CN1187899A - Non-water permeating power transmission cable - Google Patents
Non-water permeating power transmission cable Download PDFInfo
- Publication number
- CN1187899A CN1187899A CN95197903A CN95197903A CN1187899A CN 1187899 A CN1187899 A CN 1187899A CN 95197903 A CN95197903 A CN 95197903A CN 95197903 A CN95197903 A CN 95197903A CN 1187899 A CN1187899 A CN 1187899A
- Authority
- CN
- China
- Prior art keywords
- cable
- filling compound
- polymer
- water
- filling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A power transmission cable and method of making such cable including first and second filling compounds which function to prevent degradation in cable performance as a result of the permeation of water through the polyethylene sheath of the cable and which do not liquefy at high temp. The first filling compound includes a gel matrix having a water reactive polymer dispersed therein and fills the space inside the outer jacket of the cable and outside of the metallic shield that surrounds the conductor (s). The second filling compound includes a gel matrix and water reactive polymer, as well as a material which makes the second compound electrically conductive, and fills the space between the conductor and the insulation surrounding the conductor.
Description
The present invention relates to a kind of alternating current (AC) power transmission cable.More particularly, power cable provided by the present invention can not resemble that the intrusion owing to water is damaged insulation property traditional power transmission cable.
Water is penetrated in the power transmission cable and destroys the existing a lot of records of (troubling) phenomenon of its insulation property.Briefly, this phenomenon is that it is inner and condense in polyethylene insulation screen inside because the polyethylene layer of steam permeable power cable enters.Thereby this condensate of gathering has facilitated electrochemical reaction to cause the decreased performance of cable, and this is at United States Patent (USP) 5,010,209 and corresponding European patent application EP 0416728A2 in existing more complete argumentation.This patent documentation has been introduced some trials of the well-known problem of enumerating in the relevant solution United States Patent (USP) 4,703,132.Though the problem that above-mentioned United States Patent (USP) and european patent application proposed also attempts to be overcome as everyone knows, problem does not achieve a solution always.The present invention be directed to same problem and the method that adopts in the listed patent document of the preceding paragraph improved.Specifically, United States Patent (USP) 4,703,132 have narrated a kind of filling compound and the cable that includes this filling compound, this filling compound is made up of a kind of low-molecular-weight and the rubber that mixes the small amount of fines material, it is swelling after absorbing moisture content, and quality is enough soft, must not use extrusion equipment just can be coated onto on the conductor.As indicated in this patent, filling compound is coated onto on the lead, the formation concentric layer is intertwined, then when the lead that has filling compound is twisted together, by extruding covering, this stress control layer fills up the space in the wire external layer outer surface of bundle conductor fully by a kind of traditional semiconductor stresses key-course.Being coated with the adhesive tape that last layer is filled with semi-conducting rubber then, is the insulating barrier of extruding and other layers of all having done to describe in detail in second hurdle of this patent below again.
When patent 4,703, when 132 described filling compounds are painted on one deck of lead, can will scribble the conductor layer of this filling compound thereon by the container of water swellable particles of material is housed, and in the mode on the filling compound that particulate is sticked to exposure they are dispelled, come like this this filling compound is exposed in the particulate of water swellable material.The third column of this patent is also advised and water swellable powder and this filling compound can be mixed and be coated on the conductor with the same manner.Yet this patent is not introduced mixture how to make this mixture and filling compound and powder and how to be solved foregoing problems by means of the high hydrophobicity energy of filling compound.In fact, filling compound has so hydrophobic property, makes it stop interaction between Powdered water absorbent and the water.
Though its objective is and to overcome the thorny problem that These characteristics is arranged, United States Patent (USP) 5,010 in the statement once of invention described in the list of references, 209 existence clearlys show true really not so, 5,010,209 promulgations are given and patent 4,703, the 132 identical tissues and same thorny problems of also touching upon.Patent 5,010,209 discloses the application to identical filling compound and water swellable material, but employing is so-called spiral extension hardware, it is around insulation screen, and each hardware has the particulate of water swellable material at least at its neighboring edge.As patent 4,703,132 do not provide the way that solves this thorny problem the same, patent 5,010, and 209 also fail to provide its solution.
United States Patent (USP) 4,703,132 described cables yet have problems on making.When the polyethylene cover of this cable or overcoat were expressed on the conductor that scribbles filling compound, temperature can be high enough to melt the filling compound (having or do not have the described water swellable material of this patent) that is coated in the conductor outside.Therefore be necessary in manufacture process, to take some steps protection filling compounds to make it not be exposed under the high like this temperature or adopt infusible filling compound.
The present invention relates to a kind of power transmission cable, its be not subjected to the still unsolved problems such as decreasing insulating that make power transmission cable because of humidity invade, and fill with a kind of composition, said composition can not melt under insulating barrier is expressed into temperature on the cable.The present invention includes a kind of cable, the core that this cable is made up of one or more conductor, around the insulating barrier of this conductor, around the layer of metal of this insulating barrier and/or plastic shielded, be expressed into one layer of polymeric screen and one or more filling compounds on this metal screen layer.Space between polymer shield layer and metal or the plastic shielded outer surface is with first kind of filling compound filling, this filling compound is made up of a kind of infusible and nonconducting gel-type vehicle and a kind of water absorbent polymer of being heated, this water absorbent polymer is a kind of superabsorbers, is made up of the main polymer chain that contains side ion radical (pendant ionic groups).The metal of space between each conductor and conductor and innermost layer or plastic shielded between the space with second kind of filling compound filling, in general this filling compound and first kind of filling compound are made up of identical materials, specifically, be a kind of water absorbent polymer to be distributed in a kind of infusible gel matrix material of being heated make, this filling compound also comprises a kind of semi-conducting material.
The present invention also provides a kind of method of making power transmission cable, it may further comprise the steps: prepare first kind of filling compound and second kind of filling compound, first kind of filling compound is a kind of water absorbent polymer to be distributed in a kind of infusible gel matrix material of being heated make, and second kind of filling compound then is a kind of water absorbent polymer and a kind of semi-conducting material to be distributed to make in a kind of infusible gel matrix material of being heated; Second kind of filling compound forced to be pressed in the container under pressure, and one or more conductor passed pressurization filling compound in the container, the import and the outlet that promptly allow conductor dbus cross container, filling compound just is expressed on the conductor and/or in the space between each lead as a result; Coat insulating barrier, metal and/or the plastic shielded layer and the outer polymer cover layer of above-mentioned characteristic again, and with outside first kind of filling compound filling screen and the space of polymer covering inboard.
Come now referring to accompanying drawing, Fig. 1 is the schematic diagram that the method and apparatus of the power transmission cable that contains gel combination of the present invention is made in expression.
Fig. 2 is the broken-open perspective view of a kind of power cable made from equipment shown in Figure 1.
As if gel-type vehicle in first kind of cable of the present invention and the second filling compound is the front The gel-type vehicle that is used for this class cable filler compound of mentioning is characterized in hydrophobicity, thus it Formed in the cable the diffusion of water and/or the initial shielding of migration. Yet, when water exists, this Trickle powdery polymer particle in the bright Cable gels just to the adjoining water of gel-type vehicle in move. This kind effect can obtain in this gel promoting that it is so that the water imbibition polymerization by the hydrophily material is added to Thing discharges the adsorbed water of making a return journey, and this is because the electrification between the ion base of moisture and water imbibition polymer Learn and attract event. When in a single day water contacts with the polymer that discharges from gel, because water and polymerization The combination of thing and form a kind of full-bodied material, thus so that usually residing in power transmission cable It is impossible that fluid motion under the fluid static pressure becomes. Polymer condenses to seeing through the insulation layer and is gathered in certain The attraction of the moisture content at place will cause producing at this place the accumulation of high-viscosity material, and this passes through to produce in inside Counter-pressure stops water vapour further to penetrate polyethylene layer (then condensing again) effectively, thereby prevents The generation of aforementioned troubling phenomenon, otherwise this kind phenomenon will go out owing to the accumulation of extra moisture content Existing.
Therefore, utilization of the present invention exists the water of assembling and condensing to solve aforementioned thorny asking in polyethylene Topic. It has done basic change in the mode that overcomes this problem really, and for example it provides a kind of and contains The cable of filling compound is not that the way of being commonly used in the prior art cable before adopting is arranged moisture content Except cable or with moisture content, siphoning away, but recognize that moisture content penetrates in the cable with the form of water vapour Be inevitably, when this kind phenomenon truly occurs, utilize the water that exists to produce a kind of buffer brake Barrier stops condensate water further to be assembled at this place thus, thereby has avoided the appearance of troublesome problem.
The water absorbent polymer that is suitable for as cable filler compound of the present invention is those main chains with side ion radical, and this side ion radical is attached on the polymeric chain, and preferably the polymer of monomers of non-natural existence makes it not too responsive to bacterial degradation.This ion radical can be carboxylate, sulfate, phosphate, sulfonate, phosphonate, ammonia, perhaps any other groups that can become electrified body when being exposed in the water.Wherein preferred polycarboxylate.Preferred carboxylate polymer is made by following material: unsaturated α, β-ethene list and two carboxylic acid and/or acid anhydrides are as acrylic acid, α-Jia Jibingxisuan, Beta-methyl acrylic acid, maleic acid, the acid of good fortune horse and separately maleic anhydride and Fu Ma acid anhydrides.Successful especially is adopts the diacrylate ester polymer, is referred to as polyacrylic acid or acrylic acid usually, and their derivative, and their anionic carboxylic acid root is when being exposed to aqueous conditions following time, along the very strong negative electrical charge of polymer chain generation.Can adopt the different kinds of ions form of these polymer salts, in the middle of them including, but not limited to alkali metal, as lithium, sodium, potassium; Perhaps alkaline-earth metal is as magnesium, calcium, strontium, barium, zinc or aluminium.Used salt depends on the chemical valence attached to the anion base on the main polymer chain.The polymer of this class polyacrylic acid derivative can obtain from a plurality of producers, comprising DOW chemical company, and the fine alkane wire chemical of Stockhausen limited company and Hoechst company etc.
Though preferred water absorbent polymer is a polycarboxylate, but some other have the super absorbent polymer that is connected in the ion radical on the main polymer chain to use effect also good, they comprise: acrylate, acrylamide, methacrylate, Methacrylamide, acrylonitrile, methacrylonitrile, triethyl group and/or tetraethyl ethylene glycol, acrylate, and the starch-grafted polymer of these polymer such as starch polyacrylonitrile graft polymers, cellulose and cellulosic derivative such as carboxylic acid methyl cellulose etc.Except top listed producer, this base polymer also can be from Proctor ﹠amp; Gamble company and cereal processing company obtain.This base polymer was all once done introduction in many patents, in following patent literature (but being not limited to these documents) water absorbent polymer once was described:
U.S. Patent number:
3,589,364 4,442,173 European Patent Application No.: 158,959
3,661,815 4,443,312
3,669,103 4,446,261 Japanese patent application No.:
3,880,751 4,497,930 5,125,871
4,105,033 4,626,063 59?3299
4,129,544 4,690,971
4,295,987 4,849, though 484 polymer dispersed with cellulose and cellulose derivative work when being formed for composition of the present invention in gel-type vehicle in the above described manner, have biodegradable at this base polymer after after a while.Therefore, the polymer of monomers that non-natural exists is collectively referred to as " the inanimate object degraded " polymer owing to their biodegradation is very weak, and they are preferably used than the polymer of cellulose and cellulose derivative in this manual.For example, aforesaid acrylic acid polymer and derivative thereof still have anti-degradation capability through after the several years; Test shows that this base polymer is not through occurring any signs of degradation in 1 year.
Water absorbent polymer is incorporated in the filling compound of cable of the present invention by about 5% to about 33.3% concentration of filling compound weight, and concrete concentration depends on selected particular polymers.Though all can obtain satisfied result (so this scope described in use " approximately " this speech) when the concentration of contained polymer is in the two ends of aforementioned proportion scope in the composition, concentration is preferably approximately with 10% to 15%.As general standard,, then preferably adopt the polymer concentration of higher concentration if use the polymer of cellulosic polymer or cellulose derivative.
There is multiple composition to be used as gel-type vehicle.This matrix should make polymer be evenly distributed in the gel fully.Will change the viscosity of gel below and do an explanation, it depends on multiple factor, comprises the employed method of filling compound lead-in cable.
The gel-type vehicle that is used for filling compound comprises silicones, oil/hydrocarbon lubricating oil, full-bodied ester class, ethylene glycol, polyethylene glycol, olefine and fluorocarbon.The mixture of polyolefin glycol, poly alpha olefin and polyisobutene also can use, and the hydrocarbon lubricating oil of this class mixture and various molecular weight is preferred for the gel-type vehicle of cable filler compound of the present invention.Oils gel-type vehicle in use by weight concentration is about 40% to about 95 to be favourable, and this part depends on the use of the thickener that cannot not be heated moltenly.Preferred concentration depends on specific material, is about 40% to about 85% by weight.
Hydrophobic gel-type vehicle makes it have a kind of coated polymeric also in fact with polymer and the isolated tendency of water.A spot of hydroaropic substance is added in this class hydrophobic gel matrix offsets this tendency.Hydroaropic substance seems to provide a conduit that water is contacted with the water living polymer, thereby makes polymer move in the water.Have a variety of materials to be suitable for as the hydroaropic substance in the cable filler compound of the present invention (second kind of filling compound will mentioning particularly), in use percentage by weight approximately is from 1% to about 15%.Adopt monobasic, binary and the polyalcohol of various straight chains and branched structure, comprise that various polyolefin glycols and composition thereof and its derivative, various alkanols and composition thereof and derivative obtained special success.For example, isopropyl alcohol is the same with 2-Ethylhexyl Alcohol all to be used well as adopting with the copolymer of ethylene glycol, hexylene glycol and the polyolefin glycol of oxirane and the random replacement of expoxy propane.Other are suitable for comprising as the hydroaropic substance in the cable filler compound of the present invention: the following semi-conducting material that will be described in more detail, the unrighted acid of monoene and polyenoid and the mixture of aliphatic acid, as oleic acid, palmitoleic acid, linolenic acid, linoleic acid, the washing agent that can buy on tall oil (wherein containing oleic acid) and the various market and the mixture of surfactant and washing agent and/or surfactant, as sorbate list-9-octadecylene acid esters polyoxy-1,2-second two bases and 2,4,5,9-tetramethyl-5-decine-4, the derivative of 7-glycol.
In the gel-type vehicle of cable filler compound of the present invention, use thickener required to be heated not that meltdown property and viscosity are good for obtaining.Suitable thickening comprises those well-known material, gel and lubricating grease such as paraffin and vaseline, microspheroidal polyethylene, styrene-ethylene butylene-styrene (S-EB-S) block polymer (as those products of buying according to the trade mark of KRATON (shell chemical company)), coking silica, organophilic clay such as bentonite and hectorite, soap class such as metallic stearates with oil and fluorocarbon oil thickening in the industry, and urea.
The employed amount of thickener depends on desired viscosity, thickener therein particular fluid and adopted certain thickener or several thickener.Usually, the concentration of used thickener is about 0.4% to about 24% of gel combination by weight.For example, if close organic substance clay such as the BARAGEL 3000 (N.L. chemistry limited company) that self activates is used for as oleogel matrix as thickener, the preferred concentration of thickener is between about 5% to about 10% by weight.Yet, the concentration of this class thickener is decided to be from about 4% to about 15% in use achieves success.If petroleum hydrocarbon, for example, the liquid state of the mixture of the paraffin of aliphat or naphthene series or two kinds of paraffin is used for the thickening of gel-type vehicle, then the amount of paraffin that adds as thickener or vaseline preferably about 0.4% to about 12% scope.The mean molecule quantity of preferred paraffin is 200 to 1000, and this class paraffin is used to prepare filling compound, and its viscosity depends on the ratio that thickener is shared, generally is 5 to 200 centistokes in the time of 40 ℃.
Particularly preferred thickener has comprised the mixture of the various materials of listing above, this hybrid thickener can comprise as account for the gel combination total weight about 4% to about 10% between close organic clay such as bentonite, account for paraffin or vaseline between the total weight about 2.1 to about 12%, the microspheroidal ethene (or polyethylene) or the S-EB-S block polymer that account for the coking silica between the total weight about 0.5% to about 9.81% and account for total weight about 0.4% to about 18%.
Cable filler compound of the present invention can have various viscosity according to making needs.About 90,000 centistokes when the gel viscosity excursion of general preferred employing is about 2 centistokes to 40 ℃ in the time of 100 ℃.The problem that the viscosity of composition is just selected according to the needs that use, thereby there is no need to be confined in the above-mentioned preferred viscosity specification limit.
The cable of the present invention of being used for of several sections narrations in front is filled the inboard filling compound with around the space between outside the outermost metal of conductor or the plastic shielded layer of outermost layer polyethylene coating or cover layer, they is called first kind of filling compound here.In order to prepare the second kind of filling compound that is used for cable of the present invention, adding is a kind of in first kind of filling compound makes first kind of filling compound have the material of electric conductivity.Second kind of filling compound is to be used for packing ring around on lead, the lead and the space between the outer surface of lead and outermost metal or the plastic shielded layer inboard, perhaps comprise under the situation of stranded conductor at a cable, this second kind of filling compound be the not only space between space between each strand of filling lead but also the filling bundle conductor outside and the outermost screen inboard then.
This class electric conducting material comprises carbon ink, graphite, silica, talcum, and titanium dioxide and other are the known various types of clays of people in the industry.Also comprise the such class material of water-soluble salt solution within the scope of the invention, halide, hydroxide, carbonate, bicarbonate, nitrite, nitrate, sulphite, sulfate, phosphite and the phosphate of preferred sodium, potassium, calcium, magnesium, manganese, iron and copper.Particularly preferably be magnesium carbonate, magnesium chloride, magnesium sulfate and magnesium phosphate solution, and sodium salt and calcium salt, as the solution of sodium chloride and calcium chloride, sodium carbonate and calcium carbonate, sodium acid carbonate, sodium acetate, sodium metasilicate, natrium citricum, sodium fluoride and calcirm-fluoride, prodan, sodium phosphate and NaOH and calcium hydroxide.The amount that electric conducting material is incorporated in second kind of filling compound of cable of the present invention depends on the certain material that is adopted, material and the desired conductive characteristic of cable operational factor that is used as the oil ingredient of filling compound.Usually, the use amount of electric conducting material is by weight to the calculating recently of weight, if promptly the oil ingredient of gel-type vehicle is approximately 100 parts, then this kind material is approximately 15 to 150 parts.
Cable filler compound of the present invention also has immobilising characteristic under 200 ℃ and higher temperature except having water absorption character.Filling compound of the present invention so can not occur softening with regard to the high temperature that is able to take cable and produces under the sunlight exposure and/or at big load transmission of electric energy the time and viscosity reduces, and if in a single day viscosity reduce filling compound and will flow at (position that low spot is arranged in cable) or even ooze from cable along cable.
Be first kind and the applicating example of second kind of filling compound special use in cable of the present invention below.According to the example of the filling compound of the present invention preparation is not to be restriction to range of application of the present invention, but to being used for implementing illustrating of compound of the present invention.
Embodiment 1
The preparation of first kind of filling compound is to use the polyisobutene lubricating oil (AmocoINDOPOLL-100) of 20 weight portions, the polyolefin glycol of the poly alpha olefin of 41/2 weight portion and a weight portion (POLY-G9150 of Olin chemical company).Polyolefin glycol is a kind of random copolymer, contains 75% oxirane and 25% expoxy propane, and its mean molecule quantity is 12,000 to 15,000, and its hydroxyl value is that every gram has 5 to 10 milligrams KOH.The viscosity of polyisobutene in the time of 38 ℃ is 210-227 (pressing American Standard of Testing Materials ASTM D-445), and viscosity index (VI) is 95 (ASTMD-567).The poly alpha olefin that is adopted is a kind of long-chain poly alpha olefin SHF-61 that is produced by the Mobil oil company, and viscosity is 30.5 (ASTM D-445) in the time of 38 ℃, and viscosity index (VI) is 132 (ASTM D-2270).The product poly alpha olefin SHF-61 of Mobil company that gives an example used is that molecular weight is 200 to 800 typical hydrocarbon.This SHF-61 product is a kind of oligomer of 1-decene.Poly alpha olefin has gratifying range of viscosities, 100 centistokes during 2 centistokes to 40 during from 100 ℃ ℃.
The mixture of 12 parts of generations is mixed mutually with a coking silica as thickener.The gel-type vehicle of this generation is to be stirred by the water absorbent polymer of the gelatinous mass of two parts of weight and a weight to form, and this polymer is the part sodium salt of cross linked polyacrylate, and what select for use here is the 2-polyacrylate that DOW chemical company produces.In fact use a kind of filling compound that is equal to also can reach same result, this filling compound has comprised the polyacrylic acid of selling with trade (brand) name FAVOR C96 (the Stockhausen limited company by Greensboro city, state, Carolina, U.S. north makes).When testing according to ASTM D150 regulated procedure, said composition presents is characterized as and has less than 2.3 dielectric constant and be approximately 0.01 the power consumption factor, and when testing according to ASTM D357, specific volume resistance is approximately 4.99 * 10
12Said composition does not melt when being heated to 200 ℃, and the water-responsive time less than 12 minutes is arranged.
Embodiment 2
Prepare the first kind of filling compound that is used for cable of the present invention according to embodiment 1 described method, it has following component (weight portion):
DRAKEOL 34 (Penreco company) 610
REOMET 39 (Ciba-Geigy company) 2.5
BENTONE (bentonite) 24 (NL chemistry limited company) 50
AEROSIL R74 (Degussa company) 20
FAVOR C96 (Stockhausen limited company) 150
MICROTHENE FA 640 (Quantum Chemical Corp) 157.5
When according to embodiment 3 described sequence tests, the feature that said composition presents is: dielectric constant is 2.12, and specific volume resistance is 5.91 * 10
12, and the power consumption factor is 0.01.When said composition is heated to 200 ℃, do not melt, and response time less than 10 minutes is arranged.
Embodiment 3
Polyester also is used to prepare first kind of filling compound of cable of the present invention.The molecular weight of polyester is 300 to 800, and viscosity is 25 to 100 centistokes in the time of 40 ℃.Polyester mixes with about 10% to 30% polymer phase.Adopted polyester is the ester of trimethylolpropane, pentaerythrite and triallyl mellic acid ester, and its result of the test is similar to the composition results among the embodiment 2.
Embodiment 4
The second kind of filler that is used for cable of the present invention mixed by following ingredients (by total amount percentage):
70% oil-rubber blend (seeing below)
8％CABLO?C800SF(Stockhausen)
5％BARAGEL?3000(Rheox)
15%665 grades of talcums (Montana talcum company)
2%PHINTEX XE 2 superconduction carbon blacks (Degussa company) wherein oil-rubber blend are made up of following ingredients (by weight percentage):
94.77％?N1500(Pennzoil)
3.3% KRATON 1701 (shell chemical company)
1.58% IRGANOX 1035 (Ciba-Geigy company)
The absorbent time of second kind of filling compound of 0.35% IRGAMET 36 (Ciba-Geigy company) is 11-12 minute, and dielectric constant is greater than 3.65, and specific volume resistance is less than 5 * 10
6, cone penetration is 152, the oily separating degree in the time of 80 ℃ after 24 hours is 0.8%.
Embodiment 5
The second kind of filling compound that is used for cable of the present invention mixed by following ingredients (by weight percentage):
82% oil-rubber blend (seeing embodiment 4)
5% AEROSIL R74 (Degussa company)
8% FAVOR C96 (Stockhausen limited company)
This mixed salt solution of the aqueous solution of 5% mixed metal salt is made by water and several calcium salt, sodium salt and magnesium salts, and the total concentration of all these salts is less than 1%.When carrying out above-mentioned test, the dielectric constant that records said composition is 3.22, and the power consumption factor is 0.0321, and specific volume resistance is 71.89 * 10
6
Embodiment 6
The second kind of filling compound that is used for cable of the present invention mixed by following component (by weight percentage):
77.5% oil-rubber blend (seeing embodiment 4)
4.5% AEROSILR74 (Degussa company)
8% FAVOR, 900 series polymers (Stockhausen company)
10% hybrid metal saline solution (seeing embodiment 5) is when carrying out above-mentioned test, and the dielectric constant that records this compound is 3.78, and power consumption factor number is 0.0356, and specific volume resistance is 28.7 * 10
5
Embodiment 7
The second kind of filling compound that is used for cable of the present invention mixed by following component (by weight percentage):
71.03％?N1500(Pennzoil)
2.47% KRATON 1702 (shell chemical company)
1.8% IRGANOX 1035 (Ciba-Geigy company)
1.31% IRGAMET 36 (Ciba-Geigy company)
4% AEROSIL 200 (Degussa company)
8% FAVOR, 900 series polymers (Stockhausen company)
2% polyethylene glycol
The aqueous solution of 10% salt-mixture (seeing embodiment 5) is when carrying out above-mentioned test, and the dielectric constant that records this compound is 6.95, and the power consumption factor is 0.2766, and specific volume resistance is 22.59 * 10
6, the water soak time is approximately 12 seconds.
* * * * *
Come referring to accompanying drawing 1 now, it has schematically represented to make the method and apparatus that includes the power transmission cable of first kind and second kind filling compound of the present invention.This cable as shown in Figure 2.This cable of indicating by reference number 10, in common knowledge as this area, in overcoat 14, include multiply cable or conductor 12.
In order to make cable 10, be pulled through the filled chamber 16 of lead 12 on being fixed on filling head bearing 18, in this chamber, second kind of filling compound 20 of cable of the present invention is extruded on the conductor 12 that contains cable core.Fig. 1 shows that five strip conductors 12 enter among each of five filled chambers 16.Filled chamber 16 on the filled chamber bearing 18 is connected with vibrating shaft 22 on a kind of bobbing machine 24 of pattern commonly used in the sector again and is vibrated, five leads in the filled chamber 16 are by a kind of fine finishining edge known in the art mouthful (sizing insert) (not expressing among the figure), so, be expressed on each bar lead 12 and the amount of second kind of filling compound in the space between the lead just by standardization.When lead 12 leaves on the bobbing machine 24, just be pooled to together. at this moment the semiconductor layer 26 of a routine (a kind of plastic material) just in the filled section of being illustrated by reference number 28 (because in the industry, knowing altogether) quilt around to or be expressed on the filling compound layer, semiconductor layer 26 has constituted the stress control layer of lead.Subsequent layer 26 is aggregated thing (as polyethylene) insulating barrier 30 and is expressed on the layer 26 at extruding zone 32 places around, this layer.The second plastics stress control layer 34 also can be expressed on the insulating barrier 30 at another extruded segment 34 places, also schematically shows among the figure.
On the metal screen layer made from copper or aluminium foil (band) 38 and 40 sections method spirals of knowing altogether with the industry are wound into by constriction around together and the lead that be insulated He be filled subsequently.After this, the lead of conductively-closed sent into be installed in filled chamber second filling head 42 with similar chamber 16, so that first kind of filling compound 44 is expressed into by on the electric wire 12 constriction, that insulated, that filled and that shielded and all around.After leaving filling head 42, this cable then is wrapped by the overcoat 14 that the extruded polymer material forms at extruding zone 46 places.
The second kind of filling compound 20 that is used for cable of the present invention got in the filling head 16 with pump under being similar to the temperature of room temperature and kept certain pressure so that it is expressed into lead 12.A kind of similar arrangement and condition also are used in second filling head, 42 places, are convenient to extruding of first kind of filling compound 44.
Claims (3)
1. power transmission cable comprises:
Center conductor;
One deck is around the insulating barrier of this lead;
One metal screen layer on this insulating barrier;
Be looped around the polyethylene cover on this metal screen layer;
First kind of filling compound between described polyethylene cover and said metal screen layer, and comprised a kind of dielectric gel that is dispersed with the water reactive polymer therein; And
Second kind of filling compound, between described center conductor and described insulating barrier, described second kind of filling compound contains the gel and the electric conducting material of the water reactive polymer that is dispersed in wherein.
2. according to the described cable of claim 1, also comprise stranded conductor, and have the described second kind of filling compound in the space between described each strand lead.
3 according to the described cable of claim 1, and wherein said gel-type vehicle contains oil and thickener.