CN1193060A - Water-proof air-permeable fabric and producing method thereof - Google Patents
Water-proof air-permeable fabric and producing method thereof Download PDFInfo
- Publication number
- CN1193060A CN1193060A CN 97102948 CN97102948A CN1193060A CN 1193060 A CN1193060 A CN 1193060A CN 97102948 CN97102948 CN 97102948 CN 97102948 A CN97102948 A CN 97102948A CN 1193060 A CN1193060 A CN 1193060A
- Authority
- CN
- China
- Prior art keywords
- manufacture method
- fabric
- film
- membrane
- ptfe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a water-proof permeability fabric and its preparation method. Said preparation method includes the following steps: combining a hydrophobic ventilating film on fabric substrate, said composite material has no need of hydrophilic treatment, and said ventilating film is a porous film made of polytetrafluoroethylene resin with elasticity obtained by multiple expanding-forming process. By adding additive, said film possesses high strength and good wear resistance.
Description
The invention relates to a kind of proofed breathable fabric and manufacture method thereof, relate more particularly to a kind of perforated membrane and manufacture method thereof.
Everyone wishes that the clothes oneself worn are can weather dual-purpose, and the rainy day not only can waterproof can also breathe freely, and on one's body sweat gas is expanded to the clothes outside, no matter fine, cloudy day, various environment of rainy day wear all comfortable.This has just required a kind of high Air permenbility, high water resistance, and anti-folding, wrinkle, some also requires resilient high-performance garment material, use silicone, the polymer coating that fabric that fluorine carbon and other hydrophober are handled and development are recently released, though it is ventilative good, but once friction, folding, wrinkle, stretch and wait just infiltration, water pressure resistance is also very low ≯ the 1000mm water column, and the life-span is very short, washing just loses water resistance several times, and patent EPO110626 and US4194041 make the hydrophobic air-permeable layer in hydrophilic film and the compound waterproof breathable garment lining that manufactures of fabric with poly tetrafluoroethylene, can reach hydrostatic pressing 250mm, 20 minutes no seepages, Air permenbility＞1000g/m
2My god, but it must be in the one side of water-repellent layer, and promptly the lining face of lining is compounded with hydrophilic film, as the hydrophilic film made from hydrophiles such as polyethers-poly-urethane, poly-perfluorinated sulfonic acids.The preparation of this hydrophilic layer is very complicated, in addition need carry out on PTFE film surface polymerization or with its glycerol polymerization, hydrophilic layer thickness reaches 170 μ.Usually real rainproof actual requirement is: resistance to hydrostatic pressure 1400mm, extra torrential rain requires greater than 2000mm.Air permenbility＞1000g/m
2My god, large amount of exercise requirement＞3500-4000g/m
2My god.Obviously the product of above-mentioned two patent gained can not meet the demands.
Disclose a kind of waterproof breathable garment and manufacturing method of fabric thereof in the patent CN-94113980 of Fragrance Hill, palace application, garment material is that fabric and hydrophobic ventilated membrane directly are composited, and ventilated membrane prepares with low-molecular-weight resin, and the elasticity of film obtains with the retraction method.
A kind of weather water proof air penetrating shoes and manufacturing method of fabric thereof are disclosed in the patent CN-94113981 of Fragrance Hill, palace application, this lining is well-pressed waterproof and breathable composite, be compounded with polytetrafluoroethylene (PTFE) hydrophobic film, lining in the middle of the bilaminar fiber fabric, compound available various natural, the synthetic direct composite membrane of the viscose glue surface of lining and film needn't hydrophilic treatment.
A kind of new method for preparing perforated membrane with low molecular weight tetrafluoro ethylene resin is disclosed in the patent CN-94112057 of Fragrance Hill, palace application, it utilize mix between different trade mark low-molecular-weight resins and surface tension between atomic little difference, they are mixed by a certain percentage, under-10 ℃～1000 ℃, expand typing with physics expansion method then.But this method applicable surface is narrow, is only applicable to the low-molecular-weight resin of several trades mark, and is difficult to other trade mark resin.And the equipment of usefulness is to heat on the face, non-uniform temperature, about 50,000 yuan of expense.Film-strength with above-mentioned feedstock production is low, wear no resistance, and the expansion typing is only carried out once, and film easily breaks.
The above patent is introduced by reference in this application.
One of purpose of the present invention provides a kind of proofed breathable fabric and preparation method thereof.
Two of purpose of the present invention provides a kind of hydrophobic ventilated membrane and preparation method thereof.
Three of purpose of the present invention provides a kind of perforated membrane and preparation method thereof.
These purposes of the present invention and other purpose will further be launched and illustrate by following detailed description and explanation.
In proofed breathable fabric of the present invention, a compound hydrophobic ventilated membrane on the fabric base cloth does not need hydrophilic treatment hydrophobic ventilated membrane to prepare with polyflon, and the elasticity of film obtains the Air permenbility＞6000g/m of film with the expansion typing method
2My god, hydrostatic pressing＞7000mm water column, 2 hours are non-leakage, water feeler＞90 ℃.And the hydrophobic ventilated membrane is direct and fabric is compound.The hydrophobic ventilated membrane can be a polytetrafluoroethylene (PTFE) perforated membrane.
In the present invention, the polytetrafluoroethylene (PTFE) perforated membrane can not be the hydrophobic ventilated membrane also, and can prepare as follows;
A, batching; PTFE is added an amount of extrusion aid and additive, stir evenly;
B, pre-molding: the PTFE powder is pressed into blank in advance at 50～60 ℃;
C, pushing: blank is squeezed into strip at 50～60 ℃;
D, calendering: under uniform temp, strip is rolled into cummerbund;
E, drying: extrusion aid is removed clean at 100～300 ℃;
F, stretching: at 300～350 ℃ belt is carried out longitudinal stretching, make it to become base band;
G, expansion: base band is carried out lateral magnification, and repeatedly typing promptly becomes the PTFE perforated membrane.
Wherein, the expansion temperature is-20～1500 ℃, and expansion typing number of times is more than secondary, below ten times.Additive can be inorganic salts and inorganic oxide and pigment and conventional powder additive, and addition can be ten thousand of total batching/to 1 15.Wherein, inorganic salts can be for the salt of periodic table of elements IA family and IIA family metal, as Nacl, and KNO
3, CUSO
4Deng, inorganic oxide can be zinc oxide, aerosil, magnesia, precipitated calcium carbonate etc.
Expansion temperature of the present invention is more extensive, can be-20～1500 ℃ of expansion down, and high temperature expansion typing number of times is more than ten times, every expansion typing once makes heat conduct once to the profound level of film, all reaches requirement until film, the film of expansion typing can not break like this, and intensity is good.
In the present invention, can not only prepare the hydrophobic ventilated membrane with method of the present invention, and can prepare the membrane product in various fabric widths and thickness and aperture, as film, band, villous themeda, rod, be more suitable for some special goods, as hydrophilic film, reverse osmosis membrane, spy sense film, filter membrane, the prescription that specifically prepares various films is known in Fragrance Hill, palace aforementioned patent and prior art, in this few narration.
In the present invention, above-mentioned prescription and preparation method and technology thereof can be with reference to those patents of chatting before the Fragrance Hill, palace, and all patents are incorporated herein and as a part of the present invention.
Adopt method of the present invention, just unrestricted to raw material, all brands both at home and abroad, no matter the polytetrafluoroethylene (PTFE) resin of high and low molecular weight all can be processed, and uses; Expansion adds the HEAT SETTING area and doubles abovely than art methods, is linear heating, and expense only is 1,000 yuan; And owing to added additive, and the film-strength height, ABRASION RESISTANCE is good; Be more preferably and adopt lateral magnification repeatedly to finalize the design, so film can not break; Certainly also have many advantages and make us surprised part with method of the present invention, do not enumerate one by one at this.
The raw material that the present invention adopts can obtain from commercially available, and the equipment of employing also is that the industry is known.
Below further specify and set forth the present invention by specific embodiment, but embodiment only is used for explanation, and can not limit claim scope of the present invention.
Example l;
Prepare polytetrafluoroethylporous porous membrane as follows.
A, batching: get 6-J by weight respectively accounting for 1/3, F-103 and FR-202B, stirring and evenly mixing adds the millesimal calcium sulfate of conventional extrusion aid and gross weight;
B, above-mentioned batching is pressed into blank in advance, at 50～60 ℃ blank is squeezed into strip then at 50～60 ℃; At uniform temp strip is rolled into cummerbund; And then about 236 ℃, extrusion aid is removed totally by dry;
C, about 300 ℃ belt is carried out longitudinal stretching, make it to become base band, then base band is carried out lateral magnification, three typings promptly become the PTFE perforated membrane.
The perforated membrane and the fabric (polyester-cotton blend) of above-mentioned preparation is compound, Air permenbility 4700 gram/rice
3My god, at 6000mm, ne-leakage under 2 hours hydrostatic pressings, washing is not come unstuck after 30 times in washing machine.
Example 2:
The raw material band made from homemade low-molecular-weight polyflon, get 4 times of longitudinal stretchings, width is 5cm, thickness is respectively 0.04mm, 0.2mm, 0.4mm, 1mm, and respectively to be cut into length be that 20cm makes base band, pack into then and clamp with clip in the dilator, it is 50cm that lateral magnification becomes width for 10 times, and every 9cm is equipped with one group of high temperature heat source in the dilator, open one group, two groups, three groups, four groups, five groups thermals source successively and carry out lateral magnification, result such as table one.
Table one
Expansion heating thickness (mm)
Temperature groups several 0.04 0.2 0.4 1
1 is broken
2 broken 500 degree 3 broken (Celsius) 4 are broken
5 is uneven broken broken
1 is broken
2 uneven broken broken 1000 degree 3 still can uneven broken (Celsius) 4 one's likes or preferences can break
5 is good uneven carefully
1 is uneven broken broken
2 still can uneven broken broken 1500 degree, 3 one's likes or preferences can uneven broken (Celsius) 4 good one's likes or preferences can be uneven
5 one's likes or preferences can carefully
Can find out that from table one the thick more required heating number of times of film is just many more; Temperature is high more, and required heating number of times just reduces.
Example 3:
Get the raw material band that did not stretch, put into and be shaped as:
Adjustable secondary vertical, horizontal stretcher.2 times of the first section longitudinal stretchings; 3.5 times of the second section lateral magnifications; The 3rd section stretches 2 times again; 3 times of the lateral magnifications again of the 4th section.One group of heating source is housed in every section.Result of the test such as table two.Several 0.04 0.2 0.4 1500 degree 1 broken (Celsius) 2 of table two expansion heating thickness (mm) temperature groups are uneven broken broken
3 good uneven broken (Celsius) 4 are uneven carefully
1 uneven broken broken broken 1000 degree 2 still can uneven uneven (Celsius) but 3 one's likes or preferences Shang Keshang can
4 carefully
1 still can uneven uneven uneven 1500 degree, 2 one's likes or preferences can be still can uneven (Celsius) 3 carefully
4 carefully
From table two, as can be known, be better than once expanding the method for heating for multiple times with secondary lateral magnification method.
Example 4;
Equipment in the example two is adjusted into three stretching expansions of vertical, horizontal, whenever is assembled with two thermals source.
Result of the test such as table three.
Table three
Expansion heating thickness (mm)
Temperature groups several 0.04 0.2 0.4 11 is uneven
2 uneven 500 degree, 3 uneven (Celsius) 4 still can be uneven uneven
5 Shang Keshangkeshangkeshang can
But 6 one's likes or preferences Shang Keshang can
1 is uneven
2 uneven uneven uneven uneven 1000 degree, 3 Shang Keshangkeshangkeshang can (Celsius) 4 Shang Keshangkeshangkeshang can
5 one's likes or preferences can carefully
6 carefully
1 is uneven
2 Shang Keshangkeshang can uneven 1500 degree, 3 good one's likes or preferences can uneven (Celsius) 4 one's likes or preferences can carefully
5 carefully
6 carefully
From table three data as can be known, under supercritical temperature through repeatedly vertical, horizontal stretch, expansion, even all can prepare membrane under relatively lower temp, quality is also better relatively.
Claims (9)
1, a kind of proofed breathable fabric is characterized in that a compound hydrophobic ventilated membrane on the fabric base cloth, does not need hydrophilic treatment, and the hydrophobic ventilated membrane prepares with polyflon, and the elasticity of film obtains the Air permenbility＞6000g/m of film with the expansion typing method
2My god, hydrostatic pressing＞7000mm water column, 2 hours are non-leakage, water feeler＞90 ℃.
2, the manufacture method of proofed breathable fabric as claimed in claim 1 is characterized in that the hydrophobic ventilated membrane is direct and fabric is compound.
3, proofed breathable fabric as claimed in claim 1 is characterized in that the hydrophobic ventilated membrane is a polytetrafluoroethylene (PTFE) perforated membrane.
4, the manufacture method of proofed breathable fabric as claimed in claim 2 is characterized in that preparing as follows polytetrafluoroethylporous porous membrane:
A, batching; PTFE is added an amount of extrusion aid and additive, stir evenly;
B, pre-molding: the PTFE powder is pressed into blank in advance at 50～60 ℃;
C, pushing: blank is squeezed into strip at 50～60 ℃;
D, calendering: under uniform temp, strip is rolled into cummerbund;
E, drying: extrusion aid is removed clean at 100～300 ℃;
F, stretching: at 300～350 ℃ belt is carried out longitudinal stretching, make it to become base band;
G, expansion: base band is carried out lateral magnification, and repeatedly typing promptly becomes the PTFE perforated membrane.
5, manufacture method as claimed in claim 4 is characterized in that expanding temperature and is-20～1500 ℃.
6, manufacture method as claimed in claim 4 is characterized in that expansion typing number of times is more than secondary, below ten times.
7, manufacture method as claimed in claim 4 is characterized in that additive can be inorganic salts and inorganic oxide and pigment, and addition can be ten thousand of total batching/to 1 15.
8, manufacture method as claimed in claim 7 is characterized in that inorganic salts can be the salt of periodic table of elements IA family and IIA family metal.
9, manufacture method as claimed in claim 2 is characterized in that inorganic oxide can be zinc oxide, aerosil, magnesia, precipitated calcium carbonate.