CN1219520A - Dry mortar for construction - Google Patents
Dry mortar for construction Download PDFInfo
- Publication number
- CN1219520A CN1219520A CN97107227A CN97107227A CN1219520A CN 1219520 A CN1219520 A CN 1219520A CN 97107227 A CN97107227 A CN 97107227A CN 97107227 A CN97107227 A CN 97107227A CN 1219520 A CN1219520 A CN 1219520A
- Authority
- CN
- China
- Prior art keywords
- mortar
- construction
- weight
- cement
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A dry mortar for building is prepared from cement (10-25 wt.%), sand (70-85), flyash (1.5-9) and activating agent for mortar (0.5-6) through stirring in mixer, unloading, inspection and packaging. Its advantages include simple process, saving cement, and high strength.
Description
What the present invention relates to is a kind of dry mortar for construction and preparation method thereof, is specially adapted to construction cement mortar and the building mixed mortar and the highway bridge and culvert mortar of various labels.
Construction cement mortar, building mixed mortar are used for construction work, and the highway bridge and culvert mortar is used for highway bridge, culvert, pond.Because mortar material is purchased respectively, wherein main raw cement, sand are gathered materials on the spot mostly, buy nearby, do not make the mensuration of constituent content before the use basically, cause the mortar quality very unstable, even therefore cause accident resulting from poor quality of projects.And sand and ash all be in bulk, causes working-yard and in transit dust pollution, influence ecological environment and health of human body.Increase the pressure of place, working-yard and warehousing simultaneously.
The purpose of this invention is to provide a kind of dry mortar for construction and preparation method thereof, the preparation of mortar is under the prerequisite of basicly stable material, through the proportioning of science mix flyash and add can the replacing whole mixed mortar in lime material and excite flyash activity and the active Activting agent for mortar of mortar material, complete processing is simple, easy and simple to handle, save cement, save the nature mineral resources.
Dry mortar for construction takes following scheme to realize: dry mortar for construction is mixed and is formed by cement, sand, flyash, Activting agent for mortar according to a certain ratio.
The dry mortar for construction proportioning raw materials is
Cement 10-25% (weight)
Sand 70-85% (weight)
Flyash 1.5-9% (weight)
Activting agent for mortar 0.5-6% (weight)
Wherein Activting agent for mortar is made through mixing to stir by by weight ratio alkali lignin colliery powder or red-mud coal ash auxiliary agent.
The Activting agent for mortar proportioning raw materials is
Alkali lignin 5-10% (weight)
Colliery powder or red mud 60-70% (weight)
Flyash 5-15% (weight)
Auxiliary agent 15-25% (weight)
Wherein auxiliary agent is stirred and is made by by weight ratio ethyl cellulose, Vltra tears aluminum oxide, ferric oxide mixing.
The auxiliary agent proportioning raw materials is:
Ethyl cellulose 1-5% (weight)
Vltra tears 4-10% (weight)
Aluminum oxide 50-65% (weight)
Ferric oxide 20-35% (weight)
The dry mortar for construction process for making:
By proportioning raw materials weighing cement, sand, flyash, Activting agent for mortar, the input stirrer stirred 3-8 minute, with stir in the mortar blanking, test package product.
The processing units that dry mortar for construction adopts is simple and crude; complete processing is simple; operative technique is easy; the product weight of producing is stable; good physical performance; every cubic metre of mortar ratio is saved cement 10-35% with the label mortar; improve intensity 30-50% simultaneously; in mixed mortar, all save stone sand; save the nature mineral resources; the integrated dust pollution that reduces the working-yard of building mortar material; the 15-45% that the direct digestibility and utilization flyash of mortar is cement amount for the flyash digestion process provides wide channel, reduces and pollutes; the protection environment has higher technical economic benefit and social benefit.
Embodiment 1, takes by weighing raw material cement 10Kg (proportioning is 10%) by weight ratio, sand 80Kg (proportioning is 80%), flyash 5Kg (proportioning is 5%), Activting agent for mortar 5Kg (proportioning is 5%) is standby, and load weighted raw material is all imported stirrer, stirred 4 minutes, the blanking test package becomes product.
Embodiment 2, take by weighing raw material cement 25Kg (proportioning is 25%) by weight ratio, sand 70Kg (proportioning is 70%), flyash 4Kg (proportioning is 4%), Activting agent for mortar 1Kg (proportioning is 1%) is standby, and load weighted raw material is all imported stirrer, stirred 6 minutes, the blanking test package becomes product.
The dry mortar for construction ultimate compression strength that adopts the present invention to make is M15, breaks through the standard of the high grade M10 of building mortar, for development Highrise buildings dedicated mortar is laid a good foundation.
Claims (2)
1, a kind of dry mortar for construction is characterized in that being made up of according to a certain ratio cement, sand, flyash, Activting agent for mortar mixing.
2, dry mortar for construction according to claim 1 is characterized in that the dry mortar for construction proportioning raw materials is:
Cement 10-25% (weight)
Sand 70-85% (weight)
Flyash 1.5-9% (weight)
Activting agent for mortar 0.5-6% (weight)