CN1293163A - Pearlite admixture for concrete - Google Patents
Pearlite admixture for concrete Download PDFInfo
- Publication number
- CN1293163A CN1293163A CN 00127571 CN00127571A CN1293163A CN 1293163 A CN1293163 A CN 1293163A CN 00127571 CN00127571 CN 00127571 CN 00127571 A CN00127571 A CN 00127571A CN 1293163 A CN1293163 A CN 1293163A
- Authority
- CN
- China
- Prior art keywords
- concrete
- admixture
- pearlite
- cement
- exciting agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A pearlite admixture for concrete contains pearlite powder and trigger (less than 5%). Said trigger is prepared from water glass, sodium hydroxide, calcium hydrogen carbonate and gypsum in weight ratio of 1:(0-0.3):(0-0.8):(0-2). It mey be used as substitute of cement in concrete and serves to decrease concrete cost by 20-30%, increase concrete strength by 10-15% and improve concrete durability.
Description
The present invention relates to a kind of concrete admixture, relating in particular to a kind of is the concrete admixture of main component with the perlite powder.
The Application and Development of high-quality active mineral admixture is development concrete---the gordian technique of high-strength concrete and high performance concrete particularly.The high-quality adulterant of domestic main use has Industrial emissions: silicon ash, first level flour coal ash and blast furnace slag pulverized powder, and the former measures few valency height (＞2000 yuan/ton), and it is required that the latter two quantity also far can not satisfy growing concrete.Therefore, both at home and abroad all actively seek suitable material through being processed into the high-quality active mineral admixture from natural resource hardy, China in this respect except that Tsing-Hua University more successfully Application and Development the zeolite rock powder, almost also be in the technology exploration stage.At present domesticly perlitic Application and Development is limited to the calcination swelling perlite powder serves as lightweight in cement-base composite material concrete, mortar etc., heat insulating gathers materials, and plays negative effect in this intensity to material.
The objective of the invention is to: to provide a kind of be main component with the perlite powder, especially for substituting part cement in high-strength concrete and the high performance concrete, the concrete admixture that performances such as concrete intensity, weather resistance are improved.
The present invention with the natural peral rock through Mechanical Crushing, grind to form the powder of certain fineness, add an amount of industrial chemicals and make exciting agent, form high-quality adulterant with height pozzolanic activity, be used for substituting part cement, performances such as concrete intensity, weather resistance are improved at high-strength concrete of concrete batching-particularly and high performance concrete.
Major technique content index is as follows:
1. main raw material perlite class acid volcanic rock: chemical ingredients SiO
2〉=70%, glassiness structure or ash structure, clumpy structure, less because of containing small pore proportion.
2. perlite powder preparation technology: dry grinding method.
3. adulterant mainly is made up of perlite powder and a small amount of exciting agent, wherein exciting agent content＜5%.
(1) the perlite powder fineness is preferably 80 μ m square hole sieve surplus≤10%, with＜5% the best.
(2) exciting agent is mixed by proportionings such as water glass, sodium hydroxide, Calcium hydrogen carbonate, gypsum, and the proportioning between them (WT) scope is 1: 0～0.3: 0～0.8: 0～2, and sodium hydroxide, Calcium hydrogen carbonate, gypsum three content can not be zero simultaneously.
4. the use of adulterant:
(1) volume: in high-strength concrete and high performance concrete this adulterant equivalent substitution 525# or more cement of high index can wherein be obtained concrete reinforced effects the best up to 40% with 10～20% equivalent substitution cement.If adopt the excess method of substitution or in normal concrete, this adulterant place of cement amount can be bigger.
(2) usage: identical with cement.
The present invention is described in detail below in conjunction with embodiment.
Embodiment:
The perlite place of production: Hu Wan town, Jinxi County, Jiangxi Province; The perlite feature: redness, glassiness structure contains the phenocryst or the crystallite of inequality, is a kind of volcanic eruption lava, and its chemical ingredients (WT%) is: SiO
2(76.89); Al
2O
3(10.51); Fe
2O
3(2.48); K
2O (8.25); Na
2O (0.80); CaO (0.12).
Perlite powder adulterant: by perlite powder: exciting agent=form at 98: 2; Wherein the perlite powder fineness is 80 μ m square hole water sieve surpluses 2.2%; The exciting agent proportioning is a water glass: Calcium hydrogen carbonate: gypsum=1: 0.6: 0.2.
The perlite powder adulterant is used in high performance concrete: during adulterant place of cement 15%, concrete work degree improves greatly, and early anti pressured intension (3 days) is approaching, and late period (28 days) and later stage (91 days) ultimate compression strength improve 26% and 33% respectively.See the following form: concrete mix and performance table
| Material usage (Kg/m) | Workability (cm) | Ultimate compression strength (Mpa) | ||||||||
| 525#R type cement | Adulterant | Medium sand | Limestone gravel | Water | FDN | Slump | Diffusibleness | 3 days | 28 days | 91 days |
| ?500 | ?0 | ?560 | ?1206 | ?150 | ?5 | ?18．5 | ?38．0 | ?51．2 | ?61．6 | ?62．5 |
| ?425 | ?75 | ?560 | ?1206 | ?150 | ?5 | ?25．5 | ?50．0 | ?50．1 | ?77．4 | ?83．8 |
The present invention program has the following advantages:
1. the admixture made of this technology can reach 20～30% thereby reduce Cost of Concrete as the cement substitute in concrete, and it is about 10～15% to improve concrete strength simultaneously, and strengthens concrete durability.
2. the high-quality active mineral admixture of a kind of natural resources of this technological development is for high-strength concrete and the requisite raw material of high performance concrete select to have increased kind. For Application and Development high-quality active mineral admixture more widely and promote the development of high-strength concrete and high performance concrete to set up the model.
3. compare with replaced thing cement, the technology production technology of this admixture is simple, and plant investment is few, energy and resource consumption are little, and low cost of manufacture is to the pollution of environment and endanger little, be typical " green " building materials, have obvious economic benefit and social benefit.
Claims (4)
1, a kind of pearlite admixture for concrete is made up of perlite powder and exciting agent, wherein exciting agent content＜5%.
2, the described pearlite admixture for concrete of claim 1, it is characterized in that: exciting agent is mixed by proportionings such as water glass, sodium hydroxide, Calcium hydrogen carbonate, gypsum, proportioning between them (WT) scope is 1: 0～0.3: 0～0.8: 0～2, and sodium hydroxide, Calcium hydrogen carbonate, gypsum three content can not be zero simultaneously.
3, pearlite admixture for concrete according to claim 1 and 2 is characterized in that: the perlite powder fineness is preferably 80 μ m square hole sieve surplus≤10%, with＜5% the best.
4, pearlite admixture for concrete according to claim 1 is characterized in that: as the adulterant of high-strength or high performance concrete.