CN1263127A - Mildewproof rubber - Google Patents
Mildewproof rubber Download PDFInfo
- Publication number
- CN1263127A CN1263127A CN 00101490 CN00101490A CN1263127A CN 1263127 A CN1263127 A CN 1263127A CN 00101490 CN00101490 CN 00101490 CN 00101490 A CN00101490 A CN 00101490A CN 1263127 A CN1263127 A CN 1263127A
- Authority
- CN
- China
- Prior art keywords
- rubber
- antioxidant
- smoked sheet
- zinc oxide
- paraffin wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The rubber with excellent mechanical, physical properties and mildew resistance is characterized by that it is made up by using chloroprene rubber, smoked sheet No.1 rubber, zinc oxide, accelerant DM, accelerant TMTD, antioxidant D, high wear-resisting cabron black, octadecanoic acid, calcium carbonate, paraffin wax, pottery clay powder, salicylanilide and No.20 engine oil according to a reasonable formula, and adopting mixing process.
Description
The present invention relates to a kind of rubber, its machinery, physicals are good, the fungicidal properties excellence.
At present, under the environment for use higher to ageing-resistant, the mildew-resistant of rubber, anti-wet goods performance requriements, employed rubber often adopts chloroprene rubber as main raw material, but because electrical insulating property, rebound resilience, the less stable of chloroprene rubber, influences the use properties of rubber.
The objective of the invention is in order to solve the deficiencies in the prior art, it is good to propose a kind of mechanical and physical performance, the rubber of mildew-resistant, anti-wet goods excellent performance.
Mildewproof rubber adopts chloroprene rubber, smoked sheet 1# natural rubber as main raw material among the present invention, add other Synergist S-421 95s and mould inhibitor-Salicylanlide by rational prescription and make mildewproof rubber through technology such as mixing, its various composition weight percent proportionings are as follows:
Proportioning raw materials % (w/w)
Chloroprene rubber 28%
Smoked sheet 1# natural rubber 12%
Zinc oxide 3.2%
Altax 0.8%
TM monex TD 0.48%
Antioxidant D 0.8%
High wear-resistant carbon black 12%
Stearic acid 1.2%
Lime carbonate 12.52%
Paraffin wax 2%
Potter's clay powder 20%
Salicylanlide 5%
20# machine oil 2%.
Compare with existing technology, mildewproof rubber adopts chloroprene rubber, smoked sheet 1# natural rubber as main production raw material among the present invention, because of natural rubber has advantages such as extraordinary tensile strength, low temperature softness, springiness, electrical insulation capability is good, and chloroprene rubber has the characteristic of anti-burning, anti-atmospheric performance, oil resistant, mildew-resistant, Good Heat-resistance, therefore, mildewproof rubber among the present invention combines the advantage of chloroprene rubber and natural rubber, and its machinery, physical property are good, the fungicidal properties excellence.
Below in conjunction with drawings and Examples the present invention is elaborated:
Fig. 1 is production technology principle figure of the present invention.
At first prepare raw materials for production by following each composition weight percent proportioning:
Chloroprene rubber 28%
Smoked sheet 1# natural rubber 12%
Zinc oxide 3.2%
Altax 0.8%
TM monex TD 0.48%
Antioxidant D 0.8%
High wear-resistant carbon black 12%
Stearic acid 1.2%
Lime carbonate 12.52%
Paraffin wax 2%
Potter's clay powder 20%
Salicylanlide 5%
20# machine oil 2%.
Then, process by conventional production process flow process in the prior art as shown in fig. 1, products obtained therefrom is a mildewproof rubber.
Claims (1)
1, a kind of mildewproof rubber, it is characterized in that: be made up of chloroprene rubber, smoked sheet 1# rubber, zinc oxide, altax, TM monex TD, antioxidant D, high wear-resistant carbon black, stearic acid, lime carbonate, paraffin wax, potter's clay powder, Salicylanlide, 20# machine oil, each composition weight percent proportioning is as follows:
Chloroprene rubber 28%
Smoked sheet 1# natural rubber 12%
Zinc oxide 3.2%
Altax 0.8%
TM monex TD 0.48%
Antioxidant D 0.8%
High wear-resistant carbon black 12%
Stearic acid 1.2%
Lime carbonate 12.52%
Paraffin wax 2%
Potter's clay powder 20%
Salicylanlide 5%
20# machine oil 2%.