CN1267571C - Process for preparing tungsten-cobalt hard alloy - Google Patents
Process for preparing tungsten-cobalt hard alloy Download PDFInfo
- Publication number
- CN1267571C CN1267571C CN 200310120820 CN200310120820A CN1267571C CN 1267571 C CN1267571 C CN 1267571C CN 200310120820 CN200310120820 CN 200310120820 CN 200310120820 A CN200310120820 A CN 200310120820A CN 1267571 C CN1267571 C CN 1267571C
- Authority
- CN
- China
- Prior art keywords
- powder
- granularity
- alloy
- hard alloy
- fine particle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The present invention discloses a method for preparing tungsten-cobalt hard alloy, which comprises steps that WC powder and (6 to 8)wt% of Co powder are blended, milled in a wet mode, dried, mixed with a shaping agent to be granulated, pressed, and shaped, removes the shaping agent, are sintered, etc. During blending, the WC powder of coarse granules and fine granules is used, wherein the granularity of the coarse granule WC powder is from 20 to 30 mum, the granularity of the fine granule WC powder is from 1.2 to 1.8 mum, and the weight ratio of the coarse granule WC powder to the fine granule WC powder is 60:40 to 80:20. The method of the present invention can be used for effectively coordinating the abrasion resistance and the toughness of the hard alloy, improving the combination property of the alloy, and enlarging the application range of alloy for mines.
Description
One, technical field
The present invention relates to a kind of preparation method's of tungsten-cobalt hard alloy, particularly mining tungsten-cobalt hard alloy preparation method.
Two, background technology
At present, a series hard alloy of using in the rock drilling field is that cobalt contents is the middle coarse grain tungsten cobalt alloy of (6~8) wt%.The preparation method of such alloy generally comprise with WC powder and Co powder through batching, wet-milling, drying, mix binder granulation, press forming, take off steps such as forming agent, sintering, wherein the size range of WC powder is at (4~13) μ m, the Co content range is controlled at (6~8) wt%, the alloy of producing like this, its hardness value is for being generally (88.0~90.5) HRA, intensity level is generally (1800~2600) MPa, and notched bar impact strength is generally (3.0~4.0) J/cm
2The wear resistance of such alloy is fabulous, but toughness is lower, and therefore, the use range of this alloy is restricted, and generally is applicable to the rock stratum that the f=10 level is following.
Three, summary of the invention
The present invention aims to provide a kind of preparation method of tungsten cobalt alloy, coordinates its wear resistance and toughness effectively, improves the over-all properties of alloy, enlarges the range of application of mine alloy, and the alloy of super quality and competitive price is provided for the rock drilling field.
In order to reach this purpose, technical scheme of the present invention comprise Co powder with WC powder and (6~8) wt% through batching, wet-milling, drying, mix binder granulation, press forming, take off steps such as forming agent, sintering, select two kinds of particulate WC of thickness powder during batching for use, wherein the granularity of coarse particles WC powder is (20~30) μ m, the granularity of fine particle WC powder is (1.2~1.8) μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 60: 40~80: 20.
Owing to adopted the WC grain heterogeneous texture, alloy structure improves: the WC grain adjacent degree reduces, and Co is more evenly distributed mutually, and porosity reduces, and formation of crack significantly reduces.Make the wear resistance of this alloy and toughness all be better than the coarse grain alloy with cobalt, this hardness of alloy value is (88.0~90.0) HRA, and intensity level is (2000~2800) MPa, and notched bar impact strength is (3.5~4.5) J/cm
2Because this alloy has the high-wearing feature and the high toughness of low cobalt alloy simultaneously,, can be used for the following rock stratum of f=12 level so its range of application obtains expanding.
As a further improvement on the present invention, adopt thin cobalt powder (1.0~1.5) μ m than better with the performance of common cobalt powder (2~3) μ m, its tough performance improves 5~10%, and after adding the TaC of (0.3~0.6) wt%, its hardness (HRA) improves 0.2~0.3, and promptly its wear resistance also can be enhanced.
Four, embodiment
Embodiment 1: the Co powder of two kinds of WC powder of thickness and 8.0wt% is prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 24.0 μ m when batching, and the granularity of fine particle WC powder is 1.4 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 70: 30, and Co powder degree is 2.0 μ m.
Embodiment 2: the Co powder of two kinds of WC powder of thickness and 7.0wt% is prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 28.4 μ m when batching, and the granularity of fine particle WC powder is 1.2 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 70: 30, and Co powder degree is 1.0 μ m.
Embodiment 3: the Co powder of two kinds of WC powder of thickness and 6.0wt% is prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 20.0 μ m when batching, and the granularity of fine particle WC powder is 1.8 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 70: 30, and Co powder degree is 1.5 μ m.
Embodiment 4: the Co powder of two kinds of WC powder of thickness, 6.0wt% and the TaC of 0.3wt% are prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 30.0 μ m when batching, and the granularity of fine particle WC powder is 1.4 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 60: 40, and Co powder degree is 2.6 μ m.
Embodiment 5: the Co powder of two kinds of WC powder of thickness and 6.0wt% is prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 24.0 μ m when batching, and the granularity of fine particle WC powder is 1.4 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 80: 20, and Co powder degree is 3.0 μ m.
Embodiment 6: the Co powder of two kinds of WC powder of thickness, 8.0wt% and the TaC of 0.5wt% are prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 24.0 μ m when batching, and the granularity of fine particle WC powder is 1.4 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 70: 30, and Co powder degree is 3.0 μ m.
Embodiment 7: the Co powder of two kinds of WC powder of thickness, 7.0wt% and the TaC of 0.6wt% are prepared burden by certain requirement, wet-milling discharging after 20~23 hours, precipitate 5~8 hours, drying shake sieve, mix binder granulation, press forming, take off forming agent and 1450 ℃ the insulation 50 minutes steps such as sintering make Wimet.Wherein, the granularity of coarse particles WC powder is 24.0 μ m when batching, and the granularity of fine particle WC powder is 1.4 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 70: 30, and Co powder degree is 1.34 μ m.
Table 1 has been listed the granularity and the concrete proportioning of powder when embodiment 1 prepares burden in 7, table 2 provides hardness, intensity and the notched bar impact strength of the Wimet of the method preparation of adopting embodiment 1 to 7.
Table 1
Numbering | Co Wt% | WC Wt% | Wc grain size (μ m) | Co powder degree (μ m) | TaC Wt% | WC thickness ratio (weight ratio) | |
Slightly | Carefully | ||||||
1 | 8.0 | Surplus | 24.0 | 1.4 | 2.0 | 0 | 70∶30 |
2 | 7.0 | Surplus | 28.4 | 1.2 | 1.0 | 0 | 70∶30 |
3 | 6.0 | Surplus | 20 | 1.8 | 1.5 | 0 | 70∶30 |
4 | 6.0 | Surplus | 30 | 1.4 | 2.6 | 0.3 | 60∶40 |
5 | 6.0 | Surplus | 24.0 | 1.4 | 3.0 | 0 | 80∶20 |
6 | 8.0 | Surplus | 24.0 | 1.4 | 3.0 | 0.5 | 70∶30 |
7 | 7.0 | Surplus | 24.0 | 1.4 | 1.34 | 0.6 | 70∶30 |
Table 2
Claims (3)
1, a kind of preparation method of tungsten-cobalt hard alloy, comprise Co powder with WC powder and 6~8wt% through batching, wet-milling, drying, mix binder granulation, press forming, take off forming agent, sintering step, it is characterized in that: select two kinds of particulate WC of thickness powder during batching for use, wherein the granularity of coarse particles WC powder is 20~30 μ m, the granularity of fine particle WC powder is 1.2~1.8 μ m, and the weight ratio of coarse particles WC powder and fine particle WC powder is 60: 40~80: 20.
2, the preparation method of tungsten-cobalt hard alloy according to claim 1 is characterized in that: the Co powder of selecting 1.0~1.5 μ m during batching for use.
3, according to the preparation method of claim 1 or 2 described tungsten-cobalt hard alloys, it is characterized in that: the TaC that adds 0.3~0.6wt% during batching.