CN1255844A - Stabilized absorbent material and systems for personal care products having controlled placement of visco-elastic fluids - Google Patents

Abstract

There is provided a distribution material for personal care products which is a fabric which wicks artificial menses according to a horizontal wicking test a distance of about 1 inch in less than about 1.5 minutes. Materials meeting this performance criteria generally have a pore size distribution with a high percentage (usually more than 50 percent) of pore diameters between about 80 and 400 microns and a density below about 0.15 g/cc. There is also provided a personal care product system having a distribution/retention layer and a pad shaping layer wherein each layer has a stain length ratio of 0.5 or less and the distribution/retention layer has a saturation profile of 4 or less.

Description

Stable hygroscopic material and system that the goods next to the shin of viscoelastic fluid controlled location are used

The application requires the priority of the U.S. Provisional Application NO.60/046701 that submitted on May 14th, 1997 and the NO.60/070657 of NO.60/046480 and submission on March 27th, 1998.

Invention field

The present invention relates to be used for material structure and the absorbent structure or the system of goods next to the shin such as disposable sanitary napkin, diaper or incontinence protection.More particularly, the present invention relates to handle the complicated viscoid such as the moisture absorption system of menstrual fluid.

Background of invention

Absorbent product such as menopad or sanitary towel, diaper and incontinence protection are used for absorbing and protecting body fluid.Current product has weak point on these functions, cause to exceed sewing of tolerance level, pollution clothes.In addition, current product yet there are no can offer comprehensively other consumers with other attribute as dry, comfortable and reliability.Many meetings in this generic attribute are subjected to the influence of product liquid handling property.Although in this field, constantly improving, for example introduce have " fin " so that woman month prevents to sew through the part of the pad underwear around the wearer, still need reduce for feminine hygiene article and sew and improve comfortableness.

The commercially available menstruation of the overwhelming majority is lined with higher leakage rate.The current crash rate that has up to 30% of this class pad, about 20% crash rate then is quite common.The inefficacy of this respect it is believed that it is because the high viscosity of menstruation and on the output volume very big variability is arranged, thereby causes menopad due to the target area overload sews then.Menstruation distributes to such an extent that insufficient it is believed that is the key factor of target area overload.

Urine process field in goods next to the shin such as diaper, the distribution of urine are normally provided by the material with the narrow aperture of pore size distribution.This class material must in time shift out a large amount of low viscosity urine dirts the target area and be enough to make this target area can receive dirt next time.Urine motion can overcome significant hydrostatic and arrive diaper than distal part.On the contrary, feminine hygiene products then can run into less but the fluid dirt that viscosity is bigger of total amount and more be difficult to make it to flow.Must significantly be different from the mainly relevant product used for the used distributed material of feminine hygiene products with the urine processing.

The several examples that improve the urine processing see the U.S. Patent application 08/754414 and 08/755136 of common transfer, have wherein proposed improved hygroscopic material and system design.Although the physical process of liquid handling has some similarity for menstruation and urine, the service condition of the complicated character of menstruation and polytropy thereof and its goods then need have visibly different design when handling with urine for hygroscopic material and system.Sew the previous trial of feminine hygiene article and comprise United States Patent (USP) 5549589,5466232 and 5200248 for providing low, they have discussed the distributed architecture that is used for menstruation.But the excellent combination that neither one provides that the present invention provides in these lists of references does relevant attribute.

One of purpose of the present invention is the feminine hygiene article that provides such, and it has excellent distribution performance, can make menstruation shift out the target area and can provide comfort and dry sensation to have the leakage rate lower than traditional menopad simultaneously.

The improvement that another object of the present invention is to provide such feminine hygiene article, it makes it arc in fact and stands on material in the regional area by adopting the sort of menstrual fluid can the importing through being designed to adapt to the menstruation characteristic in this absorption system, sew and improve comfortableness and can reduce.Still a further object of the present invention is that the feminine hygiene article that provides such, the hole that it has can be used for effectively keeping the liquid of appropriate amount and do not hinder and absorb and distribute.

Summary of the invention

The objective of the invention is to realize that this material comprises, and stable can highly moistening fiber cloth being set to can provide capillary dimensions and the degree of wetting that is ideally suited for the wicking viscoelastic fluid by such distributed material.When being exposed to viscoelastic fluid and simulation substance, material demonstrates at wicking distance, wicking rate and the aspects such as Fluid Volume removed and has improved the fluid distribution performance like this.

The distributed material of goods next to the shin of the present invention is such fabrics, and it can absorb artificial menses according to horizontal wicking test is time of about 1 inch distance to be less than about 1.5 minutes.The general pore size distribution that has of material that satisfies this performance criteria is that pore diameter then is lower than about 0.15g/cc for very high percentage rate (the surpassing about 50% usually) density that accounts for of about 80-400 micron.

Such goods next to the shin system also is provided, and it has distribution/maintenance layer and mat forming layer, and wherein the stained length that has of each layer is than for being equal to or less than 0.5, and layer saturation distribution that is had of this distribution/maintenance simultaneously is equal to or less than 4.

The accompanying drawing summary

Fig. 1 is the curve chart of pore size distribution of the 0.05g/cc material of example 1, circulation 1;

Fig. 2 is the curve chart of pore size distribution of the 0.05g/cc material of example 1, circulation 2;

Fig. 3 is the curve chart of pore size distribution of the 0.1g/cc material of example 1, circulation 1;

Fig. 4 is the curve chart of pore size distribution of the 0.1g/cc material of example 1, circulation 2;

Fig. 5 is the curve chart of pore size distribution of the non-oriented 0.028g/cc material of example 2;

Fig. 6 is the curve chart of pore size distribution of the 0.68g/cc material of example 2;

Fig. 7 is the curve chart of pore size distribution of the 0.028g/cc material of example 2;

Fig. 8 shows bright multilamellar design;

Fig. 9 illustration cover material;

Figure 10 shows bright blot coat;

Figure 11 shows bright distribution/maintenance layer;

Figure 12 shows bright bottom or mat forming layer;

Figure 13 shows the bright two-layer design that is used for feminine hygiene article;

Figure 14 shows bright a kind of four layers of design;

Figure 15 be have top layer, as the second layer of distributions/maintenance layer and as the bar shaped curve chart of trilaminar two systems of mat forming layer.This bar shaped curve chart is that unit has shown liquid load with the gram;

Figure 16 shows the bright design that comprises the feminine hygiene products of sine wave pattern; And

Figure 17 shows the convex-concave pattern of the individual goods next to the shin that bright shell is patterned.

Definition

" disposable " comprises and uses rear discarding, and do not prepare to wash and re-use.

" front " and " afterwards " are the relation that is used to refer to respect to relevant clothing itself in this whole specification, rather than any position relationship of getting when the wearer locates with it of this clothing.

" hydrophily ", the surface of description fiber or fiber, it is liquid, aqueous wetting by what contact with fiber. The degree of wetting of material can be described with contact angle and the surface tension of relevant liquid and material again. The equipment and the technology that are applicable to measure the degree of wetting of special fiber material can be provided by the system of Cahn SFA-222 surface force analyzer systems or in fact equivalence. When with this systematic survey, contact angle is called " wettable " or " hydrophilic " less than 90 ° fiber, and contact angle is equal to or greater than 90 ° fiber and is called " non-wettable " or hydrophobic.

" inwardly " and " outwards ", refer to position relation with respect to moisture absorption clothing center, concrete promptly along laterally and/or vertically near or away from the vertical and horizontal center of moisture absorption clothing.

" layer " can have the double meaning of single part or a plurality of parts when using by odd number.

" liquid ", refer to mobile and can get its perfusion or the position at the material and/or the material of internal tank shape.

" fluid connection ", refer to liquid can from one deck to another the layer or within one deck from a position to another position.

" vertically " and " laterally ", has its usual meaning.The longitudinal axis be in goods when tiling and the plane of spreading out fully in, generally be parallel to the wearer who wears this goods and stand be divided in the plane of vertical plane of left halfbody and right halfbody.Transverse axis is in the plane that is approximately perpendicular to the longitudinal axis of goods.Shown goods are longer in the vertical.

" particle " relates to any geometric format, for example, but is not limited to spherolite, cylindricality fiber or yarn, smooth surface or matsurface, sheet, band, line, silk, or the like.

" spraying " and modification thereof comprise forced jet liquid, or as liquid stream form or for example eddy flow liquidus or atomized fine particle shape, by pore, nozzle etc., by applying air pressure or other gas pressures, gravity or centrifugal force.Spraying can be continuous or discontinuous.

Here used speech " supatex fabric or fabric " refers to such fabric, and the structure of wherein each fiber or yarn is interlacing but unlike the sort of discernible mode in the knit goods.Supatex fabric or fabric are formed by several different methods, and for example meltblown, spun-bond process and bonded carded become the net method.Basis weight of nonwoven fabrics is typically expressed as the gram number (gsm) of ounce number (osy) or every square metre of every square yard of material, and the diameter of used fiber is expressed as micron (note, when osy is transformed to gsm, osy be multiply by 33.91).

Here used speech " spun-bonded fibre " refers to such small diameter fibers, they are that many tiny normally circular capillary tube by spinneret is with fusion thermoplastic extruding filamentation, fast tube reducing forms then, for example can referring to following United States Patent (USP): Appel etc. 4340563, Dorschner etc. 3692618, Matsuki etc. 3802817, Kinney 3338992 and 3341394,3502763 and the Dobo etc. of Hartman 3542615.It on cohesion face generally is noncohesive that spun-bonded fibre is deposited at it.Spun-bonded fibre is always successive, and average diameter (according at least 10 samples) is in particular about 10-20 micron greater than 7 microns.The shape that this fiber had for example is same as described in the following United States Patent (USP): Hogle etc. 5277976, Hills 5466410, Largman etc. 5069970 and 5057368, they have described the fiber of unconventional shape.

Here used speech " meltblown fibers " is meant by many tiny spinneret orifice capillary tubies that are generally circle, the fusion thermoplastic is squeezed into fused silk or fiber, entering the high speed of convergence usually is during the hot silk gas (for example air) directly that reduces the melting heat plastics flows, make their tube reducings, can be reduced to the microfibre diameter.By on the high velocity air carrying meltblown fibers and the cohesion face of depositing to, form the meltblown fiber web of random distribution then.This method for example discloses in the United States Patent (USP) 3849241 of Butin etc.Meltblown fibers is a microfibre, and it can be continuous or discontinuous, and average diameter is generally less than 10 microns, is deposited on the cohesion face often to viscosity.

Here used speech " is shaped altogether " and refers to a kind of like this method, wherein is provided with one at least near skewed slot and melts and sprays the extrusion plate, adds other materials by above-mentioned skewed slot to fabric in shaping.This class other materials for example can be pulp, superabsorbent pellet, natural polymer (for example staple fibre or cotton fiber) and/or synthetic polymer (for example polypropylene or polyester) fiber, and this fiber can have fibre length.Altogether forming process is shown in the United States Patent (USP) 4100324 of the United States Patent (USP) 4818464 of Lau of common transfer and Anderson etc., and the fabric of being produced by forming process altogether generally is called common shaping material.

Here used speech " polymer " generally comprises but is not limited to homopolymer; Copolymer is as block, grafting, random and alternative copolymer; Trimer, or the like, and their mixture and remodeling.In addition, unless be added with special restriction in addition, " polymer " speech will comprise that the institute of molecule might geometric configuration.This configuration include but not limited to isotactic, a rule with atactic symmetries.

Here used speech " machine direction " or MD are meant the direction of production fabric at the length place of fabric; " crosscut machine direction " or CD refer to fabric wide to, promptly be generally perpendicular to the direction of MD.

Here used speech " one-component fiber " is meant the fiber that is only formed by one or more extruders with a kind of polymer.This does not also mean that eliminating in the fiber by a kind of polymer formation, for painted, antistatic behaviour, lubricated, hydrophilic etc. are added with minor amounts of additives.This additive for example is used for painted titanium dioxide, is generally less than 5% by weight, and more common about 2%.

Here used speech " conjugate fibre " is meant from different extruders and pushes a kind of fiber of respinning and form together behind at least two kinds of polymer formation fibers.Conjugate fibre is referred to as multicomponent fiber or bicomponent fibers sometimes.Above-mentioned polymer is normally differing from each other, but conjugate fibre then can be the one-component fiber.These polymer are positioned at zones different on the conjugate fibre cross section with being arranged to substantial constant and extend along the length of conjugate fibre continuously.This conjugate fibre for example can be constructed cutification/cored structure.Wherein a kind of polymer be another kind of polymer ring around, or also can be arrangement arranged side by side, pie formula structure or get " day starlike matrix " and arrange.Conjugate fibre has been described in the following United States Patent (USP): Kaneko etc. 5108820, Kraeger etc. 4795668, Marcher etc. 5540992 with the United States Patent (USP) 5336552 of Strack etc.Conjugate fibre also is described in the United States Patent (USP) 5382400 of Pike etc., and the breathing rate that can utilize two (or many) to plant polymer forms curling in fiber.Crimped fibre also can form with the method for machinery and Deutsche Bundespatent DT2513251A1.Concerning bicomponent fibers, the ratio of these polymer can be 75/25,50/50,25/75 or any other required ratio.Conjugate fibre also can have the shape described in for example following United States Patent (USP), Hogle etc. 5277976,5466410 and the Largman of Hills 5069970 and 5057368, this several patents has been described the fiber with unconventional shape.

Here used speech " bicomponent fibers " refers to by at least two kinds of polymer and extrudes as mixture from same extruder and the fiber that forms.Term " mixture " is defined as follows.Bicomponent fibers is not to make various polymeric components be arranged on more constant different zone on the cross section of fiber, various polymer neither be successive along the total length of fiber usually simultaneously, and normally form fibril or protofibre all random when beginning and finishing.Bicomponent fibers is considered as multicomponent fiber sometimes.The fiber of this GENERAL TYPE for example is discussed in the United States Patent (USP) 5108827 and 5294482 of Gessner.Two compositions and bicomponent fibers also are discussed in the textbook " polymeric blends and composition " of John A.Manson and LeslieH.Sperling, 1976 by Plenum Press, the branch of New York Plenum publishing company, IBSH 0-306-30831-2 publishes, PP273-277.

Above used speech " mixture " be meant two or more mixture of polymers, and the back is meant a subclass of mixture with the speech of using " cementing thing ", but wherein each component is immiscible can the coupling." miscibility " and " immiscibility " be defined into be meant on the mixture for the free energy of mixing have respectively on the occasion of with the situation of negative value.In addition, " couplingization " then is defined as the method for the interfacial property that changes the immiscible polymer mixture, forms the cementing thing.

" bonded carded fabric " refers to the fabric that is manufactured like this by short fiber, and these short fibers sent combing unit or carded unit, and ruptured and along machine direction alignment short fiber, to form the roughly cellulosic supatex fabric of machine direction orientation.This fibrid be generally the bag buy, place a scutcher, before fiber is delivered to the carded unit with fiber separation.In case behind the formation fabric, promptly use one or more known adhesive bonding methods bonding, a kind of adhesive bonding method of this respect is a powder-stuck, and wherein with the activation then to the whole fabric of the adhesive distribution of powdered, this normally adds heating fabric and binding agent by hot-air.The another kind of adhesive bonding method that is suitable for is that decorative pattern is bonding, wherein adopts the calender or the ultrasonic bonds equipment of heating that fiber is bonded together, and is normally bonding by partial bond pattern, certainly whenever necessary also can be bonding on whole surface.Another kind of being suitable for and known adhesive bonding method, particularly when adopting bicomponent staple fiber, it is that blowing air is bonding.

" air lay " is the technology that a kind of known can be used to forms the cellulosic non-woven layer.In air-laid process, with the fubril bundle of typical length about 6 to about 19mm separately and be embedded in air source, depositing to by vacuum source usually then on the screen that is shaped.Use such as hot-air or spraying binder these random sedimentary fibers are bonding mutually then.

" goods next to the shin " are meant medicated underpants, hygroscopicity underwear, the adult's incontinence articles that diaper, training are urinated, binder and feminien hygiene product etc.

Test method

The material thickness material thickness is to be the result of unit measurement under 0.05psi pressure with mm with Starret type bulk tester.

The density of density material is to remove the weight (gsm) of the per unit area of every square of Mick of sample with the bulk density (millimeter) of sample under 68.9Pa, then this result is taken advantage of 0.001 to be transformed to every cubic centimetre of gram (g/cc).Tackle this and calculate altogether the meansigma methods that three samples are got this density.

The sample material band that the wicking time of absorbent structure and horizontal liquid energy are flatly placed about 1 inch (2.5cm) * 8 inch (20cm) makes and just in time contacts liquid level when this sample band this sample band when on-test is arranged in liquid container.During test, relative humidity should remain about 90-98%.The sample band is placed in a large number near (actual endless) liquid, just starts stopwatch in case the edge of sample band contacts with liquid level.

Note the liquid weight that horizontal range that each liquid constantly advances to forward position sample band and sample band are absorbed.Also measure the liquid weight that this sample band was absorbed when about 1/2 inch (1.3cm), 1 inch, 2 inches (5cm) and 3 inches (7.6cm) from on-test according to this data.

Used liquid is to be designed to simulate the viscoelasticity of menstruation and the fluid of other character in this test, and is to make according to the method that provides in the following test procedure.

The flat system test method

Purpose:, measure the fluid mobility of each moisture absorption system by analyzing each component contamination length of this system, saturated capacity and fluid-load.

Equipment: the acrylic panel of hourglass shape (there is 0.25 inch hole at the center), about 330 grams of weighing; The Tygon pipe of syringe, 1/8 inch internal diameter; The pipette pump; Menses simulant; Test chamber balance (being accurate to 0.00 gram).

Prepare

1. parts being cut into required form (is generally 1.5 inches * 5.5 inches, is used for sucking and distribution layer, 1.75 inches * 5.5 inches, be used for the transfer lag layer; The hourglass shape that 200mm is long is used for peripheral tier).

2. 5.5 inches layer mark zones are divided into 1.1 inches sections, in the time of in being marked on the peripheral tier on the sample band is fixed, with this peripheral tier corresponding to above-mentioned labelling segmentation.

3. each parts of weighing write down its weight.

4. each parts are formed required component system, keep mark zone segmentation collimation, indicate that an end is as the top.

5. menses simulant fill syringe is attached to the Tygon pipe on the syringe simultaneously.

6. syringe is placed the pipette pump.

7. compile and edit program (syringe that generally adopts 30cc is by the menses simulant of distributing 10ml in 1 hour) to said pump.

8. the open end with aforementioned tube places beaker, start said pump and from pipe, discharge and pipe is ready to until all air, then menses simulant stained end from then on bank of tubes go out.

9. the component system that this is to be tested places near the pipette seat, places the 10d BCU of the 2 inches * 25gsm of 6 inches (approximations) at the top of this system centre, and acrylic panel is set in the top of this system is fixed again.

10. the free end with pipe inserts in the hole of acrylic panel.For all the other system's above-mentioned steps of testing.

11. starting pipette pump makes stained beginning.

12. when finish stained period, take off this pipe and acrylic panel.Carefully remove BCW (not mobile bottom) and discard it.

13. this component system and each layer are photographed, and print.

14. each layer weighed respectively, write down this weight.

15. from indicating this end as the top, its weight is write down in the first mark zone segmentation that cuts and weigh.All the other each sections and each layer are repeated described operation.

16. measure and write down the stained length of each layer.

17. relevant data imported is used for render image and analyzing in the expansion card.

The menses simulant that is used for this test is made according to following method.

Blood, usefulness is to take off fine Sanguis sus domestica here, through 30 minutes the centrifugalize of 3000rpm, also can adopt other effective methods or speed and time certainly.Buffy coat is removed in the separated and independent storage of blood plasma, and the while is the erythrocyte of storage density independently.

Egg, usefulness is huge egg here, the ligament at egg yolk and egg yolk two ends is then rejected and is kept albumen.Again this albumen is divided into thick white and thin albumen, method is that the nylon sieve aperture that makes albumen pass through 1000 microns filters about 3 minutes, and rarer part is removed.Note also can using other screen size, and when viscosity was needed degree at least, used time or method also can change.Remain in the albumen that dense thick part on the screen cloth is collected and the syringe of suction 60cc in, be put into then on the syringe pump able to programme, make it homogenize by its inclusions being carried out discharge and refill for 5 times.At this moment, this homogenize amount is subjected to the control of about 10ml/min syringe pump pumping rate, and about 0.12 inch of the internal diameter of pipe.After homogenize was handled, the viscosity of thick white was at 150sec ^-1Be at least 20c.p (centipoise), place centrifuge under 3000rpm, to rotate then about 10 minutes, remove residue and bubble, can adopt any effective method to remove residue and bubble at this.

After centrifugal treating, the albumen of homogenize that contains the ovum mucoitin is added to the Fenwal  transport box of 300cc with syringe.Blood plasma with the 60cc pig is added in this transport box then.Clamp this transport box, remove all bubbles, be placed in then in the stomacher lab mixer, mixed about 2 minutes by standard (or middle) speed.From then on take out this transport box in the blender again, add the erythrocyte of the pig of 60cc, mediate by hands and mixed this inclusions about 2 minutes, or even until the outward appearance of this inclusions.According to this example, for the artificial menses that makes, in the indicated final mixture of hematocrit, erythrocytic content should be about 30% weight, and generally is at least 28-32% weight.Protein content is 40% weight approximately.

The composition and the equipment that are used to prepare this artificial menses are easy to obtain.List the source of goods of related item below, can certainly utilize other sources of goods, as long as their equivalences basically.

Blood (pig): Cocalico Biologicals, Inc., 449 StevensRd., Reamstown, PA 175 67, (717) 336-1990.

Fenwal  conveying and packaging container, 300ml, Belt connector, trade mark 4R2014:BaxterHealthcare Corporation, Fenwal Division, Deerfield, IL 60015.

Harvard Apparatus syringe pump model able to programme 55-4143; HarvardApparatus, South Natick, MA 01760

Stomacher 400 test chamber mixing machine model BA 7021, series number 31968:SewardMedical, London England, UK.

1000 tm screen, item number .CMN-1000-B:Small Parts, Inc.PO BOX4650, Miami Lakes, FL 33014-0650,1-800-220-4242.

Hemata Stat-II device is measured blood cell, series number 1194Z03127; SpearationTechnology Inc., 1096 Rainer Drive, Altamont Springs, FL 32714.

The pore size distribution of pore size distribution material is according to " textile research magazine " (Textile Research Journal); In 356 pages of 37 volumes (1967), the used porous plate method of Burgeni and Kapur is that the equipment on basis is measured.Use the said equipment, it is related with the radius of the hole of giving material to make sample material separate the Fluid Volume of sucking-off under different pressure.This method is described in the Absorbency of Chattterjee, Elsevier SciencePubl shers, B.V.1985, pp36-40.

Used this improved system comprise one with by the stepper motor able to programme of personal computer control and the traveling table of electronic scale interface.The control sequence here makes this automatically move to desired height, collects data until reaching balance by specific sampling rate, moves to next computed altitude then.Adopt the supporting structure of the plexiglass of commodity Plexiglas  by name, the material porous plate is remained in the vertical position of a level in whole test.The pore-size scope that the controllable parameter of this method comprises sampling rate, balance index and measures., as test fluid the data of these test materials are collected with mineral oil (0.82g/cc, 32dyne-cm, 0 ° of fluid contact angle)., during on-test sample material is placed on the porous plate in each time, reduce perforated plate construction then, sample is soaked fully.Use the mass data mensuration pore-size that raises collected along with pressure (being the height of platform).If the variation behind 4 60 seconds intervals is less than 0.05g/min, just established balance.

Data are expressed as the relation of percentage of pore volume with respect to pore radius (micron), and pore-size indicates that on X-axis the increment of quality changes then to be indicated on Y-axis divided by total variable quantity of quality.

Describe in detail

The present invention is a class distributed material, it comprise stable can highly moistening fiber, be arranged in to provide and be fit to ideally the capillary dimensions of wicking viscoelastic fluid and degree of wetting.Stabilisation can any other known method realizes in liquid adhesive, binder fibre, heating or the present technique by adopting.When being exposed to viscoelastic fluid or this fluidic analogies, distributed material of the present invention has improved the fluid distribution performance in wicking distance, wicking rate and fluid amount of movement direction.The characteristic of hole is stable, no matter be drying or when moistening, when being the moistening of viscoelastic fluid analogies, has only the minimum swelling or the rate of collapsing, and less than about 25%, is 20% when better when desirable, is 15% when particularly desirable.All these character all are crucial for the overall performance of the distributed material in the target area that is arranged at goods next to the shin such as menopad.

Described material is at dried state and wet condition, is the thickness (inch) of menses simulant when saturated, by measurement result following show of compressometer under 0.02psi pressure and 2 inch diameter bases.

Heavy (gms) density (g/cc) percentage rate of the dried wet basis of pulp/binding agent thickness thickness collapses 100 0.06 90,/10 0.075 0.069 0.006

0.077??????0.065???0.012

0.078??????0.067???0.011

Average 0.077 0.067 0.010100 0.10 90,/10 0.059 0.054 0.005

0.062??????0.060???0.002

0.064??????0.056???0.008

Average 0.062 0.057 0.005200 0.08 90,/10 0.109 0.091 0.018

0.110??????0.098???0.012

0.103??????0.095???0.008

Average 0.107 0.095 0.013200 0.20 90,/10 0.046 0.052 0.006

0.050??????0.047???0.003

0.042??????0.044???-.002

Average 0.046 0.048-.002

The capilar bore gap structure that fluid distribution ability requires to match is in the particular range of relevant fluidic degree of wetting.Developed some distributed materials by several processes, they demonstrate to improving the required this basic material characteristic of performance.This examples of material is as follows.

Example 1

In this example, this distributed material comprises that (RayonierR-9401 mercerising southern softwood rolling pulp and about 20% weight Danaklon are short to cut (5mm) 2.2 danier polyethylene/polypropylene (PE/PP) skin/core conjugation binder fibres, has the S2/B2/39 finishing agent for fine hair (short fiber) slurry of about 80% weight.This finishing agent is claimed and can repeated stained back maintenance hydrophilic.Described material is produced under three kinds of different densities: 0.05g/cc, 0.1g/cc and 0.2g/cc, the about 100-250gsm of basic weight, and the example of material of showing the about 125gsm of basic weight that understands 0.05g/cc, 0.1g/cc and 0.2g/cc simultaneously is as a comparison.

These materials are tested according to horizontal wicking, have repeated three tests altogether with 1 inch * 8 inches samples.Table 1 shows understands relevant result, and wherein wt is to provide by the fluidic gram number that is kept, and unit of time is second, and DNR means and do not reach.

Used fluff pulp is available from Rayonier Inc.of Jessup, GA31545.Binder fibre is positioned at Engdraget 22 available from Danaklon a/s, KD-6800 Varde, and Denmark is 2.2 danier conjugation PE/PP skin/core fibres, is cut into 5mm length.

This distributed material is produced by the Dan-Web air-laid process.Any other satisfied method known to the expert personage all can be used to produce this material.To some sample testing pore volume distribution.The result is shown among Fig. 1,2 and 3 with the curve chart form, and these diagrams are understood the pore volume distribution of 0.05g/cc circulation 1, circulation 2 and 0.1g/cc circulation 2.The result shows that along with the reduction of density, pore-size increases, and has improved wicking properties significantly.

Circulation 1 circulation 2 circulations 3

(inch) weight (g) time (s) weight (g) time (s) weight (g) time (s) 0.05g/cc 0.5 1.26 50 1.15 50 1.13 54

1.0???1.80??161????1.77???170???????1.55????170

2.0???1.56??633????1.71???611???????1.48????714

3.0???1.02??DNR????0.89???DNR???????0.72????DNR0.1g/cc???0.5???0.86??20?????0.68???24????????0.76????18

1.0???1.14??155????1.07???123???????1.03????139

2.0???0.95??811????0.91???868???????0.9?????810

3.0???0.32??DNR????0.16???DNR???????0.23????DNR0.2g/cc???0.5???0.79??56?????0.83???43????????0.73????56

1.0???1.11??253????1.03???174???????0.98????245

2.0???0.62??DNR????0.96???1074??????0.76????DNR

0.21???DNR

Example 2

In this example, distributed material is the bonded carded fabric, and it comprises can be available from the eccentric sheath/core conjugate fibre of 100% weight of being made up of polyethylene and polypropylene of Japanese Chisso chemical company.Scribble the HR6 finishing agent on these fibers.The wicking result of 0.028g/cc sample, 0.068g/cc sample and 0.028g/cc sample that the clear wherein fiber of following expression has been orientated in carded technology.In the following table, parasang is that inch, unit of weight are that gram, unit of time are for dividing and second.Tested pore volume distribution, branch is shown among Fig. 4,5 and 6 as a result.These data show, when the voidage of high percent has when being of a size of about 400 microns of about 200-, can obtain wicking result preferably.

Density is apart from the weight time

0.028g/cc	1.0		?1.7	50 seconds
						2.0		?1.1	10 minutes
	3.0		?0.9	17 minutes
0.068g/cc	1.0		?0.6	1.5 divide
						2.0		?0.1	?DNR
					0.028g/cc	1.0		?1.7	1 minute
Orientation	2.0		?1.2	6.6 divide
						3.0		?0.9	18 minutes
	4.0		?0.1	The 20+ branch

Distributed material of the present invention should time of 1 inch (2.5cm) distance of wicking artificial menses fluid in the horizontal wicking test less than 1.5 minutes just at last successfully.The about 80-400 micron of pore diameter of the general pore size distribution high percentage that has of the material that satisfies this performance criteria (usually greater than 50%, more particularly greater than 60%, particularly especially greater than 70%) and density is lower than about 0.15g/cc.Can believe that the degree of wetting that improves pore surface can produce bigger wicking driving force, can keep the motion of liquid in smaller aperture with higher resistance like this.

Goods next to the shin of the present invention system in a concentrated area on the length of this goods menopad, can controlledly store final liquid through being designed to.This functional behavior is sewed special hope for the side that prevents the principal mode that menopad is sewed and is had.Such storage behavior is to be realized by the moisture absorption design that can comprise three layers or multiple structure.The bottom also promptly away from this one deck of wearer, is compared with other layers in the above and to be had bigger X-Y size.So just, formed the contour structures of protuberance, as shown in Figure 8, can improve menstruation and arrive probability on the narrow sanitary belt from the wearer.Multiple structure design shown in Figure 8 has the bottom 1, top layer or blot coat 3 and intermediate layer 2.

Aperture on each material layer is designed to and can combines with the geometry of each layer, and forms the filling design of special control in the moisture absorption system.The average pore size in the second layer or intermediate layer is less than the average pore size of top layer and bottom.So can think that fluid is attracted and distribution by the intermediate layer.The average pore size of bottom it is believed that this can stop FLUID TRANSPORTATION to bottom at the beginning of lifetime of product greater than the intermediate layer.Fluidic minimizing is sewed most crucially in the bottom for minimizing, and this is owing to it is believed that any fluid in this wideest layer all can begin to wick into edge and cause side to sew.In addition, each layer is stable, thereby the pore-size that helps to keep required in whole uses of goods concerns.Can also keep required micro perfection for the shape of menopad in addition.

In another embodiment, described bottom can be lobed or portion's section of densification, and vertical drawing lines for example is to cause fluid when the intermediate layer transfers to bottom under the high saturation, for example at contingent situation of product life later stage, the center that helps to keep flowing under the fluid bottom.

Top layer is also referred to as blot coat, and it is to have low density simultaneously near this layer of wearer to be about 0.02-0.06g/cc, and the about 125gsm of the about 25gsm-of basic weight.This makes that pore diameter is the 80-1000 micron, is applicable to well to suck viscid menstrual fluid.

This top layer or blot coat can be made with various technology.The example of nonexcludability comprises the bonded carded fabric of 100% weight synthetic fibers formation or the air lay mixture of cellulose fibre and synthetic adhesive usefulness fiber.

Layer under the top layer is designed to be used for distribute and keep fluid, so be referred to as distribution/maintenance layer or band.Its density range is for the about 0.2g/cc of about 0.1g/cc-but must be height than blot coat.Strengthening density in this wise it is believed that and help the blot coat desorbing made fluid to enter distribution/maintenance layer.The basic weight of this distribution/maintenance layer should be the about 300gsm of about 175-, the about 40-500 micron of average pore diameter.The material that is applicable to this layer comprises airlaid material, wherein mixing a large amount of cellulose fibre (80-95% weight) and synthetic fibers (5-20% weight), can make the fabric stabilityization that realizes this distribution function like this, but the fiber that requires to constitute this one deck is highly wettable.

The density of bottom or mat forming layer is lower than distribution/maintenance layer.Its major function is to promote and the cooperating of health.Make the wearer comfortable, set up cover layer simultaneously.Its density is the about 0.10g/cc of about 0.03g/cc-, makes to cause its not this distribution of desorbing immediately/maintenance layer keeping more fluid in this distribution/maintenance layer.In some design, this mat forming layer can be an airlaid fabric, and the synthetic adhesive fiber of the cellulose fluff pulp mixing of 80-90% weight with 10-20% weight wherein arranged.The main purpose of this one deck is to be used for mat forming, but particularly also can be from wherein receiving liquid when distribution/maintenance layer loads for liquid height.This mat forming layer also can comprise the decorative pattern of relief such as lines, sinusoidal wave form, Fructus Querci acutissimae shape etc.

Of the present invention is the feature of mat forming on the other hand, and wherein uppermost two-layer (blot coat and distribution/maintenance layer) can have vertically (long to) slit, is preferably in the center, can be crooked when bottom begins to be subjected to the sidepiece compression to allow their.So just can with the health close fit, equally also be to reduce the key measure sew.

Be mentioned to and have " layer " although be noted that the present invention, this does not also mean that and must produce independent material and they are laminated to together." layer " this speech also means and comprises single integral material, and all character wherein then can change and satisfies function of the present invention and physical characteristic.For example the characteristic of producing by a step process that material possessed can change from the top to the bottom zone and satisfies requirement of the present invention, and this feature will be spoken of in the appended claim book.The discussion of this material for example can referring to the application in the patent application of the common transfer that attorney docket 14002 times was submitted in same day.

For the product form of giving wide scope provides advantage on the function, the present invention can have various change forms.Fig. 9,10,11 and 12 illustrative modular constructions, purpose are to want the design form as thin as a wafer of type for user provides it.A kind of cover material that contacts with the wearer of Fig. 9 illustration, the about 80mm of its center width, the wide about 90mm of the widest part is about 238mm.Figure 10 shows the wide about 37mm of bright blot coat, long 218mm, and the slit at center is about 101mm.Distribution shown in Figure 11/maintenance layer has identical size with blot coat.Bottom shown in Figure 12 or its profile of mat forming layer are roughly the same with the cover layer, but the wide 60mm in center, the wide 70mm of the widest part.Bottom among Figure 12 has the drawing lines of 5 projectioies of unequal length, and they separate equidistantly from the center of pad.Figure 11,11 and 12 the bed of material also will be described in table 1 again.

Example given below is used to illustrate distribution character of the present invention.

Example 3

Go out supatex fabric by fluff pulp and synthetic adhesive with fiber production with air-laid process.Other fluff pulp comprises the cork of Coosa 054,100% weight, can be available from Kimberly-Clark company; Weyerhaeuser NB 416 or NF 405 100% weight corks, Rayonier 9401; Or any other has the fluff pulp of similarity.Synthetic adhesive then is Hoechst-Celanese T-255 (H-C T-255) with fiber, from 1.8 daniers to 3 daniers.Every energy all can adopt for this compound fabric with similar fusible any other binding agent.

Relevant basic weight and density are shown in table 1

Table 1 figure function is formed basic weight density 10 and is sucked air lay 90/10 100gsm 0.1g/cc

Fluff pulp/binder fibre 11 distribution air lays 90/10 200gsm 0.2g/cc

Keep fluff pulp/binder fibre 12 mat forming air lays 90/10 175gsm 0.1g/cc

Keep fluff pulp/binder fibre

Example 4

In the two-layer design here, as shown in figure 13, the density of top layer 4 is in the scope that can suck, distribute and keep menstrual fluid.Bottom or mat forming layer 5 have lower density, unless thereby top layer can the suppression fluid input when highly saturated itself.This design has kept the required thinness of some user.The character of illustrative each layer is as follows among Figure 13:

Function is formed basic weight density

Suction/distribution/maintenance air lay 90/10 250gsm 0.1g/cc

Mat forming/maintenance air lay 90/10 175gsm 0.05g/cc

Example 5

The another kind of modification of moisture absorption of the present invention system can also be liked the thick product of form for user provides it.Figure 14 shows this design of understanding four stratotypes, and wherein uppermost is blot coat 6, down be in turn to distribute to keep layer 7, transportation lag layer 8, and be mat forming layer 9 at last.

In this example and as shown in figure 14, blot coat 6 provides intake function, following one deck 7 then is the higher distribution of density/maintenance layer.The 3rd layer 8 density is lower than distributions/maintenances layer 7, thereby can postpone fluid and be sent to broad and thicker mat forming layer 9, and the while can also provide comfortableness and satisfy its thickness requirement for this series products form.Prevent that fluid from entering into this wideest layer and just can reduce and wick into the edge and cause the chance of sewing.Mat forming layer 9 can lobed decorative pattern, is used for preventing that liquid core suction is to the edge when the later stage in life-span of goods has liquid to pass through this transportation lag layer 8.

Though above these three examples help to illustrate the present invention, the present invention is not limited to this several examples.The absorbent product that the present invention includes can make liquid controlled navigating under the moisture absorption system centre, sews in order to prevent the edge.

Below test data shown this controlled filling pattern for a series of moisture absorption system example.In the following discussion, " top layer " refers to blot coat, and " intermediate layer " refers to distribution/maintenance layer, " bottom " thumb pad shaping layer.This test procedure relates to assembling moisture absorption system unit, presses the speed of 10ml/hr with the menses simulant 10ml that describes in detail in front test method one joint and comes stained these parts.

Two kinds of system designs under fluid load, have been tested.The result is shown among Figure 15 with image, and system 1 is in the left side, and system 2 is on the right side, and in Figure 15, first stick of each system is a top layer, and second stick is a distribution/maintenance layer, and the 3rd stick is the mat forming layer.The scale in left side is liquid load (gram).These two liquid load systems be by top detailed description and sketch under Coosa pulp and synthetic fibers make.In should pointing out that any is shown below, mention " hourglass " shape and promptly be meant the bottom of getting such shape, remaining layer then is a rectangle.

The explanation of fluid load system

Basic weight % pulp % binding agent density size

90％Coosa????????10％2.8dH-C

System I top layer 100gsm 0054 T-255 0.10g/cc 38mm * 152mm

90％Coosa????????10％2.8dH-C

Middle level 200gsm 0054 T-255 0.20g/cc 38mm * 152mm

hourglass-60mm?ctr，

90％Coosa????????10％2.8dH-C

70mm?lobes，218mm

Bottom 175gsm 0054 T-255 0.10g/cc long

90％Rayonier?????10％1.7d

System II top layer 125gsm 9401 Danaklon 0.10g/cc 38mm * 152mm

90％Rayonier?????10％1.7d

Middle level 250gsm 9401 Danaklon 0.20g/cc 38mm * 152mm

hourglass-60mm?ctr，

80％Rayonier?????20％1.7d????????????????????????70mm?lobes，218mm

Bottom 250gsm 9401 Danaklon 0.10g/cc long

Stick among Figure 15 is represented is the average data that the absorption of fluids from initial data partly obtains.The initial data of image is as follows among Figure 15: the fluid load data

The fluid that the dry weight weight in wet base absorbs

Bottom top layer middle level, top layer middle level bottom top layer middle level first floor system I 1 0.66 1.37 2.56 2.02 6.81 5.21 1.36 5.44 2.65

2?????0.63????1.34????2.37????2.00????6.98????4.73????1.37????5.64???2.36

3?????0.59????1.30????2.73????1.78????5.98????6.02????1.19????4.68???3.29

Average 0.63 1.34 2.55 1.93 6.59 5.32 1.31 5.25 2.77 II of system 1 0.64 1.55 3.19 2.45 5.82 7.02 1.81 4.27 3.83

2?????0.65????1.70????3.45????2.32????5.96????7.30????1.67????4.26???3.85

3?????0.64????1.61????3.26????1.99????6.41????6.77????1.35????4.80???3.51

4?????0.64????1.67????3.52????1.98????6.17????7.33????1.34????4.50???3.81

5?????0.72????1.58????3.33????2.32????6.17????6.64????1.60????4.59???3.31

6?????0.68????1.52????3.50????1.92????6.09????7.05????1.24????4.57???3.55

Average 0.66 1.61 3.38 2.16 6.10 7.02 1.50 4.50 3.64

Available a kind of stained size is recently described parts of the present invention and system.Stained size than be defined as when stained width (W) stained after reaching balance divided by stained length (1).The stained size ratio of mat forming layer and distribution/maintenance layer need be less than or equal to 0.5, is less than or equal to 0.375 and be less than or equal to 0.1875 particularly specifically more specifically.Tested the sample of mat forming layer with 8.7 inches long and 6 inches long distribution/maintenance layers, but should point out, the long or short goods with aforementioned ratio also are to belong in the scope of the present invention.Each layer of the system of being tested is described below, and being right after description then is relevant data afterwards.Notice that the I of this system is identical with aforementioned system I.Stained length system description

Basic weight % pulp % binding agent density size

90％Coosa???10％2.8dH-C

The I 100gsm of top layer system 0054 T-255 0.10g/cc 38mm * 152mm

90％Coosa???10％2.8dH-C

The middle level

200gsm????0054????????T-255??????????0.20g/cc??38mm×152mm

Hourglass shape-60mm ctr,

90%Coosa 10%2.8dH-C 70mm leaf lobe rate 218mm

Bottom

175gsm 0054 T-255 0.10g/cc is long

100％3.0d

The III of top layer system

25gsm?????????????????Chisso?ESC-????0.03g/cc??38mm×152mm

90％Coosa???10％2.8dH-C

The middle level

175gsm????0054????????T-255??????????0.20g/cc??38mm×152mm

Hourglass shape-60mm ctr,

90%Coosa 10%2.8dH-C 70mm leaf lobe rate 218mm

Bottom

Long stained length of 200gsm 0054 T-255 0.10g/cc and ratio data

The stained ratio of the stained width of stained length

Bottom top layer middle level, top layer middle level bottom top layer middle level first floor system I

1?????4.70???5.80???5.30???1.5????1.5????1.5???0.32????0.26????0.28

2?????4.70???5.80???5.70???1.5????1.5????1.5???0.32????0.26????0.26

3?????5.20???5.90???5.70???1.5????1.5????1.5???0.29????0.25????0.26

Average 4.87 5.83 5.57 1.5 1.5 1.5 0.31 0.26 0.27

The stained ratio of the stained width of stained length

Bottom top layer middle level, top layer middle level bottom top layer middle level first floor system III

1?????1.40???6.00???6.00???1.5????1.5????1.5???1.07????0.25????0.25

2?????1.40???6.00???6.00???1.5????1.5????1.5???1.07????0.25????0.25

3?????1.40???6.00???5.70???1.5????1.5????1.5???1.07????0.25????0.26

The stained width of average 1.40 6.00 5.90 1.5 1.5 1.5 1.07 0.25 0.25 all samples all is 1.5 inches

Remove stained length ratio, saturation distribution middle or distribution/maintenance layer also is important.So-called saturation distribution is meant the position of liquid when passing through the length of this layer.In order to determine this saturation distribution, can will be somebody's turn to do distribution/retainer belt, following each equal length part distributes:

Get (C+D) ratio simultaneously divided by (A+F).This be equivalent to approximately the amount of liquid (gram) of the center of this layer 1/3rd divided by this layer sixth each end amount of liquid (gram) and the result.If the distribution of being tested/maintenance layer is not the rectangle shown in here, then this layer should be divided into approximately equalised each section of dry weight.Saturated distribution ratio of the present invention must be about 4 at the most, is more preferably approximately less than 2, particularly is more preferably about 1.6 or littler, and preferably approximately less than 1.4 (with 6 parts time).Example and this result of the test of material therefor provide as follows in the test saturation distribution: the saturation distribution system specialization

Basic weight % pulp % binding agent density size

90％Coosa??????10％2.8dH-C

The I of top layer system

100gsm????0054???????????T-255??????0.10g/cc??38mm×152mm

90％Coosa??????10％2.8dH-C

The middle level

200gsm????0054???????????T-255??????0.20g/cc??38mm×152mm

Hourglass shape-60mm ctr,

Bottom

90%Coosa 10%2.8dH-C 70mm leaf lobe shape 218mm

175gsm 0054 T-255 0.10g/cc is long

90％Coosa??????10％2.8dH-C

The IV of top layer system

100gsm????0054???????????T-255??????0.10g/cc??38mm×152mm

90％Coosa??????10％2.8dH-C

The middle level

175gsm????0054???????????T-255??????0.20g/cc??38mm×152mm

Hourglass shape-60mm ctr,

90%Coosa 10%2.8dH-C 70mm leaf lobe shape 218mm

Bottom

200gsm 0054 T-255 0.10g/cc is long

94％Coosa??????6％2.8dH-CT-

The V of top layer system

100gsm????0054???????????255????????0.10g/cc??38mm×152mm

94％Coosa??????6％2.8dH-CT-

The middle level

200gsm????0054???????????255????????0.20g/cc??38mm×152mm

Hourglass shape-60mm ctr,

94%Coosa 6%2.8dH-CT-70mm leaf lobe shape 218mm

Bottom

The long middle level of 200gsm 0,054 255 0.10g/cc saturation distribution

The part than

A B C D E F (C+D)/(A+F) I of system

1?????2.24???4.30???4.34???4.30???4.17???3.47????1.51

2?????2.85???4.60???4.60???4.51???4.51???2.81????1.61

3?????1.40???4.03???4.54???4.58???4.35???1.17????3.55

Average 2.16 4.31 4.49 4.45 4.34 2.45 2.22

Than system IV

A??????B??????C??????D??????E??????F????(C+D)/(A+F)

1?????2.83???3.91???4.04???3.85???3.60???1.74????1.73

2?????2.61???4.25???4.39???4.39???4.32???2.88????1.60

3?????2.47???4.05???3.99???4.24???4.05???2.85????1.55

On average

2.64???4.07???4.14???4.16???3.99???2.49???1.62

Than system V

A??????B??????C??????D??????E??????F????(C+D)/(A+F)

1?????3.32???3.94???4.00???4.23???4.23???2.84???1.34

2?????3.20???3.77???3.91???4.06???4.15???2.87???1.31

3?????3.61???4.57???4.57???4.47???4.04???2.07???1.59

Average 3.38 4.01 4.19 4.27 4.14 2.63 1.41 structures of having tested thick product for saturation distribution, this structural information is as follows with the data of saturation ratio,

Basic weight % pulp % binding agent density size system I top layer 100gsm 90%Coosa 10%2.8dH-C T-255 0.08g/cc 38mm * 140mm

Middle level 200gsm 90%Coosa 0054 10%2.8dH-C T-255 0.1g/cc 38mm * 140mm

100gsm????90％Coosa?????????10％2.8dH-C??T-255?????0.06g/cc???52mm×154mm

Hourglass shape-60mm

Ctr, 70mm leaf lobe shape

The long saturation distribution data of bottom 470gsm 100%Coosa 0,054 0% 200mm

Ratio

A??????B??????C??????D??????E??????C/A??????C/E

1?????4.04????6.69???6.35???6.24????2.99????1.57????2.12

2 2.62 6.17 6.38 6.07 3.67 2.42 1.73 average 3.33 6.43 6.35 6.15 3.33 2.00 1.93

Top example 5 has been described the women with transportation lag function and has been used sanitary belt.In example 5, this transportation lag material has lower density than the layer below it, thereby can postpone liquid and be transported to bottom.Though the density of material is to have influence on fluid to postpone to be transported to one of reason in the lower layer, other material properties also can cause fluidic delay.Can cause alternative other materials of delay to comprise supatex fabric such as spunbond, fabric that conjugation is spunbond or bonded carded effectively.The porous coating materials also can be used for providing in the moisture absorption system this function.

When selecting non-woven fabric or coating materials as the transportation lag material, this class material is preferably non-wettable.Spunbond, conjugation is spunbond and the coating materials situation, below used structure slightly some " flat " in each example.In other words, the density of these structures is unnecessary low than its lower floor in the moisture absorption system design, and working of they is by being provided with the hydrophobic layer of part obturation, begins to carry liquid after layer height that can be in the above is saturated.

In the example that utilizes the bonded carded fabric,, can play the effect of transportation lag best when this fabric when being hydrophobic.But concerning this material, density and hydrophobicity all can work to postponing to carry.

Below each example comprise six thin moisture absorption systems and seven thick moisture absorption systems altogether, used all transportation lag materials among them.The data of result of the test show, by using this class material, can obtain saturation distribution ratio preferably, and in some situation, compare with the original design according to density/porosity gradient, can obtain stained preferably length ratio.

Though these test datas have utilized special material, other hydrophobic materials or hydrophobicity are combined with the density material lower than its material beneath again, also can provide the transportation lag function.

Another aspect of relevant these data is, the data before all are divided into six equal parts with this zonation, and this also is a method used in the appended claim book.Following data as described below, make stained point just in time not be on the demarcation line of two parts five moieties of this layer distribution.The saturation distribution ratio can be by two groups of data computation.In the situation that adopts five parts, this saturated distribution is as core amount of liquid recently calculating two end portions amount of liquid sum.

Saturation distribution with thin moisture absorption system of transportation lag layer

A

??B

??C

??D

??E

C/((A+E)/2)

Upper strata saturation distribution (g/g)

Part

Ratio

A B C D E C/ ((A+E)/2) system 11 5.58 5.85 5.68 6.15 5.51 1.024

2??????5.48???5.82???5.51???5.26???5.19????1.032

The average 2 A B C D E C/ ((A+E)/2) of 5.53 5.83 5.59 5.70 5.35 1.028 systems

1??????5.90???5.97???6.01???5.65???5.62????1.043

2??????5.04???5.36???5.56???5.23???5.07????1.099

The average 3 A B C D E C/ ((A+E)/2) of 5.47 5.67 5.78 5.44 5.35 1.071 systems

1??????5.51???5.88???5.68???5.58???5.58????1.024

2??????5.70???5.81???5.81???5.84???5.35????1.052

The average 4 A B C D E C/ ((A+E)/2) of 5.61 5.84 5.74 5.71 5.47 1.038 systems

1????4.99????6.41???5.74????5.88???5.42??1.103

2????5.57????6.03???5.68????5.96???5.47??1.028

The average 5 A B C D E C/ ((A+E)/2) of 5.28 6.22 5.71 5.92 5.44 1.066 systems

1????4.51????5.68???5.75????5.50???5.28??1.174

2????4.87????5.63???5.63????5.92???5.34??1.102

The average 6 A B C D E C/ ((A+E)/2) of 4.69 5.65 5.69 5.71 5.31 1.138 systems

1????5.88????6.06???6.38????5.91???5.81??0.874

2????5.78????6.37???6.04????6.15???6.30??1.000

Average 5.83 6.21 6.21 6.03 6.05 0.937 have the stained length of thin moisture absorption system of transportation lag layer than T=top layer M=middle level B=bottom

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 11 6.00 NA, 3.30 1.5 NA, 1.5 0.25 NA 0.45 of system

2????6.00???NA??2.00??1.5????NA??1.5??0.25??NA??0.75

Average 6.00 NA, 2.65 1.5 NA, 1.5 0.25 NA 0.60

Stained stained

Length width

Ratio

W/L

Layer T M B T M B T M B 11 6.00 NA, 2.60 1.5 NA, 1.5 0.25 NA 0.582 of system

2????6.00???NA??4.30??1.5???NA???1.5???0.25??NA???0.35

Average 6.00 NA, 3.45 1.5 NA, 1.5 0.25 NA 0.47

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 0.90 1.5 NA, 1.5 0.25 NA 1.673 of system

2??????6.00????NA????2.10????1.5????NA???1.5???0.25???NA????0.71

Average 6.00 NA, 1.50 1.5 NA, 1.5 0.25 NA 1.19

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 1.50 1.5 NA, 1.5 0.25 NA 1.004 of system

2??????6.00????NA????1.40????1.5????NA????1.5???0.25???NA???1.07

Average 6.00 NA, 1.45 1.5 NA, 1.5 0.25 NA 1.03

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 5.80 NA, 4.90 1.5 NA, 1.5 0.26 NA 0.315 of system

2???????6.00????NA????4.10????1.5????NA????1.5????0.25??NA???0.37

Average 5.90 NA, 4.50 1.5 NA, 1.5 0.25 NA 0.34

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 0.00 1.5 NA, 1.5 0.25 NA of system unlimited 6

2 6.00 NA, 0.00 1.5 NA, 1.5 0.25 NA are unlimited

Unlimited all the thin systems of average 6.00 NA, 0.00 1.5 NA, 1.5 0.25 NA comprise

Basic weight % pulp % binding agent density size

Wt top layer 250gsm 90% 10%2.8dH-CT-0.14g/c 38mm *

Weyerheauser?255??????????????c?????????140mm

The NB416 middle level referring to following explanation 52mm *

154mm

175gsm 88% 12%2.8dH-CT-0.08g/c hourglass shape-bottom

Weyerheauser??????255????????????c????????60mm?ctr，

NB 416 70mm leaf lobe shapes

The long transportation lag middle level that is used for said system of 200m

System 1:27gsm (0.8osy), 2.2 daniers are polypropylene spun-bonded

System 2:34gsm (1.0osy), 2.2 daniers are polypropylene spun-bonded

System 3:1.0osy, 2.0 danier polypropylene, polyethylene conjugate fibre arranged side by side

System 4:51gsm (1.5osy), 2.0 danier polypropylene, polyethylene conjugate fibre arranged side by side

System 5:1.0mil porous polyethylene membrane

System 6:50gsm bonded carded fabric has the saturation distribution of the thick moisture absorption system of transportation lag layer

A

?B

?C

?D

?E

C/((A+E)/2)

Top layer saturation distribution (g/g)

Part is than the 1 A B C D E C/ ((A+E)/2) of system

1????6.48????7.90???8.10????8.05????7.38??????1.16

2????6.43????7.81???8.24????8.00????4.76??????1.47

The average 2 A B C D E C/ ((A+E)/2) of 6.45 7.86 8.17 8.02 6.07 1.32 systems

1????7.24????7.90???8.24????8.05????7.52??????1.12

2????6.98????8.13???8.09????8.18????7.46??????1.12

The average 3 A B C D E C/ ((A+E)/2) of 7.11 8.02 8.16 8.12 7.49 1.12 systems

1????6.79????8.86???8.01????7.87????7.51??????1.12

2????7.99????8.66???8.71????8.71????8.28??????1.12

The average 4 A B C D E C/ ((A+E)/2) of 7.39 8.76 8.36 8.29 7.90 1.12 systems

1?????7.59???8.22???7.93???8.66????8.17?????1.00

2?????8.01???8.55???8.11???8.50????7.91?????1.02

The average 5 A B C D E C/ ((A+E)/2) of 7.80 8.39 8.02 8.58 8.04 1.01 systems

1?????0.31???6.62???7.04???6.43????3.44?????3.75

2?????0.12???5.29???7.35???7.04????2.26?????6.17

The average 6 A B C D E C/ ((A+E)/2) of 0.21 5.96 7.19 6.73 2.85 4.96 system

1?????5.31???5.35???5.22???5.03????5.57?????0.96

2?????4.82???5.27???5.01???5.11????5.27?????0.99

The average 7 A B C D E C/ ((A+E)/2) of 5.07 5.31 5.12 5.07 5.42 0.98 systems

1?????3.65???5.94???6.33???6.22????3.51?????1.77

2?????3.65???6.11???6.15???6.15????2.49?????2.00

Average 3.65 6.03 6.24 6.19 3.00 1.89 have the stained length ratio of the thick moisture absorption system of transportation lag layer

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 3.20 1.5 NA, 1.5 0.25 NA 0.471 of system

2??????5.60????NA????3.80????1.5????NA?????1.5????0.27????NA????0.39

Average 5.80 NA, 3.50 1.5 NA, 1.5 0.26 NA 0.43

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 1.50 1.5 NA, 1.5 0.25 NA 1.002 of system

2???????6.00????NA????2.50???1.5?????NA?????1.5????0.25????NA????0.60

Average 6.00 NA, 2.00 1.5 NA, 1.5 0.25 NA 0.80

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 0.50 1.5 NA, 1.5 0.25 NA 3.003 of system

2???????6.00????NA????1.50???1.5??????NA?????1.5???0.25????NA????1.00

Average 6.00 NA, 1.00 1.5 NA, 1.5 0.25 NA 2.00

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 6.00 NA, 1.50 1.5 NA, 1.5 0.25 NA 1.004 of system

2??????6.00????NA????1.00???1.5??????NA?????1.5????0.25???NA????1.50

Average 6.00 NA, 1.25 1.5 NA, 1.5 0.25 NA 1.25

Stained stained

The length width ratio

W/L

Layer T M B T M B T M B 1 5.30 NA, 4.20 1.5 NA, 1.5 0.28 NA 0.365 of system

2??????4.60?????NA????3.70???1.5??????NA????1.5?????0.33???NA???0.40

Average 4.95 NA, 3.95 1.5 NA, 1.5 0.31 NA 0.38

Stained stained

The length width ratio

Layer W/L

The 1 T M B T M B T M B of system

1???????6.00????NA???0.50???1.5?????NA????1.5???0.25???NA????3.006

2???????6.00????NA???0.70???1.5?????NA????1.5???0.25???NA????2.14

Average 6.00 NA, 0.60 1.5 NA, 1.5 0.25 NA 2.57

Stained stained

The length width ratio

The layer W/L 1 T M B T M B T M B of system

1???????4.7????4.4???2.0????1.5????1.5????1.5???0.32???0.34??0.757

2??????4.8????3.7???1.7????1.5????1.5????1.5???0.31???0.41??0.88

Average 4.75 4.05 1.85 1.5 1.5 1.5 0.31 0.38 0.82 all thick systems comprise:

Basic weight % pulp % binding agent density size

Wt top layer 250gsm 90% 10%2.8dH-CT-0.12g/c 38mm *

Weyerhaeuser??255?????????????c??????????140mm

The NB416 middle level referring to following explanation 52mm *

154mm

The 60mm ctr that 435gsm 100%Coosa 0% hourglass shape-bottom 0054 protrudes,

Sinusoidal wave form 70mm leaf lobe shape

200m is long

The transportation lag middle level that is used for said system:

System 1:0.8osy, 2.2 dawn, polypropylene spun-bonded

System 2:1.0osy, 2.2 dawn, polypropylene spun-bonded

System 3:1.0osy, 2.0 dawn, polypropylene, polyethylene conjugate fibre

System 4:1.0osy, 2.0 dawn, polypropylene, polyethylene conjugate fibre

The porous polyethylene membrane of system 5:1.0mil

System 6:50gsm bonded carded fabric

The mixture of system 7:Weyerhaeuser NB 416 pulps and H-C 7-255 binder fibre prepares according to air-laid process.

The form of implementation of the goods next to the shin that the present invention is included includes the feminien hygiene pad, and this sanitary belt has side liner, distribution/maintenance layer, transportation lag layer, mat forming or secondary moisture absorption layer and tergite.These materials can be remained to together by all devices, comprise binding agent bonding mode, mechanical system and thermal bond pattern.

Above-mentioned lining can be the laminate of supatex fabric or supatex fabric and film.In the laminate situation, the perforate and can allow fluid pass through in some way of this lining.The supatex fabric that is used for the satisfaction of this laminate is by the bonding conjugated polypropylene/low density polyethylene (LDPE) of blowing air, and the concentric 6-10 denier fiber of 50/50 core/skin is made, and this fiber has finishing agent and produces wettability.The non-woven fabric that is suitable for can have the density of about 0.03g/cc and the basic weight of about 0.7osy (24gsm).The suitable film that is used for this laminate for example can be a kind of available from Edison Plastics, this film comprises 94%Rexene  low density polyethylene (LDPE), have melt index 5.5 and density 0.923g/cc, also comprise the titanium dioxide concentrate of 6%Ampacet .This film and supatex fabric can be by the thermal bonding pattern laminations of for example 8-12% bond area, have simultaneously hole shape into about 27% perforated area to pass through fluid.

This backing layer can be with binding agent for example National Starch NS 34-5610 or equivalent, and is according to the addition of about 5gsm, bonding with distribution/maintenance layer.Any binding agent or any other adhesive bonding method must must not hinder the fluid flow between the described layer naturally.

Above-mentioned distribution/maintenance layer can be prepared by air-laid process, and comprise for example 90%Wegerhaeuser ' s NB-416 or NF-405 south softwood pulp and 10%Hoechst-Celanese T-255 polyethylene terephthalate/copolyalkenamer, 50/50 core/skin, concentric 2.8 denier fibers.The basic weight of this distribution layer can be about 250gsm, and the about 0.14g/cc of density.This distribution/maintenance layer can longitudinally have the line of rabbet joint as mentioned above, makes these goods next to the shin in use can upwards arch upward, and improves the adaptability with health.This slit can be successive or be interrupted, also can be located at the center of these goods.

The transfer delay layer that is suitable for can be made by spun-bond process by polyolefinic as polyacrylic fiber, the about 0.8osy of basic weight, and fiber number is the fibrous fabric of 2.7 daniers.This layer can be greater than distribution layer on X-Y plane, and has the color of the white of differing from, and is used for prompting wearer when fluid had moved on to outside the edge of distributions/maintenances layer already.A kind of like this color can be that pink is to provide beautiful outward appearance to product.

In case the fluid maintenance dose in the distribution/maintenance layer reaches maximum and/or has pressure to act on this goods, the transportation lag layer just can allow fluid to move on in the mat forming layer along Z direction (downwards).

Mat forming layer or secondary absorbed layer can by with distribution layer use identical proportioning is arranged but all lower same material of density and basic weight is made, for example about 0.08g/cc of this lower density, this lower basic weight for example is about 175gsm.The mat forming layer that is suitable for can have the passage of ridge design formation longitudinally to come direct fluid longitudinally, makes it be unlikely the comfortableness that can improve health along the side direction effusion simultaneously.

The another kind of mat forming layer that is suitable for can have two-layer pulp.Wherein one deck can have 500gsm, 100% southern softwood, similar Coosa 0054, Weyerhauser HB-416 or HF-405 or Georgia Pacific Golden Isles grade 4821 pulps, be about 200mm, wide about 60-70mm, and can have sinusoidal wave decorative pattern for example shown in Figure 16 or other vertical ridge design.Wherein another layer then can have material same as described above, is about 160mm, wide about 45mm, and can have an acorn or other ridge design.

Above-mentioned mat forming layer can be adhered on backing layer or the barrier layer by less than the binding agent of the amount of about 15gsm NationalStarch NS 34-5610 for example.

The backing layer of described goods or barrier layer can be by the thick polyethylene films of low-density 1mil, and for example Edison Plastic ' s XP 746A is peach has the film of the protruding decorative pattern of nick to make.This backing layer also can adopt any other color.

The discussing widely of method and apparatus that is used for producing goods of the present invention can be referring under the attorney docket 13817, the common transfer, co-pending patent application.

As mentioned above, whole material can have ridge design, and preferably from the lining side on side this decorative pattern is arranged.Such ridge design only can be thinned to and occur in side liner, or also can relate to other layers.This ridge design can be chosen to make material densification to greatest extent, to strengthen suction and the dispersion of fluid on whole goods, improves fluid simultaneously along forward and backward axial distribution.Ridge design also can provide visual signal to the wearer.Show that the capacity of bright this goods should abandon near the limit, can also be used for providing beautiful outward appearance.Suitable ridge design example is given in the accompanying drawing.The ridge design that is used for goods next to the shin among Figure 16 is so-called sine wave pattern, and the ridge design that is used for goods next to the shin among Figure 17 is called the hull shape pattern.

Obviously, have the goods system women next to the shin such as the feminine hygiene article of attribute required for the present invention, can make the quite good spreading of stained thing.This spreading can have been used whole goods more effectively before sewing, thereby can make the wearer comfortable especially.

Although only be to have described several typical embodiment of the present invention in detail above, the expert can make many change forms to this class embodiment under the prerequisite that does not deviate from novel imagination of the present invention and advantage basically.Therefore, all these change forms should be thought and are included within the scope of appended claim book defined.In this claim, device and what is claimed is of function aspects are used for containing the structure of the function that enforcement described here mentions, and are not only the result that the equivalent of structure also comprises equivalence.For example, aspect nail and screw, then utilizing helical surface in the environment of fastening timber components because of nail has adopted the garden cylindrical surface that timber components is secured together screw, so they structurally are inequivalences, but can be the structure of equivalence.

Claims (46)

1. distributed material that goods next to the shin are used, its included fabric can the wicking artificial menses reach at least about 1 inch distance in less than 1.5 minutes time according to the horizontal wicking test.

2. distributed material as claimed in claim 1, wherein, the density of described fabric is less than about 0.15g/cc.

3. distributed material as claimed in claim 1, wherein, the hole that this material had has that its diameter is the 80-400 micron more than 50%.

4. distributed material as claimed in claim 1, wherein, the hole that this material had has that its diameter is the 80-400 micron more than 60%.

5. distributed material as claimed in claim 1, wherein, the hole that this material had has that its diameter is the 80-400 micron more than 70%.

6. feminien hygiene pad that includes the described fabric of claim 1.

7. distributed material as claimed in claim 1, it includes conjugate fibre.

8. distributed material as claimed in claim 1, it has stability.

9. goods next to the shin system, it comprises distribution/maintenance layer and mat forming layer, wherein the stained length ratio that has of each layer is 0.5 or littler, and the saturation distribution that distributes/keep layer is 4 or littler.

10. goods next to the shin as claimed in claim 9 system, wherein, described distribution/maintenance layer and described mat forming layer respectively have 0.375 or littler stained length ratio.

11. goods next to the shin as claimed in claim 9 system, wherein, described distribution/maintenance layer and described mat forming layer respectively have 0.1875 or littler stained length ratio.

12. goods next to the shin as claimed in claim 9 system, wherein, the saturation distribution ratio of described distribution/maintenance layer is 2 or littler.

13. goods next to the shin as claimed in claim 9 system, wherein, the saturation distribution ratio of described distribution/maintenance layer is 1.4 or littler.

14. goods next to the shin as claimed in claim 9 system, wherein, the density of described distribution/maintenance layer is 0.1-0.2g/cc.

15. goods next to the shin as claimed in claim 14 system, wherein, the basic weight of described distribution/maintenance layer is 175-300gsm.

16. goods next to the shin as claimed in claim 9 system, wherein, the density of described mat forming layer is the about 0.1g/cc of about 0.03-.

17. goods next to the shin as claimed in claim 9 system, wherein, the aperture of described mat forming layer is greater than distribution/maintenance layer.

18. goods next to the shin as claimed in claim 9 system, wherein, described system also comprises blot coat.

19. goods next to the shin as claimed in claim 18 system, wherein, the aperture of described mat forming layer is greater than distribution/maintenance layer, and the aperture of this distributions/maintenance layer is less than described blot coat.

20. goods next to the shin as claimed in claim 18 system, wherein, described each layer is the zone of single piece of material.

21. goods next to the shin as claimed in claim 18 system wherein, has at least one deck that slit is arranged in described each layer.

22. goods next to the shin as claimed in claim 18 system, wherein, having one deck at least is to become net according to air lay method or wet laying process or bonded carded method is made.

23. goods next to the shin as claimed in claim 22 system, wherein, one deck is by being selected from cellulose fibre at least, foam, and the material in synthetic fibers and its mixture is made.

24. goods next to the shin as claimed in claim 18 system wherein, also comprises the transportation lag layer.

25. goods next to the shin as claimed in claim 18 system wherein, has at least one deck that ridge design is arranged.

26. goods next to the shin as claimed in claim 25 system, wherein, described mat forming layer processes sinusoidal wave decorative pattern.

27. goods next to the shin as claimed in claim 25 system, wherein, described each layer processes the hull shape decorative pattern together.

28. feminine hygiene article that comprises the described system of claim 9.

29. a feminine hygiene article, these goods comprise:

Blot coat, its density is the about 0.06g/cc of about 0.02-, and basic weight is the about 125gsm of about 25-, and the aperture is about 80-1000 micron, and has a middle length at least to slit.

Distribution/maintenance layer, its density is the about 0.2g/cc of about 0.1-, the about 300gsm of the about 175-of basic weight, the aperture is about 500 microns of about 40-, and has a middle length at least to slit; And

The mat forming layer of ridge design is arranged, and its density is about 0.03-0.2g/cc.

30. a feminine hygiene article, these goods comprise: side liner, distribution/maintenance layer, transportation lag layer, mat forming layer and tergite, wherein:

Described lining is selected from the porose laminate that supatex fabric or supatex fabric and film are formed;

Described distribution/maintenance layer is to be adhered on the above-mentioned lining and comprised pulp and binder fibre by binding agent;

Described transportation lag layer comprises the fabric of polyolefine fiber goods, and it greater than described distribution/maintenance layer, can inform through color treatments whether the relevant fluid of wearer surpasses the edge of described distribution/maintenance layer simultaneously in X-Y plane;

Described mat forming layer has that ridge design forms passage and direct fluid longitudinally; With

Described tergite comprises the low-density film, and this film is adhered on the above-mentioned mat forming layer;

Wherein, described distribution/the maintenance layer is 0.5 or littler with the stained length ratio that the mat forming layer has, and the saturation distribution of this distribution/maintenance layer is 4 or littler.

31. feminine hygiene article as claimed in claim 30, wherein, described lining is a laminate, it comprises: wettable conjugated polypropylene/low density polyethylene (LDPE), 50/50, fiber number is the blowing air bonded fabric of the concentric fibers at about 6-10 dawn, the about 0.03g/cc of the density of this supatex fabric and the about 0.7osy of basic weight (24gsm); And a kind of film, this film has melt index about 5.5 and 94% low density polyethylene (LDPE) and the 6% titanium dioxide concentrate of the about 0.9g/cc of density.

32. feminine hygiene article as claimed in claim 31, wherein, described lining is film and non-woven 's a laminate, and be to form with a kind of thermal bonding pattern lamination, the bond area that this thermal bonding pattern has about 8-12% also has through hole and produces about 27% perforated area and be used to pass through fluid.

33. feminine hygiene article as claimed in claim 30, wherein, described lining is to be attached on distribution/maintenance layer by the addition of binding agent by about 5gsm.

34. feminine hygiene article as claimed in claim 30, wherein, described distribution/maintenance layer is to be prepared by air-laid process, comprise about 90% softwood pulp and polyethylene terephthalate/copolyalkenamer of 10%, 50/50 core/skin, concentric 2.8 denier fibers, and the about 250gsm of basic weight of this distribution/maintenance layer and density is about 0.14g/cc.

35. feminine hygiene article as claimed in claim 34, wherein, described distribution/maintenance layer longitudinally has slit and these goods can in use be swelled and improves suitability with health.

36. feminine hygiene article as claimed in claim 35, wherein, above-mentioned slit be successive or be interrupted and be provided with along the center of goods.

37. feminine hygiene article as claimed in claim 30, wherein, described transportation lag layer is the nonwoven fabric of the polyolefine fiber of about 2.7 daniers of fiber number, and the about 0.8osy of the basic weight of this fabric (27gsm).

38. feminine hygiene article as claimed in claim 37, wherein, the color of described transportation lag layer is not a white.

39. feminine hygiene article as claimed in claim 30, wherein, described mat forming layer is by air-flow or network process preparation, comprise about 90% softwood pulp and polyethylene terephthalate/copolyalkenamer of 10%, 50/50 core/skin, concentric 2.8 denier fibers, and the basic weight of this mat forming layer is about 175gsm and density is about 0.8g/cc.

40. feminine hygiene article as claimed in claim 30, wherein, described mat forming layer has two-layer pulp, and ground floor comprises the softwood pulp of about 500gsm and have sinusoidal wave ridge design that the second layer comprises the softwood pulp of about 400gsm and has ridge design.

41. feminine hygiene article as claimed in claim 30, wherein, described tergite comprises the polyethylene film of low-density 1mil.

42. feminine hygiene article as claimed in claim 30, wherein, described tergite is peach.

43. a feminine hygiene article, these goods comprise side liner, distribution/maintenance layer, mat forming layer and tergite, wherein:

Described lining is a laminate, comprise: wettable conjugated polypropylene/low density polyethylene (LDPE), 50/50, fiber number is the blowing air bonded fabric of about 6-10 danier, the about 0.03g/cc of the density of this fabric and the about 0.7osy of basic weight (24gsm), and a kind of film, this film has melt index about 5.5 and 94% low density polyethylene (LDPE) and the 6% titanium dioxide concentrate of the about 0.9g/cc of density, formed by the thermal bonding pattern lamination, the bond area that this thermal bonding pattern has about 8-12% also has through hole and is used to pass through fluid to produce about 27% perforated area;

Described distribution/maintenance layer is to be attached on the described lining by binding agent, prepare by air-laid process, comprise about 90% softwood pulp and polyethylene terephthalate/copolyalkenamer of 10%, 50/50 core/skin, concentric 2.8 denier fibers, the about 250gsm of basic weight of this distribution/maintenance layer and density are for about 0.14g/cc and have interruption or successive longitudinal center slit;

Described mat forming layer is to be prepared by air-laid process, included fabric has about 90% softwood pulp and polyethylene terephthalate/copolyalkenamer of 10%, 50/50 core/skin, concentric 2.8 denier fibers, and have the basic weight of about 175gsm and density and the vertical ridge design of about 0.08g/cc, this decorative pattern has formed passage and has been able to direct fluid longitudinally;

Described back sheet comprises the low density polyethylene (LDPE) pink film that 1mil is thick, is adhered on the above-mentioned mat forming layer by binding agent.

44. feminine hygiene article as claimed in claim 43, wherein, also comprise the transportation lag layer between above-mentioned distribution/maintenance layer and the mat forming layer, the sticking yarn fabric that this transportation lag layer comprises in X-Y plane greater than described distribution/maintenance layer and be, polyolefine fiber by 2.7 daniers constitutes, and the about 0.8osy of the basic weight of described fabric (27gsm) and getting differs from the color of white.

45. a feminine hygiene article, these goods comprise side liner, distribution/maintenance layer, mat forming layer and tergite, wherein:

Described lining is a laminate, comprise: wettable conjugated polypropylene/low density polyethylene (LDPE), 50/50, core/skin, fiber number is the blowing air bonded fabric of about 6-10 danier, the about 0.3g/cc of the density of this fabric and the about 0.7osy of basic weight (24gsm), and a kind of film, this film has melt index about 5.5 and 94% low density polyethylene (LDPE) of the about 0.9g/cc of density and 6% titanium dioxide concentrate are formed by the thermal bonding pattern lamination; This thermal bonding pattern has the bond area of about 8-12%, also has through hole and is used to pass through fluid to produce about 27% perforated area;

Described distribution/maintenance layer is to be attached on the described lining by binding agent, prepare by air-laid process, comprise about 90% softwood pulp and poly terephthalic acid ethanedioic acid/copolyalkenamer of 10%, 50/50, core/skin, concentric 2.8 denier fibers, the about 250gsm of the basic weight of this distribution layer and density is about 0.14g/cc;

Described mat forming layer is the fabric that two-layer pulp is arranged, and ground floor comprises the softwood pulp of about 500gsm and have sinusoidal wave ridge design that another layer comprises the softwood pulp of about 400gsm and have ridge design;

Described back sheet comprises the low density polyethylene (LDPE) pink film that 1mil is thick, is adhered on the above-mentioned mat forming layer by binding agent.

46. feminine hygiene article as claimed in claim 45, wherein, also be included in the transportation lag layer between described distribution/maintenance layer and the mat forming layer, the nonwoven fabric that this retardation layer comprises in X-Y plane greater than described distribution/maintenance layer and be that polyolefine fiber by 2.7 daniers constitutes, and the about 0.8osy of the basic weight of described fabric (27gsm) and get and differ from white color.

Images