CN1204553A - Organotin sulfonate catalysts and their manufacture method - Google Patents

Organotin sulfonate catalysts and their manufacture method Download PDF

Info

Publication number
CN1204553A
CN1204553A CN98115488.3A CN98115488A CN1204553A CN 1204553 A CN1204553 A CN 1204553A CN 98115488 A CN98115488 A CN 98115488A CN 1204553 A CN1204553 A CN 1204553A
Authority
CN
China
Prior art keywords
catalyst
formula
reactant
general formula
composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN98115488.3A
Other languages
Chinese (zh)
Other versions
CN1185239C (en
Inventor
S·R·塞沙德赖
W·D·霍尼克
M·H·吉特利茨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Arkema Inc
Original Assignee
Elf Atochem North America Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Elf Atochem North America Inc filed Critical Elf Atochem North America Inc
Priority to CNB981154883A priority Critical patent/CN1185239C/en
Publication of CN1204553A publication Critical patent/CN1204553A/en
Application granted granted Critical
Publication of CN1185239C publication Critical patent/CN1185239C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Dual cure organotin salts of strong organic acids, the use of such salts as catalysts and an improved process for producing the catalysts are provided. The catalysts are capable of effectively catalyzing esterification and transesterification reactions and urethane, silicone, melamine, ester and acrylic forming reactions and can simultaneously catalyze more than one reaction in a mixture of urethane, silicone, amino, ester and acrylic polymer forming reactants to produce a polymer mixture.

Description

Organotin sulfonate catalysts and their and manufacture method thereof
The polymer that the present invention relates to organotin sulfonate catalysts and their, makes with organotin catalysts and the preparation method of organotin catalysts.
Catalyst is usually used in the polymerization or the cross-linking reaction of monomer or resinous substances, to form polymer.Catalyst, polymerizable components and other additive can be coating, particle, goods, solution or dispersion form.These compositions can " pure " composition, does not promptly have solvent or carrier to have processed and polymerization down, is disposed and polymerization with organic solution or aqueous dispersion or water and milk composition.Every kind of composition all has its merits and demerits.
When selecting used special catalyst, the chemical property of polymerizable components is a principal element.Yet, there is not experiment confirm, just be difficult to predict the applicability of catalyst.The catalyst of usually effectively a kind of reaction of catalysis (forming reaction as polyether polyols with reduced unsaturation) can not be applicable to the dissimilar reaction of catalysis (as the butylated melamines polymerisation) well.Therefore, when polyurethane forms reactant and polyamines (as melamine) and forms reactant and be blended in a kind of ingredients, need to add two kinds of different catalyst, a kind of catalyze polyurethane forms reaction, another kind of catalysis melamine forms reaction, and two kinds of different reactions can be carried out simultaneously with reasonable comparable reaction rate.
More known poly-tin oxygen alkane, and confirmed that some reaction is had catalytic activity, for example referring to:
" distannoxane reverse micelle type catalyst, to the novel solvent effect of ester exchange reaction speed " JunzoOtera, Shingi Ioka; With Hitosi Nozaki, Journal of Organic Chemistry, 1989,54,4013-4014.
" the novel template effect of Distannoxane catalysts in efficient ester exchange reaction and the esterification ", JunoOtera, Nobuhisa Dan-oh and Hitosi Noaki, Journal of Organic Chemistry, 1991,56,5307-5311.
Though disclosed poly-tin oxygen alkane, its sulfonate derivatives does not also occur in the prior art.For example, United States Patent (USP) 2,720,507 have disclosed the organo-tin compound that many kinds allegedly can be used as the catalyst for preparing polyester.Yet, do not disclose poly-tin oxygen alkyl sulfonate.
United States Patent (USP) 3,681,271 have disclosed the catalyst when three tin oxygen alkane are used as the preparation polyurethane foamed material.But do not disclose organotin sulfonate.
United States Patent (USP) 3,676,402 have disclosed eight tin alkyl oxygen alkane as the catalyst in the polyurethane system that contains blocked isocyanate.But do not disclose organotin sulfonate.
United States Patent (USP) 3,194,770 have disclosed many kinds of organo-tin compounds as Application of Catalyst in the hardening composition (particularly foamed material).Disclose tin oxygen alkane but do not disclosed poly-tin oxygen alkyl sulfonate.
Now disclosed monokaryon (monomer) organotin sulfonate composition, and disclosed it as the polyurethane foam Application of Catalyst.For example:
United States Patent (USP) 3,095,434 have disclosed many two and three organotin sulfonate, and have described the application as pesticide.Also disclosed the catalyst applications that is used for polyurethane foam.
United States Patent (USP) 4,286,073 claimed two and trialkyltin sulfonate as the polyurethane foam catalyst.
United States Patent (USP) 4,611,049 has disclosed the manufacture method of aromatic polyester.Catalyst can be the organo-tin compound that uses with the sulfonic acid co-catalyst, but catalyst and co-catalyst do not constitute organotin sulfonate.Do not disclose the ability of the simultaneously effective several different polymerisations of catalysis of monokaryon organotin sulfonate.
The invention provides can distinguish or catalytic polymerization, esterification, ester exchange reaction and condensation reaction simultaneously effectively in the organotin sulfonate catalysts and their of reaction more than.Novel organotin sulfonate catalysts and their is provided, and it comprises and contains organic sulfonic polysiloxanes salt, corresponding to following general formula:
Figure 9811548800061
Each R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula;
Each R 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, condition is R 1At least a selection be OSO 2R, the R in the formula have above-mentioned identical implication;
Each R 2Be selected from respectively and R and R 1Identical group;
N is that mean value is the integer of 0-20;
X represents the quantity in conjunction with water, and x can be low to moderate 0, when this catalyst is in the aqueous solution, and the x approach infinity.
Above-mentioned general formula is called " general formula 1 " sometimes.
The catalytic activity of the monomer organotin that has also disclosed above-mentioned expansion general formula 1 and represented with following general formula and two abilities to cure:
Figure 9811548800062
R, R in the formula 2Have the implication identical, each R with x with above-mentioned general formula 1 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, the R in the formula has above-mentioned identical implication, and condition is at least one R 1Derived from pKa less than 1 organic acid (being called general formula 2 later on).
Found that catalysis and two extend type that solidifies the general formula I of purposes are:
Figure 9811548800071
Each R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula;
Each R 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, the R in the formula has above-mentioned identical implication, and condition is at least one R1 derived from pKa less than 1 organic acid;
Each R 2Be selected from respectively and R and R 1Identical group;
N is that mean value is the integer of 0-20;
X represents the quantity in conjunction with water, and x can be low to moderate 0, when this catalyst dissolution is in the aqueous solution, and the x approach infinity.
Above-mentioned general formula is called " general formula 1 of expansion " sometimes.The difference of general formula 1 and expansion general formula 1 is R 1Definition.In expansion general formula 1, at least one R 1Must be derived from pKa less than 1 organic acid, and the derivative of organic acid is confined to OSO in the general formula 1 2R.Therefore, expansion general formula 1 comprises all compounds and the R of general formula 1 1Value is different from OSO 2The compound of R.
Find also that now the organo-tin compound of general formula 1, expansion general formula 1 and general formula 2 is an above polymerisation of catalytic preparation polyurethane, polyureas, polysiloxanes or amino polymer simultaneously.Catalysis simultaneously more than one this reaction be called " two curing " in this application.
Also provide water and at least a other polar solvent to prepare the novel method of general formula 1, expansion general formula 1 and general formula 2 compounds.
Novel organotin sulfonate is the poly-tin oxygen alkane salt of the organic acid represented with general formula 1.Have now found that the organo-tin compound of representing with general formula 1, expansion general formula 1 and general formula 2 is the good catalyst of the polymerisation of esterification, ester exchange reaction or preparation polyurethane, polyureas, polysiloxanes and amino polymer.Though organotin catalysts of the present invention can be represented with above-mentioned general formula, obtains the mixture of organo-tin compound during preparation.This mixture meets above-mentioned structural formula with reasoning by analysis, and wherein n and x are mean value.The analysis result of The compounds of this invention is consistent with the structure of representing with general formula 1, expansion general formula 1 or general formula 2, and this analysis result is also with consistent with the following comparable compound of representing than empirical formula simultaneously.It is believed that said structure formula and empirical formula are of equal value for the objective of the invention is.X value in general formula 1, expansion general formula 1 and the general formula 2 can marked change, for example, the mean value of x can be 0-250, for the water-soluble substances of general formula 1, expansion general formula 1 and general formula 2, the upper limit of x can be than 250 much bigger, and approach infinity in the aqueous solution.In the aqueous solution, general formula of equal value is not have " x (H 2O) " general formula.
At least one R in general formula 1, expansion general formula 1 and the general formula 2 1Better be selected from as next group:
(a) OSO 2R, R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula;
(b) RCOO, R is an alkyl or aryl in the formula, contains at least one F of bonding, Cl, Br, I, CN mutually with it with carbon atom that the COO group connects;
(c) RPO 3H, R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula;
(d) RCrO 4H, R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula;
(e) F; NO 3ClO 4(NO) 2C 6H 2OH.
R in expansion general formula 1 or general formula 2 1When being selected from preferred this group, except when to select be F, NO 3Or ClO 4In addition, just satisfied at least one R in the general formula 1Derived from the requirement of pKa less than 1 organic acid.R 1Most preferred selection is p-methyl benzenesulfonic acid root or methanesulfonate.R and R 2The preferred selection is butyl.Preferred n value is 0-3 in general formula 1 and the expansion general formula 1.
Synthetic
United States Patent (USP) 3,094 has disclosed the synthetic method of single tin oxygen alkyl sulfonate of representing with general formula 2 in 434.This patent reference is incorporated among the present invention.
Synthetic with following several distinct methods with the poly-tin oxygen alkyl sulfonate that general formula 1 and expansion general formula 1 are represented, for example:
1. 130.0 gram (0.52 mole) Dibutyltin oxides (DBTO), 99.34 gram (0.52 mole) hydration p-methyl benzenesulfonic acid and heptane are joined in 1 liter of flask that thermometer, dasher, Dean-Rodney Stark separator and condenser are housed.Under stirring this mixture is added hot reflux.With the way of distillation remove in water that dereaction produces and the p-methyl benzenesulfonic acid in conjunction with water.Condensed vapor collection is removed the water of sub-cloud in Dean-Rodney Stark separator, allow the organic facies on upper strata return in the reaction bulb.
Reflux after 3 hours, remove thermal source, allow mixture be cooled to room temperature.Filter out solid, and be allowed to condition in 60 ℃ of vacuum dry 12 hours.This solid product has " gluing " consistence.The analysis result of product is as follows:
Analyze: measured value
%Sn???????????28.8
Acid number 134 (milligram KOH/ gram)
%H 2O???????????2.74????????????(Karl-Fisher)
%LOD 0.59 (100 ℃, 75 torrs, 2 hours)
Produce the poly-tin oxygen alkane that available general formula I is represented, wherein R and R like this 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root, n is 0-0.1, and x is 0-0.3, same, and the analysis result of this product and empirical formula are R 2SnAO-[R 2SnO] x-SnR 2A (H 2O) nPoly-tin oxygen alkane consistent, all R are butyl in the formula, A is the derivative of p-methyl benzenesulfonic acid root, organic acid, x is 0-0.1, n is about 0.3.No matter product (as the product that makes and use above-mentioned analytical method to identify with above-mentioned synthetic method) is to represent with empirical formula, still represent that with general formula 1 they are of equal value for purpose of the present invention.
2. 124.45 gram (0.50 mole) Dibutyltin oxides, 95.11 gram (0.50 mole) hydration p-methyl benzenesulfonic acid, 150.0 gram 2-propyl alcohol and 150 gram deionized waters are joined in 1 liter of flask that thermometer, dasher and cooler are housed.Under stirring this mixture is added hot reflux, and keep refluxing 1 hour.Stop heating, allow reactant mixture be cooled to about 25 ℃, filter out solid product, and be allowed to condition in 50 ℃, 50 torr vacuum dry 2.5 hours.Opposite with synthetic 1 product, the product that produces in the mixed solvent system of water and organic polar solvent is easy to filter, and is easy to be dried to the crystalline particulate solid of non-" viscosity ".
Analyze: measured value
%Sn???????????27.3
Acid number 128 (milligram KOH/ gram)
%H 2O?????????8.46????????????(Karl-Fisher)
%LOD 5.64 (100 ℃, 75 torrs, 2 hours)
Analysis result confirms that this product is the poly-tin oxygen alkane of representing with general formula 1, and all R are butyl, all R 1Be the p-methyl benzenesulfonic acid root, the mean value of n is 0-0.1, and the value of x is 3.1.Equally, analysis result and empirical formula are R 2SnAO-[R 2SnO] x-SnR 2A (H 2O) nPoly-tin oxygen alkane product consistent, all R are butyl in the formula, A is the derivative of organic acid and is the p-methyl benzenesulfonic acid root that x is 0-0.2, n is about 3.
3. 124.44 gram (0.50 mole) Dibutyltin oxides, 95.11 gram (0.50 mole) hydration p-methyl benzenesulfonic acid, 150.0 gram 2-propyl alcohol and 150 gram deionized waters are joined in 1 liter of flask that thermometer, dasher and cooler are housed.Under stirring this mixture was added hot reflux 1 hour.Stop heating, allow reactant mixture be cooled to about 25 ℃, filter out solid product, and be allowed to condition in 80 ℃, 50 torr vacuum dry 8 hours.This product is easy to filter, and is easy to be dried to the crystalline particulate solid of non-" viscosity ".
Analyze: measured value
%Sn???????????28.3
Acid number 131 (milligram KOH/ gram)
%H 2O???????????4.28????????????(Karl-Fisher)
%LOD 1.87 (100 ℃, 75 torrs, 2 hours)
Produce the poly-tin oxygen alkane of representing with general formula 1 like this, all R are butyl, all R 1Be the p-methyl benzenesulfonic acid root, the mean value of n is 0-0.1, and the value of x is 1.0.Equally, the analysis result of this product and empirical formula are R 2SnAO-[R 2SnO] x-SnR 2A (H 2O) nPoly-tin oxygen alkane consistent, all R are butyl in the formula, A is the derivative of organic acid, and is the p-methyl benzenesulfonic acid root, x is 0-0.2, n is about 1.
Shown in synthetic method 2 and 3, preferred synthetic method is used at least two kinds of polar solvents.A kind of solvent better is a water, and another kind of polar solvent is alcohol, particularly C 1-C 5Aliphatic alcohol is specially methyl alcohol, ethanol, propyl alcohol and butanols (comprising isomers).The synthetic method of carrying out in the solvent mixture of water and another kind of at least organic polar solvent produces the crystal type organo-tin compound of representing with general formula 1, expansion general formula 1 and general formula 2, and this organo-tin compound has allows this compound be easy to be dried to the peculiar property of non-sticky crystalline powder.Water better account for the polar solvent mixture at least about 25%, preferably account for 50%.
Esterification and ester exchange reaction
At least one R in general formula 1, expansion general formula 1 or general formula 2 1Be OSO 2During R, the organotin sulfonate that is produced (poly-tin oxygen alkane, monomer tin oxygen alkane or organotin sulfonate) is except being the effective catalyst of polyurethane, siloxanes and amino polymerisation or condensation reaction or the effective catalyst of esterification and ester exchange reaction astoundingly.
Two curing
Good catalytic activity and two ability to cure of the organotin catalysts of general formula 1, expansion general formula 1 and general formula 2 expressions have now also been found.When containing the reactant of more than one polyurethane, siloxanes, amino and ester formation reaction in a kind of composition, the catalyst of representing with expansion general formula 1 and general formula 2 has the surprised ability of two or more polyurethane of catalysis simultaneously, ester, siloxanes and amino formation reaction.This while catalysis is called " two curing " catalysis hereinafter.For catalyst can be in the mixture of various reactants two kinds of different reactions of catalysis simultaneously, the various reactions of reaction rate catalysis that catalyst must be worked as with reasonable grade, thus make do not have a kind ofly obviously to reach complete substantially before being reflected at other reaction.In other words, if a reaction reaches required curing or completeness with specific catalyst in the regular hour, then another required reaction should be in the time of the same order of magnitude with the same catalyst of same concentrations and more fortunately first reaction time+or reach comparable state of cure within-50%.This can determine by testing required reaction respectively with the target catalyst.On the contrary, present industry (commercial) standard is to use at least two kinds of various reactions of different catalysts, and single organotin catalysts of the present invention can respond as the catalysis of different industrial standard catalyst.Therefore, the single catalyst this reaction of representing with general formula 1, expansion general formula 1 or general formula 2 more than of catalysis simultaneously effectively.A special advantage of two abilities to cure of catalyst is in two kinds or the laminated coating.Which floor coating is the coating of automotive paints and so on generally divide, as tint lating and clear top coat.The coating ingredients (formulation) that is used for bottom is to contain the coloured composition that polyurethane, siloxanes and/or melamine form reactant, and clear top coat contain usually polyurethane and/melamine forms reactant, do not contain pigment.For of the present invention pair of curing catalysts, this catalyst can be joined in the coating ingredients of ground floor (being bottom), with the second layer (being face coat) be coated in bottom above, and before bottom solidified, face coat did not contain or contains less catalyst.During curing, bottom may be owing to the catalyst that contains more effective dose solidifies sooner.In the bottom solidification process, catalyst migration impels superficial layer to solidify in superficial layer (being the upper strata).This also causes the strong combination of interlayer, can also allow volatile component pass through also uncured upper strata volatilization in the bottom solidification process.Though the upper strata does not better contain catalyst, the catalyst more less than bottom also can be contained in the upper strata.Less catalyst is the catalytic amount that (more than the twice as bottom curing) solidifies the upper strata in the long time.Use the multilayer coating system of catalyst of the present invention and each interlayer catalyst concn alternation to have the advantage of single curing step after each layer coating, and catalyst has improved the effective catalyst concentration on upper strata in the upwards migration gradually of each interlayer in the solidification process.
Application of Catalyst
Press the weight metal in the catalyst and the total weight of polymerizable solid, the catalytically effective amount of catalyst is about 0.01-5% usually, particularly about 0.05-2%.If do not explain in addition, all percentages among the application or other umber are all by weight.The catalyst of general formula 1, expansion general formula 1 and general formula 2 can use with other catalyst combination, and the catalyst of stanniferous and zinc particularly is as dibutyl tin laurate, Dibutyltin oxide and new zinc pelargonate.
Reactant
The reactant of ester exchange reaction and esterification:
The reactant that carries out ester exchange reaction and esterification is well-known for those skilled in the art.For example, the reactant of ester exchange reaction comprise can with the monomeric ester and the polymer esters of the carboxylic acid of monomeric polyol or polymer alcohol reaction.The reactant of esterification comprise can with the monocarboxylic acid or the polybasic carboxylic acid of monomeric polyol or polymer alcohol reaction.
Polymer forms reactant
The reactant that is used to form the base polymer of polyurethane, polyureas, polysiloxanes and amino polymer is well-known for the technical staff in the polymer arts.The reactant that is used to form polyurethane normally can with aromatics and the aliphatic isocyanate and the blocked isocyanate of polyalcohol and the reaction of polyamino compound.
The reactant that is used to form polysiloxanes normally can with the alkoxy silane (with alkoxyl acrylyl silane) of polymer hydroxy compounds reaction.The popular response product that is used to prepare the amino resins of melamine polymer and so on comprise common can with the condensation product reactant of the urea of formaldehyde or buranol reaction, melamine, carbamoyl methyl melamine, glycoluril, benzoguanamine and so on.Propenoic methyl carbamate (acrylic carbamate) also can form reactant reaction with melamine.
Other (optional) component
Other component (as co-catalyst, pigment, filler, extender and polymer modifiers) that can add usually in coating or the polymer composition can add in the composition as shown in the application.
Embodiment
Embodiment A
Prepare the conventional ingredients of simple urethane reaction (urethane reaction) with polyalcohol (neophenyl alcohol) and isocyanates (NSC 87419), form urethane.Because above-mentioned isocyanates and alcohol is not polyfunctional, thus urethane formed, rather than polyurethane.This directly (straight forward) reaction is used to screen the catalyst with urethane catalytic activity.Listed several catalyst of the present invention (general formula 1 and general formula 2) and the catalytic activity that is used for the industrial standard catalyst (dibutyl tin laurate) of this urethane reaction among the comparison sheet A.On the basis of waiting weight tin, compare, to calculate the catalytic amount that adds in the ingredients.After catalyst added ingredients, allow reaction at room temperature carry out.With FTIR monitoring isocyanates consumption degree (formation urethane) in time.Measure relative reaction rate by first order kinetics.Reaction rate is high more, and urethane forms fast more.Compare with well-known urethane catalyst (dibutyl tin laurate), not having a kind of catalyst of the present invention is the effective urethane catalyst that is used for alcohol and isocyanate reaction.Confirmed like this in this area about the acidic group general understanding of urethane reaction that can slow down, and can to make the people draw catalyst of the present invention be not the conclusion that urethane forms the effective catalyst of reaction.Following embodiment illustrate the present invention with and embodiment preferred.
Embodiment 1
Estimate the catalytic activity of conventional automobile polyurethane surface trimming.According to the result of embodiment A, when (dibutyl tin laurate when DBTDL) comparing, can not expect that catalyst of the present invention (general formula 1, expansion general formula 1 and general formula 2) is effective with present industrial standard catalyst.With dimethylbenzene and ketone is the aliquot that solvent prepares the pure and mild hexamethylene diisocyanate ingredients of acrylate-based polyester polyols, and every part of sample contains enough catalyst, and by the weight of tin in the ingredients and the total weight of solid, catalyst accounts for 0.14%.After adding catalyst, ingredients is remained on 25 ℃, the record ingredients forms the time (Hour) of gel, as an index of " working life ".In addition, prepare coating, and coating reaches the time (Hour) of the drying parameter of sol-gel transition and with B.K.Drying recorder recording surface drying time under the record room temperature with every kind of ingredients.The results are shown in Table 1.The performance of catalyst of the present invention is the same with the industrial standard of DBTDL good.
Embodiment 2
Evaluation is used to prepare the catalytic action of the blocked isocyanate of polyurethane coating.(dibutyl tin laurate DBTDL) compares with present industrial standard catalyst with catalyst of the present invention (general formula 1, expansion general formula 1 and general formula 2).The HDI of preparation MEKO end-blocking, the aliquot of acrylate polylol ingredients in MAK (2-heptanone) and MIBK (methyl iso-butyl ketone (MIBK)) solvent.Every part of sample contains enough catalyst, and by the weight of tin in the ingredients and the total weight of solid, catalyst accounts for 0.14%.Ingredients is preheating to 70-80 ℃, thereby selected catalyst can be dissolved in the ingredients.After catalyst joins in the ingredients of preheating, ingredients is warming up to 130 ℃, reach the required time (Minute) of gel point (2500 centipoise) with Brookfield viscosimeter record ingredients.Described gel point represents to have finished basically reaction.The results are shown in Table 2.The performance of catalyst of the present invention is better than the industrial standard of DBTDL.
Embodiment 3
Combine with containing zinc co-catalyst (zinc neodecanoate), be used to prepare the catalytic action of the blocked isocyanate of polyurethane coating by embodiment 2 described method evaluations.(dibutyl tin laurate DBTDL) compares with zinc neodecanoate will to contain and not contain the catalyst of the present invention (general formula 1, expansion general formula 1 and general formula 2) of co-catalyst and present industrial standard catalyst.Prepare the aliquot of the ingredients of the isocyanates, MAK and the MIBK that contain acrylate polylol, oxime end-blocking, every part of sample contains the catalytic amount shown in the table 3 (by the weight of tin, for zinc neodecanoate, by the weight of zinc).If necessary, with the ingredients preheating, so that selected catalyst can be dissolved in the ingredients.After catalyst joins in the ingredients of preheating, ingredients is warming up to 120 ℃, the record ingredients reaches gel point (2500 centipoise) the required time.This gel point shows that reaction finishes basically.The results are shown in Table 3.The performance of catalyst of the present invention is better than the industrial standard of DBTDL, and adds the zinc neodecanoate co-catalyst, has improved the performance of catalyst of the present invention.
Embodiment 4
Compare with DBTDL, the present embodiment evaluation prepares the concentration of reacting middle catalyst of the blocked isocyanate of polyurethane coating and polyalcohol to the influence of the catalytic performance of the catalyst represented with expansion general formula 1.With catalyst of the present invention and present industrial standard catalyst, dibutyl tin laurate (DBTDL) is made comparisons.Used catalyst is the poly-tin oxygen alkane of representing with expansion general formula 1, and R is a butyl in the formula, R 1All be OCOCF 3, n is 0, x is 0.It with use empirical formula R 2SnAO-[R 2SnO] x-SnR 2The poly-tin oxygen alkane that A (HxO) n represents is consistent, and all R are butyl in the formula, and A is the derivative of organic acid, and is OCOCF 3, x is 0, n is about 0.Preparation contains the aliquot of the ingredients of Desmophen A565 (a kind of acrylic compounds polyalcohol available from Bayer), DesmodurBI3175A (a kind of isocyanates of the oxime end-blocking available from Bayer), MAK and MIBK, and every part of sample contains the different catalysts amount (the % catalyst calculates by the weight and the total weight of solids of tin in the ingredients) of the abundance shown in the table 4.After in the ingredients of catalyst adding preheating, ingredients is warming up to the temperature shown in the table 4, the record ingredients reaches the required time (Minute) of gel point (2500 centipoise).This gel point shows that reaction finishes basically.The results are shown in Table 4.Even when the concentration of DBTDL exceeds 250%, the performance of catalyst of the present invention is also better than the industrial standard of DBTDL.
Embodiment 5
Compare with DBTDL, estimate the ability of catalyst siloxane polymerization reaction of the present invention.Reactant is the silicic acid orthocarbonate crosslinking agent that is used for silanol stopped polydimethyl siloxane oil.The ingredients that will contain required catalyst in the plastic beaker that stirs is heated to 140 ℃.Record reaches the required time of gel point (Minute).Except that catalyst is insoluble to the situation of reactant mixture, obtain excellent performance with catalyst of the present invention.The results are shown in Table 5.
Embodiment 6
Compare with DBTDL and Nacure 5626 (available from King Industries, a kind of DBSA of amine end-blocking), estimate the ability of catalyst melamine formaldehyde (MF) of the present invention and acrylic compounds polyol crosslink reaction.The used reactant of ingredients is 60.2 gram hexa methoxy melamines (Cymel 303) and the 140.71 gram acrylic compounds polyalcohols (Joncryl 500) that are dissolved in the 100 gram butanone (MEK) in each test.The ingredients that will contain required catalyst in the plastic beaker that stirs is heated to 140 ℃.Record reaches the required time of gel point (Minute).Compare with the tin-based catalyst (DBTDL) of contrast, obtain excellent performance with catalyst of the present invention.The results are shown in Table 6.
Embodiment 7
Compare with Dibutyltin oxide (DBTO) and butyl stannonic acid (BSA), present embodiment is estimated the ability of catalyst esterification of the present invention and ester exchange reaction.Reactant is phthalic anhydride and 2-Ethylhexyl Alcohol, and reaction temperature is 220 ℃, alcohol excessive 5%.The ingredients that will contain required catalyst remains on 220 ℃, the monitoring acid number in time (hour) minimizing.Catalyst adds in the weight identical with tin and in the ratio of 100 milligrams of tin/100 gram phthalic anhydrides.Acid number is less than about thought that reaction was complete at 3 o'clock.Obtain excellent performance with catalyst of the present invention.The results are shown in Table 7.
Table A
The catalyst relative speed
Dibutyl tin laurate 1.0
Bu 2Sn (OSO 2CH 3) 2 (1)Do not dissolve
Bu 2Sn(pTSA) 2 (2)???????????????0.17
[Bu 2Sn(pTSA)] 2O (3)????????????0.07
1. general formula 2, R and R 2Be butyl, R 1Be methanesulfonate
2. general formula 2, R and R 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root
3. general formula 1, R and R 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root, n=0, x is about 0.
Table 1
Catalyst performance catalyst sol-gel transition surface drying time working life in the polyurethane coating (hour)
(hour) (hour) dibutyl tin laurate 3.0 3.8 6.0Bu 2Sn (OSO 2CH 3) 2 (1)5.0 8.0 7.8Bu 2Sn (pTSA) 2 (2)3.0 6.5 6.0[Bu 2Sn (pTSA)] 2O (3)3.0 4.0 5.0
1. general formula 2, R and R 2Be butyl, R 1Be methanesulfonate
2. general formula 2, R and R 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root
3. general formula 1, R and R 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root, n=0, x is about 0.
Table 2
Catalyst % tin Ning Jiaoshijian @130 Ning Jiaoshijian @125
DBTDL ????0.14 ????23.4
Bu 2Sn(OCOCCl 3) 2 (1)??? ????0.14 ????25.2
{Bu 2Sn(OCOCCl 3)} 2O (2) ????0.14 ????14.9
{Bu 2Sn(OCOCF 3)} 2O (3) ????0.14 ????15.1
Bu 2Sn(OSO 2CH 3) 2 (4) ????0.14 ????15.7
{Bu 2Sn(OSO 2CH 3)} 2O (5) ????0.14 ????15.2
{Bu 2Sn(OSO 2CH 3)} 2O (5) ????0.14 ????22.6
{Bu 2Sn(OSO 2CH 3)} 2O (5) ????0.11 ????26.2
{Bu 2Sn(OSO 2CH 3)} 2O (5) ????0.095 ????30.4
{Bu 2Sn(OSO 2CH 3)} 2O (5) ????0.082 ????33.4
1. general formula 2, R and R 2Be butyl, R 1It is the trichloroacetic acid root
2. expand general formula 1, R and R 2Be butyl, R 1Be the trichloroacetic acid root, n=0 and x are about 0
3. expand general formula 1, R and R 2Be butyl, R 1Be the trifluoroacetic acid root, n=0 and x are about 0
4. general formula 2, R and R 2Be butyl, R 1It is methanesulfonate
5. general formula 1, R and R 2Be butyl, R 1Be methanesulfonate, n=0 and x are about 0
Table 3
Catalyst The % metal Ning Jiaoshijian @120C Note
Dibutyl tin laurate ??0.2%Sn ????48.7
Zinc neodecanoate ??0.35%Zn ????>40
Bu 2Sn(OSO 2CH 3) 2(1) ??0.2%Sn ????26.4 70 ℃ of dissolvings
Bu 2Sn(OSO 2CH3) 2 (1)+ zinc neodecanoate ??0.2%Sn ??0.07%Zn ????22.1 70 ℃ of dissolvings
{Bu 2Sn(OCOCF 3)} 2O (2) ??0.2%Sn ????27.3 70 ℃ of dissolvings
{Bu 2Sn(OCOCF 3)} 2O (2)+ zinc neodecanoate ??0.2%Sn ??0.07%Zn ????20.4 7O ℃ of dissolving
Bu 2Sn(OCOCCl 3)} 2 (3) ??0.2%Sn ????27.2 40 ℃ of dissolvings
Bu 2Sn(OCOCCl 3) 2 (3)+ zinc neodecanoate ??0.2%Sn ????13.4 40 ℃ of dissolvings
{Bu 2Sn(OCOCCl 3)} 2O (4) ??0.2%Sn ????25.5 25 ℃ of dissolvings
{Bu 2Sn(OCOCCl 3)} 2O (4)+ zinc neodecanoate ??0.2%Sn ??0.07%Zn ????12.7 25 ℃ of dissolvings
1. general formula 2, R and R 2Be butyl, R 1Be methanesulfonate
2. expand general formula 1, R and R 2Be butyl, R 1Be the trifluoroacetic acid root, n=0, x is about 0
3. general formula 2, R and R 2Be butyl, R 1Be the trichloroacetic acid root
4. expand general formula 1, R and R 2Be butyl, R 1Be the trichloroacetic acid root, n=0, x is about 0
Table 4
Catalyst concn increases Effect on Performance
Catalyst %Sn Min@130℃ Min@125℃ Min@120℃
Dibutyl tin laurate 0.20 18.6 48.7
Dibutyl tin laurate 0.50 17.3 33.5
{Bu 2Sn(OCOCF 3)} 2}O (1) 0.20 13.0 18.6 27.3
{Bu 2Sn(OCOCF 3)} 2}O (1) 0.5 11.8 16.2 24.0
1. expand general formula 1, R and R 2Be butyl, R 1Be the trifluoroacetic acid root, n=0, x is about 0
Table 5
Solidification temperature ℃ Catalyst g Gel time (branch)
140 Dibutyl tin laurate 0.63 149.9
140 Bu 2Sn(OAc) 2 (1) 0.35 96.4
140 Bu 2OAcSnOSnOAcBu 2 (2) 0.44 Not>130.0 (not dissolving)
140 Bu 2Sn(OCOCCl 3) 2 (3) 0.56 11.5
140 [Bu 2(OCOCCl 3)Sn] 2O (4) 0.40 12.4
140 [Bu 2(OCOCF 3)Sn] 2O (5) 0.35 10.7
140 Bu 2Sn(OCOCF 3) 2 (6) 0.46 8.8
1. general formula 2, R and R 2Be butyl, R 1Be acetate
2. expand general formula 1, R and R 2Be butyl, R 1Be acetate, n=0, x is about 0
3. general formula 2, R and R 2Be butyl, R 1Be the trichloroacetic acid root
4. expand general formula 1, R and R 2Be butyl, R 1Be the trichloroacetic acid root, n=0, x is about 0
5. expand general formula 1, R and R 2Be butyl, R 1Be the trifluoroacetic acid root, n=0, x is about 0
6. general formula 2, R and R 2Be butyl, R 1Be the trifluoroacetic acid root
Table 6
Melamine is crosslinked
Catalyst Room temperature solubility Ning Jiaoshijian @115 ℃ (branch)
Bu 2Sn(OSO 2CH 3) 2 (1) Be partly dissolved 6.1
{Bu 2Sn(OSO 2CH 3)} 2O (2) Be partly dissolved 5.9
Nacure 5625 (sulfonic acid of amine end-blocking) Dissolving 6.4
Dibutyl tin laurate Dissolving >100
Dibutyltin oxide Dissolving >100
1. general formula 2, R and R 2Be butyl, R 1Be methanesulfonate
2. general formula 1, R and R 2Be butyl, R 1Be methanesulfonate, n=0, x is about 0
Add catalyst Deng mole
Catalyst concn=0.18 mM is by the gross weight of solid
Gel time is measured (Brookfield viscosimeter) and is carried out at 115 ℃
Measure bodying speed to gel point (2500 centipoise)
Table 7
Acid number and time relation
Time (hour) DBTO (1) BSA (2) BuSn(MSA) 3 (3) Bu 2Sn(MSA) 2 (4) (Bu 2SnMSA) 2O (5) (Bu 2SnpTSA) 2O (6)
????0.5 ????63.9 ??60.5 ????27.5 ????32.2 ????41.8 ????43.6
????1.0 ????40.5 ??69.1 ????10.5 ????15.8 ????23.2 ????22.6
????1.5 ????29.2 ??23.0 ????5.3 ????9.1 ????14.2 ????14.2
????2.0 ????22.4 ??12.1 ????3.3 ????5.6 ????9.2 ????9.3
????2.5 ????17.5 ??7.6 ????3.8 ????6.5 ????5.9
????3.0 ????13.4 ??4.7 ????3.9 ????3.8
????3.5 ????10.1
????4.0 ????7.2
????4.5 ????5.3
????5.0 ????3.8
1. Dibutyltin oxide
2. butyl stannonic acid
3. general formula 2, and R is a butyl, R 1And R 2Be methanesulfonate
4. general formula 2, R and R 2Be butyl, R 1Be methanesulfonate
5. general formula 1, R and R 2Be butyl, R 1Be methanesulfonate, n=0, x is about 0
6. general formula 1, R and R 2Be butyl, R 1Be the p-methyl benzenesulfonic acid root, n=0, x is about 0

Claims (15)

1. have the poly-tin oxygen alkane salt of the organic acid of multiple catalytic activity, it is characterized in that it contains the compound that useful following general formula is represented:
Each R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula; Each R 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, condition is R 1At least a selection be OSO 2R, the R in the formula have above-mentioned identical implication; Each R 2Be selected from respectively and R and R 1Identical group; N is that mean value is the integer of 0-20; X is 0 to convergence infinity when this catalyst is in the aqueous solution.
2. tin oxygen alkane as claimed in claim 1 is characterized in that each R 1Be selected from OSO respectively 2R, R has the implication identical with R in the claim 1 in the formula; R 3COO, R in the formula 3Be alkyl or aryl, contain at least one F of bonding, Cl, Br, I, CN mutually with it with carbon atom that the COO group connects; RPO 3H, R has the implication identical with R in the claim 1 in the formula; RCrO 4H, R has the implication identical with R in the claim 1 in the formula; F; NO 3ClO 4(NO) 2C 6H 2OH; Condition is R 1At least a OSO that is chosen as 2R.
3. improved curable polymer coating composition is characterized in that its logically mixes at least one group and be selected from polyurethane and form reactant, siloxanes and form reactant, aminoly form polymer that reactant and ester form reactant and form reactant and constitute or make; Its improvement is included in the catalyst of the organic tin salt of adding organic acid in the described composition as described polymer formation reactant reaction, and described catalyst is selected from the organo-tin compound of representing corresponding to following general formula:
Figure 9811548800022
With
Figure 9811548800031
Each R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula; Each R 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, the R in the formula has above-mentioned identical implication; Condition is at least one R 1Derived from pKa less than 1 organic acid; Each R 2Be selected from respectively and R and R 1Identical group; N is that mean value is the integer of 0-20; X is 0 to convergence infinity when this catalyst is in the aqueous solution.
4. composition as claimed in claim 3 is characterized in that each R 1Be selected from OSO respectively 2R, R has the implication identical with R in the claim 1: R in the formula 4COO, R in the formula 4Be alkyl or aryl, contain at least one F of bonding, Cl, Br, I, CN mutually with it with carbon atom that the COO group connects; RPO 3H, R has the implication identical with R in the claim 1 in the formula; RCrO 4H, R has the implication identical with R in the claim 1 in the formula; F; NO 3ClO 4(NO) 2C 6H 2OH; Condition is R 1At least a OSO that is chosen as 2R.
5. composition as claimed in claim 3 is characterized in that it is that polyurethane forms reactant that described one group of polymer forms reactant.
6. composition as claimed in claim 3 is characterized in that it is that siloxane polymer forms reactant that described one group of polymer forms reactant.
7. composition as claimed in claim 3 is characterized in that it also comprises the co-catalyst that contains zinc or tin.
8. composition as claimed in claim 3 is characterized in that it is that amino resins forms reactant that described one group of polymer forms reactant.
9. composition as claimed in claim 3 is characterized in that two groups of polymer form reactant and are blended in the described composition.
10. composition as claimed in claim 9 is characterized in that it is that amino polymer forms reactant and polyurethane forms reactant that described two groups of polymer form reactant.
11. composition as claimed in claim 10 is characterized in that it is that melamine forms reactant that described amino polymer forms reactant.
12. improved coating, it is two-layer at least to it is characterized in that it comprises, ground floor contains coating composition as claimed in claim 3, the second layer that also contacts with it above the ground floor contains coating composition as claimed in claim 3, but does not contain catalytic component as claimed in claim 3 or contain the catalyst more less than ground floor.
13. improving one's methods of an organic tin salt for preparing the organic acid of representing with following general formula: Or
Figure 9811548800042
Each R is selected from alkyl, aryl and the alkaryl that contains 1-20 carbon atom respectively in the formula; Each R 1Be selected from OR, OH, OOCR, halogen and the pKa derivative less than 1 organic acid respectively, the R in the formula has above-mentioned identical implication; Condition is at least one R 1Derived from pKa less than 1 organic acid; Each R 2Be selected from respectively and R and R 1Identical group; N is that mean value is the integer of 0-20; X is 0 to convergence infinity when this catalyst is in the aqueous solution; It is characterized in that described method is included in the reactant reaction that makes the described organic tin salt of preparation in the dicyandiamide solution; Its improvement comprises that the mixture with at least two kinds of polar solvents is used as dicyandiamide solution, and wherein a kind of solvent is a water, and another kind of solvent is an alcohol.
14. as claimed in claim 13 improving one's methods is characterized in that it also comprises the steps:
(a) the tin oxygen alkane in the above-mentioned polar solvent mixture is cooled off and crystallization;
(b) from described mixture, separate tin oxygen alkane;
(c), produce crystallization, graininess, non-sticky solid with this tin oxygen alkane drying.
15. the crystallization, graininess, the non-sticky solid that make with the described method of claim 12.
CNB981154883A 1997-07-09 1998-07-09 Organotin sulfonate catalysts and their manufacture method Expired - Fee Related CN1185239C (en)