CN1268411A - Vibration-reducing composite steel plate production process - Google Patents
Vibration-reducing composite steel plate production process Download PDFInfo
- Publication number
- CN1268411A CN1268411A CN 00115432 CN00115432A CN1268411A CN 1268411 A CN1268411 A CN 1268411A CN 00115432 CN00115432 CN 00115432 CN 00115432 A CN00115432 A CN 00115432A CN 1268411 A CN1268411 A CN 1268411A
- Authority
- CN
- China
- Prior art keywords
- steel plate
- resin
- shock
- composite roll
- production technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a production technology for vibration attenuation composite steel plate. A steel plate after coated with a layer of polymer damping resin, is sent into a heating furnace for heating the resin solvent is volatilized or resin main component is activated, and at the same time, another steel plate is preheated in heating furnace, then the two steel plates are hot-rolled together, the suprinposed composite steel plate is heat-solidified in a solidification furnace, after leaving the furnace, it is further recombined by cold-recombination rolling and is straightened on-line, and finally it undergoes forced cooling. Said teachnology not only causuit most polymer damping resin, but also possesses strong workability.
Description
The present invention relates to a kind of production technology of shock-resisted complex steel sheet.
In the prior art, the production technology that a kind of Japanese Ri Xin steel mill that has that the flat 1-188331 of disclosed day disclosure special permission communique A on July 27th, 1989 provides produces shock-resisted complex steel sheet, its main technique flow process is: adopt two roll coaters respectively at the inboard of two steel plates coating one deck liquid thermosetting (or thermoplasticity) macromolecule damping resin, two-layered steel plates is superimposed with a pair of composite roll at hot time after two heating furnaces bakings respectively, cool off then, carry out on-line straightening, finish the production overall process of shock-resisted complex steel sheet.In this technology, critical process---the curing of macromolecule damping resin is to finish in the short time before and after the coincidence process, does not have the insulation of curing measure.The most suitable production thermoplasticity of this technological process shock-resisted complex steel sheet, but difficulty is bigger when producing the thermosetting product, because curing characteristics according to thermosetting resin, in such production technology, macromolecule damping resin must be in the interstage of curing when going out to heat fire door, this just requires to have proposed the requirement of intimate harshness to the control of curing process: the resin solidification degree is higher, easily produces the splitting phenomenon between two layers of resin in the superimposed back of steel plate; If the resin state of cure is low excessively, then since superimposed back plate temperature sharply reduce, thereby the curing of terminated resin has ahead of time reduced the peel strength, anti-of final products and has cut intensity and damping characteristic.
The production technology that the steel mill of another kind of Japanese Nippon Steel that also has the flat 3-231850 of disclosure special permission communique A in disclosed day of on October 15th, 1991 to provide produces shock-resisted complex steel sheet, its technological process be only therein the inboard of a steel plate with roll coater coating one deck liquid thermosetting macromolecule damping resin, under cold conditions, directly carry out two steel plates superimposed with a pair of composite roll, steel plate after superimposed enters in the heating furnace and is cured, and finishes the production overall process of shock-resisted complex steel sheet after coming out of the stove.In this technological process, macromolecule damping resin is superimposed in two-layered steel plates under cold conditions, and then enters in the heating furnace and be heating and curing.This mode can guarantee that curing process finishes under high stability state, the peel strength and anti-the opening that help stablizing final products are cut intensity; Its shortcoming is that the inboard coating of a steel plate is therein gone up behind the resin directly and another steel plate has carried out superimposed.Adopt this technology distribution meeting that the macromolecule damping resin of centre is proposed excessive restriction, promptly can only adopt the damping resin of no-solvent type, other are all inapplicable as solvent type, water miscible damping resin, otherwise will cause the thorough cracking (being caused by the solvent effusion) of clad steel plate after curing.
In a word, more than the production technology of two kinds of shock-resisted complex steel sheets, wherein one to curing process control has proposed the requirement of intimate harshness, and another person has done extremely strict restriction to macromolecule damping resin, is unfavorable for the seriation of product.
The object of the present invention is to provide a kind of production technology of improved shock-resisted complex steel sheet, can be adapted to the macromolecule damping resin of most of type, as solvent-borne type, no-solvent type or water miscible macromolecule damping resin, the working range of broad is arranged again on technology controlling and process, have stronger operability.
For achieving the above object, the present invention adopts following technical proposals:
A kind of production technology of shock-resisted complex steel sheet, it is characterized in that by roll coater behind roller coat one deck macromolecule damping resin on the steel plate, enter the heating furnace heating, carry out resin solvent volatilization or the activation of resin host, simultaneously another steel plate is entered the heating furnace preheating; It is superimposed then two steel plates to be carried out roll-in by hot composite roll; Clad steel plate after superimposed enters curing oven and is heating and curing, and compound and on-line straightening is carried out by cold composite roll in the back of coming out of the stove again, at last through forcing cooling.
The build of above-mentioned roller coat macromolecule damping resin is 30～150 μ m.
The technological parameter of above-mentioned technology can adopt: furnace temperature of heating furnace is 100～380 ℃, and hot composite roll linear pressure is 200～80000N/m, and the curing oven furnace temperature is 200～500 ℃, and cold composite roll linear pressure is 200～80000N/m.
Above-mentioned cold composite roll can adopt 4～8 couples many to composite roll, and it is compound that wherein preceding 1～3 pair roller carries out the degree of depth, and later several pair rollers carry out on-line straightening to clad steel plate.
The present invention compared with prior art, have following conspicuous outstanding feature and remarkable advantage: 1. be applicable to various types of macromolecule damping resins: owing to behind roll coater, set up heating furnace, solvent part of solvent type resin and water-soluble resin is fully overflowed before superimposed, also can make thermoplastic resin before superimposed, carry out the appropriateness activation, thereby bring into play the adhesion strength of damping resin self to greatest extent.2. guaranteed the abundant curing of macromolecule damping resin: whether macromolecule damping resin solidification is abundant, the vibration and noise reducing characteristic and the adhesion strength of final products will directly be influenced, therefore this technology adopts hot composite roll to pressurize compound in two-layered steel plates and the compound back of resin bed, then enter heating in the sintering oven again, guaranteed the full cross-linked curing of resin.3. combining of compound and aligning: the steel plate after superimposed comes out from curing oven, and to carry out the degree of depth compound to preceding 1～3 pair the composite roll by many in the back, make product have higher and more stable peel strength and resist to open and cut intensity, and later severally can carry out on-line straightening to product to steel rider, guaranteed that final products have desirable plate shape.Adopt production technology of the present invention, with plated steel sheet, hot-dip galvanizing sheet steel, cold rolling phosphatization steel plate is base material, middle macromolecule damping resin can be a kind of in thermoplastic resin, thermosetting resin, no-solvent type resin, solvent type resin, the water-soluble resin (resin bed build 3～100 μ m), carry out the production of shock-resisted complex steel sheet, if Choice of Resin is suitable, can produce peel strength more than 50N/cm, damping characteristic value η 〉=0.2, template wave height is not more than the shock-resisted complex steel sheet of substrate.The material object analysis that the import shock-resisted complex steel sheet carries out is found that its damping characteristic value (η value) only is 0.15, can illustrate that the present invention is to stabilizing and increasing the advantage of vibration damping steel plate product quality.
Accompanying drawing is the process chart of a kind of shock-resisted complex steel sheet production technology of the present invention.
Provide embodiment below:
Embodiment one:
Referring to accompanying drawing, the production technology of this shock-resisted complex steel sheet is: by roll coater 9 behind roller coat one deck macromolecule damping resin on the steel plate 10, enter heating furnace 8 heating, carry out resin solvent volatilization and the activation of resin host, simultaneously another steel plate 1 is entered heating furnace 2 preheatings; It is superimposed then two steel plates 10,1 to be carried out roll-in by hot composite roll 3; Clad steel plate 4 after superimposed enters curing oven 7 and is heating and curing, and carries out compound and on-line straightening by the cold composite roll 5 of four pair rollers again after coming out of the stove again, and forces cooling through cooling device 6 at last.The main material of present embodiment and technological parameter are: substrate is the thick electrogalvanizing phosphatization of a 0.6mm steel plate; Macromolecule damping resin is phenolic resinoid+rubber, and solid content is 25wt%; The resin dry film thickness is 50 μ m; Roll coating model is coated with for contrary; Heating furnace 2 furnace temperature are 200 ℃, and heating furnace 8 furnace temperature are 200 ℃, and curing oven 7 furnace temperature are 350 ℃.The product main performance index of producing: peel strength value is 50N/cm, and anti-is cut intensity level is 10MPa, and internal loss factor peak value is 0.20.
Embodiment two:
The technological process of present embodiment is same as the previously described embodiments.And main material and technological parameter are: substrate is the thick electrogalvanizing phosphatization of a 0.6mm steel plate; Macromolecule damping resin is phenolic resinoid+rubber, and solid content is 25wt%; The resin dry film thickness is 50 μ m; Roll coating model is coated with for contrary; Heating furnace 2 furnace temperature are 100 ℃, and heating furnace 8 furnace temperature are 100 ℃, and curing oven 7 furnace temperature are 250 ℃, the product main performance index of producing: peel strength value is 20N/cm, and anti-is cut intensity level is 5MPa, and internal loss factor peak value is 0.15.
Embodiment three:
The technological process of present embodiment is also identical with embodiment one.And main material and technological parameter are: substrate is the thick electrogalvanizing phosphatization of a 0.6mm steel plate; Macromolecule damping resin is phenolic resinoid+rubber, and solid content is 25wt%; The resin dry film thickness is 50 μ m; Roll coating model is coated with for contrary; Heating furnace 2 furnace temperature are 200 ℃, and heating furnace 8 furnace temperature are 200 ℃, and curing oven 7 furnace temperature are 450 ℃.The product main performance index of producing: peel strength value is 80N/cm, and anti-is cut intensity level is 15MPa, and internal loss factor peak value is 0.3.
Claims (4)
1. the production technology of a shock-resisted complex steel sheet, it is characterized in that by roll coater (9) after a steel plate (10) is gone up roller coat one deck macromolecule damping resin, enter heating furnace (8) heating, carry out resin solvent volatilization or the activation of resin host, simultaneously another steel plate (1) is entered heating furnace (2) preheating, it is superimposed then two steel plates (10,1) to be carried out roll-in by hot composite roll (3); Clad steel plate after superimposed (4) enters curing oven (7) and is heating and curing, and carries out compound and on-line straightening by cold composite roll (5) again after coming out of the stove again, at last through forcing cooling.
2. the production technology of shock-resisted complex steel sheet according to claim 1, the build that it is characterized in that roller coat macromolecule damping resin is 30～150 μ m.
3. the production technology of shock-resisted complex steel sheet according to claim 1, it is characterized in that heating furnace (8,2) furnace temperature is 100～380 ℃, hot composite roll (3) linear pressure is 200～80000N/m, curing oven (7) furnace temperature is 200～500 ℃, and cold composite roll (5) linear pressure is 200～80000N/m.
4. the production technology of shock-resisted complex steel sheet according to claim 1 is characterized in that the many to composite roll of 4～8 pairs of cold composite roll (5) employings, and it is compound that wherein preceding 1～3 pair roller carries out the degree of depth, and later several pair rollers carry out on-line straightening to clad steel plate.