CN1272520A - Normal temp. solidified conveying band joint chloroprene rubber adhesive - Google Patents
Normal temp. solidified conveying band joint chloroprene rubber adhesive Download PDFInfo
- Publication number
- CN1272520A CN1272520A CN 00109244 CN00109244A CN1272520A CN 1272520 A CN1272520 A CN 1272520A CN 00109244 CN00109244 CN 00109244 CN 00109244 A CN00109244 A CN 00109244A CN 1272520 A CN1272520 A CN 1272520A
- Authority
- CN
- China
- Prior art keywords
- component
- chloroprene rubber
- conveying band
- compound
- band joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invented adhesive contains the ingredients of chloroprene rubber, rosin resin, heat-resisting phenolic resin, antioxidant, MgO, water and solvent and possesses the characteristics of short solidifying time, high storage temp., long storage time, normal temp. and normal pressure adhesion, high adhesive strength, water-proofing, acid-resistance, alkali-resisting, antiageing, heat-resisting and flame-retardant, and can be extensively used for quick adhesion of various conveyer belting joints within 18 min. at normal temp..
Description
The present invention relates to a kind of novel neoprene adhesive, particularly relate to a kind of ambient cure conveying band joint chloroprene rubber adhesive and preparation method thereof.
The solvent-borne type neoprene adhesive is well-known a kind of rubber-type general purpose adhesive, be widely used in the shoe-making industry, but this neoprene adhesive quality instability is easily come unstuck, bond strength can not meet the demands, and does not particularly also have suitable adhesive at conveying band joint.That sells in the market is used for conveying band joint with import and homemade tackiness agent, as Beijing 401 tackiness agents, long 4-8 hour set times such as Shandong 303 tackiness agents, Shanghai 202 tackiness agents, long-lived 202 adhesive glues in Sichuan, storage temperature≤20 ℃, period of storage 6 months, came unstuck in the bonding back of joint in 3-6 month, 8Kg/cm need pressurize when joint is bonding
24 hours, 4 hours shearing resistance 9Kg/cm
2, stripping strength 4 hours was shortcomings such as 5.3Kg/cm, can't satisfy the growing needs in market.
The contriver through in researching and developing for many years and putting into practice at the above-mentioned shortcoming that exists, it is short to develop a kind of set time, storage temperature is high 40 ℃, storage period is long, normal temperature and pressure is bonding, the novel high temperature resistant flame resistant neoprene adhesive that bond strength is high.
The object of the invention provides 18 minutes universal conveying band joint chloroprene rubber adhesives of fast setting of a kind of novel normal temperature and preparation method thereof.
Another purpose of the present invention provides 18 minutes fast setting high temperature modifications of a kind of novel normal temperature conveying band joint chloroprene rubber adhesive and preparation method thereof.
A further object of the invention provides a kind of novel ambient cure nonflammable conveying band joint chloroprene rubber adhesive and preparation method thereof.
The universal conveying band joint chloroprene rubber adhesive of ambient cure of the present invention comprises following component:
The described component A of component A 80-90% (weight) comprises (weight part):
Chloroprene rubber 80-100
Gum Rosin 5-50
Anti-aging agent 0.5-3
Solvent 400-600 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
Ambient cure nonflammable conveying band joint chloroprene rubber adhesive of the present invention comprises following component: component A 80-90% (weight)
Described component A comprises (weight part):
Chloroprene rubber 80-100
Gum Rosin 15-30
Anti-aging agent 0.5-4
Para-tert-butyl phenolic resin 30-60
MgO 5-12
H
2O 0.5-2
Trieline 500-890 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
Ambient cure high temperature modification conveying band joint chloroprene rubber adhesive of the present invention comprises following each component: component A 80-90% (weight)
Described component A comprises (weight part)
Chloroprene rubber 80-100
Rosin modified phenolic resin 5-40
Anti-aging agent 0.5-4
Heat-resistant phenolic resins 25-100
MgO 3-10
H
2O 0.5-2
Potter's clay 3-10
White carbon black 2-10
Trieline or benzene 570-750 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
In the ambient cure conveying band joint chloroprene rubber adhesive of the present invention, described chloroprene rubber is the homopolymer and/or the multipolymer of chlorbutadiene.Described multipolymer is a 2-chloro-1,3-divinyl and copolymerisable monomer such as 1-chloroprene, 2, the multipolymer of 3-dichloroprene, vinyl substituted aromatic hydrocarbon such as vinylbenzene or alpha-methyl styrene, diolefine such as isoprene, acrylic monomer such as vinylformic acid, (methyl) acrylate such as methyl methacrylate etc., be preferably the multipolymer of chlorbutadiene and acrylic acid or the like.Chloroprene rubber homopolymer and multipolymer are preferably adhesion type, long-lived chemical plant, Sichuan for example, 204 of chemical plant, Qingdao, the A-90 that NEC chemical company produces, Bayer A.G produce 320, the adhesive purpose chloroprene rubbers such as AF that du pont company is produced.These chloroprene rubber homopolymer and multipolymer preferably mix use, can give high temperature adhesives.The chloroprene rubber consumption is 80-100 (weight part).
Described anti-aging agent is a chloroprene rubber; special adhesive purpose chloroprene rubber is with anti-aging agent for example N-phenyl alpha-naphthylamine (antioxidant A), N-Phenyl beta naphthylamine (antioxidant d), diphenyl-para-phenylene diamine, N-phenyl N ' (p-toluenesulfonyl-) Ursol D etc., and its consumption is 0.5-4 (weight part).
Described resol is rosin modified phenolic resin, para-tert-butyl phenolic resin, heat-resistant phenolic resins, all is the commercially available prod.
Described magnesium oxide is the special incinerating high reactivity MgO of common MgO or warp, is preferably through incinerating high reactivity MgO.During described magnesium oxide can play and the receptor acting of emitting HCI in the chloroprene rubber weathering process, can improve intensity simultaneously, play normal temperature crosslinked effect, its consumption is 3-12 (weight part).
Described solvent is ethyl acetate, butylacetate, benzene,toluene,xylene, gasoline, trieline, methylene dichloride etc., these solvents can use separately or two or more mixes use, be preferably two or more and mix use, ratio did not have particular requirement between mixing was used, and decided on kind.
In the ambient cure conveying band joint chloroprene rubber adhesive of the present invention, described component B is an aromatics tetraisocyanate polymerisate.The polymerisate of described aromatics tetraisocyanate is to have the aromatics tetraisocyanate (20%) of following array structure, methylene dichloride is solvent (80%), in reactor, in nitrogen atmosphere, in 20-50 ℃, be preferably 30-40 ℃, stir polymerization after 2-4 hour sampling Detection NCO content 〉=7% finish to react polymerisate, directly as component B of the present invention.
R wherein
1And R
2Be independently selected from hydrogen, C
1-C
10Alkyl; R is C
1-C
10Alkylidene group, or the C of phenyl replacement
1-C
10Alkylidene group, preferred methylene radical, phenylmethylene, ethylene, phenyl ethylidene, 1,1-industry ethyl, 2,2-propylidene, propylene, trimethylene, butylidene and various isomer thereof.
Described aromatics tetraisocyanate object lesson is
2,2 '-dimethyl-3,3 ', 5,5 '-four isocyanos-ditan
2,2 '-dimethyl-3,3 ', 4,4 '-four isocyanos-ditan
2,2 '-dimethyl-3,3 ', 6,6 '-four isocyanos-ditan
2,2 '-dimethyl-3,3 ', 5,5 '-four isocyanos-diphenyl propane
2,2 '-dimethyl-3,3 ', 6,6 '-four isocyanos-diphenylethane
3,3 '-dimethyl-2,2 ', 4,4 '-four isocyanos-ditan
3,3 '-dimethyl-2,2 ', 6,6 '-four isocyanos-ditan
3,3 '-dimethyl-2,2 ', 6,6 '-four isocyanos-diphenyl propane
4,4 '-dimethyl-2,2 ', 6,6 '-four isocyanos-ditan
4,4 '-dimethyl-2,2 ', 6,6 '-four isocyanos-diphenyl propane
4,4 '-dimethyl-3,3 ', 5,5 '-four isocyanos-diphenylethane
4,4 '-dimethyl-3,3 ', 6,6 '-four isocyanos-ditan
5,5 '-dimethyl-2,2 ', 4,4 '-four isocyanos-ditan
5,5 '-dimethyl-2,2 ', 4,4 '-four isocyanos-diphenyl propane
5,5 '-dimethyl-4,4 ', 6,6 '-four isocyanos-ditan
3,3 '-dimethyl-triphenyl methane-4,4 ', 6,6 '-tetraisocyanate
Be preferably
2,2 '-dimethyl-3,3 ', 5,5 '-four isocyanos-ditan
2,2 '-dimethyl-3,3 ', 5,5 '-four isocyanos-diphenyl propane
3,3 '-dimethyl-4,4 ', 6,6 '-four isocyanos-ditan
3,3 '-dimethyl-2,2 ', 4,4 '-four isocyanos-ditan
3,3 '-dimethyl-triphenyl methane-4,4 ', 6,6 '-tetraisocyanate
More preferably
3,3 '-dimethyl-triphenyl methane-4,4 ', 6,6 '-tetraisocyanate
This solidifying agent and chloroprene rubber are used, have the chloroprene rubber curing speed fast, the binding property height, elasticity is big, vibration resistance is low temperature resistant, antifatigue, characteristics such as the storage at normal temperature time is long, its consumption is 10-20% (weight).
The preparation method of 20 minutes universal conveying band joint chloroprene rubber adhesives of fast setting of normal temperature of the present invention comprises following each step;
1, the preparation of component A,
Described in component A, comprise each component, press weight part in the prescription, in mixing stirred reactor,, mix and stirred 8-14 hour, get the compound of component A in 40-70 ℃;
2, in use, with above-mentioned compound and the component B one aromatics four isocyanide ester polyisocyanate polyaddition products that obtain component A, in ratio in the prescription, but mixing and stirring gets brushwork adhesive in mixing stirred reactor.
The preparation method of 20 minutes fast setting nonflammables of normal temperature of the present invention conveying band joint chloroprene rubber adhesive comprises the following steps:
The preparation of one component A:
1 with chloroprene rubber, Gum Rosin, anti-aging agent, part trieline, by weight part in the above-mentioned nonflammable prescription, in mixing stirred reactor,, mixed 8-12 hour in 40-60 ℃, compound.
2 with para-tert-butyl phenolic resin, MgO, water and all the other trieline partly, by weight part in the above-mentioned nonflammable prescription, in mixing stirred reactor, mixed 12-16 hour in 70-90 ℃, compound.
3 compounds that step 1 and 2 is obtained mixed 2 hours in mixing stirred reactor, component A mixed solution material.
Two in use, and with above-mentioned component A compound and the component B-aromatics four isocyanide ester polyisocyanate polyaddition products of making, wherein NCO 〉=7% in ratio in the above-mentioned prescription, but gets brushwork adhesive after mixing.
The preparation method of 20 minutes fast setting high temperature modifications of normal temperature of the present invention conveying band joint chloroprene rubber adhesive comprises the following steps:
The preparation of one component A:
1 with chloroprene rubber, rosin modified phenolic resin, anti-aging agent, potter's clay, white carbon black and part trieline or benzene, by weight part in the above-mentioned high temperature modification prescription, in mixing stirred reactor, in 60-90 ℃, mixed 10-16 hour, gets compound.
2 with heat-resistant phenolic resins, MgO, water and all the other partly trieline or benzene, by weight part in the above-mentioned high temperature modification prescription, in mixing stirred reactor, mixed 8-12 hour in 40-60 ℃, compound.
3 compounds that above-mentioned steps 1 and 2 is obtained mixed 2 hours in mixing stirred reactor, component A mixed solution material.
Two in use, and with above-mentioned component A compound and the component B one aromatics four isocyanide ester polyisocyanate polyaddition products of obtaining, wherein NCO 〉=7% in ratio in the above-mentioned high temperature modification prescription, but gets brushwork adhesive after mixing.
The characteristic and the characteristics of 20 minutes fast setting conveying band joint chloroprene rubber adhesives of normal temperature of the present invention are as follows:
Curing speed is fast, gets final product load operation in bonding 20 minutes.
Ambient cure (25-40 ℃), the pressurization that need not to heat, technology is simple.
Storage period long (36 months), storage temperature 0-40 ℃.
Difficult combustion is met naked light and is not burnt (560 ℃ of burning-points) convenient transportation.
Soaked 46 months in acidproof, alkaline-resisting, ageing-resistant, water-fast, the water, shearing resistance descends 1%, and stripping strength descends 2%.
Long service life is more than 3 years.
Heatproof can operation continuously under 90-150 ℃ of condition.
The intensity height, shearing resistance (Kg/cm
2) be 27-36, stripping strength is 17-19Kg/2.5cm.
Ambient cure conveying band joint chloroprene rubber adhesive of the present invention is widely used in the bonding of various conveying band joints, bonding such as the conveying band joint of ore deposit enterprises of factory such as ore deposit factory, power plant, cement mill, chemical plant, automobile factory.
The present invention further specifies the present invention with the following example, but protection domain of the present invention is not limited to embodiment.
The preparation example of component B aromatics tetraisocyanate polymerisate
With 3; 3 '-dimethyl-triphenyl methane-4; 4 ' 6; 6 '-tetraisocyanate 20% (Jiangling, Hubei insecticide factory produces and sells product), methylene dichloride is that solvent 80% drops in the reactor, under nitrogen protection; in 30-40 ℃; stir about 4 hours of polymerization, sampling Detection NCO content 〉=7% termination reaction gets polymerisate, directly as component B.
Embodiment 1
The universal conveyer belt joint chloroprene rubber adhesive of table 1 Formulation Implementation example 123 component A:%, (weight) 80-90 80-90 80-90 component A comprises following component, (weight portion): neoprene 80 90 100 abietic resins, 5 20 45 antioxidant ds or first 0.5 12 gasoline 180 222.75-ethyl acetate 100 123.75-benzene 120 148.5 600 component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition product %, (weight) 10-20 10-20 10-20
The preparation of one component A:
With chloroprene rubber, Gum Rosin, anti-aging agent, gasoline, vinyl acetic monomer, benzene, press embodiment 1 formulation weight part in the table 1, in mixing stirred reactor, under 40-70 ℃ of temperature, mix and stir the compound that got component A in 8-14 hour.
During two uses, with above-mentioned component A compound that obtains and component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition products, but get brushwork adhesive by 1 formula rate of example in the table 1 at mixing stirred reactor uniform mixing respectively, its shearing resistance is 23Kg/cm
2, stripping strength is 11Kg/2.5cm.
Embodiment 2
Embodiment 2 is identical with embodiment 1 preparation process, is not both the each component prescription shown in embodiment in the table 12, and the gained adhesive shear strength is 27Kg/cm
2, stripping strength is 15Kg/2.5cm.
Embodiment 3
Embodiment 3 is identical with embodiment 1 preparation process, is not both the each component formula rate shown in embodiment in the table 13, and the gained adhesive shear strength is 25Kg/cm
2, stripping strength is 18Kg/2.5cm.
Embodiment 4
Table 2 is nonflammable conveyer belt joint chloroprene rubber adhesive Formulation Implementation example 456 component A:%, (weight) 80-90 80-90 80-90 component A comprises following component, (weight portion): neoprene 80 90 100 abietic resins, 16 20 45 antioxidant ds or first 123 trichloro-ethylenes 440 540 650 para-tert-butyl phenolic resins 40 50 60 MgO 6 10 12 water 0.6 1.2 2 trichloro-ethylenes 100 120 180 component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition product %, (weight) 10-20 10-20 10-20
The preparation of one component A:
1 with chloroprene rubber (80 weight part), Gum Rosin (16 weight part), antioxidant d or first (1 weight part), trieline (440 weight part), in mixing stirred reactor, under 40-60 ℃ of temperature, mixes 8-12 hour, gets compound.
2 with para-tert-butyl phenolic resin (40 weight part), MgO (6 weight part), water (0.6 weight part), trieline (100 weight part), in mixing stirred reactor, under 70-90 ℃ of temperature, mixes 12-16 hour, gets compound.
3 compounds that above-mentioned steps 1 and 2 is obtained, uniform mixing is 2 hours in mixing stirred reactor, component A mixed solution material.
Two with above-mentioned component A compound and the component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition products of obtaining, and press embodiment 4 formula rates in the table 2, and uniform mixing gets the products with adhesive agent that can brush in mixing agitator.The shearing resistance of gained tackiness agent is 25Kg/cm
2, stripping strength is 13Kg/2.5cm.
Embodiment 5
Embodiment 5 is identical with embodiment 4 preparation processes, and it is listed not to be both in each component recipe ratio such as the table 2 embodiment 5, and the gained adhesive shear strength is 29Kg/cm
2, stripping strength is 16Kg/2.5cm.
Embodiment 6
Embodiment 6 is identical with embodiment 4 preparation processes, and it is listed not to be both in each component recipe ratio such as the table 2 embodiment 6, and the gained adhesive shear strength is 27Kg/cm
2, stripping strength is 19Kg/2.5cm.
Embodiment 7
Table 3 is high temperature modification conveying band joint chloroprene rubber adhesive formulation Example 789 component A:1% (weight) 80-90 80-90 80-90
Component A comprises following component (weight part)
Chloroprene rubber 90 95 100
210 rosin modified phenolic resins 5 10 15
Antioxidant d or first 0.5 12
Potter's clay 57 10
White carbon black 358
Trieline or benzene 495 570 600
Heat-resistant phenolic resins 30 60 90
MgO 5 6 8
Water 0.5 12
Trieline or benzene 60 80 100
Component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition product % (weight) 10-20 10-20 10-20
The preparation of one component A:
1 with chloroprene rubber (90 weight part), rosin modified phenolic resin (5 weight part), antioxidant d (0.5 weight part), potter's clay (5 weight part), white carbon black (3 weight part), trieline or benzene (495 weight part), in mixing stirred reactor, in 60-90 ℃, mixed 10-16 hour, and got compound.
2 with heat-resistant phenolic resins (30 weight part), MgO (5 weight part), water (0.5 weight part) trieline or benzene (60 weight part), in mixing stirred reactor, mixed 8-12 hour in 40-60 ℃, compound.
3 compounds that above-mentioned steps 1 and 2 is obtained, uniform mixing is 2 hours in mixing stirred reactor, component A compound.
Two in use, with above-mentioned component A compound and the component B one preparation example aromatics four isocyanide ester polyisocyanate polyaddition products of obtaining, presses embodiment 7 formula rates in the table 3, and uniform mixing obtains the high-temperature-resistant adhesive that can brush in mixing stirred reactor.This adhesive shear strength is 27Kg/cm
2, stripping strength is 15Kg/2.5cm, 150 ℃ of heatproofs.
Embodiment 8
Embodiment 8 is identical with embodiment 7 preparation processes, and it is listed not to be both in each component recipe ratio such as the table 3 embodiment 8, and the gained adhesive shear strength is 31Kg/cm
2, stripping strength is 19Kg/2.5cm, 150 ℃ of heatproofs.
Embodiment 9
Embodiment 9 is identical with embodiment 7 preparation processes, and it is listed not to be both in each component recipe ratio such as the table 2 embodiment 9, and the gained adhesive shear strength is 29Kg/cm
2, stripping strength is 17Kg/2.5cm, 150 ℃ of heatproofs.
Claims (11)
1, a kind of universal conveying band joint chloroprene rubber adhesive comprises following each component: component A 80-90% (weight)
Described component A comprises (weight part):
Chloroprene rubber 80-100
Gum Rosin 5-50
Anti-aging agent 0.3-3
Solvent 400-600 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
2, a kind of nonflammable conveying band joint chloroprene rubber adhesive comprises following each component: component A 80-90% (weight)
Described component A comprises (weight part):
Chloroprene rubber 80-100
Gum Rosin 15-30
Anti-aging agent 0.5-4
Para-tert-butyl phenolic resin 30-60
MgO 5-12
H
2O 0.5-2
Trieline 500-890 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
3, a kind of high temperature modification conveying band joint chloroprene rubber adhesive comprises following each component: component A 80-90% (weight)
Described component A comprises (weight part):
Chloroprene rubber 80-100
Rosin modified phenolic resin 5-40
Anti-aging agent 0.5-4
Heat-resistant phenolic resins 25-100
MgO 3-10
H
2O 0.5-2
Potter's clay 3-10
White carbon black 2-10
Trieline or benzene 570-750 component B one aromatics four isocyanide ester polyisocyanate polyaddition products, NCO 〉=7% wherein, 20-10% (weight)
4, according to the conveying band joint chloroprene rubber adhesive of claim 1-3, wherein said component B aromatics tetraisocyanate polymerisate is 3,3 '-dimethyl-triphenyl methane-4,4 ', 6,6 '-polymerisate of tetraisocyanate, its NCO content 〉=7%.
5, according to the conveying band joint chloroprene rubber adhesive of claim 1-3, wherein chloroprene rubber is the homopolymer and the interpolymer of adhesion type chlorbutadiene.
6, according to the conveying band joint chloroprene rubber adhesive of claim 1-3, wherein said anti-aging agent is N-methyl-alpha-naphthylamine and N-methyl-beta-naphthylamine.
7, according to the conveying band joint chloroprene rubber adhesive of claim 1-3, wherein said MgO is incinerating high reactivity MgO.
8, a kind of preparation method of universal conveying band joint chloroprene rubber adhesive, this method comprises the following steps;
1) preparation of component A:
Earlier with chloroprene rubber, Gum Rosin, anti-aging agent, solvent by universal weight part in the prescription in mixing stirred reactor, under 40-70 ℃ of temperature, mix and stirred 8-14 hour, the compound of component A;
2) in use, with above-mentioned component A compound and the component B one aromatics four isocyanide ester polyisocyanate polyaddition products of obtaining, respectively in ratio in the above-mentioned universal prescription, in mixing stirred reactor, but mixing and stirring gets brushwork adhesive.
9, a kind of preparation method of nonflammable conveying band joint chloroprene rubber adhesive, this method comprises the following steps:
The preparation of one component A:
1) with chloroprene rubber, Gum Rosin, anti-aging agent, part trieline, by weight part in the above-mentioned nonflammable prescription, in mixing stirred reactor,, mixed 8-12 hour in 40-60 ℃, compound;
2) with para-tert-butyl phenolic resin, MgO, water and all the other partly trieline or benzene, by weight part in the above-mentioned nonflammable prescription, in mixing stirred reactor, mixed 12-16 hour in 70-90 ℃, compound;
3) compound that step 1 and 2 is obtained mixed 2 hours in mixing stirred reactor, got component A mixed solution material;
Two in use, with above-mentioned component A compound and the component B one aromatics four isocyanide ester polyisocyanate polyaddition products of making, in ratio in the above-mentioned nonflammable prescription, but gets brushwork adhesive after mixing.
10, a kind of preparation method of high temperature modification conveying band joint chloroprene rubber adhesive, this method comprises the following steps:
The preparation of one component A:
1) with chloroprene rubber, rosin modified phenolic resin, anti-aging agent, potter's clay, white carbon black and part trieline or benzene, by weight part in the above-mentioned high temperature modification prescription, in mixing stirred reactor,, mixed 10-16 hour in 60-90 ℃, get compound;
2) with heat-resistant phenolic resins, MgO, water and all the other partly trieline or benzene, by weight part in the above-mentioned high temperature modification prescription, in mixing stirred reactor, mixed 8-12 hour in 40-60 ℃, compound;
3) compound that step 1 and 2 is obtained mixed 2 hours in mixing stirred reactor, got component A mixed solution material;
Two in use, with above-mentioned component A compound and the component B one aromatics four isocyanide ester polyisocyanate polyaddition products of making, in ratio in the above-mentioned high temperature modification prescription, but gets brushwork adhesive after mixing.
11, according to Claim 8 preparation method-10, wherein said component B aromatics tetraisocyanate polymerisate is 3,3 '-dimethyl-triphenyl methane-4,4 ', 6,6 '-polymerisate of tetraisocyanate, its NCO content 〉=7%.