CN1225299A - Combination hardening method for water glass sand by vacuum replacement-ester curing - Google Patents
Combination hardening method for water glass sand by vacuum replacement-ester curing Download PDFInfo
- Publication number
- CN1225299A CN1225299A CN 99101176 CN99101176A CN1225299A CN 1225299 A CN1225299 A CN 1225299A CN 99101176 CN99101176 CN 99101176 CN 99101176 A CN99101176 A CN 99101176A CN 1225299 A CN1225299 A CN 1225299A
- Authority
- CN
- China
- Prior art keywords
- sand
- ester
- special
- weight
- moulding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Based on VRH-CO2 vacuum displacement and dewaterring hardening, the present invention adds an improved self-hardening sand solidifier organic ester specially used for casting. The operation method consists of sequentially adding certain quantity of organic ester and water glass into new sand, mixing to form moulding sand, then evacuating vacuum and blowing CO2 treatment, and demoulding after hardening.
Description
The invention belongs to the molding and core making technology of casting.
Background technology of the present invention: 1. CO
2-water-glass sand hardening process.Characteristics: be the most general using method, by logical CO
2The dehydration sclerosis has the moulding sclerosis soon, and easy and simple to handle, cost is low, and adaptability is strong.Not enough point: waterglass addition height (general 〉=7%), molding sand retained strength height, collapsibility is poor, the cleaning difficulty of shaking out, if easily crack with water explosition blast cleaning self-care foundry goods, casting quality is poor, and the molding sand property deposited is poor, and winter, hard saturating property was poor, consumption CO
2Gas is many, regenerating used difficulty, discarded then contaminated environment.2. ester sodified water glass is from the hard technology of lacking.Characteristics: the eighties new technology, the alcohol that generates by organic ester dewaters from hard to waterglass is strong, has core sand intensity height, and waterglass adds few, and foundry goods shakes out and clears up better, and casting quality is good, and is easy and simple to handle, but old sand dry back usefulness, environmental pollution is seldom.Not enough point: waterglass and organic ester belong to not cast special use more, thus supporting weak effect, the molding sand process poor performance, firm time is long, and stripping time, adjustability was poor, and the hard saturating property of molding sand in winter is poor, is difficult to adapt to batch production on production.3. VRH-CO
2Water-glass sand vacuum displacement hardening process.Characteristics: by vacuum displacement, CO
2The dehydration sclerosis.It is few to have the waterglass of adding, logical CO
2Few, sand fluidity is good, and the up time is long, and casting quality is better, and the old sand dry back is with high, and environmentally safe is applicable to production line production.Not enough point: sand mold intensity is not high, and winter is relatively poor firmly thoroughly, and foundry goods easily produces defectives such as drop, burning into sand.The collapsibility of molding sand (core) is relatively poor.4. acid-curing furan resin self-hardening sand technology.Characteristics: the eighties new technology, harden by curing agent and resin reaction.Sand mold (core) intensity height, casting quality is good, and type (core) sand collapsibility is good, and foundry goods shakes out cleaning easily, and the old sand dry back is with high, and winter, hard saturating property was good, was suitable for production line production.Not enough point: high temperature thermoplasticity is poor, easily cracks for thin-walled, complex structure, steel-casting that the wall thickness difference is big, causes that easily case-carbonizing, sulfurizing cause defectives such as the miniature and pore in surface.The casting cost height.The harmful smoke contaminated environment that produces.
Purpose of design of the present invention: avoid the weak point in the background technology, design a kind of new moulding associating hardening technique, to solve the deficiency that exists in the background technology, be implemented in cast steel batch process aspect obtain cost low, easy and simple to handle, be convenient to production of machine moulding line or hand moulding production, and the high quality casting of environmentally safe.
Design of the present invention: 1, the present invention is at VRH-CO
2The vacuum displacement dehydration is hardened on the main basis, adds the special-purpose self-hardening sand curing agent of a kind of improved casting---the organic ester of number of patent application 97119081.X.Concrete operations are: be sequentially added into a certain amount of organic ester in fresh sand and waterglass is mixed into the moulding molding sand in moulding, moulding is blown CO through vacuumizing
2Handle the sclerosis back demoulding.2, the present invention is mainly used in Steel Castings, also can be used for steel-casting and non-ferrous casting production.The used roughing sand of the present invention is forsterite sand, quartz sand and other moulding sand, and the molding sand that mixes system both can be used as facing sand and also can be used as system sand.The present invention is mainly used on the production line, also can be used for hand moulding production.6, detailed design scheme: 1. vacuum displacement---ester sodified water glass sand is united hardening process, moulding constitutes waterglass with the component of molding sand, and to add weight be 2.0%～5.5% of roughing sand weight, the adding weight of special-purpose organic ester is 0.1%～2.2% of roughing sand weight, and it is 0～50% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic ester adds weight.2. vacuum is changed hardening process, be mixed into moulding by waterglass, special-purpose organic ester, roughing sand and be mixed into the moulding molding sand with molding sand or by waterglass, special-purpose organic ester, the fast ester of special-purpose organic ester, roughing sand, moulding vacuum remains on 0.0013～0.09Mpa, retention time 2～15min or moulding vacuum remain on 0.0013～0.09Mpa, retention time 2～15min is blown into CO
2Gas is blown into pressure P
CO2=0.1～0.5Mpa, time 3～10min.It is 2.0%～5.5% of roughing sand weight that waterglass adds weight, and it is 0.1%～2.2% of roughing sand weight that special-purpose organic ester adds weight, and it is 0～50% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic vinegar adds weight.
The present invention compares with background technology, implements the mould strength height that the back is obtained, the casting mold clear-cut, and cast(ing) surface is bright and clean, and is superior in quality.1. compare with the resin sand foundry goods, its quality is suitable, but associating hardening process castings production cost reduces about 20%, and non-environmental-pollution, steel-casting are not prone to defectives such as crackle, pore.2. with CO
2-water-glass sand hardening process is compared, and associating hardening process waterglass addition reduces 40-60%, CO
2It is over half that consumption reduces, and the molding sand high-temperature residual strength reduces 40-60%, and foundry goods shakes out cleaning easily, defective such as is difficult for cracking, and cast(ing) surface is bright and clean, and quality is good.Old sand reuse height.3. compare from hard technology with ester sodified water glass sand, the sand fluidity of associating hardening process is good, and the instant tensile strength of sand mold is that ester solidifies 8～10 times from hard instant tensile strength.Be equivalent to the tensile strength values after ester solidifies self-hardening sand 2h.Firm time is short, and stripping time, adjustability was good, was suitable for producing in batches on production line.4. with VRH-CO
2Hardening process is compared, mould strength height of the present invention.Sample tensile strength (instant, 1h, 2h) has improved 40～80%, and tensile strength (immediately) improves 20～50%, and surperficial stability improves 20～30%, and high-temperature residual strength reduces by 20～30%, and cast(ing) surface is bright and clean, has overcome VRH-CO
2The technology foundry goods is prone to defectives such as drop, burning into sand.
Embodiment of the present invention:
Embodiment of the present invention, its performance of used waterglass is: modulus: 2.0～2.4, density: 1.3～1.55g/cm
3.25 ℃, viscosity: 15～30CPs.25 ℃.
In the embodiment of the present invention, used its performance of special-purpose organic ester is:
Density: 1.1～1.2g/cm
3.25 ℃, viscosity:＜100MPs, ester content: 80～95%, residual acid amount :≤2%.
The invention process is in ZGMn13 railroad frog foundry goods, and the preferred version of molding sand preparation is:
| Roughing sand | Binding agent | Curing agent | |||
| Type | Weight | Type | Weight | Type | Weight |
| Forsterite sand | 100％ | Waterglass | ?2.5～ ?4.5％ | Special-purpose organic ester | ?0.13～ ?1.3％ |
And with adding the fast ester 0～50% of special-purpose organic ester season to regulate firm time.
VRH-CO of the present invention
2The preferred version of vacuum displacement is:
Vacuum remains on 0.00133～0.09MPa, and retention time 5～15min is blown into CO
2Time 3～10min, it is blown into pressure P
CO2=0.1～0.5MPa.
Embodiment 1: vacuum displacement---ester sodified water glass sand associating hardening process, and it is 2.0% of roughing sand weight that moulding constitutes waterglass adding weight with the component of molding sand, the adding weight of special-purpose organic ester is 0.1% of roughing sand weight.
Embodiment 2: vacuum displacement---ester sodified water glass sand associating hardening process, moulding constitutes waterglass with the component of molding sand, and to add weight be 5.5% of roughing sand weight, the adding weight of special-purpose organic ester is 2.2% of roughing sand weight, and it is 50% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic ester adds weight.
Embodiment 3: vacuum displacement---ester sodified water glass sand associating hardening process, moulding constitutes waterglass with the component of molding sand, and to add weight be 3.25% of roughing sand weight, the adding weight of special-purpose organic ester is 1.15% of roughing sand weight, and it is 25% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic ester adds weight.
Embodiment 4: vacuum conversion hardening process, be mixed into moulding by waterglass, special-purpose organic ester, roughing sand and be mixed into the moulding molding sand with molding sand or by waterglass, special-purpose organic ester, the fast ester of special-purpose organic ester, roughing sand, moulding vacuum remains on 0.0013Mpa, retention time 15min or moulding vacuum remain on 0.0013Mpa, retention time 15min is blown into CO
2Gas is blown into pressure P
CO2=0.1Mpa, time 10min.
Embodiment 5: vacuum conversion hardening process, be mixed into moulding by waterglass, special-purpose organic ester, roughing sand and be mixed into the moulding molding sand with molding sand or by waterglass, special-purpose organic ester, the fast ester of special-purpose organic ester, roughing sand, moulding vacuum remains on 0.09Mpa, retention time 2min or moulding vacuum remain on 0.09Mpa, retention time 2min is blown into CO
2Gas is blown into pressure P
CO2=0.5Mpa, time 3min.
Embodiment 6: vacuum conversion hardening process, be mixed into moulding by waterglass, special-purpose organic ester, roughing sand and be mixed into the moulding molding sand with molding sand or by waterglass, special-purpose organic ester, the fast ester of special-purpose organic ester, roughing sand, moulding vacuum remains on 0.045Mpa, retention time 8.5min or moulding vacuum remain on 0.045Mpa, retention time 8.5min is blown into CO
2Gas blows people's pressure P
CO2=0.3Mpa, time 6.5min.
Claims (6)
1, a kind of vacuum displacement---ester sodified water glass sand associating hardening process, it is characterized in that: moulding constitutes waterglass with the component of molding sand, and to add weight be 2.0%～5.5% of roughing sand weight, the adding weight of special-purpose organic ester is 0.1%～2.2% of roughing sand weight, and it is 0～50% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic ester adds weight.
2, a kind of vacuum conversion hardening process, it is characterized in that: be mixed into moulding by waterglass, special-purpose organic ester, roughing sand and be mixed into the moulding molding sand with molding sand or by waterglass, special-purpose organic ester, the fast ester of special-purpose organic ester, roughing sand, moulding vacuum remains on 0.0013～0.09Mpa, retention time 2～15min or moulding vacuum remain on 0.0013～0.09Mpa, retention time 2～15min is blown into CO
2Gas is blown into pressure P
CO2=0.1～0.5Mpa, time 3～10min.
3, vacuum displacement hardening process according to claim 2, it is characterized in that: it is 2.0%～5.5% of roughing sand weight that waterglass adds weight, it is 0.1%～2.2% of roughing sand weight that special-purpose organic ester adds weight, and it is 0～50% of roughing sand, waterglass, special-purpose organic ester weight sum that the fast ester of special-purpose organic vinegar adds weight.
4, vacuum displacement according to claim 1 and 2---ester sodified water glass sand associating hardening process, it is characterized in that: the moulding that is constituted can be used for steel-casting, ironcasting, non-ferrous casting with molding sand.
5, vacuum displacement according to claim 1 and 2---ester sodified water glass sand associating hardening process, it is characterized in that: the moulding that is constituted can be used as the preparation of facing sand, system sand with molding sand.
6, vacuum displacement according to claim 1 and 2---ester sodified water glass sand associating hardening process, it is characterized in that: roughing sand is forsterite sand, quartz sand or other moulding sand.