CN1269191A - Bathtub - Google Patents
Bathtub Download PDFInfo
- Publication number
- CN1269191A CN1269191A CN 99116417 CN99116417A CN1269191A CN 1269191 A CN1269191 A CN 1269191A CN 99116417 CN99116417 CN 99116417 CN 99116417 A CN99116417 A CN 99116417A CN 1269191 A CN1269191 A CN 1269191A
- Authority
- CN
- China
- Prior art keywords
- bathtub
- silver
- glaze
- far
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A bathtub includes bathtub body, and the composition of its glaze is (by weight portion) formed from 10 portions of base glaze and 1-3 portions of far infrared material and anti-bacterial material which are prepared according to the ratio of 10 : 1, in which the far infrared material is one or a combination of several kinds of Al2O3, BeO, Cr2O3, Fe2O3, NiO, CaO, MnO2, CuO, Co2O4 and Co2O3, and the anti-bacterial material is one or a combination of several kinds of gold, silver, copper, silver-contained zeolite, silver-contained calcium phosphate, titanium dioxide and silver phosphate.By adopting far infrared material and anti-bacterial material to make bathtub coating material and mounting several and magnetotherapeutic health-care effects.
Description
The present invention relates to a kind of commodity, relate to a kind of bathtub specifically.
Raising day by day along with people's living standard, the public requires more and more higher to the health care of family room, as all kinds of different types of bathtubs, people not only require it to wash Mu Gongneng, wish that also it has health and health-care effect, and mostly family's bathtub commonly used is to make improvements in structure at present, does not still have a kind of bathtub with antibiotic health-care function so far.
Purpose of the present invention just is to provide a kind of Mu Gongneng that washes that can not only keep original bathtub, also has the bathtub of certain health and health magnetotherapy effect simultaneously.
Purpose of the present invention can realize by following measure:
The present invention includes the bathtub body, the composition of the used glaze of bathtub and proportioning are: 10 parts of basic glaze, and far-infrared material and anti-biotic material are prepared 1 part to 3 parts in 10: 1 ratio; Wherein far-infrared material is AL
2O
3, BeO, Cr
2O
3, Fe
2O
3, NiO, CaO, MnO
2, CuO, Co
2O
4, Co
2O
3In one or more combinations; Anti-biotic material is gold, silver, copper, cultivation silver zeolite, plant one or more combinations in silver-colored calcium phosphate, titanium dioxide, the silver orthophosphate.
Composition and the proportioning of the used glaze of bathtub of the present invention are: 10 parts of basic glaze, and far-infrared material and anti-biotic material are prepared 1 part to 3 parts in 10: 1 ratio; Wherein the composition of far-infrared material and each composition degree are: AL
2O
365%-78%, SiO
27%-20%, MgO 3%-4%, Fe
2O
35%-6%, TiO
23%-6%, CaO 3%-5%; Anti-biotic material adopts Ag
3Po
4The present invention is at the described magnetic patch that is mounted with on bathtub, and concrete riding position should design as required, on the outer wall that can be installed in cylinder body.
Because the present invention adopts far-infrared material and anti-biotic material to make bath paint, and at bathtub a plurality of magnetic patch is installed, and makes it to have stronger antibacterial action and magnetic therapeutic health function, has satisfied people's demand.
The present invention is described in further detail below in conjunction with embodiment:
The composition of embodiment 1, the used glaze of this bathtub and proportioning are: 10 parts of basic glaze, and far-infrared material and anti-biotic material are prepared 2 parts in 10: 1 ratio; Wherein composition and each the composition degree selected of far-infrared material is: AL
2O
365%-78%, SiO
27%-20%, MgO 3%-4%, Fe
2O
35%-6%, TiO
23%-6%, CaO 3%-5%; Anti-biotic material adopts Ag
3Po
4During manufacturing, earlier with sheet metal by punching press, bending, fry in shallow oil cut, operation such as degreasing is processed into bathtub embryo spare; Ground-coat enamel adopts conventional formulation to make compound, adds the water that accounts for compound weight 40% again and puts into ball grinder and grind, and crosses 180 mesh sieves control screen over-size at last and is no more than 1.5% and makes the ground-coat enamel glaze slip, sprays the ground-coat enamel drying then and is fired into; Cover-coat enamel is to add the anti-biotic material of said ratio and far-infrared material and mixed by 10: 1.5 on the basis of conventional formulation, adding the water that accounts for compound weight 50% again carries out crossing 200 mesh sieves behind the ball milling, screen over-size is controlled at about 1.5% and makes the cover-coat enamel glaze slip, the metal fittings surface is put in this glair application of slip, should be coated with evenly, can carry out twice application of slip, also can be coated with and be coated with the pool in the pool first and be coated with basic glaze earlier at secondary, spray far ultrared paint and antibiotic paint when secondary is coated with the pool again, settle a plurality of magnetic patch at the correct position of cylinder body at last.
The composition of embodiment 2, the used glaze of this bathtub and proportioning are: 10 parts of basic glaze, and far-infrared material and anti-biotic material are prepared 2.5 parts in 10: 1 ratio; Wherein composition and each the composition degree selected of far-infrared material is: AL
2O
365%-78%, SiO
27%-20%, MgO 3%-4%, Fe
2O
35%-6%, TiO
23%-6%, CaO 3%-5%; Anti-biotic material adopts Ag
3Po
4During manufacturing, earlier with sheet metal by punching press, bending, fry in shallow oil cut, operation such as degreasing is processed into bathtub embryo spare; Ground-coat enamel adopts conventional formulation to make compound, adds the water that accounts for compound weight 40% again and puts into ball grinder and grind, and crosses 180 mesh sieves control screen over-size at last and is no more than 1.5% and makes the ground-coat enamel glaze slip, sprays the ground-coat enamel drying then and is fired into; Cover-coat enamel is to add the anti-biotic material of said ratio and far-infrared material and mixed by 10: 1.5 on the basis of conventional formulation, adding the water that accounts for compound weight 50% again carries out crossing 200 mesh sieves behind the ball milling, screen over-size is controlled at about 1.5% and makes the cover-coat enamel glaze slip, the metal fittings surface is put in this glair application of slip, should be coated with evenly, can carry out twice application of slip, also can be coated with and be coated with the pool in the pool first and be coated with basic glaze earlier at secondary, spray far ultrared paint and antibiotic paint when secondary is coated with the pool again, settle a plurality of magnetic patch at the correct position of cylinder body at last.
Claims (3)
1, a kind of bathtub, it comprises the bathtub body, it is characterized in that: the composition of the used glaze of bathtub and proportioning are: 10 parts of basic glaze, far-infrared material and anti-biotic material are prepared 1 part to 3 parts in 10: 1 ratio; Wherein far-infrared material is AL
2O
3, BeO, Cr
2O
3, Fe
2O
3, NiO, CaO, MnO
2, CuO, Co
2O
4, Co
2O
3In one or more combinations; Anti-biotic material is gold, silver, copper, cultivation silver zeolite, plant one or more combinations in silver-colored calcium phosphate, titanium dioxide, the silver orthophosphate.
2, bathtub according to claim 1 is characterized in that: the composition of the used glaze of bathtub and proportioning are: 10 parts of basic glaze, and far-infrared material and anti-biotic material are prepared 1 part to 3 parts in 10: 1 ratio; Wherein the composition of far-infrared material and each composition degree are: AL
2O
365%-78%, SiO
27%-20%, MgO3%-4%, Fe
2O
35%-6%, TiO
23%-6%, CaO 3%-5%; Anti-biotic material adopts Ag
3Po
4
3, bathtub according to claim 1 is characterized in that: be mounted with magnetic patch on bathtub.