CN1188780A - Porcelain surface paint - Google Patents
Porcelain surface paint Download PDFInfo
- Publication number
- CN1188780A CN1188780A CN97107936A CN97107936A CN1188780A CN 1188780 A CN1188780 A CN 1188780A CN 97107936 A CN97107936 A CN 97107936A CN 97107936 A CN97107936 A CN 97107936A CN 1188780 A CN1188780 A CN 1188780A
- Authority
- CN
- China
- Prior art keywords
- water
- base
- filler
- paint
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An enamel-like paint is prepared from basic materials including water, nonyl-propyl emulsion, polyvinyl acetate emulsion, and carboxymethyl cellulose, and filler containing light calcium carbonate, heavy calcium carbonate and barium sulfate through mixing, and features water-base paint, no poison, combustion and corrosion, high water-proof, antialkali and anticorrosion nature, high weatherability and adhesion to wall, high compactness and hardness of painted surface, and easy coating.
Description
The present invention relates to a kind of coating composition, particularly a kind of porcelain surface paint.
Coating series such as toughened paint, ceramic glaze paint is because dense, the calcification of blade coating facing, thus scrubbing resistance, hardness height, but only be applicable to blade coating.As then not making facing dense, so can not reach the effect of blade coating with brushing.High viscosity agglomerative polyvinyl alcohol easily brush is opened, and infiltration is too many, can brush out though reduce its colloid concentration, can make the not anti-wiping of facing, even touches with hand, and ash is promptly arranged on hand.Hardness is not high though emulsion paint is applicable to blade coating.
The purpose of this invention is to provide a kind of can the brushing and the high porcelain surface paint of surface hardness.
Task of the present invention realizes with following mode: the present invention by with water, the ninth of the ten Heavenly Stems acrylic emulsion, aqueous polyvinyl acetate emulsion, carboxymethyl cellulose be the base-material formed of main raw material and by being that filler that raw material is formed mixes and constitutes with light calcium carbonate, barium sulfate and water-ground limestone, the usage ratio of base-material and filler is a base-material: filler=100: 30--45.The main raw material usage ratio of base-material is a water: the ninth of the ten Heavenly Stems acrylic emulsion: aqueous polyvinyl acetate emulsion: carboxymethyl cellulose-100: 20-25: 10--20: 0.1-0.2.The raw material usage ratio of filler is: light calcium carbonate: barium sulfate: water-ground limestone=100: 25--40: 60--75.
The present invention is aq. type coating, and is nontoxic, do not fire and non-corrosiveness, and excellent water tolerance, anti-alkalescence, weathering resistance and anti-scrubbing character are arranged, and metope is had good adhesivity.It is good that this paint brush is covered with paint, lacquer, colour wash, etc. the surface current levelling, the easy brush application of plate, and the anti-xerotripsis of facing, wash, and firm compact, the hardness height has overcome the shortcoming of emulsion paint difference of hardness, must not make bottom layer treatment during construction, long and oxidation jaundice of the time of can not being stranded of filming.Coating has fabulous flexibility, and coating is difficult for chapping, and good cracking resistance line is arranged.Be applicable to the surface decoration coating of body of wall or other facing.
Below the present invention is described in further detail: the YX-301 acrylic emulsion in the ninth of the ten Heavenly Stems that the present invention produces with resin copolymerization such as VEOVA is a base-material, improve its emulsifying property and thermoplasticity with the Vinyl Acetate Copolymer fat liquor, because the ninth of the ten Heavenly Stems, the Calcium ion stability of acrylic emulsion was good, so can adopt calcic class pigment extender and stopping composition, thereby greatly reduce the cost of coating.The usage ratio of base-material and filler is 100: 40.The main raw material amount ratio of base-material be 100 parts in water, the ninth of the ten Heavenly Stems 25 parts of acrylic emulsions, 10 parts of aqueous polyvinyl acetate emulsions (PVAC), 0.1 part of carboxymethyl cellulose.And can add 0.15 part of dibutyl phthalate (0.12 part-0.18 part of amount ranges) and make softening agent, and can add 0.15 part of alcohol and make defoamer (amount ranges is at 0.1 to 0.15 part).The raw material amount ratio of filler is: 28 parts of light calcium carbonates, 8 parts in barium sulfate, 19 parts of light calcium carbonates.
Its making processes: be ready to raw material by said ratio,, place in the reactor, heat, stir, disperse to 60 ℃ with adding acrylic emulsion in 25 parts of ninth of the ten Heavenly Stems in 100 parts of water.Cool to the carboxymethyl cellulose that adds 0.1 part of dilute with water after 40 ℃, the dissolving back adds 10 parts of aqueous polyvinyl acetate emulsions, stir, reacted 30 minutes, add softening agent O-phthalic ester dibutylester, add sanitas, wetting agent and defoamer alcohol then successively, can obtain base-material of the present invention.Again base-material and filler are placed in the stirrer in proportion to stir, pour paste roller mill into after stirring and fully grind, promptly make porcelain surface paint.Can it barrelling is standby.
Claims (3)
1. porcelain surface paint, it is characterized in that by with water, the ninth of the ten Heavenly Stems acrylic emulsion, aqueous polyvinyl acetate emulsion, carboxymethyl cellulose be the base-material formed of main raw material and by being that filler that raw material is formed mixes and constitutes with light calcium carbonate, barium sulfate and water-ground limestone, the usage ratio of base-material and filler is: base-material: filler=100: 30--45.
2. according to the described porcelain surface paint of claim 1, it is characterized in that the main raw material usage ratio of base-material is:
Water: the ninth of the ten Heavenly Stems acrylic emulsion: aqueous polyvinyl acetate emulsion: carboxymethyl cellulose=100: 20--25: 10--20: 0.1--0.2.
3. according to the described porcelain surface paint of claim 1, it is characterized in that the raw material usage ratio of filler is:
Light calcium carbonate: barium sulfate: water-ground limestone=100: 25--40: 60--75.