it is characterized in that smelting Mo60 molybdenum-iron, the content percentage and the used share of the used composition of furnace charge are: MoO
3Be 100 parts of 69.82% concentrated molybdenum ores; Silicon is 30～32 parts of 75% ferrosilicon powders, 4～6 parts in the lime of CaO 〉=75%, CaF
21～2 part in 〉=85% fluorite, 15～17 parts in steel scrap bits.
5. according to the method for the direct smelting of ferroalloy with very low carbon content of the described plasma smelting reduction of claim 1～4, the raw material that it is characterized in that adding in the plasma furnace is the dry powder of crossing, granularity＜20 orders.
6. according to the method for the direct smelting of ferroalloy with very low carbon content of the described plasma smelting reduction of claim 1～5, it is characterized in that toward the mode of the interior addition material of plasma heating furnace be by gas powder evenly to be sprayed into plasma heating furnace arc district through an aperture Graphite Electrodes with the fluidisation dusting device.
7. device that is used for the direct smelting of ferroalloy with very low carbon content of melting and reducing is characterized in that it is made up of three-phase AC plasma generator and body of heater.The three-phase alternating current producer is made of three aperture Graphite Electrodess " 2 ", " 8 ", " 9 ".Make gas carrier with Ar gas or coke-oven gas.Body of heater is made up of bell " 4 " and garden platform shape furnace shell " 5 ", liner is a high-temperature refractory, and bell " 4 " and furnace shell " 5 " are welded with double-layer plate, all water flowing coolings, bell has the hole on " 4 ", and furnace bottom has iron alloy spout " 7 " and slag-drip opening " 6 ".
8. smelting of ferroalloy with very low carbon content device according to claim 7 is characterized in that described three electrodes " 2 ", " 8 ", " 9 " vertically installation parallel to each other, and the garden heart of three electrodes " 2 ", " 8 ", " 9 " is equilateral triangle and evenly arranges.
9. smelting of ferroalloy with very low carbon content device according to claim 8 is characterized in that three root graphite electrodes " 2 ", " 8 ", " 9 " bore a φ 4～φ 8mm aperture along the axle center.
10. smelting of ferroalloy with very low carbon content device according to claim 9 is characterized in that with one in three root graphite electrodes " 2 ", " 8 ", " 9 ", as the reinforced utmost point that dusts.