CN1224647C - Method of inorganic whisker surface treatment - Google Patents
Method of inorganic whisker surface treatment Download PDFInfo
- Publication number
- CN1224647C CN1224647C CN 200410015677 CN200410015677A CN1224647C CN 1224647 C CN1224647 C CN 1224647C CN 200410015677 CN200410015677 CN 200410015677 CN 200410015677 A CN200410015677 A CN 200410015677A CN 1224647 C CN1224647 C CN 1224647C
- Authority
- CN
- China
- Prior art keywords
- whisker
- inorganic
- crystal whisker
- coupling agent
- inorganic crystal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for treating the surface of inorganic whiskers. The method belongs to a material field and comprises: the surface of the inorganic whisker is inorganically coated: the whisker is mixed with water according to a solid content of 10% to be rapidly dispersed; a precursor is weighed and coated according to a coating amount of 5% to 10% to be prepared into diluted solution; precursor solution is slowly added in the state of stirring, and diluted sulfuric acid with a weight percentage of 0.1% is slowly added in a singly dropping mode till a pH value is from 8 to 10; the temperature of the product is preserved, and the product is aged for 5h to be filtered, washed and dried to obtain an inorganic whisker sample which is inorganically coated; the surface of the inorganic whisker is organically modified: a powdery coupling agent is used to be added to ethanol solution or water solution, and powder is added to be ultrasonically dispersed and stirred in a heat preservation mode; the product is filtered and dried to obtain the inorganic whisker sample which is modified by the coupling agent; the inorganic whisker sample is compounded in a melting and mixing mode; the melted and mixed whiskers are mixed with polymer mixed material at processing temperature and under the condition of mechanically stirring to obtain inorganic whisker / polymer composite material. The present invention has the advantages of low cost, simple technology, great enhancement of complex material mechanical performance and universality.
Description
Technical field
What the present invention relates to is a kind of inorganic crystal whisker surface-treated method, thereby specifically is the method that surface treatment at inorganic crystal whisker improves itself and macromolecule resin matrix affinity.Belong to the material field.
Background technology
Whisker is a kind of fiber that grows into the monocrystalline form under the manual control condition, general diameter is several microns of zero points, long tens microns, be a kind of ideal and flawless perfect crystal, because its diameter is very little, so that be difficult to be contained in the normal defective that occurs in the macrocrystal, thereby intensity approaches the theoretical value of perfect crystal.
Because the surface energy height of inorganic crystal whisker is easily reunited, the surface active groups number is less relatively, thereby and plastic substrate between interface interaction be the key factor that can decision whisker performance demonstrate fully in matrix material.Therefore, the effect of inorganic crystal whisker being carried out surface modification and taking various approach to improve modification is the difficult point and the focus of present metal whisker composite research.The direct coupling method effect of most researchers employing at present is not remarkable.Find by literature search, application number is: 88106414.9, publication number is: 1032152, name is called: the silicon carbide whisker-alumina composite material of alumina-coated, this patented technology is expressed as: the invention provides the brilliant engineering goods of strengthening the substrate of alumina substrate of a kind of SiC of having palpus, its outside surface also has alumina coating.Have now found that these goods can be used as the high speed roughing tool empiecement of steel.It is characterized by: carry out inorganic bag Al at the SiC whisker
2O
3Handle.This method Application Areas is very narrow, only limits to the SiC whisker, other inorganic particulates are not related to, and matrix used be metal matrix, be very different with polymer property.
Summary of the invention
The object of the invention is to overcome the deficiencies in the prior art, a kind of inorganic crystal whisker surface-treated method is provided, it is the method for improving after the inorganic crystal whisker surface modification with the polymeric matrix affinity, its composite materials property that obtains is improved a lot, and inorganic crystal whisker and polymer-based physical efficiency are compatible well.
The present invention is achieved by the following technical solutions, the present invention at first carries out inorganic coating to inorganic crystal whisker, adopt coupling agent to carry out surface organic modification then, the inorganic crystal whisker and the polymkeric substance of modification carried out melt blending, obtain the inorganic crystal whisker/polymer composites of good mechanical property.The present invention adopts the mode that inorganic coating-organic coupling modification combines first, bigger improvement the affinity of inorganic crystal whisker and polymer-based carbon.
Below the invention will be further described, method steps is as follows:
(1) the inorganic crystal whisker surface inorganic coats: whisker is pressed solid content 10% and is mixed with water, disperses fast.Take by weighing the coating presoma by covering amount 5%-10%, make dilute solution, under whipped state, slowly add precursor solution, the dilute sulphuric acid that single droplet method slowly adds 0.1% weight percent to pH between 8-10, insulation ageing 5h.The filtration washing drying obtains the inorganic crystal whisker sample after the inorganic coating;
(2) inorganic crystal whisker surface organic modification: the coupling agent consumption be after the inorganic coating modification the whisker powder quality 1%, at first coupling agent is joined in 95% ethanolic soln or the aqueous solution, add the whisker powder then, ultra-sonic dispersion.Keep temperature to stir at least 4 hours down for 60 ℃, filtration drying obtains the inorganic crystal whisker sample after coupling agent modified;
(3) melt blending is compound: melt blending whisker and polymer composition under the mechanical stirring, and blend under processing temperature, blending temperature and time are determined according to concrete polymkeric substance, obtain the inorganic crystal whisker/polymer composites of good mechanical property.
The whisker that the present invention was suitable for comprises most of inorganic crystal whiskers such as potassium titanate crystal whisker, ZnOw, aluminium borate whisker, calcium sulfate crystal whiskers.
The inorganic coating of the present invention comprises silicon, alclad, and used presoma is common chemical reagent.Bag silicon is generally used water glass, splashes into dilute sulphuric acid and adjusts the pH value; Alclad is generally used sodium aluminate, splashes into dilute sulphuric acid and adjusts the pH value.
Described bag silicon is to coat the fine and close SiO of one deck on the inorganic crystal whisker surface
2Film.Its process is: whisker is pressed solid content 10% and is mixed with water, disperses fast.5%-10% takes by weighing water glass by covering amount, is made into dilute solution, adds sodium silicate solution under whipped state, slowly splashes into dilute sulphuric acid then to the pH=9.5 value, insulation ageing 5h.The filtration washing drying obtains wrapping the whisker sample behind the silicon.
Described alclad is to coat the fine and close Al of one deck on the inorganic crystal whisker surface
2O
3Film.Its process is: whisker is pressed solid content 10% and is mixed with water, disperses fast.5%-10% takes by weighing sodium aluminate by covering amount, is made into dilute solution, adds sodium aluminate solution under whipped state, slowly splashes into dilute sulphuric acid then to pH=8.5, insulation ageing 5h.The filtration washing drying obtains wrapping the whisker sample behind the silicon.It is the same substantially to coat mechanism.
The organically-modified used coupling agent of the present invention is commercially available silane coupling agent or aluminate coupling agent or titanate coupling agent, selects suitable model for use according to whisker and polymer-based carbon volume property.The general formula of silane coupling agent is RSiX
3, R represents groups such as amino, sulfydryl, vinyl, epoxy group(ing), cyano group and methacryloxy in the formula, and these groups all have stronger response capacity with different matrix resins, the alkoxyl group (as methoxyl group, oxyethyl group etc.) that X representative can hydrolysis.The silane coupling agent trade mark commonly used has: KH-550, KH-560, KH-570 etc.Aluminate coupling agent also is widely used in plastics (polyvinyl chloride, ABS, polystyrene, polycarbonate.Polymeric amide, polyethylene, polypropylene), production field such as rubber, coating, laminated product, fire retardant, can improve the goods processing characteristics significantly, improve the quality of products.The aluminate coupling agent trade mark commonly used has: DL-411, DL-414 etc.
Compared with prior art, the raw material of utilization of the present invention be easy to get and production cost lower, production cost is lower, helps technology popularization; The surface modifying method operating process is simple, and industrialization feasibility height is fit to large-scale production; The composite materials property that obtains improves a lot, and higher utility is arranged; Present method is the modification that is used for numerous inorganic crystal whiskers and even inorganic particulate, thereby improves and macromolecule resin matrix affinity, has universality.
Embodiment
Provide following examples in conjunction with content of the present invention, the whisker sample surfaces that obtains coats the fine and close SiO uniformly of last layer
2Film, crystal whisker of hexa potassium titanate after the modification and polyolefinic compatible situation are improved greatly, occur bonding between whisker and the polymkeric substance, and affinity obviously improves.
Embodiment 1
1. the inorganic coating of potassium titanate crystal whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 5% (SiO
2/ TiO
2Weight ratio) takes by weighing water glass, be made into dilute aqueous soln B.Under 85 ℃, whipped state B is added among the A, the dilute sulphuric acid that slowly splashes into 0.1% weight percent is to pH=9.5 then, insulation ageing 5h.The filtration washing drying obtains wrapping the potassium titanate crystal whisker sample behind the silicon; 2. potassium titanate crystal whisker surface organic modification: consumption is after the silane coupling agent of inorganic crystal whisker powder 1% adds 95% ethanolic soln, to add the inorganic crystal whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the potassium titanate crystal whisker sample after silane coupler modified; 3. melt blending: take by weighing whisker and polyolefine by potassium titanate crystal whisker weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property crystal whisker of hexa potassium titanate/composite polyolefine material.
Crystal whisker of hexa potassium titanate/composite polyolefine material that aforesaid method obtains, notched Izod impact strength remained unchanged more substantially, and 5% and 10% prescription tensile strength improves about 14% and 40% respectively.
Embodiment 2
1. the inorganic coating of potassium titanate crystal whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 10% (SiO
2/ TiO
2Weight ratio) takes by weighing water glass, be made into dilute aqueous soln B.Under 85 ℃, whipped state B is added among the A, the dilute sulphuric acid that slowly splashes into 0.1% weight percent is to pH=9.5 then, insulation ageing 5h.The filtration washing drying obtains wrapping the potassium titanate crystal whisker sample behind the silicon; 2. potassium titanate crystal whisker surface organic modification: consumption is after the silane coupling agent of whisker powder 1% adds 95% ethanolic soln, to add the whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the potassium titanate crystal whisker sample after silane coupler modified; 3. melt blending: take by weighing whisker and polyolefine by potassium titanate crystal whisker weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property crystal whisker of hexa potassium titanate/composite polyolefine material.
Crystal whisker of hexa potassium titanate/composite polyolefine material that aforesaid method obtains, notched Izod impact strength remained unchanged more substantially, and 5% and 10% prescription tensile strength improves about 16% and 43% respectively.
Embodiment 3
1. the inorganic coating of potassium titanate crystal whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 7.5% (Al
2O
3/ TiO
2Weight ratio) takes by weighing sodium aluminate, be made into dilute aqueous soln B.Under 85 ℃, whipped state B is added among the A, the dilute sulphuric acid that slowly splashes into 0.1% weight percent then is to pH=8.5, insulation ageing 5h.The filtration washing drying obtains the potassium titanate crystal whisker sample behind the alclad; 2. potassium titanate crystal whisker surface organic modification: consumption is after the aluminate coupling agent of inorganic crystal whisker powder 1% adds 95% ethanolic soln, to add the whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the potassium titanate crystal whisker sample after the aluminate coupling agent modification; 3. melt blending: take by weighing whisker and polyolefine by potassium titanate crystal whisker weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property crystal whisker of hexa potassium titanate/composite polyolefine material.
Crystal whisker of hexa potassium titanate/composite polyolefine material that aforesaid method obtains, notched Izod impact strength remained unchanged more substantially, and 5% and 10% prescription tensile strength improves about 17% and 45% respectively.
Embodiment 4
1. the inorganic coating of aluminium borate whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 5% (SiO
2/ B
2O
3Weight ratio) takes by weighing water glass, be made into dilute aqueous soln B.Under 85 ℃, whipped state, B is added among the A, slowly splash into 0.1% dilute sulphuric acid (wt%) then, insulation ageing 5h to pH=9.5.The filtration washing drying obtains wrapping the aluminium borate whisker sample behind the silicon; 2. aluminium borate whisker surface organic modification: consumption is after the silane coupling agent of inorganic crystal whisker powder 1% adds 95% ethanolic soln, to add the whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the aluminium borate whisker sample after silane coupler modified; 3. melt blending: take by weighing whisker and polyolefine by aluminium borate whisker weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property aluminium borate whisker/composite polyolefine material.
Aluminium borate whisker/composite polyolefine material that aforesaid method obtains, notched Izod impact strength remained unchanged more substantially, and 5% and 10% prescription tensile strength improves about 12% and 36% respectively.
Embodiment 5
1. the inorganic coating of aluminium borate whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 10% (Al
2O
3/ B
2O
3Weight ratio) takes by weighing sodium aluminate, be made into dilute aqueous soln B.Under 85 ℃, whipped state B is added among the A, the dilute sulphuric acid that slowly splashes into 0.1% weight percent is to pH=8.5 then, insulation ageing 5h.The filtration washing drying obtains the aluminium borate whisker sample behind the alclad; 2. aluminium borate whisker surface organic modification: consumption is after the aluminate coupling agent of whisker powder 1% adds 95% ethanolic soln, to add the whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the aluminium borate whisker sample after the aluminate coupling agent modification; 3. melt blending: take by weighing whisker and polyolefine by aluminum borate weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property aluminium borate whisker/composite polyolefine material.
Aforesaid method obtain aluminium borate whisker/composite polyolefine material, notched Izod impact strength remained unchanged more substantially, 5% and 10% the prescription tensile strength improve about 20% and 47% respectively.
Embodiment 6
1. the inorganic coating of aluminium borate whisker: whisker is pressed solid content 10% and is mixed with water, disperses fast, gets dispersion liquid A.Press covering amount 7.5% (Al
2O
3/ B
2O
3Weight ratio) takes by weighing sodium aluminate, be made into dilute aqueous soln B.Under 85 ℃, whipped state, B is added among the A, slowly splash into 0.1% weight percent dilute sulphuric acid then, insulation ageing 5h to pH=8.5.The filtration washing drying obtains the aluminium borate whisker sample behind the alclad; 2. aluminium borate whisker surface organic modification: consumption is after the aluminate coupling agent of inorganic crystal whisker powder 1% adds 95% ethanolic soln, to add the whisker powder again, and mixed slurry is carried out ultra-sonic dispersion.Keep 60 ℃ to stir 0.5h, filtration drying obtains the aluminium borate whisker sample after the aluminate coupling agent modification; 3. melt blending: take by weighing whisker and polyolefine by aluminum borate weight percent 5%, 10%, stir melt blending whisker and PO mixed powder under the mechanical stirring, 200 ℃ of processing temperatures, 10 minutes blend time, obtain good mechanical property aluminium borate whisker/composite polyolefine material.
Aluminium borate whisker/composite polyolefine material that aforesaid method obtains, notched Izod impact strength remained unchanged more substantially, and 5% and 10% prescription tensile strength improves about 21% and 49% respectively.
Claims (6)
1, a kind of inorganic crystal whisker surface-treated method, it is characterized in that, at first inorganic crystal whisker is carried out inorganic coating, adopt coupling agent to carry out surface organic modification then, the inorganic crystal whisker and the polymkeric substance of modification are carried out melt blending, obtain inorganic crystal whisker/polymer composites, method steps is as follows:
(1) the inorganic crystal whisker surface inorganic coats: whisker is pressed solid content 10% and is mixed with water, disperse fast, take by weighing the coating presoma by covering amount 5%-10%, make dilute solution, under whipped state, slowly add precursor solution, the dilute sulphuric acid that single droplet method slowly adds 0.1% weight percent to pH between 8-10, insulation ageing 5h, the filtration washing drying obtains the inorganic crystal whisker sample after the inorganic coating;
(2) inorganic crystal whisker surface organic modification: the coupling agent consumption be after the inorganic coating modification the whisker powder quality 1%, at first coupling agent is joined in the ethanolic soln or the aqueous solution, add the whisker powder then, ultra-sonic dispersion, insulated and stirred, filtration drying obtain the inorganic crystal whisker sample after coupling agent modified;
(3) melt blending is compound: melt blending whisker and polymer composition under the mechanical stirring, and blend under processing temperature, blending temperature and time are determined according to concrete polymkeric substance, obtain the inorganic crystal whisker/polymer composites of good mechanical property.
2, inorganic crystal whisker surface-treated method according to claim 1 is characterized in that, described inorganic coating is bag silicon or alclad, used presoma is common chemical reagent, and bag silicon water glass splashes into dilute sulphuric acid and adjusts the pH value, the alclad sodium aluminate splashes into dilute sulphuric acid and adjusts the pH value.
3, inorganic crystal whisker surface-treated method according to claim 2 is characterized in that, described bag silicon is to coat the fine and close SiO of one deck on the inorganic crystal whisker surface
2Film, its process is: whisker is pressed solid content 10% and is mixed with water, disperse fast, 5%-10% takes by weighing water glass by covering amount, be made into dilute solution, under whipped state, add sodium silicate solution, slowly splash into dilute sulphuric acid then to the pH=9.5 value, insulation ageing 5h, the filtration washing drying obtains wrapping the whisker sample behind the silicon;
Described alclad is to coat the fine and close Al of one deck on the inorganic crystal whisker surface
2O
3Film, its process is: whisker is pressed solid content 10% and is mixed with water, disperse fast, 5%-10% takes by weighing sodium aluminate by covering amount, be made into dilute solution, under whipped state, add sodium aluminate solution, slowly splash into dilute sulphuric acid then to pH=8.5, insulation ageing 5h, the filtration washing drying obtains the whisker sample behind the alclad.
4, inorganic crystal whisker surface-treated method according to claim 1 is characterized in that, described inorganic crystal whisker surface organic modification, used coupling agent are a kind of in silane coupling agent, aluminate coupling agent, the titanate coupling agent.
5, according to claim 1 or 4 described inorganic crystal whisker surface-treated methods, it is characterized in that, described organically-modified in, the coupling agent consumption be after the inorganic coating modification the whisker powder quality 1%, at first coupling agent is joined in 95% ethanolic soln, add the whisker powder then, ultra-sonic dispersion, keep temperature to stir at least 4 hours down for 60 ℃, filtration drying obtains the inorganic crystal whisker sample after coupling agent modified.
6, inorganic crystal whisker surface-treated method according to claim 1 is characterized in that, is applicable to potassium titanate crystal whisker, ZnOw, aluminium borate whisker, calcium sulfate crystal whiskers.