CN1191287C - Method for manufacturing flocculant of modified polyacrylamide for concrete keeping together underwater - Google Patents
Method for manufacturing flocculant of modified polyacrylamide for concrete keeping together underwater Download PDFInfo
- Publication number
- CN1191287C CN1191287C CNB021296391A CN02129639A CN1191287C CN 1191287 C CN1191287 C CN 1191287C CN B021296391 A CNB021296391 A CN B021296391A CN 02129639 A CN02129639 A CN 02129639A CN 1191287 C CN1191287 C CN 1191287C
- Authority
- CN
- China
- Prior art keywords
- weight
- acrylamide
- polyvinyl alcohol
- parts
- weight part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a modified polyacrylamide flocculant for keeping concrete together underwater and a manufacturing method thereof. The flocculant is used for depositing concrete underwater. Nitrogen, hydrogen peroxide, ferrous sulfate or cerium ammonium nitric acid are added to acrylamide monomers and polyvinyl alcohol to be polymerized and prepared into an acrylamide-polyvinyl alcohol multipolymer, or the acrylamide-polyvinyl alcohol multipolymer is mixed with a condensation compound of naphthalenesulfonic acid and formaldehyde to prepare the modified polyacrylamide flocculant. The flocculant can make a mixed comound of underwater concrete have excellent dispersivity resistance, can reduce water pollution in construction and can reduce the loss of strength, which is caused by the dispersion of the mixed compound of the concrete.
Description
Technical field
The present invention relates to a kind of modified polyacrylamide for concrete keeping together underwater flocculation agent and manufacture method, be used for the tremie concrete engineering.
Background technology
Existing non-dispersible underwater concrete flocculation agent, adopt cellulose-based flocculation agent, glycan base polymer based flocculating agent or polyacrylamide flocculant, its weak point is that anti-dispersing property deficiency, the flowability of underwater concrete mixture is relatively poor, loss of slump is big, maturing is bigger because of the loss of strength that dispersion of materials causes.Existing polyacrylamide flocculant generates straight chain type or homopolymerization type polyacrylamide flocculant by the acrylamide monomer polymerization, to anti-dispersiveness, the flowability of underwater concrete mixture be still waiting to improve, loss of slump remains further to be reduced.
Summary of the invention
The objective of the invention is to avoid above-mentioned weak point of the prior art and a kind of anti-dispersiveness that can improve underwater concrete mixture, flowability, minimizing loss of slump are provided, reduce the modified polyacrylamide for concrete keeping together underwater flocculation agent and the manufacture method of disperseing the loss of strength that causes because of concrete mix.
The technical solution used in the present invention
Modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, add 0.005~0.01 weight part hydrogen peroxide after feeding nitrogen 15min, 0.005~0.01 parts by weight of ferrous sulfate, carry out polyreaction, after polyase 13~6h with the acrylamide-polyvinyl alcohol copolymer of gained through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
More excellent modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.15 weight account polyethylene alcohol in advance, add 3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add 0.01 weight part hydrogen peroxide afterwards, 0.01 parts by weight of ferrous sulfate, carry out polyreaction, after the polymerization 6h with gained acrylamide-polyvinyl alcohol copolymer through granulation, drying, the made acrylamide-polyvinyl alcohol copolymer powder of pulverization process.
More excellent modified polyacrylamide for concrete keeping together underwater flocculation agent is characterized in that containing 2 weight part naphthalene sulfonic acidformaldehyde condensation product powder by 1 weight part acrylamide-polyvinyl alcohol copolymer powder mixes.
The modified polyacrylamide for concrete keeping together underwater flocculation agent that can also adopt, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.005~0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polyase 13~6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
More excellent modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.15 weight account polyethylene alcohol in advance, add 3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polymerization 6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
More excellent modified polyacrylamide for concrete keeping together underwater flocculation agent is characterized in that containing 2 weight part naphthalene sulfonic acidformaldehyde condensation product powder by 1 weight part acrylamide-polyvinyl alcohol copolymer powder mixes.
The manufacture method of the modified polyacrylamide for concrete keeping together underwater flocculation agent that can also adopt, it is characterized in that in 1 weight part acrylamide monomer, adding and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add 0.005~0.01 weight part hydrogen peroxide afterwards, 0.005~0.01 parts by weight of ferrous sulfate is carried out polyreaction, after polyase 13~6h with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, pulverization process is made acrylamide-polyvinyl alcohol copolymer powder.
The manufacture method of the modified polyacrylamide for concrete keeping together underwater flocculation agent that can also adopt, it is characterized in that in 1 weight part acrylamide monomer, adding and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.005~0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polyase 13~6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, pulverization process is made acrylamide-polyvinyl alcohol copolymer powder.
Modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention, carry out polyreaction by acrylamide monomer and polyvinyl alcohol and generate the band grafted modified polyacrylamide water-soluble polymers that acrylamide-polyvinyl alcohol copolymer promptly generates band side chain type or copoly type, its molecular weight is more than 5,000,000.The hydrogen peroxide of Shi Yonging, ferrous ion compound ferrous sulfate, CAN are used for the initiator of acrylamide monomer grafted polyethylene alcohol in the mill, the deionized water that uses is by the deionized water of tap water through the exchange of zwitterion exchange column, and the purpose that feeds nitrogen is to drive away dissolved oxygen in the polymerization reaction system.The naphthalene sulfonic acidformaldehyde condensation product that uses helps to improve the anti-dispersive ability of underwater concrete mixture, and the flowability, minimizing water consumption, the maturing intensity that improves that improve concrete mix.
The present invention's beneficial effect compared with prior art
1, modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention, can make underwater concrete mixture have good anti-dispersiveness, toughness, high-ductility, self-leveling and bleeding, water pollution in the time of can reducing underwater concreting, cast has good fillibility to close gap, the loss of the maturing intensity that causes because of the concrete mix dispersion can be reduced, and the cohesive force of maturing and reinforcing bar can be improved.The underwater concrete engineering, the slope protection works in sea, river, rivers and lakes, the dam foundation that can be applicable to Tall Building Foundation are washed in a pan recovery project, the back cover engineering of bridge foundation open caisson and the antiseptic project of underwater steel construction thing at empty position by water.
2, the manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention, technology is simple, cost is lower, compare approximately low 25% with common non-dispersible underwater concrete flocculation agent cost.
Embodiment
Embodiment 1
The manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention-1.In polyethylene plastic bag, add 1 weight part acrylamide monomer, the solid state polyvinyl alcohol of 0.15 weight part is dissolved with 1 parts by weight of deionized water in advance, add wherein then, add 3 parts by weight of deionized water again, said mixture is heated to 30 ℃, in plastics bag, feed nitrogen 15min, in plastics bag, add 0.01 weight part hydrogen peroxide afterwards again, 0.01 weight part ferrous ion compound ferrous sulfate carries out polyreaction, after the polymerization 6h with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, pulverization process is made acrylamide-polyvinyl alcohol copolymer powder, i.e. flocculant of modified polyacrylamide-1.
Embodiment 2
The manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention-2.In acrylamide-polyvinyl alcohol copolymer powder that the manufacture method identical with embodiment 1 made, mix the naphthalene sulfonic acidformaldehyde condensation product powder of 2 weight parts, make flocculant of modified polyacrylamide-2 by its 1 weight part.
Embodiment 3
The manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent of the present invention-3.In polyethylene plastic bag, add 1 weight part acrylamide monomer, add again and use 1 parts by weight of deionized water dissolved, 0.15 weight account polyethylene alcohol in advance, add 3 parts by weight of deionized water again, be heated to 30 ℃, feed after the nitrogen 15min, add and carry out polyreaction with 0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, after the reaction 6h, gained acrylamide-polyvinyl alcohol copolymer is made acrylamide-polyvinyl alcohol copolymer powder, i.e. flocculant of modified polyacrylamide-3 through granulation, drying, pulverization process.
Embodiment 4
Manufacture method as correlated polyacrylamide flocculant.In polyethylene plastic bag, add 1 weight part acrylamide monomer, 3 parts by weight of deionized water, be heated to 30 ℃, feed nitrogen 15min, add 0.0007 weight part Ammonium Persulfate 98.5 afterwards, 0.0007 weight part sodium bisulfite carries out after polyreaction, the polymerization 6h gained polyacrylamide polymers being obtained polyacrylamide flocculant through granulation, drying, pulverization process.
Flocculant of modified polyacrylamide 1-3 that is made by embodiment 1 to embodiment 3 and embodiment 4 make is used for the underwater concrete performance test that correlated polyacrylamide flocculant prepares and lists in table 1, table 2, table 1 is the slump test of underwater concrete mixture, table 2 is the underwater concrete compressive strength test, and wherein underwater concrete mixture proportioning by weight is as follows:
Cement: water: sand: stone :=1: 0.44: 1.5: 2.3
Wherein flocculant of modified polyacrylamide-2 is by 0.03 weight part for the flocculation agent volume, and all the other are by 0.02 weight part.
Table 1 underwater concrete slump consistancy test
The flocculation agent kind | The slump of underwater concrete mixture, cm | |
0min | 60min | |
Flocculant of modified polyacrylamide-1 | 60 | 59 |
Flocculant of modified polyacrylamide-2 | 60 | 58 |
Flocculant of modified polyacrylamide-3 | 60 | 59 |
Polyacrylamide flocculant-Comparative Examples | 38 | 9 |
The compressive strength test of table 2 underwater concrete
The flocculation agent kind | Underwater concrete ultimate compression strength, MPa | |
7 days | 28 days | |
Flocculant of modified polyacrylamide-1 | 27 | 36.5 |
Flocculant of modified polyacrylamide-2 | 26 | 36 |
Flocculant of modified polyacrylamide-3 | 26 | 36 |
Polyacrylamide flocculant-Comparative Examples | 24 | 31 |
Claims (7)
1, a kind of modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, add 0.005~0.01 weight part hydrogen peroxide after feeding nitrogen 15min, 0.005~0.01 parts by weight of ferrous sulfate, carry out polyreaction, after polyase 13~6h with the acrylamide-polyvinyl alcohol copolymer of gained through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
2, modified polyacrylamide for concrete keeping together underwater flocculation agent according to claim 1, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.15 weight account polyethylene alcohol in advance, add 3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add 0.01 weight part hydrogen peroxide afterwards, 0.01 parts by weight of ferrous sulfate, carry out polyreaction, after the polymerization 6h with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
3, modified polyacrylamide for concrete keeping together underwater flocculation agent according to claim 2 is characterized in that containing 2 weight part naphthalene sulfonic acidformaldehyde condensation product powder by 1 weight part acrylamide-polyvinyl alcohol copolymer powder mixes.
4, a kind of modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.005~0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polyase 13~6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
5, modified polyacrylamide for concrete keeping together underwater flocculation agent according to claim 4, it is characterized in that containing by adding in the 1 weight part acrylamide monomer and use 1 parts by weight of deionized water dissolved, 0.15 weight account polyethylene alcohol in advance, add 3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polymerization 6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, acrylamide-polyvinyl alcohol copolymer powder that pulverization process is made.
6, a kind of manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that in 1 weight part acrylamide monomer, adding and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add 0.005~0.01 weight part hydrogen peroxide afterwards, 0.005~0.01 parts by weight of ferrous sulfate is carried out polyreaction, after polyase 13~6h with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, pulverization process is made acrylamide-polyvinyl alcohol copolymer powder.
7, a kind of manufacture method of modified polyacrylamide for concrete keeping together underwater flocculation agent, it is characterized in that in 1 weight part acrylamide monomer, adding and use 1 parts by weight of deionized water dissolved, 0.05~0.15 weight account polyethylene alcohol in advance, add 2~3 parts by weight of deionized water again, be heated to 30 ℃, feed nitrogen 15min, add afterwards and carry out polyreaction with 0.005~0.01 weight part CAN of 0.1 weight part nitric acid dissolve in advance, polyase 13~6h afterwards with gained acrylamide-polyvinyl alcohol copolymer through granulation, dry, pulverization process is made acrylamide-polyvinyl alcohol copolymer powder.