CN1255324C - Method for synthesizing high-purity cobalt disulfide powder under normal pressure system - Google Patents
Method for synthesizing high-purity cobalt disulfide powder under normal pressure system Download PDFInfo
- Publication number
- CN1255324C CN1255324C CN 03156711 CN03156711A CN1255324C CN 1255324 C CN1255324 C CN 1255324C CN 03156711 CN03156711 CN 03156711 CN 03156711 A CN03156711 A CN 03156711A CN 1255324 C CN1255324 C CN 1255324C
- Authority
- CN
- China
- Prior art keywords
- constant temperature
- powder
- purity
- sulphur
- warmed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to the technical field of inorganic synthesis, and particularly relates to a method for obtaining high-purity fine-particle cobalt disulfide powder by using simple substance powder as a raw material and performing secondary high-temperature synthesis under a normal pressure system. The method is carried out under the protection of vacuum and inert atmosphere such as argon or nitrogen. The purity of the high-purity cobalt disulfide powder is more than 99 percent, and the high-purity cobalt disulfide powder can be used as a positive material of a high-temperature thermal battery.
Description
Technical field
The invention belongs to inorganic synthesis technical field, being particularly related to a kind of is raw material with the simple substance powder, under the normal pressure system, be synthesized into method high-purity, particulate cobalt disulfide powder through secondary high temperature, this high-purity cobalt disulfide powder can be used as the positive level material of elevated temperature heat battery.
Background technology
High-purity cobalt disulfide powder can be used as the electrode materials of lithium/disulphide thermobattery, increases the electrode high-temperature stability, improves its chemical property, causes people's extensive attention in recent years." synthetic method that mineral compound synthesizes in the handbook (publication in October nineteen eighty-three) report mainly contains: (1) is raw material with the cobalt powder and the SULPHUR POWDER of 1: 1 mol ratio, mix and vacuum-sealing in silica tube, heat 72 hours synthetic cobaltous sulfides down at 700 ℃; After product shrend grinding, matching well cobaltous sulfide and sulphur according to 1: 1 (sulphur excessive 5%) mole, vacuum-sealing was calcined 168 hours down in 700 ℃ in silica tube, obtained cobalt disulfide.Under the vacuum-sealing condition, the pressure of system is difficult to control, and building-up process has bigger potential safety hazard.(2) vacuum drying rose vitriol is heated to 350 ℃ in nitrogen gas stream, heating 6 hours in hydrogen sulfide and hydrogen mixed gas stream again, chilling it, can obtain cobalt disulfide.This method synthetic product crystallinity is poor, and the easy contaminate environment of hydrogen sulfide.
Summary of the invention
Purpose of the present invention is exactly in order to overcome the shortcoming of aforesaid method, a kind of not only safety but also the easy low-cost method of synthesizing high-purity cobalt disulfide of normal pressure system to be provided.
The method steps of the synthetic high-purity cobalt disulfide powder of normal pressure system of the present invention comprises:
(1). high purity elemental cobalt powder and SULPHUR POWDER are mixed, put into high-temperature resistant container, as quartz glass tube, wherein the consumption of SULPHUR POWDER is 1~5 times of theoretical weight; System is carried out vacuum outgas, under inert atmosphere protections such as argon gas or nitrogen, place then in the retort furnace of thermograde, begin under the normal pressure to heat up, 100~150 ℃ of following constant temperature 3 days, be warmed up to 200 ℃ of constant temperature 5~6 days again, be warmed up to 420~440 ℃ of constant temperature 2 hours at last; Sulphur is separated with product, be cooled to room temperature, obtain crude product through fragmentation;
(2). the crude product that step (1) is obtained grinds, sieves or classification, be reentered in the high-temperature resistant container after making the product particle less than 0.074mm, under inert atmosphere protections such as argon gas or nitrogen, place in the retort furnace of thermograde, 200 ℃ of following constant temperature 2 days, be warmed up to 380 ℃ of constant temperature 6~7 days again, be warmed up to 420~440 ℃ of constant temperature 2 hours at last; Sulphur is separated with product, be cooled to room temperature, promptly obtain high-purity cobalt disulfide powder, purity is greater than 99%.
Described vacuum tightness is 0.001~0.1Pa.
The consumption of described SULPHUR POWDER is 1~3 times of theoretical weight.
It is to adopt thermograde to carry out separating of product and sulphur that described sulphur separates with product.
Method of the present invention with " mineral compound synthesizes other method of report in the handbook (publication in October nineteen eighty-three) to be compared, and has following characteristics: the normal pressure system, synthesis temperature is low, security is good; Reaction vessels can use repeatedly, and synthetic quantity is changeable, has greatly reduced synthetic cost, is a kind of method of reliable and economic synthetic high-purity cobalt disulfide powder.This high-purity cobalt disulfide powder can be used as the positive level material of elevated temperature heat battery.
Below in conjunction with embodiment method of the present invention is further described, but these embodiment limit technical scheme of the present invention.
Embodiment
Embodiment 1.
In nitrogen protection atmosphere; with high-purity cobalt powder (〉=99.5%) 3.3 gram and specpure SULPHUR POWDER 7.2 grams (making excessive 2 times of SULPHUR POWDER weight) by mixing, in the quartz glass tube of packing into, after system is evacuated down to 0.1Pa and outgases than being listed as; quartz glass tube is put into retort furnace; feed argon shield, begin to warm to 100 ℃, constant temperature 3 days; be warmed up to 200 ℃ again; constant temperature 6 days is raised to 420 ℃ of constant temperature 2 hours at last, is cooled to room temperature.The extract abrasive lapping, the 0.074mm that sieves (200 order), the extracting screen underflow material is packed in another quartz glass tube; after sulphur is added according to the excessive 2 times ratio of theoretical weight; put into retort furnace once more, feed argon shield, begin to warm to 200 ℃; constant temperature 2 days; be warmed up to 380 ℃ again, constant temperature 6 days is raised to 440 ℃ of constant temperature 2 hours again; be raised to 700 ℃ of constant temperature 1 hour at last, be cooled to room temperature.Promptly obtain cobalt disulfide powder 6.7 grams, purity is greater than 99%.
Embodiment 2.
According to material and step similarly to Example 1; add cobalt powder 100 grams and SULPHUR POWDER 162.7 and restrain (excessive 1.5 times), system is evacuated down to the 0.1Pa processing that outgases, quartz glass tube is put into retort furnace; feed argon shield; begin to warm to 100 ℃, constant temperature 3 days is warmed up to 200 ℃ again; constant temperature 5 days; be warmed up to 440 ℃ of constant temperature 2 hours again, be raised to 700 ℃ of constant temperature 1 hour at last, be cooled to room temperature.After cooling off, grinding, sieve, sulphur reloads in the silica tube, under same condition after adding according to the excessive 1.5 times ratio of theoretical amount, begin to warm to 200 ℃, constant temperature 2 days is warmed up to 380 ℃ again, constant temperature 7 days is raised to 440 ℃ of constant temperature 2 hours at last, is cooled to room temperature.Obtain cobalt disulfide powder 204 grams, purity is greater than 99%.
Embodiment 3.
According to material and step similarly to Example 1; add cobalt powder 300 grams and SULPHUR POWDER 650.8 grams (excessive 2 times); after system was evacuated down to 0.01Pa and outgases, quartz glass tube was put into retort furnace, feeds argon shield; begin to warm to 150 ℃; constant temperature 3 days is warmed up to 200 ℃ again, constant temperature 6 days; be raised to 440 ℃ of constant temperature 2 hours at last, be cooled to room temperature.After cooling off, grinding, sieve, sulphur is added according to the excessive 1.5 times ratio of theoretical amount, reloads in the silica tube, under same condition, begin to warm to 200 ℃, constant temperature 2 days is warmed up to 380 ℃ again, constant temperature 7 days is raised to 420 ℃ of constant temperature 2 hours at last, is cooled to room temperature.Obtain cobalt disulfide powder 625.1 grams, purity is greater than 99%.
Claims (3)
1. the method for the synthetic high-purity cobalt disulfide powder of a normal pressure system, it is characterized in that: described method steps comprises:
(1). high purity elemental cobalt powder and SULPHUR POWDER are mixed, put into high-temperature resistant container, wherein the consumption of SULPHUR POWDER is 1~5 times of theoretical weight; System is carried out vacuum outgas, under argon gas or nitrogen inert atmosphere protection, place in the retort furnace of thermograde then, begin under the normal pressure to heat up, 100~150 ℃ of following constant temperature 3 days, be warmed up to 200 ℃ of constant temperature 5~6 days again, be warmed up to 420~440 ℃ of constant temperature 2 hours at last; Sulphur is separated with product, be cooled to room temperature, obtain crude product through fragmentation;
(2). the crude product that step (1) is obtained grinds, sieves or classification, be reentered in the high-temperature resistant container after making the product particle less than 0.074mm, under argon gas or nitrogen inert atmosphere protection, place in the retort furnace of thermograde, 200 ℃ of following constant temperature 2 days, be warmed up to 380 ℃ of constant temperature 6~7 days again, be warmed up to 420~440 ℃ of constant temperature 2 hours at last; Sulphur is separated with product, be cooled to room temperature, promptly obtain high-purity cobalt disulfide powder.
2. the method for claim 1, it is characterized in that: described vacuum tightness is 0.001~0.1Pa.
3. the method for claim 1, it is characterized in that: the consumption of described SULPHUR POWDER is 1~3 times of theoretical weight.