CN1276402A - Temp phase-transfer process of full-free dispersed rosin size - Google Patents
Temp phase-transfer process of full-free dispersed rosin size Download PDFInfo
- Publication number
- CN1276402A CN1276402A CN 00104424 CN00104424A CN1276402A CN 1276402 A CN1276402 A CN 1276402A CN 00104424 CN00104424 CN 00104424 CN 00104424 A CN00104424 A CN 00104424A CN 1276402 A CN1276402 A CN 1276402A
- Authority
- CN
- China
- Prior art keywords
- rosin
- rosin size
- water
- type
- full
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A temp phase-transfer process for preparing full-free dispersed rosin size includes adding the aqueous solution of emulsifier to molten mixed rosin while stirring, adding water until oil-water ratio is 1 : (0.8-1.2), stirring uniformly to obtain W/O type emulsion, and cooling to obtain O/W-type full-free dispersed rosin size. Its advantages are simple operation, smooth reaction, easy control, high producibility and stable quality. Obtained rosin size has solid content greater than 50%, rosin content up to 40% or more, pH value of 5-6, viscosity less than 25 CP and long quality guarantee period of 30 days at 54 deg.C.
Description
The present invention relates to the mutual dispersive technological process of a kind of profit, exactly is a kind of complete free dispersion rosin size temperature phase inversion novel process.
The saponification gum rosin is a sizing agent traditional in the paper industry.Still is using in domestic most of paper mills at present.This sizing agent consumption is big, and plain paper dry pulp per ton will consume 15-20 kilogram rosin, not only wastes resource, and the finished paper quality is low, also the fugitive sizing phenomenon can take place in summer.
Dispersion rosin size is as the upgraded product of saponification gum rosin, the U.S., Japan etc. as far back as twentyth century the seventies just begun research and development, just replaced the saponification gum rosin to the eighties comprehensively.Up-to-date research direction remains from molecular structure carries out modification to rosin, makes the anionic dispersion rosin size.Domestic each related research units also begins rosin sizing agent is researched and developed from the seventies, successively develops fortified rosin rubber powder and sizepine P.This sizing agent greatly reduces rosiny consumption, but is inconvenient to be difficult to promote because of using.Researched and developed dispersion rosin size again in succession to late nineteen eighties, but its emulsifying stability, especially also unsatisfactory, promoted the use of and be restricted in summer.
Dispersion rosin size its essence is a kind of stable dispersion system, and promptly rosin is evenly dispersed in the emulsion of the oil-in-water-type (O/W) in the water.Yet the initial stage system but is water-in-oil-type (W/O) in preparation process.This just requires should solve dispersed uniform in technological process, realizes again by the mutually transformation of w/o type to the O/W type, but also will guarantee the stability of system (product) behind the phase inversion.Dispersed general modified rosin (rosin improves the rosiny acid number with the addition of cis-butenedioic anhydride diene, strengthens wetting ability) and the emulsifying agent of using; Change mutually by the CONTROL PROCESS condition and realize, the phase inversion that has in the prior art with the change of system component, and the present invention utilizes the change of system temperature and phase inversion.
According to reported in literature, the technology of preparation dispersion rosin size has three kinds.The one, solvent method is dissolved in rosin in the organic solvent, then with rosin solution with the emulsifier aqueous solution mixing and emulsifying, last vacuum precipitation reclaims organic solvent, obtains the stable emulsion of solid content 35~40% simultaneously.This method of Japan waste river chemistry of forest product Co., Ltd..The 2nd, high temperature and high pressure method with fusion and be warmed up to 160~190 ℃ rosin and mix the back by the high pressure homogenisers forced emulsification with the emulsifier aqueous solution that is preheating to 80~90 ℃, is cooled to rapidly obtain the stable emulsion of solid content 30~40% below 38 ℃ then.U.S. Monsanto Company promptly uses this method.Solvent method need use and reclaim solvent, makes originally simple process complications, and pollution is arranged.The required high pressure homogenisers of high temperature and high pressure method costs an arm and a leg, facility investment is big, operation also has certain degree of difficulty, so having developed a kind of normal pressure, more domestic professional institutes add water anti-phase method, at first emulsifier aqueous solution is put into preparation w/o type emulsion in the mixed rosin (rosin and modified rosin) under the molten state, under high-speed stirring (1600 rev/mins) condition, add phase inversion water (hot water) then fast, variation by the system component realizes changing mutually, be that phase reversal of emulsion becomes the O/W type, last cooling rapidly obtains dispersion rosin size.This method technology is simple, operational safety, but require a high-speed mixing equipment, and adding water and want fast, cooling is wanted rapidly, and process is wayward, and unstable product quality, and precipitation appears in heat-storage sometimes, can not satisfy the needs of paper industry.
The objective of the invention is provides a kind of new phase transfer process for the preparation of dispersion rosin size, smooth operation not only, and control, and quality product easily improves comprehensively, especially has excellent heat-storage stability.
The present invention is under specific emulsifying agent existence condition, realizes system by the transformation of w/o type to the O/W type by variation of temperature, and guarantees the stability of system behind the phase inversion.Concrete technology is as follows: at first just mixed rosin intensification fusion, under agitation condition, drop into the emulsifier aqueous solution for preparing then and make the w/o type emulsion, continue to add water, water oil ratio in system is 1: 0.8~1.2, and holding temperature is between 100~120 ℃, and under this temperature, oil is still successive in the system, water is disperse phase, is the w/o type emulsion.After water injection and after stirring slowly lower the temperature, along with decrease of temperature, the rerum natura of rosin and water changes thereupon, thereby the realization system is by the transformation of w/o type to the O/W type.The temperature of phase inversion point is different with the difference of emulsifying agent, can be under 60~90 ℃ of differing tempss phase inversion.Emulsifying agent in the present invention, dispersiveness and the stability of being not only system are necessary, and are that system realizes that the temperature phase inversion is necessary.Selected emulsifying agent is
As N=16,18,20 the time, its code name is respectively SOP-16, SOP-18 and SOP-20.
This technology uses general chemical industry equipment just can satisfy processing requirement, and whole process of preparation is finished in a still, and technology is simple, smooth operation, control easily, favorable reproducibility, steady quality.Product appearance is the emulsion of milky white colour band blue streak, solid content 〉=50%, and wherein rosin content is up to more than 40%, and pH value is 5~6, viscosity≤25CP (25 ℃), 10 days (with storing 1 year equivalence naturally) no changes of heat-storage (54 ℃) still can use after one month.Because product Heat stability is good, so summer is normally applying glue still, improve paper strength, feel and water tolerance simultaneously, and can save the rosiny consumption, only 2~4 kilograms of plain paper dry pulp rosin per ton consumption, other auxiliary agents such as Tai-Ace S 150 etc. also reduce usage quantity in proportion significantly.
Embodiment:
1, gets 333g rosin and 111g modified rosin and drop in the beaker heat fused together; Get the 180gSOP-20 aqueous solution (active constituent content 30%) and stirring (60 rev/mins, drop in the fused mixed rosin down down together), continue to add water to system and reach 1100g, stir, and 100~120 ℃ of holding temperatures, be the w/o type emulsion at this temperature lower body.Close thermal source, just obtain the free full dispersion rosin size of O/W type when being cooled to 60 ℃ under stirring.Appearance milky white has blue streak.
2, get 333g rosin and 111g modified rosin and drop in the beaker heat fused together; Get the 200gSOP-18 aqueous solution (active constituent content 25%) and under agitation drop in the fused mixed rosin, continue to add water to 1000g, stir, and 100~120 ℃ of holding temperatures.Close thermal source, just obtain O/W type oyster white when under agitation being cooled to 75 ℃, the complete free dispersion rosin size of band blue streak.
3, get 333g rosin and the 111g modified rosin drops in the beaker together, heat fused is got the 220gSOP-16 aqueous solution (active constituent content 20%) and is under agitation dropped in the fused mixed rosin, continues to add water to system and reaches 900g, stir, and 100~120 ℃ of holding temperatures.Close thermal source, just obtain O/W type oyster white when under agitation being cooled to 90 ℃, the complete free dispersion rosin size of band blue streak.
Above process has been amplified 3000 times, at 3M
3Finish in the reactor.
Claims (1)
1, a kind of complete free dispersion rosin size temperature phase inversion novel process, under agitation condition, the emulsifier aqueous solution for preparing is dropped in the fused mixed rosin, continuing to add water to water oil ratio is 1: 0.8~1.2, when temperature system when slowly reducing to 60~90 ℃ for 100~120 ℃ changes oil-in-water-type into by water-in-oil-type, it is characterized in that: this changes mutually is at emulsifying agent
(N=16.18.20) existence realizes down.