CN1227655A - Disaster prevention building material - Google Patents
Disaster prevention building material Download PDFInfo
- Publication number
- CN1227655A CN1227655A CN 97197197 CN97197197A CN1227655A CN 1227655 A CN1227655 A CN 1227655A CN 97197197 CN97197197 CN 97197197 CN 97197197 A CN97197197 A CN 97197197A CN 1227655 A CN1227655 A CN 1227655A
- Authority
- CN
- China
- Prior art keywords
- light
- composition
- resin
- particulate composition
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A disaster prevention building material which comprises a figure or pattern, which is indicative of direction, position and the like, and is formed of a luminous material or a fluorescent material or t he both materials. The luminous material and the fluorescent material are driven or inlaid into a base material, which contains at least an inorganic material or resins as its constituents, to be integral with the base material.
Description
Technical field
Invention among the application relates to disaster prevention building material.When more detailed saying, the invention among the application relate to a kind of electricity failure at night and under the dark surrounds of disaster when taking place,, be used for the building materials of the usefulness of taking precautions against natural calamities such as dwelling house, communal facility by means of light indication Evacuation Route and position, explosive area etc.
Background technology
Past, though the countermeasure during at disasters such as earthquakes has the whole bag of tricks, but the experience explanation of the big earthquakes in Osaka and Kobe in recent years, under dark surrounds during electricity failure at night, how to avoid collapsing or half collapsed house, buildings and tunnel etc., and avoid aspects such as the poison gas indicate and position, tank explosive area, remain in very big problem.
Found out already that when having a power failure under the black status or be in the dark surrounds space that is closed, the means that are used for indicating Evacuation Route or position, explosive area were extremely incomplete.
Past is as representing under the dark surrounds or clearly indicate the means of using that adopt coating to be dispersed with the coating or the paint of light-storing material, perhaps stickup is dispersed with the methods such as adhesive tape of light-storing material.But adopt the problem of these traditional means to be, the substrates such as glass, concrete and resin that have been coated with coating and paint or pasted adhesive tape destroy because of disaster, or because of paint and adhesive tape wear and tear and peel off, can not realize required effect in case of necessity.Therefore, also must safeguard often.
And these traditional means, be used for lacking aesthetic appearance on dwelling house and the communal facility because of additional, and impair ornamental and aesthetic property.
In view of the foregoing, purposes such as present inventor have been to propose a kind of new disaster prevention building material, this building materials can overcome the above-mentioned shortcoming that exists in the past and avoid daily servicing, even because of disaster taking place when destroyed, also can and indicate the explosive area, and be to be suitable for dwelling house and the communal facility design is used and the semipermanent building materials of high abrasion resistance at direction indication under the night black status.
Disclosure of an invention
Invention among the application provides a kind of disaster prevention building material as the means that address the above problem, it is characterized in that on the said disaster prevention building material that the two forms by light-storing material or fluorescent material or its for the figure of expression direction and position or pattern, with said light-storing material and fluorescent material casting or be embedded into and contain at least with inorganic material or resin integrated forming in the base material as constituent.
In addition, as embodiment, in the above-mentioned disaster prevention building material that invention among the application provides, said inorganic material is more than one materials in natural stone, pottery, cement, metal and the glass at least, said resin is a thermoset resin, and said light-storing material and fluorescent material are inorganic material etc.As its embodiment, the invention among the application is also with light-storing material and fluorescent material, and at least a above material is cast or embedded in the resin, cement and the glass that use as bonding agent.
Brief description of drawings
Fig. 1 and Fig. 2 are the sectional views that illustrates as the artificial stone structure of embodiment of the present invention in the accompanying drawing.
Fig. 3 and Fig. 4 are the synoptic diagram that illustrates operation in the manufacture method of the present invention.
Implement best mode of the present invention
Below just the invention among the application be described in further detail.
As the disaster prevention building material of the object of the invention, basically should have following key element:
(A) form expression direction, position light-storing material or fluorescent material with figure or pattern, or its two;
(B) contain organic and/or inorganic materials or resin at least as constituent, wherein casting or embed has the two base material of above-mentioned light-storing material or fluorescent material or its.
At first illustrate as above-mentioned just (A), must use light-storing material or fluorescent material or its two, even, perhaps indicate the present position of confirming that ad-hoc location is used so that, also can indicate Evacuation Route and position, explosive area at night that disaster takes place under the dark surrounds.
Wherein, " light-storing material " stipulated among the present invention is meant to absorb the luminous energy of accumulating sunshine and fluorescent light, has the general name of characteristics of luminescence material under dark surrounds such as night.And " fluorescent material " is to have the general name of the material of lighting function through the ultraviolet ray irradiation.
As light-storing material and fluorescent material in such cases, can be inorganic material or organic material, but from performances such as permanance and wearing qualities being the light characteristic and the continuation viewpoint thereof of the light-storing material and the fluorescent material of representative, usually preferred inorganic material.
This inorganic material can be enumerated the sulfide of the oxide such as aluminium, strontium of strontium aluminate and terres rares activation and composite oxides, various other oxides and zinc, barium, strontium etc. or the material of its activation etc.
This light-storing material or fluorescent material can adopt powder or cake mass, and should use with composite powder or the blocks as bonding agent such as resin, glass, cement.As described below, should be with light-storing material and the fluorescent material under various these forms, casting (pouring is provided with) or embedding (imbedding) are in base material.
About (B) base material, can be by inorganic material or resin as constituent, or inorganic material and resin are formed.
Wherein, said inorganic material, more than one materials in preferred at least natural stone, pottery, cement, metal and the glass.And, the resin when using, thermoset resins such as preferred acrylic resins, methacrylic resin, epoxy resin, unsaturated polyester resin with resin combination.
Inorganic material, in disaster prevention building material of the present invention, itself also have aggregate or bonding agent effect, and resin also is same except using as base material.
For example with cement, glass etc. when using as bonding agent, its shred and fine powder can also use as aggregate.On the other hand, natural stone, pottery and metal itself can be used as base material and use, and its fine powder and shred can also use as aggregate.
Can be used in combination under the situation of inorganic material with resin, except above-mentioned material, also can use inorganic fibres such as rock wool, glass wool and slag etc.
With regard to the casting or embedded mode of light-storing material or fluorescent material, the embodiment under the different substrate materials for example can illustrate as follows.
1) with the blending constituent form light-storing material or fluorescent material are cast in the base material component.
1-1) for example with light-storing material or fluorescent materials such as powdery or fritter shapes, mix with the base material component that uses cement, glass, resin etc. as adhesive ingredients, be configured as tabular or blocks with reservation shape.
At this moment, can with natural stone, watt etc. powdery or shred shape materials such as pottery, glass, be that aggregate element is made base material perhaps with slag, inorganic fibre etc.Use under the situation of these aggregate elements, make bonding agent with resin and can make artificial stone.
1-2) this pouring operation also can utilize casting positions such as the ditch that exists, cave on the base material that is shaped in advance, the method realization that light-storing material or fluorescent material and resin and glass, cement etc. as bonding agent are solidified with admixture casting back.
1-3) also can cast with above-mentioned opposite way.That is, make light-storing material and fluorescent material be configured as certain reservation shape, as all parts of goods, base material component is solidified into one with after the slurry mixture form casting, utilize this mode also can realize with this with bonding agent.
1-4) at above-mentioned 1-2) and 1-3) in, building material made also can be made stacking material, i.e. integrated forming behind stacked light-storing material and fluorescent material layer on the substrate surface.
1-5) at above-mentioned 1-2), 1-3) and 1-4) in, not only can be firming body before the formed body casting, but also can be semi-cured state.
2) also light-storing material, fluorescent material can be embedded in the base material among the present invention.
That is to say, be embedded in the base material that is shaped in advance and form one being configured as the light-storing material of reservation shape and fluorescent material.This embedding operation also can form the duplexer with base material.
This embedding operation, bonding agent or the adhesive bonds that can use the present invention to use become whole, also can carry out physical combination and embed.
For disaster prevention building material of the present invention, no matter be above-mentioned 1) casting handle still above-mentioned 2) embedding handle, all should adjust the color harmony shape according to the purposes and the purpose of building materials; Simultaneously with regard to its shape, also can with form one as peculiar parts such as the metal of constituent, pottery, resins.These parts can be projection and bolt, cooperation hook, strengthen with various other objects such as plate or grid bodies.For example, also can be the shielding electromagnetic wave object.Can also form one with various parts with construction and processing as residential building material.
About casting, the embedding operation of light-storing material and fluorescent material, will utilize its representational embodiment of description of drawings.
Its embodiment for example can use accompanying drawing 1 and accompanying drawing 2 to be illustrated.In the accompanying drawing 1, on the plane of the substrate portion (2) of formed body (1), jut (3) is arranged, these juts (3) are shaped according to predetermined pattern and pattern setting.And these juts (3) also have the photosensitiveness of holding or follow the absorption ultraviolet ray to have luminiferous luminous component.Substrate (2) itself does not form this luminous component.
Go up embedding in substrate portion (2) in the accompanying drawing 2 and embedded part (4) is arranged as luminous component.
As the jut (3) of luminous component shown in the accompanying drawing 1, for example can have braille block function daytime, and night or the disaster dark surrounds when taking place can have the Direction Signs function of direction indication and position down.Under the situation of accompanying drawing 2, embedded part (4) equally also can be used as Direction Signs and uses.Certainly, take place at ordinary times, can also constitute the decoration at night in no disaster.
As mentioned above, only optionally utilizing light-storing material and fluorescent material as luminous component jut (3) and embedded part (4), is one of purpose of the present invention.This is that institute is irrealizable in the past.
The invention is characterized in that the jut (3) that will have lighting function and embedded part (4) constitute the building materials of the usefulness of taking precautions against natural calamities as the part of goods, for realizing this inventive features, just must cast or embedding operation.
Much less, can certainly for example above-mentioned jut (3) and embedded part (4) be made expression and suitable figure or patterns such as Evacuation Route and position, explosive area.
Below will describe in detail and use under the artificial stone situation the preferred embodiments of the invention.
[artificial stone building materials]
As the basis that the artificial stone forms, can be for example in the substrate portion (2) shown in accompanying drawing 1 and the accompanying drawing 2 and jut (3) and/or embedded part (4), to contain organic and/or inorganic materials and resin stone material as aggregate.Inorganic material in this case for example can comprise the far-ranging material such as inorganics, glass, metal of natural stone, natural minerals, synthetic.
And, constitute in the luminous component of jut (3) and embedded part (4), can use noctilucence or epipolic light-storing material and fluorescent material, as at least a portion in the inorganic aggregates or whole.
[formation of luminous component]
Luminous component contains noctilucence or epipolic light-storing material and fluorescent material, also contains resin simultaneously, but also can contain the transparent inorganic aggregate.Contain simultaneously under the situation of this transparent inorganic aggregate, the weight ratio between the two is preferably 1: 2 to 1: 10, and sum of the two is shared ratio in luminous component is all formed, and is preferably 80-95 weight %.
In addition, also can contain the transparent inorganic aggregate that the surface is covered by noctilucence or epipolic light-storing material, fluorescent material sintering at luminous component, the composition weight of luminous component in this case preferably accounts for the 5-65 weight % of total weight.
From the angle of physical properties such as anti-fissility, anti-deciduous, wearing quality and luminescent properties, said ratio is desirable.
As inorganic aggregates, for example preferably combination of following two kinds of materials.That is to say, a kind of material is the fine inorganic particle composition of 5~70 order granularities, this particulate composition can be from mineral such as silica, peridot, feldspar, pyroxene, micas, with natural rocks such as grouan, metamorphosed rocks, and the suitable fine inorganic particle composition of selecting in pottery, glass and the metal etc.
And, preferably use the particulate composition of the following granularity of 100 orders simultaneously with this particulate composition.This particulate composition can be enumerated natural or artificial various particulate compositions.For example, the particulate composition that obtains easily such as lime carbonate, aluminium hydroxide, silica powder.
In addition, part as this particulate composition, can also be used composition such as the manganese dioxide adjusting tone and use, titania, zirconium silicate, iron oxide and give compositions such as three (five) antimony oxides that flame retardancy/noncombustibility uses, boron compound, bromine compounds.
Above-mentioned particulate composition is the principal element that the outward appearance that obtains formed artificial stone and physical property are exerted an influence.The particulate composition is more tiny than particulate composition, and the material of granularity below 100 orders, particulate composition enter between the particulate composition particle, fills the locus between the particulate composition, can give the artificial stone that the obtains character with aspect such as firm, pliable and tough.Weight ratio between particulate composition and this particulate composition should be between 0.5: 1~5: 1, preferably is between 1: 1~4: 1.Be used in combination particulate composition and particulate composition and make under the situation of the artificial stone formed body of the present invention, the formation of luminous site can be considered as follows.
That is to say, part inorganic aggregates uses under the situation of noctilucence or fluorescent substance and transparent inorganic aggregate, the preferred transparent inorganic composition that uses is as at least a portion in the particulate composition, and preferably uses noctilucence or fluorescent substance at least a portion as the particulate composition.
Particulate composition as transparent inorganic aggregates uses is meant the inorganic constituents that actual light transmission is big, though its transparency has all difference, uses the bigger material of light transmission in the dead matter of natural or synthetic in the present invention.Therefore, transparent fine inorganic particle composition can also be in painted state or have under the state of inherent colour.
The representative example of the transparent fine inorganic particle composition that uses among the present invention can be enumerated quartz, silica, glass etc., but is not limited to these materials.
In addition, a part of particulate composition in the artificial stone, can contain granularity having below 100 orders hold photosensitiveness and follow absorb luminescence-utraviolet, noctilucence or epipolic light-storing material and fluorescent material.As mentioned above, strontium aluminate class light-storing material and zinc sulphide etc. are for example arranged.Various these materials all will use in the present invention.
Play the fine inorganic particle composition of artificial stone aggregate effect, its granularity as mentioned above, should be in 5~70 order scopes, and this is a conditio sune qua non when being used in combination with the inorganic particles composition.Therefore, under the situation of above-mentioned noctilucence or fluorescence composition, have the effect same, can also give artificial stone with noctilucence or this optical function of fluorescence simultaneously with the particulate composition.The granularity of noctilucence or fluorescence composition, the same with the particulate composition, must be less than 100 orders.
With regard to above each inorganic constituents, except that granularity, proportioning also is important condition.
That is to say above-mentioned fine inorganic particle composition weight (W
1), inorganic particles composition weight (W
2) and noctilucence or fluorescence composition weight (W
3) between proportionate relationship, preferably be in:
W
1∶(W
2+W
3)=0.5∶1~5∶1,
W
2: W
3=1: 2~10: in 1 scope.
With regard to W
1: (W
2+ W
3), more preferably 1: 1~4: 1; And W
2: W
3, be preferably 1: 1~5: 1.
As mentioned above, transparent fine inorganic particle components in proportions in the fine inorganic particle composition, should satisfy following relation:
(0.5~1.0)W
1。
Above-mentioned condition is for guaranteeing physical propertys such as artificial stone intensity, hardness, density, and realizes that noctilucence or this optical property of fluorescence all are necessary.
Wherein, the granularity of each composition specifically can suitably select according to the granularity and the proportioning of each composition of combination, but particulate composition and noctilucence or fluorescence composition is generally more preferably used 150~250 order granularity powder.
When further specifying the optical function of artificial stone, said smooth function is meant in the artificial stone of the present invention, by:
1) makes that transparent fine inorganic particle composition accounts for 30~100 weight % in the fine inorganic particle composition;
2) according to above-mentioned specific blend ratio, allocate the noctilucence or the fluorescence composition of the following granularity of 100 orders into, can reproduce and have noctilucence or epipolic artificial stone.Therefore, feature in the case is to make the luminous possibility that becomes in the integral thickness.Only luminous different with traditional artificial stone in surface layer part, can realize in all thickness of artificial stone luminously, so luminescent properties is good, and also cause economical less because of price high noctilucence or fluorescence composition consumption.
This is because use transparent fine inorganic particle composition as transparent aggregate, see through from the light of outside incident and to spread in artificial stone inside, its luminous energy is by noctilucence or fluorescence composition efficient absorption, and because be dispersed with the luminescent layer of light-storing material etc. in the thickness that can guarantee to comprise, so can realize long-time, high brightness luminescent in artificial stone inside.When luminous, because of the good high brightness luminescent of transparent fine inorganic particle composition light transmission.
Transparency composition shared ratio in particulate composition total amount, as mentioned above, should be in 30~100 weight % scopes, but should be preferred 100% from the viewpoint of physical property such as artificial stone intensity and appearance design, also be preferred from the viewpoint of optical property certainly.Though be not limited to this numerical range, be lower than under 30% the situation, be difficult to obtain required light function.
Use is by the transparent inorganic aggregates of light-storing material or fluorescent material surface sintering during as a part of inorganic aggregates, at least a portion in the particulate composition, can use in the present invention the transparency and its surface go up sintering photism material such as light-storing material arranged.That is to say that part or all particulate composition is that the transparent inorganic aggregates that sintering has light-storing material or fluorescent material is gone up on the surface.As the particulate composition that this light transmission inorganic aggregates uses, for example can enumerate suitable species such as glass and silica.
The particulate composition of allocating in the composition, wherein 10~100 weight % part preferably has the transparent inorganic aggregates of above-mentioned light-storing material and/or fluorescent material surface coating.
To transparent inorganic aggregates, particularly the particulate composition is carried out sintering when covering, should on transparent fine particles composition particle surface, cover a few μ m~tens μ m, 5~50 μ m for example, preferred 20~40 μ m overlayers.More specifically say, can under 120~1200 ℃ of high temperature, carry out sintering and cover.
Light-storing material that is sintered and fluorescent material can be strontium aluminate, zinc sulphide or the like materials.
Said sintering operation, the known the whole bag of tricks that adopted with the past is identical, for example can be with transparent inorganic aggregates, for example above-mentioned particulate composition mixes with dispersion liquid or the thickener that light-storing material powder such as disperseing strontium aluminate obtains, dry back sintering.
Wherein, as mentioned above, wish to use fine inorganic particle composition among the present invention with specified particle size.That is to say that the fine inorganic particle component particle size should be in 5~70 order scopes as mentioned above.Use coloured or colourless inorganic particulate composition, wish color burn or subtract under the situation such as light, can have or not according to color to change granule size, but a large amount of great particulate compositions of difference that use will make product strength reduce, thereby should not adopt.
In addition, the granularity of particulate composition as mentioned above should be less than 100 orders.Must enable fully to enter between the particle of particulate composition.More specifically say preferred size 150~250 purpose particulate compositions.
Resinous principle can extensively be selected in various thermoset resins.
For example can enumerate single resin such as acryl resin, methacrylic resin, epoxy resin, unsaturated polyester resin or its potpourri etc., and both can be homopolymer, also can be multipolymer.From viewpoints such as the transparency, hardness and intensity, methacrylic resin, epoxy resin or its potpourri are the resins that is suitable for.The blending ratio of resinous principle should be lower than 15 weight % of total composition, below the preferred 10 weight %.For the particulate composition and the particulate composition that form above-mentioned framework ingredient, the effect of this resinous principle is that it is wrapped up, and is combined into the whole artificial stone that forms, and give goods with functions such as elasticity or tensile strength this moment.Should be restricted by particulate composition and particulate become the to grade usage ratio of the inorganic aggregates formed.That is to say % meter by weight, must be in more than the 85 weight %, preferably be in more than the 89 weight %.Product becomes fragile when surpassing 95 weight %, and the product that obtains is difficult to use.And product is too soft when being lower than 85 weight %, can not obtain the character of stone material, and this moment, its usable range was identical with resin plate.
This statement of facts, the composition outside particulate composition such as natural stone and the particulate composition, promptly resinous principle can not surpass 15% weight at most in goods.
When resinous principle surpassed 15 weight %, product became plastic products, and so-called artificial stone is nominal and is not had in fact material with regard to becoming.And if the resinous principle amount of allocating into is very few, though the degree of closeness of products appearance and natural stone increases, goods but become fragile, and are unsuitable for using.From this point of view, resinous principle is in 5~11 weight % scopes.
[formation of base material]
In accompanying drawing 1 and the accompanying drawing 2, when constituting the base material artificial stone of substrate portion (2), can adopt resin identical and inorganic material to form with above-mentioned cardinal principle.
For example, the base material raw material is divided into three kinds of compositions substantially.A kind of is fine inorganic particle composition as the 10-70 order granularity of major component, this composition can use from mineral such as silica, peridot, feldspar, pyroxene, micas, with natural rocks such as grouan, metamorphosed rocks, and the fine inorganic particle composition of selecting in pottery, glass and the metal etc. that is suitable for.
Can use the particulate composition of the following granularity of 100 orders simultaneously with this particulate composition.This particulate composition can be enumerated natural or artificial various particulate compositions.For example, the particulate composition that obtains easily such as lime carbonate, aluminium hydroxide.
In addition,, can also add compositions such as allocating the manganese dioxide adjusting tone and use, titania, zirconium silicate, iron oxide into, and give compositions such as antimony trioxide that flame retardancy uses, boron compound, bromine compounds as the part of this particulate composition.
The resinous principle that has as the third composition.Resinous principle can be from suitably selecting the thermoset resin on a large scale.
For example can enumerate acryl resin, methacrylic resin, epoxy resin, unsaturated polyester resin and combination resin thereof etc.These resins and above-mentioned can be homopolymer or multipolymer equally.Wherein from viewpoints such as the transparency, hardness and intensity, methacrylic resin, epoxy resin or its composition etc. are the resins that is suitable for.
Particulate compositions such as natural stone are the principal elements that the artificial stone outward appearance that obtains and physical property are exerted an influence.Particularly under the situation that a part is exposed, become the principal element that influences appearance color and pattern with other compositions.
The particulate composition is more tiny than particulate composition, the material of granularity below 100 orders, the particulate composition enters between the individual particle of particulate composition, fills the position in space between the particulate composition, can give the artificial stone that the obtains character with aspect such as firm, pliable and tough.Weight ratio between particulate composition and this particulate composition preferably is between 0.5: 1~5: 1.
And for the particulate composition and the particulate composition that form above-mentioned framework ingredient, the effect of resinous principle is that it is wrapped up, and makes it be combined into the whole artificial stone that forms, and give goods with functions such as elasticity or tensile strength this moment.
The proportion of composing of these compositions is important among the present invention.And the composition between resinous principle and other compositions is a particular importance.The high density product that the present invention can obtain to have compact tissue is a feature.Here so-called " high density " is meant that the particulate composition and the particulate composition that comprise among the artificial stone product all exist with high density, and its degree surpasses for example scope of density 2.2 these traditional artificial stones of gram/cubic centimetre.
That is to say that big more as the composition of particulate compositions such as natural stone in goods of aggregate element, the degree of closeness of goods and natural stone is high more, but can not be fixed when this ratio is excessive, and goods can not use.And also variation of the physical property that obtains goods, not anti-well-established law uses.
Too much the shortcoming that use particulate composition can not be fixed except generation, the goods that obtain are also lackluster, are difficult to be called stoneware.
Therefore, the amount ratio of particulate composition and particulate composition should be restricted.That is to say that its weight ratio must be preferably greater than 90% greater than 85%.If but this ratio surpasses 95%, then goods become fragile, and the goods that obtain are difficult to use.Otherwise when this ratio was lower than 85%, the goods that obtain were soft excessively, and the character of stone material will be lost, and usable range will be identical with resin plate.
This situation explanation, particulate composition and particulate composition compositions in addition such as natural stone, promptly resinous principle can not surpass the existence of 15% weight at most.
Resinous principle is in case surpass 15%, and product will become plastic articles, and so-called artificial stone is nominal and is not had in fact material with regard to becoming.Otherwise if the resinous principle amount of allocating into is very few, though products appearance and natural color degree of closeness strengthen, goods become fragile and are unsuitable for using.From this point of view, resinous principle is in 3~10 weight % scopes.
Therefore, in artificial stone composition of the present invention and the artificial stone as goods, part or all above-mentioned fine inorganic particle composition is a transparent grain, and its particle or fritter also can be to cover with inorganics or organism in advance.
This overlapping operation of transparency particulate composition can be achieved as follows: make it to solidify behind covering resin on this transparency particulate composition surface, perhaps cover water glass, pottery magnetic glaze and dead matter such as light-storing material, the ultraviolet material of absorption thereon with sintering process.No matter under which kind of occasion, all should on transparent fine particles composition particle surface, cover a few μ m~tens μ m, 5~50 μ m for example, the overlayer of preferred 20~30 μ m thickness.More specifically say, for example can use compositions such as acrylic resin, metha crylic resin, epoxy resin or unsaturated polyester resin, be heated under 150~300 ℃ of temperature, perhaps under irradiate light, make and cover these resin combinations on the particulate composition particle surface and make it curing, perhaps adopt water glass, magnetic glaze etc., the method for sintering is carried out the dead matter covering under 800~1100 ℃ of high temperature.
These cover processing, and the particulate composition that can make the effect of artificial stone aggregate is with respect to organizing all compatibilities to significantly improve.And, also can make the intensity increase by the mixing of particulate composition and resinous principle, skin hardness also improves.
The particulate composition uses aforesaid transparent natural stone etc. and to carrying out on its surface after above-mentioned hard material covers, when attrition process was carried out on the artificial stone product surface, this overlayer was by partial destruction.So, transparent fine inorganic particle composition particle and tectal on every side surface texture thereof that part is exposed will produce unique effect to the light reflection.
That is to say, after light incides in the transparent particulate composition, reflected, and then become sub reflector by transparent fine particles by the overlayer around it.The transmission of this light and reflex, to have essence different with reflex that traditional artificial stone only produces on the surface, thereby can give the deep sense of the artificial stoneware of the present invention with uniqueness.Obtain having the artificial stone of the high-quality and marble grain of certain serious deep sense.
Have above-mentioned tectal transparent fine particles composition, generally can account for and sneak into 10~100% of fine inorganic particle composition total amount in the composition.
Also must do special provision among the present invention to the fine inorganic particle component particle size.That is to say that the granularity of fine inorganic particle composition as mentioned above, should be 10~70 orders.Use has or not the particulate composition of color and wishes color burn or subtract under the situation such as shallow, though can change the particulate component particle size according to having or not of color, uses the great particulate composition of granularity difference will make the product strength deterioration in a large number, so should forbid.
On the other hand, the size of particulate composition particle as mentioned above, should be defined in below 100 orders.The particulate composition can fully be entered between the particulate composition particle.More specifically say, preferably use the particulate composition of 150~250 order granularities.
For artificial stone having high density material of the present invention, except special circumstances, important problem is that the composition of wishing these materials can be dispersed among any part of goods by homogeneous.
[casting]
The disaster prevention building material of above-mentioned artificial stone formed products form for example can adopt following casing process manufacturing.
<I〉with the building materials formed body of jut as luminous component
Accompanying drawing 3 is to illustrate manufacturing with the exemplary process process chart of jut shown in the accompanying drawing 1 (3) as the formed artificial stone of luminous component.
That is to say, accompanying drawing 3 illustrates a kind of like this manufacture method of building materials, wherein have figure or pattern jut (3) with its one on the plane of substrate (2), base material is made up of inorganic aggregates and resin, and at least a portion is noctilucence or luminiferous luminous component in the above-mentioned jut (3).
The trench portions (51) that on inner bottom surface, has the shaping dies (5) of the trench portions (51) corresponding with formed body jut (3), injection contains as at least a portion of inorganic aggregates and has the photosensitiveness of holding or follow the luminiferous noctilucence of UVA or epipolic light-storing material and fluorescent material and transparent inorganic aggregates, the perhaps potpourri (6) of the transparent inorganic aggregates of surface above-mentioned noctilucence of having gone up sintering or fluorescent substance, in shaping dies (5), inject the base material mixture (7) that contains inorganic aggregates then, the demoulding behind the cure under pressure, in case of necessity, utilize methods such as grinding or water injection to do surperficial roughening treatment, in order to make the formed artificial stone (1) that only has luminous component at above-mentioned jut (3).
When the patrix (8) that closes solidifies, for example can be at 5~100kgf/cm
2Pressurize under the face pressure, under 90~140 ℃ of temperature, heated 5~20 minutes simultaneously.
Form the potpourri (6) of luminous component and the potpourri (7) of formation substrate portion (2) with jut (3), integrally formed in above-mentioned cure under pressure operation.Therefore, the jut of luminous component (3) can not peeled off and be come off.And jut (3) also forms the object of high abrasion resistance because of its composition.
Surface grinding is not particularly limited with means, can adopt instruments such as grinding stone, emery cloth, abrasive band, perhaps carries out with lapping compounds such as polishing lapping compound, friction compounds.
As abrasive substance, can suitably adopt adamas, boron carbide, corundum, aluminium oxide, zirconia based on abrasive action, and based on the silica sand lapping compound of abrasive action, rauhkalk, aluminium oxide, chromium oxide, cerium oxide etc.
Among the present invention, alligatoring processing is carried out to the formed body surface in the back that is shaped, and the particulate composition is exposed from surface portion.
Finish the method for this purpose, at first can adopt selectivity to remove the method for resinous principle.That is to say that for example from shaping dies after the demoulding, to formed products jet surface water under high pressure, it is effective that original surface is carried out method for processing.
This processing is because of thickness, different and different with various conditions such as the distance of nozzle, processing forms, thereby do not add qualification.Usually, under 2~20 centimetres of thickness situations, can be from 2~50 centimetres of nozzle heights, with 50~1400 kilograms/cm
2Left and right sides hydraulic pressure injection water.Compare with handling natural stone, hydraulic condition is lower.
The existence of resinous principle that is to say, owing to can be carried out high-grade processing easilier.
Nozzle and system thereof that inject high pressure water is used are not particularly limited, and can adopt various model product.
Utilize this original surface processing, can realize the planarization or the alligatoring on surface, can make the artificial stone of certain deep texture through the jetting action of water.
Resinous principle exists can not make surface haze yet, and compares with using the medicine etch, and liquid waste processing is also easier.
Certainly, also can use organic solvent treatment surface part in case of necessity, make resinous principle softening or dissolve and its part is removed.
The organic solvent that use this moment, can select according to the resinous principle that uses, for example can enumerate halogenated hydrocarbons such as methylene chloride, methenyl choloride, carboxylic acid and carboxylates thereof such as acetic anhydride, ethyl acetate, butyl acetate, perhaps acetone, tetrahydrofuran, DMF, DMSO etc.
Formed body is immersed in these organic solvents, perhaps with the spraying of these organic solvents or make it to flow down, can from the surface remove softening or dissolve after resinous principle, make the surface form concaveconvex shape.
Also can utilize wire brush, cutting means etc., the resinous principle that hardness is low strikes off from surface portion, forms concaveconvex shape.
After utilizing above means to make surface coarsening and carrying out original surface processing, as mentioned above, utilize the method for surface grinding can obtain to have the surperficial texture of certain unique deep sense and gloss.
<II〉with the building materials formed body of embedded part as luminous component
Accompanying drawing 4 is illustrational to be with the representativeness casting autofrettage of embedded part (4) as the formed artificial stone (1) of luminous component.
That is to say, the manufacture method of a kind of formed body of these accompanying drawing 4 expressions, wherein the planar section at substrate (2) has the integrated embedded part (4) that presents figure or pattern form, base material is made up of inorganic aggregates and resin, has embedded the luminous component of being made up of light-storing material, fluorescent material in the said embedded part of at least a portion (4).
On inner bottom surface, have with formed body and embed in the shaping dies (5) of the corresponding projection (52) in groove position (4), injection contains the base material mixture (7) of inorganic aggregates, make the demoulding behind its curing or the semi-solid preparation, then in the groove that the formed body surface forms, injection is as at least a portion inorganic aggregates, contain light-storing material and fluorescent material, perhaps also contain transparent inorganic aggregates, perhaps the potpourri (6) that sintering has the transparent inorganic aggregates of above-mentioned light-storing material or fluorescent material is gone up on the surface, and make it to solidify, make the building materials formed body (1) that luminous component is only arranged at above-mentioned embedding position (4).
Make under the occasion in this way, lean on the solidification process of press molding can adopt and the enforcement of said method the same manner, and can equally suitably grind or the surface coarsening processing formed body (1) at last.Potpourri (6) and (7) are integrated according to the same manner.For example, in no matter above which kind of method,, adopt the surface under the situation of the transparent inorganic aggregates that light-storing material or fluorescent material cover as potpourri (6), through grind wait handle after, particle and tectal section thereof will expose.
Utilize this method can make the existing good characteristics of luminescence, the artificial stone of advantageous property and texture is arranged again.
That is to say, for example cover the fluorescent material layer of light-storing material or luminescence-utraviolet as if sintering on particulate composition surface, and milled processed is carried out on the artificial stone surface, then particulate composition particle and overlayer thereof will expose with form of fracture.So,, just can inject, reach inner sintering covering material place from the transparent fine grained surface of exposing from the light of external irradiation.
Under the good situations such as methacrylic resin of the transparency, light also can be well from all seeing through.
Therefore, incident light can enter luminous component inside, and can be luminous internally.
Therefore, extinction and hold light and just become possibility at short notice, and also luminescence efficiency also increases.
Though above example is to utilize artificial stone that the formation of disaster prevention building material of the present invention is described, utilizes the formation of light-storing material, fluorescent material or base material, also can further propose various other embodiments.
For example illustrate as follows.Example 1: for example making attached Fig. 1 and 2 with resin, pottery, glass, metal etc.
On the shown substrate portion (2), casting or go into luminous component (3)
Or (4).Consider between luminous component (3) and (4) and the base material
Adaptation, can select suitable resin, glass etc. as bonding agent.Example 2: on resin that the above-mentioned artificial stone base material with semi-cured state is the semi-cured state of representative, glass etc., be pressed into light-storing material and fluorescent material according to predetermined figure and pattern, perhaps they and the composition of bonding agent make it and base material formation one.Example 3: the potpourri direct pouring of base material and light-storing material and fluorescent material is shaped,
Make the disaster prevention building material goods.
No matter under which kind of embodiment, the present invention can both provide a kind of noctilucence or fluorescence disaster prevention building material.
These building materials can be used as various interior and exterior finishes materials and use, for example ground, courtyard, wall, partition, clothes hanger and frame, post etc., perhaps building materials such as residential equipment, furniture, for example Door and window frame, desk, counter top, handrail and stair etc., and the building materials of taking precautions against natural calamities of usefulness such as bathroom, kitchen, lavatory.Also can be used as the street finishing material and use, and finishing materials such as undergrond street, tube, railway station use,, can be also used as the braille block that welfare is used in addition perhaps with uses such as piece, post, wall, road, stair, bed, fences.
Constitute with forms such as artificial stone, glass, potteries under the situation of disaster prevention building material of the present invention, for example combination is allocated under the form of antiseptics such as silver, can be used as antibacterial product and use, under form, can further improve its surcharge with electric wave, electromagnetic wave shielding function.
Even above-mentioned various disaster prevention building materials of the present invention under the dark surrounds when disaster takes place, can clearly be indicated Evacuation Route and position, explosive area owing to its illuminating effect.And these building materials are owing to be to have the building materials of certain tone, shape and outward appearance and can mate with environment at ordinary times.In addition, even night at ordinary times can make it also to have that certain is ornamental.
Embodiment below is described.Certainly, the present invention is not subjected to any restriction of following examples.EXAMPLE Example 1
The building materials of the usefulness of taking precautions against natural calamities have been made according to the method for accompanying drawing 3.
That is to say, at first in the groove (51) of the degree of depth 6mm of shaping dies (5), injected potpourri (6) with following composition.
With the strontium aluminate light-storing material in 1000 ℃ of following sintering, 60 weight %
It is tectal to form the thick surperficial sintering of about 30 μ m
10~50 order silica powder
Mean grain size 250 purpose silica powder 30 weight %
Methyl methacrylate (MMA) 10 weight %
(containing 0.15% peroxide hardening agent)
Then in shaping dies (5), injected the base material mixture (7) of following composition.
10~70 order silicon, 20 weight %
The thick yellow uitramarine sintering of 30 μ m is arranged on the surface
Tectal 10~70 order silicas
Mean grain size 225 purpose aluminium-hydroxide powders 30 weight %
Methyl methacrylate (MMA) 8 weight %
(containing 0.15% peroxide hardening agent)
The mold (8) that closes is at 12kgf/cm
2Pressurization made it to solidify in 20 minutes under pressure and the 120 ℃ of temperature.
Thick 20 millimeters of substrate portion (2), block building materials (1) that jut (3) is high 6 millimeters have been obtained after the demoulding.
Use ciamond grinder that the surface of this block building materials (1) upper process part (3) is ground, make it highly be 5 millimeters.
On the block building materials (1) that obtain, the jut (3) through grinding has the noctilucence characteristics of luminescence, has good function when using as the position Direction Signs under dark surrounds.And substrate portion (2) is ornamental good and have the yellow tabular body of deep sense, even daytime is also beautiful, jut (3) can also use with the braille block as the blind person.
Check according to Japanese Industrial Standards JIS K-7112, proportion is 2.30.In addition, water-intake rate is 0.14%.In substrate portion (2) and the incorporate zone of jut (3), the characteristic of jut (3), promptly hardness shown in the table 1 and mar proof etc. are also good.
In addition, through acid resistance and the alkaline resistance test that 3% aqueous hydrochloric acid solution flooded in 8 hours and 3% sodium hydrate aqueous solution flooded in 8 hours, no abnormal.Embodiment 2
Use the following potpourri of forming (6), be shaped according to mode similarly to Example 1.
With the strontium aluminate light-storing material at about 1000 times sintering, 50 weight %
It is tectal to form the thick surperficial sintering of about 30 μ m
10~50 order silica powder
Mean grain size 250 purpose silica powder 20 weight %
Mean grain size 220 purpose strontium aluminate light-storing material powder 20 weight %
Methyl methacrylate (MMA) 10 weight %
(containing 0.2% peroxide hardening agent)
After jut (3) grinds with ciamond grinder and silit magnesium oxide class grinding stone, at 1200 kilograms/cm
2Only removed lip-deep resin part under the water expulsion pressure (0.8 millimeter of nozzle bore, 35 millimeters of jet lengths).
The artificial stone that obtains has deep sense and antiskid function usually, can be visual for a long time on whole thickness direction because of its noctilucence at night.
When having a power failure under abnormal conditions, this artificial stone building materials can be effective as noctilucence guiding sign building materials and use.Embodiment 3
Use the following potpourri of forming (6), be shaped according to mode similarly to Example 1.
10~60 order silicon, 60 weight %
Mean grain size 220 purpose aluminium-hydroxide powders 22 weight %
Mean grain size 200 purpose strontium aluminate light-storing materials 10 weight %
Methyl methacrylate (MMA) 8 weight %
(containing 0.15% peroxide hardening agent)
Obtained all good disaster prevention building material of physical property and luminescent properties equally.Embodiment 4
In the polymethyl methacrylate resin of allocating among the embodiment 1, there is 50% part to replace with bis-phenol glycidol ether (containing amine curing agent), and used the ester moulding of being furnished with the total amount of accounting for 2 weight % organic bromine fire retardants with composition (6) and (7), obtained with the embedding trench portions (4) of 4 millimeters of the degree of depth 16 millimeters thick formed artificial stones according to the method shown in the accompanying drawing 4 as luminous component.
Grind with adamas class grinding stone on the surface.
Obtained the disaster prevention building material that all good expression Evacuation Route of physical property, anti-flammability and luminescent properties is used.Embodiment 5
Form with embodiment 3 potpourris, make the residential land flooring, the road of taking refuge when this earth material is arranged on the precalculated position and can be used for representing that disaster takes place.Embodiment 6
Mean grain size 150~200 purpose strontium aluminate class light-storing materials and brown pigments are sneaked in the polymethyl methacrylate resin together, make the parts of dwelling house with clothes hanger.Evacuation Route in the time of can utilizing this clothes hanger parts to represent the disaster generation.
The possibility of utilizing on the industry
As mentioned above, the invention provides a kind of disaster prevention building material of noctilucence characteristic good. This building materials do not have Needing to safeguard, even for example fracture also can be luminous, be semi-permanent material, and wearability is also good. Appearance property is also good when in addition, usual.
In addition, in the situation about being consisted of by artificial stone, can provide a kind of artificial stone having high density building materials, this Kind of building materials have the graceful tone with certain deep sense and gloss, luminous component do not peel off, come off and Wear problem, and have excellent physical properties. The in addition manufacturing of this good goods and tradition product phase Ratio can be realized under low cost.
Claims (5)
1, a kind of disaster prevention building material, it is characterized in that representing that the two forms by light-storing material or fluorescent material or its for the figure of direction, position etc. or pattern, by with said light-storing material and fluorescent material casting or be embedded into and contain organic and/or inorganic materials or resin at least as integrated forming in the base material of constituent and in addition.
2, according to the described disaster prevention building material of claim 1, wherein said inorganic material is an at least a above material in natural stone, pottery, cement, metal and the glass.
3, according to the described disaster prevention building material of claim 1, wherein said resin is a thermoset resin.
4, according to the described disaster prevention building material of claim 1, wherein said light-storing material and fluorescent material are inorganic material.
5, according to the described disaster prevention building material of claim 1, wherein said light-storing material and fluorescent material are bonding agent with the resin.