CN1290667A - Mixed cement material with fine active steel slag powder and method of preparing high grade cement with it - Google Patents
Mixed cement material with fine active steel slag powder and method of preparing high grade cement with it Download PDFInfo
- Publication number
- CN1290667A CN1290667A CN00124821A CN00124821A CN1290667A CN 1290667 A CN1290667 A CN 1290667A CN 00124821 A CN00124821 A CN 00124821A CN 00124821 A CN00124821 A CN 00124821A CN 1290667 A CN1290667 A CN 1290667A
- Authority
- CN
- China
- Prior art keywords
- cement
- slag powder
- slag
- steel
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The fine active steel slag powder has a specific surface area greater than 300 sq m/Kg, a 40 micron below particle content greater than 65 wt%, a 7-day activity index not less that 75 % and a 28-day activity not less than 80 % and qualified stability. During compounding cement, steel slag powder accounting for 10-15 % of total water and other mixed material for 0-35 % are mixed. Group steel slag powder, coarse cement clinker and other components may be ground either before or after mixing. The steel slag powder is produced by crushing 60 mm below steel slag in a crusher and grading in a grading machine.
Description
The present invention is a kind of cement high reactivity blending material made from ground steel slag and with the method for its preparation cement, relates to the cement material field of building material industry.
Technology related to the present invention has following:
(1) adopt slag to prepare dross slag cement as cement additive.Its major technique and more advanced technology are: water is vexed in advance with slag, makes it to be crushed into several centimetres to several millimeters particle, with these steel slag particles and the common grinding of cement clinker, slag and gypsum, reaches specific surface area 350m
2/ kg makes cement.Wherein the part by weight of each component is: slag 〉=30%, and slag+slag 〉=60%, gypsum about 5%, all the other are Portland clinker.The strength of cement of making is divided into 325 and 425 two labels.Corresponding dross slag cement national standard is arranged.
(2) utilize steel-making slag powder as cement additive, add exciting agent, preparation contains the cement of slag.Be characterized in: when manufacture of cement, add special exciting agent, improve strength of cement.The kind of exciting agent has multiple, and majority is an industrial chemicals, and some are also arranged is burnt gypsum.The common grinding of granular slag and cement clinker, gypsum and exciting agent.Strength of cement label major part is 325# and 425#, has on a small quantity to reach 525#.
Above technology has been represented slag on going result aspect the utilisation technology in cement in recent years, but the fineness for slag is not controlled, and the actual particle of slag in cement is thick excessively, and the activity of slag does not obtain performance, activity is lower, causes steel slag cement intensity low.The dross slag cement label of factory's actual production is mainly 325# and 425#.If weigh according to international standard (iso standard), strength mark is lower.If adopt the method for admixture exciting agent, though the strength of cement label can be brought up to 525#, national cement standard does not allow admixture to the influential auxiliary agent of cement performance, otherwise concrete Effect on Performance is difficult to control.This cement that has caused containing slag the competitive power on the market a little less than, this is restricted the utilize total amount of slag in cement.
The objective of the invention is to make a kind of highly active slag pulverized powder that has, as the high reactivity blending material of cement, in cement during admixture 10-35% (weight), can the preparation strength label be 525 cement; In cement during admixture 35-50% (weight), can the preparation strength label be 425 cement.This cement high reactivity blending material specific surface area is big, and is active high, is applicable to and makes 525# ordinary Portland cement, slag ordinary Portland cement, compound ordinary Portland cement, dross slag cement.Ground steel slag can be in cement admixture separately, also can with flyash, slag, volcanic ash, slag, zeolite, coal gangue, phosphorus slag and the compound admixture of other industrial residue.The cement of making is applicable to preparation normal concrete, mass concrete (as base concrete, the dam concrete of heavy construction), high-strength concrete, prestressed concrete, concrete prefabricated element etc.
Particular content of the present invention is as follows: 1. slag adopts levigate in advance and sorting, makes its specific surface area 〉=300m
2/ kg, particle diameter less than the granule content of 40 μ m greater than 65% (weight), salient features reaches: the activity index of 7 days and 28 days is respectively more than or equal to 75% and 80%, all far above country about requirement as the active standard code 70% of the industrial residue of cement additive; Density=2.90-3.30g/cm
3, press the steaming stability qualified.Wherein the test evaluation method of each index all adopts existing universal method:
Activity index: test according to " GB12957-1991 is as the industrial residue activity test method of cement additive ", represent with 28 days the ultimate compression strength of mixture of 30% (weight) ground steel slag and 70% (weight) 525# silicate cement and the ratio of 28 days ultimate compression strength of pure 525# silicate cement.That is:
Press and steam stability: after the admixture 30% high reactivity steel-making slag powder, the press-steamed method of stipulating through national cement standard is up to the standards in 525 silicate cements.
Basicity factor: the ratio with oxide content (weight) is represented: CaO/ (SiO
2+ P
2O
5)
Composition requires: metal Ferrum content≤0.8% (weight), free calcium oxide content≤3% (weight), basicity factor 〉=2.
2. admixture high reactivity steel-making slag powder mixing material is produced the method for cement of high index and is: when the preparation strength label is 525 cement, mix levigate high reactivity steel-making slag powder that accounts for gross weight 10-35% and other industrial residue that accounts for gross weight 0-30%, as mixing material; When the preparation strength label is 425 cement, mix levigate high reactivity steel-making slag powder that accounts for gross weight 30-50% and other industrial residue that accounts for gross weight 0-35%, as mixing material.Specific surface area 〉=the 300m of high reactivity steel-making slag powder wherein
2/ kg, other industrial residue comprises slag, flyash, volcanic ash, slag, zeolite, coal gangue, phosphorus slag etc.The kind of cement comprises ordinary Portland cement, slag ordinary Portland cement, compound ordinary Portland cement, Portland fly ash cement, dross slag cement.Adopt one of following three kinds of technologies to make cement: (1) also distinguishes grinding to specific surface in advance with other each component of cement except that steel-making slag powder
Long-pending 300m
2More than/the kg, and then with levigated steel-making slag powder ratio according to the rules is mixed
Close evenly, make cement.(2) other each component of cement is distinguished grinding in advance to specific surface area 200m
2More than/the kg,
And then with levigated steel-making slag powder mixed according to the rules is even, simultaneously in addition
Further grinding is made cement.(3) with the levigated steel-making slag powder with without levigated cement clinker and other each component in advance according to
The regulation ratio joins in the grinding machine simultaneously, and common grinding reaches total specific surface area
300m
2Make cement more than the/kg.3. the manufacturing process of high reactivity steel-making slag powder cement additive is as follows: less than the block slag of 60mm
Drop in the pulverizer and pulverize
Enter the grading machine sorting
Obtain specific surface area greater than 300m
2The powder-like product of/kg.Wherein when metal Ferrum content during greater than 0.8% (weight), insert magnetic separator in a link of giving birth to tight process, the blanking metallic iron makes it content less than 0.8% (weight).The specific surface area of powder-like product can be adjusted by the parameter of adjusting grading machine as required, and scope is 300-500m
2/ kg.
Advantage of the present invention and effect:
Ground steel slag proposed by the invention has that hydration reaction is active high, the manufacture of cement cost is low, strength of cement is high and advantage such as good combination property.The cement that the highly active ground steel slag of admixture part is made as mixing material is used for concrete works, can reduce concrete hydration heat temperature rise, guarantee early age strength of concrete, improve later strength, increase concrete wear resistance and corrosion resistance, improve concrete durability.
Below be embodiments of the invention: example 1: cement clinker in advance grinding to specific surface area 330m
2/ kg, the ground steel slag specific surface area
303m
2/ kg, levigate thin slag powders specific surface area 383m
2/ kg is according to following table batching, mixed
Close evenly, make cement, the pressure steaming stability that records cement is all qualified, time of coagulation
Normally, meet national standard, strength of cement such as following table:
Example 2: ground steel slag specific surface area 409m
2/ kg mixes with cement clinker, slag, gypsum then
Close the common grinding in back, make cement.Grinding is to specific surface area 310m in advance
2/ kg, levigate
Thin slag powders specific surface area 202m
2/ kg prepares burden, mixes according to following table, makes water
Mud, the pressure steaming stability that records cement is all qualified, and time of coagulation is normal, meets country
Standard, strength of cement such as following table:
Claims (5)
1. highly active fine steelslag powder mixing material of cement is characterized in that:
Described fine steelslag powder adopts levigate in advance and sorting obtains specific surface area 〉=300m
2Greater than 65% (weight), 7 days activity index 〉=75%, 28 day activity index 〉=80%, degree of mobilization is than 〉=100% less than the granule content of 40 μ m for/kg, particle diameter, density=2.80-3.30g/cm
3, metal Ferrum content≤0.8% (weight), free CaO≤3% (weight).
2. method of utilizing the described mixing material of claim 1 to produce cement of high index is characterized in that:
When the preparation strength label is 525 cement, mix levigate high reactivity steel-making slag powder that accounts for gross weight 10-35% and other industrial residue that accounts for gross weight 0-30%, as mixing material; When the preparation strength label is 425 cement, mix levigate high reactivity steel-making slag powder that accounts for gross weight 30-50% and other industrial residue that accounts for gross weight 0-35%, as mixing material; Wherein other industrial residue comprises in the Cement industry slag, flyash, volcanic ash, slag, zeolite, coal gangue, phosphorus slag commonly used, and the levigate mixing of other component of fine steelslag powder and cement is got final product.
3. method according to claim 2 is characterized in that:
Except that steel-making slag powder, other each component of cement is also distinguished grinding in advance to specific surface area 300m
2More than/the kg, and then, make cement with levigated steel-making slag powder mixed according to the rules is even.
4. method according to claim 2 is characterized in that:
Other each component of cement is distinguished grinding in advance to specific surface area 200m
2More than/the kg, and then with levigated steel-making slag powder mixed according to the rules is even, further grinding is in addition made cement simultaneously.
5. method according to claim 2 is characterized in that:
With the levigated steel-making slag powder with without levigated cement clinker and other each component in advance according to the rules ratio join simultaneously in the grinding machine, common grinding reaches total specific surface area 300m
2Make cement more than the/kg.