CN1236738A - Horizontal method for making curved strengthened glass - Google Patents
Horizontal method for making curved strengthened glass Download PDFInfo
- Publication number
- CN1236738A CN1236738A CN 99103522 CN99103522A CN1236738A CN 1236738 A CN1236738 A CN 1236738A CN 99103522 CN99103522 CN 99103522 CN 99103522 A CN99103522 A CN 99103522A CN 1236738 A CN1236738 A CN 1236738A
- Authority
- CN
- China
- Prior art keywords
- glass
- soft roller
- air grid
- curved
- combination air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A horizontal method for making curved strengthened glass with horizontal roller bed features that during furnace discharge and shaping-cooling steps in strengthening procedure a soft roller bed, whose rollers can rotate in radial direction and be curved in axial direction, is used to regulate axial curve level and a combined wind grate is used to regulate the curved shape. On strengthening, said soft roller bed swings for uniformly accepting wind. When a 5-mm glass is strengthened with said technique, its curved radius can reach about one meter and its area can reach 1.2X2 sq.m. Its advantages are lower wind pressure decreasted by 10-20% and easy regulation of bending radian.
Description
The present invention relates to the production method of curved strengthened glass.Be particularly related to the method for horizontal roller formula glass tempering.
Toughened glass is a kind of high-intensity shatter proof glass that ordinary plate glass is made after Overheating Treatment.Be widely used in the every field of industry, traffic, building and daily life.
It is described in license notification number CN2215487Y that one class is arranged in the horizontal tempering glass especially working method at horizontal curved tempered glass, the glass that heats is delivered on the curved ring mould in the forming room, rely on the glass dead load forming or rely on the model bent into shape, then send into the tempering of drying in the air grid.
Another kind of method is the preparation method of single curved surface curved tempered glass, and the method described in patent publication No. CN114361 is to rely on formed cambered surface behind the level attitude that change to transmit roller-way outside stove; Perhaps behind the tetrafluoroethylene lasso of suit different diameter on the steel shaft, form on the so-called arc roller bed, after making glass bending and bending, the method for the tempering of drying again.
The object of the present invention is to provide a kind of horizontal method for making curved strengthened glass,, make that crooked glass quality is higher, specification is bigger, cost is lower so that level is produced various curved strengthened glass.
The present invention is by using a kind of adjustable axle (radially rotatable to the flexible axle roller-way of radian in the section of coming out of the stove and moulding cooling section in the glass tempering process, axially can become the flexible roller-way of bending by linear, hereinafter to be referred as soft roller) and can adjust the strip combination grid (hereinafter to be referred as the combination air grid) of radian shape, make glass bending, tempering.
Accompanying drawing 1 is the structural representation of used of the present invention
Accompanying drawing 2 is that the A of accompanying drawing 1 is to cross section view
The A of accompanying drawing 3 accompanying drawing 1 during for curved glass of the present invention is to cross section view
As shown in drawings, used of the present invention is by soft roller (3), groove (4), top combination air grid (6), bottom combination air grid (7), soft roller support (9), last air grid sprocket wheel (10), last air grid chain sling (11), following air grid sprocket wheel (12), following air grid chain sling (13), cylinder (14), soft roller transmission case (15), soft roller transmission shaft (16), the combination air grid connects hinge (17), go up soft roller (18), following soft roller (19), groove (20), soft roller (21) constitutes, wherein bottom combination air grid (7) inboard has groove (4), soft roller (3) can be bumped into wherein, soft roller (3), soft roller (21), soft roller (19) was supported by soft roller support (9) respectively under upward soft roller (18) reached, top combination air grid (6) is by the drive flexible distortion of last air grid sprocket wheel (10) with last air grid chain sling (11), bottom combination air grid (7) is by the flexible distortion of drive of air grid sprocket wheel (12) and following air grid chain sling (13) down, cylinder (14) has several, and join with the outside of bottom combination air grid (7), soft roller (3), soft roller (21), soft roller (19) linked to each other with soft roller transmission case (15) by soft roller transmission shaft (16) respectively under upward soft roller (18) reached, connecting hinge (17) by the combination air grid between each the strip air grid in top combination air grid (6) and the bottom combination air grid (7) connects, top combination air grid (6) but also recessing of inboard (20) and be bumped into soft roller (21), the section of coming out of the stove has corresponding up and down last soft roller (18) and time soft roller (19).
Level of the present invention can make glass after the heating in the section of coming out of the stove moulding when producing curved tempered glass, also can moulding in cooling section moulding or the transport process before cooling off from coming out of the stove to, utilize the distortion of soft roller and swing to improve shaping efficiency and tempering effect in the forming processes.
As shown in drawings, when utilizing the present invention to produce curved strengthened glass, if in the section of coming out of the stove moulding, the hot glass (5) of then coming out of the stove, when falling down on the soft roller (19), the instant distortion of soft roller (19) is curved down down, glass (5) is transmitted limit sag bent moulding above that, when the glass after the bending (5) arrives between top combination air grid (6) and bottom combination air grid (7), soft roller transmission case (15) drives the positive and negative both direction conversion of soft roller (3) and rotates, make crooked glass (5) produce swing, thereby wind-engaging is even, soft roller transmission case (15) continues to drive soft roller (3) and rotates forward, and good glass reaches on the unloading piece platform transfer roller (8) to make crooked tempering, finishes the curve tempering production of glass; Also can utilize soft roller (18) to drop in the section of coming out of the stove moulding and go up soft roller (18) and following soft roller (19) while bending on the glass (5) then, clamp glass (5) jointly, roll extrusion drives its brake forming and continues and transmits, the glass of forming enters cooling section, top combination air grid (6) and bottom combination air grid (7) drive soft roller (3) and soft roller (21) also becomes curved with the glass behind the carrying bending, by above-mentioned swing air cooling way cooling tempering.
During production, if in the cooling section moulding, after then glass (5) imports in top combination air grid (6) and the bottom combination air grid (7), soft roller (3) and soft roller (21) return to respectively in groove (4) and the groove (20), top combination air grid (6) and bottom combination air grid (7) be in the wind respectively grid chain sling (11) and last air grid sprocket wheel (10) and bending under the drive of air grid chain sling (13) and following air grid sprocket wheel (12) down, after closing up glass (5) is suppressed brake forming, top combination air grid (6) lifts then, and soft roller (3) rises, by aforementioned swing air cooling way cooling tempering.
During production, also can work as after glass (5) tail end comes out of the stove, one falls down soft roller (19) go up after, go up soft roller (18) and promptly drop on the glass (5), clamp glass (5), top combination air grid (6) and bottom combination air grid (7) are also clamped glass (5) simultaneously, it is transmitted on one side, on one side integral body make glass (5) bending and molding, after glass (5) all enters between top combination air grid (6) and bottom combination air grid (7), top combination air grid (6) rises, by aforementioned swing air cooling way cooling tempering.
When utilizing the present invention to process 5 millimeters glass, bending radius can reach about 1 meter, finish size can reach 1.2 * 2 square metres, and the prerequisite katabatic wind pressure that product reaches GB can install more in the past and reduce 10~20%, regulates easy to use when producing the toughened glass of differently curved radian.
Claims (5)
1. the horizontal method for making of a curved strengthened glass, utilize brake forming, blowing quenching processed glass, it is characterized in that: when the curved glass that described blowing quenching is forming all enters into top combination air grid (6) and bottom combination air grid (7) centre, be set on the bottom combination air grid (7), can lifting in groove (4), and bend to soft roller (3) with the same shape of the glass (5) of forming and swing back and forth and make the glass wind-engaging even, described brake forming is the glass ware forming that utilizes after soft roller or air grid make heating.
2. the horizontal method for making of curved strengthened glass according to claim 1 is characterized in that: after the described distortion that utilizes soft roller to be configured as glass (5) is soft roller (19) distortion down, make glass (5) utilize deadweight curved down, be shaped while transmitting.
3. the horizontal method for making of curved strengthened glass according to claim 1 is characterized in that: describedly utilize soft roller to be configured as soft roller (19) and down after soft roller (19) distortion, clamp and rolled glass (5) makes its limit transmit that spring is bent to be shaped.
4. the horizontal method for making of curved strengthened glass according to claim 1, it is characterized in that: the described tail end that utilizes soft roller to be configured as glass (5) come out of the stove the back go up soft roller (18) and down soft roller (19) and drives of top combination air grid (6) go up soft roller (21) and bottom and make up air grid (7) and drive soft roller (3) and clamp glass (5) simultaneously, integral body makes its limit transmission Edge Bend shaping.
5. the horizontal method for making of curved strengthened glass according to claim 1, it is characterized in that: described utilize air grid to be shaped to glass (5) to import top combination air grid (6) and bottom into and make up in the air grid (7) after, soft roller (3) and soft roller (21) return to respectively in groove (4) and the groove (20), and top combination air grid (6) and bottom combination air grid (7) close up pressed glass (5) brake forming.