CN1294162A - Priming paint for coating on lampshade - Google Patents
Priming paint for coating on lampshade Download PDFInfo
- Publication number
- CN1294162A CN1294162A CN 99115610 CN99115610A CN1294162A CN 1294162 A CN1294162 A CN 1294162A CN 99115610 CN99115610 CN 99115610 CN 99115610 A CN99115610 A CN 99115610A CN 1294162 A CN1294162 A CN 1294162A
- Authority
- CN
- China
- Prior art keywords
- priming paint
- lampshade
- resin
- acrylic
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A priming paint for coating on lampshade is prepared from filming resin, diluent, optical trigger and assistant through proportional mixing. Its advantages include high productivity, stable quality, low energy consumption and no pollution.
Description
The present invention relates to a kind of coating priming paint, be specifically related to a kind of ultraviolet light polymerization coating priming paint that is used for the car light lampshade.
Existing domestic car light lampshade coating priming paint all is to adopt amino varnish baking to form, adopt this varnish technology loaded down with trivial details, during in particular for metal base, need first phosphatization, polishing, and then last twice varnish, energy expenditure is big, environmental pollution is serious, is unwell to streamline production, the product quality instability, quality can not get guaranteeing that production efficiency is low.
The present invention's purpose aim to provide a kind ofly be suitable for that streamline production, production efficiency height, product with stable quality, energy consumption are low, pollution-free, prescription rationally, the lampshade coating priming paint of simple, the excellent property of technology.
Technical solution of the present invention is: this lampshade coating priming paint is made up of film-forming resin, thinner, light trigger, auxiliary agent, and by after certain weight percent proportioning, mixing and stirring is made.
Above-mentioned film-forming resin is acrylic-amino resin or phenolic aldehyde epoxy acrylic resin or vinylformic acid silicone resin, and thinner is acrylic monoester or polyester.
Its weight percent proportioning of above-mentioned component is: film-forming resin: 35-55%, thinner: 40-60%, light trigger: 1-5%, auxiliary agent: 1-2%.
The present invention fills a prescription rationally, and manufacture craft is simple, and energy consumption is low, pollution-free, excellent property, is suitable for streamline production, the production efficiency height, and product with stable quality, excellence are widely used.
Film-forming resin of the present invention is acrylic-amino resin or phenolic aldehyde epoxy acrylic resin or vinylformic acid silicone resin, acrylic-amino resin is by aminoresin and the exchange of hydroxyl acrylate and make, thinner is acrylic monoester or polyester, as (methyl) Hydroxyethyl acrylate, (methyl) Propylene glycol monoacrylate, butyl acrylate, the vinylformic acid cyclohexyl ester, Isooctyl acrylate monomer, the N-V-Pyrol RC, isobornyl acrylate, propylene glycol diacrylate, diethylene glycol diacrylate, three diglycol ethylene diacrylates, tripropylene glycol diacrylate, polyethyleneglycol diacrylate, a 1.6 hexanediyl ester, Viscoat 295, defend the tetrol triacrylate season, defend two seasons such as tetrol six acrylate etc.But light trigger is to adopt the radical photoinitiator of hypersorption at the initiated polymerization of 200-400nm wavelength, be that light trigger is the material that produces free radical under UV-irradiation, cause radical polymerization, as benzoin ether, benzil class, Benzophenones, anthraquinone class, thioxanthones and contain Phosphorus initiator.Auxiliary agent then comprises flow agent, defoamer, hot stopper, adhesion promoter, antiaging agent etc.
The present invention is as follows as the making method of lampshade coating priming paint: at first base material is carried out pre-treatment--oil removing, dedusting, drying, metal base also will eliminate rust, then ultraviolet light polymerization coating priming paint oil polish is sprayed at substrate surface, infrared levelling is about three minutes, after treating that ultraviolet light polymerization fully, can aluminize, just obtain transmittance height, heat-resisting, plated film lampshade that ageing resistance is strong after aluminizing.
Embodiment 1: adopt following component and by certain weight percent proportioning: acrylic-amino resin or phenolic aldehyde epoxy acrylic resin: 35%, PETA:10%, TPGDA:15%, HEA:18%, HDDH:17%, 1173:4.5%, auxiliary agent: 0.5% with the above-mentioned substance mixing and stirring, makes.
Art performance (filming)
Color: water white transparency
Outward appearance: smooth smooth, fullness ratio is high
Coating method: spraying d
Sticking power :≤1
Thermotolerance: 160 ℃ * 10hr no change
Transmittance behind the plated film: pass through industry standard
Pencil hardness: 2H
Embodiment 2: adopt following component and by certain weight percent proportioning: acrylic-amino resin: 35%, PETA:15%, TPGDA:20%, butyl acrylate: vinylformic acid cyclohexanol 16%: 8%, 1173:4.5%, auxiliary agent: 1.5%, with the above-mentioned substance mixing and stirring, make.
Technical feature:
Color: water white transparency
Outward appearance: smooth smooth, the fullness ratio height
Coating method: spraying
Sticking power :≤1
Thermotolerance: 160 ℃ * 10hr no change
Transmittance behind the plated film: pass through industry standard
Pencil hardness: 2H
Embodiment 3: adopt following component and by certain weight percent proportioning: acrylic-amino resin: 38%,
Butyl acrylate: 40%, Hydroxyethyl acrylate: 12%, PETA:5%, 1173:4%, auxiliary agent: 1%, with the above-mentioned substance mixing and stirring, make.
Technical feature:
Color: water white transparency
Outward appearance: smooth smooth, the fullness ratio height
Coating method: spraying
Sticking power :≤1
Thermotolerance: 160 ℃ * 10hr no change
Transmittance behind the plated film: pass through industry standard
Pencil hardness: 2H
Claims (3)
1, a kind of lampshade coating priming paint is characterized in that being made up of film-forming resin, thinner, light trigger, auxiliary agent, and by after certain weight percent proportioning, mixing and stirring is made.
2, lampshade coating priming paint according to claim 1 is characterized in that described film-forming resin is acrylic-amino resin or phenolic aldehyde epoxy acrylic resin or vinylformic acid silicone resin, and thinner is acrylic monoester or polyester.
3, lampshade coating priming paint according to claim 1 and 2 is characterized in that the weight percent proportioning of described component is: film-forming resin: 35-55%, thinner: 40-60%, light trigger: 1-5%, auxiliary agent: 1-2%.